• Journal of Dental Rehabilitation and Applied Science
• /
• v.26 no.3
• /
• pp.253-264
• /
• 2010

The purpose of this study is to know whether Yttrium-stabilized-tetragonal -zirconia-polycrystal(Y-TZP ceramic) gets enough shear bond strength for clinical uses by applying veneering composite resin through surface treatment on it and finally to compare it with the case of applying veneering porcelain. LavaTM zirconia frameworks(3M ESPE, Seefeld, Germany) were prepared. Group P was manufactured with LavaTM Ceram(3M ESPE, Seefeld, Germany) in cylindrical shape which has 4mm diameter, 5mm height. Group ZSR disposed sandblasting and applied silane, bonding agent and after that indirect composite resin was applied. Group ZRR got tribochemical coating by RocatecTM system(3M ESPE. Seefeld, Germany) and treated silane. Finally Group ZPR took the same treatment and applied LavaTM Ceram in the size of 0.3-0.5mm height. After burning out, sandblasting, HF and silane was applied. And then, indirect composite resin was applied. 1000 cycle thermocycling was performed in $5-55^{\circ}C$ and shear bond strength was measured. There were no significant differences between combining veneering porcelain to Y-TZP ceramic group and combining veneering resin to Y-TZP ceramic group in the aspect of shear bond strength (p>.05).

• Journal of dental hygiene science
• /
• v.12 no.2
• /
• pp.123-129
• /
• 2012

The aim of study was to compare the color parameters and mean color difference of porcelain specimens by different veneering technique in order to examine the effect of veneering technique on esthetics of yttria-stabilized tetragonal zirconia polycrystalline(Y-TZP) all ceramic restoration. Three groups of square-shaped core ceramic specimens(14mm in diameter and 0.3, 0.5, 0.7 mm) and two groups of veneering ceramic specimen were prepared for analysis. Color parameter($L^*,a^*,b^*$) and color difference of zirconia core squares and core-veneer specimens were measured with ShadeEye $NCC^{(R)}$ spectrophotometer, respectively. Mean color difference(${\Delta}E^*$)were calculated using color difference formula. Two-way analysis of variance(ANOVA) combined with a Tukey multiple-range test were used to analysis the data(${\alpha}=0.05$). ${\Delta}E^*$ values were not significantly affected by core thickness and veneering porcelain(p=0.083). The color differences(${\Delta}E^*$) of core-veneer specimens with 0.5, 0.7 mm-A1,A2,A3.5 shade were mostly below 3.7 which was within the clinically acceptable range, while color differences between 0.3 mm-A1,A2 showed more than 3.7. All-ceramic system has color characteristics that clinicians have to consider when selecting materials. Also, manufacturers of different porcelain systems must make every effort to achieve color reproducibility.

• Journal of dental hygiene science
• /
• v.14 no.1
• /
• pp.29-34
• /
• 2014

The purpose of this study was to evaluate the influence of low temperature degradation (LTD) on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP). The push-shear bond test method was used to investigate the core-veneer bonding strength of industrially manufactured Y-TZP core ceramic and manufacturer recommended veneering ceramic. Four groups from ceramic-zirconia specimens (n=28; n=7 per group) were assigned into four experimental aging conditions, namely storage in an autoclave at $134^{\circ}C$ for 0, 3, 5, 10 hours. Bonding strength was obtained using a universal testing machine with crosshead speed 0.5 mm/min. Data were statistically analyzed using one-way ANOVA and Tukey's test (${\alpha}=0.05$). In bonding strength test, the group which was treated with LTD showed lower bonding strength than no treated group. The ceramic-zirconia bonding strength was affected by LTD (p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in LTD with treated Y-TZP groups.

• Journal of dental hygiene science
• /
• v.13 no.3
• /
• pp.290-295
• /
• 2013

The purpose of this study was to investigate the shear bond strength between various commercial all-ceramic system core and veneering ceramics, and evaluate the clinical stability by comparing the conventional metal ceramic system. The test samples were divided into three groups: Ni-Cr alloy (metal bond), yttria-stabilized, tetragonal zirconia polycrystal (Y-TZP) (zirconia bond), lithium disilicate (lithium disilicate bond). The veneering porcelain recommended by the manufacturer for each type of material was fired to the core. After firing, the specimens were subjected to shear force in a universal testing machine. Load was applied at a crosshead speed of 0.50 mm/min until failure. Average shear strengths (mega pascal) were analyzed with a one-way analysis of variance and the Tukey test (${\alpha}$=0.05). The mean shear bond strength${\pm}$SD in MPa was $44.79{\pm}2.31$ in the Ni-Cr alloy group, $28.32{\pm}4.41$ in the Y-TZP group, $15.91{\pm}1.39$ in the Lithium disilicate group. The ANOVA showed a significant difference among groups (p<0.05). None of the all-ceramic system core and veneering ceramics could attain the high bond strength values of the metal ceramic combination.

• Journal of Technologic Dentistry
• /
• v.35 no.4
• /
• pp.271-280
• /
• 2013

Purpose: This study was to assess the effect of surface and heat treatment on the bond strength of veneering ceramics to zirconia. Methods: The specimens were divided into 7 groups according to surface treatment and heat treatment conditions prior to porcelain application. ten specimens from each group were subjected to a 3-point flexural test. In addition the influence of surface and heat treatment on surface roughness values and phase transformation of zirconia was evaluated. Statistical analysis was performed with one-way ANOVA and post hoc Tukey's test. Results: Bond strength ranged from $20.67{\pm}3.13MPa$ to $32.69{\pm}4.52$. Bond strength of surface treatment group was lower than that of control group but only $Al_2O_3$ sandblasting group was significant difference. Bond strength of heat treatment group was higher than that of surface treatment group but there was no statistical significance. Conclusion: Bond strength of veneering ceramics to zirconia was affected by surface and heat treatment.

• Journal of the Korean Academy of Esthetic Dentistry
• /
• v.24 no.2
• /
• pp.101-121
• /
• 2015

Zirconia polycrystalline (Y-TZP) showed better mechanical properties and superior resistance to fracture than other conventional dental ceramics. Zirconia-based ceramics have been successfully introduced into the clinic to fabricate fixed dental prostheses (FDPs), along with a dental computer-aided/computer-aided manufacturing (CAD/CAM) system. It has been clinically available as an alternative to the metal framework for fixed dental prostheses (FDPs). The most frequent clinical complication with zirconia-based FDPs was chipping of the veneering porcelain that was affected by many factors. Another option was full-contour zirconia FDPs using high translucent zirconia. Full-contour zirconia FDPs has many clinical advantages but it caused concern about the wear of antagonist enamel, because the hardness of Y-TZP was over double that of porcelain. However, many articles demonstrates that highly polished zirconia yielded lower antagonist wear compared with porcelains. In this article (1) advantages of full zirconia restorations, (2) clinical applications of zirconia restorations, (3) abutment preparation, (4) surface finish of zirconia restoration and antagonist enamel wear, (5) bond of zirconia with resin-based luting agents, (6) communication in clinical & lab.procedures for full zirconia restorations are reviewed.

• Journal of Technologic Dentistry
• /
• v.33 no.3
• /
• pp.193-202
• /
• 2011

Purpose: The aim of this study was to evaluate the effect of pre-treatment of core and hydrothermal treatment on the bond strength and flexural strength of ceramic veneered zirconia. Methods: 3Y-TZP specimens(KaVo Zr, $25mm{\times}3mm{\times}1mm$)were prepared by five pre-treatment methods and divided into seven groups including control two groups, subsequently the specimens veneered with the E-MAX ceram according to manufacturer's information(total specimen thickness 1.5mm). Two groups from ceramic-zirconia specimens(n=105, n=15 per group)were assigned into two experimental fatigue conditions, namely storage in an autoclave at $134^{\circ}C$ for 5h, thermo-cycling(3,000cycles, between 5 and $55^{\circ}C$, dwell time 45s, transfer time 2s). A flexural strength test was performed in a universal testing machine(crosshead speed: 0.5mm/min). Data were statistically analyzed using one-way ANOVA and Tukey's test(${\alpha}$=0.05). Results: The ceramic-zirconia bond strength value for liner application group(LLW, $27.3{\pm}3.8$) were significantly lower than those of the pre-treatment groups($30.72{\pm}5.3$). The ceramic-zirconia bond strength and zirconia flexural strength was not affected by thermo-cycling(p>0.05), whereas it was affected by storage in an autoclave at $134^{\circ}C$ for 5h(p<0.05). Conclusion: The results indicated that the ceramic-zirconia bond strength and zirconia flexural strength was affected by low temperature degradation.

• The Journal of Korean Academy of Prosthodontics
• /
• v.54 no.4
• /
• pp.354-363
• /
• 2016

Purpose: The aim of this study was to investigate whether the application of nano-structured alumina coating to the surface of Y-TZP could enhance the bond strength with resin cement. Materials and methods: A total of 80 zirconia plates were prepared and divided into four groups. : 1) airborne particle abrasion treatment (A) : 2) Rocatec treatment after airborne particle abrasion (R) : 3) nano-structured alumina coating treatment after polishing (PC) and 4) nano-structured alumina coating after airborne particle abrasion (AC). Alumina coating was formed by the hydrolysis of aluminium nitride (AlN) powder and heat treatment at $900^{\circ}C$. Coating patterns were observed with FE-SEM. Resin block was bonded to treated zirconia ceramics using resin cement. The shear bond strengths were measured before and after thermocycling. Results: The FE-SEM images show a dense and uniform nano-structured alumina coating structure, which enhances shear bond strength by increasing micro mechanical interlocking to resin cement. PC and AC groups showed higher shear bond strengths than A and R groups before and after thermocycling. A and R groups displayed significant drops in shear bond strength after thermocycling. However, PC and AC groups did not show any meaningful decreases in shear bond strength after thermocycling. Conclusion: Treatment of Y-TZP ceramics with nano-structured alumina coating could significantly increase their shear bond strength.

• The Journal of the Korea Contents Association
• /
• v.18 no.10
• /
• pp.361-367
• /
• 2018

The purpose of this study was to evaluate the influence of hydrofluoric acid etching treatment on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal(Y-TZP). Four groups of zirconia-resin cement specimens were prepared; 1) ZGS group (zirconia, no treatment), 2) ZGSH group (zirconia, hydrofluoric acid etching treatment) 3) H-ZGS group (Hybrid zirconia, no treatment) 4) H-ZGSH group (Hybrid zirconia, hydrofluoric acid etching treatment). The shear bond strength between zirconia and porcelain was measured using a Instron Universal Testing Machine(Model DBBP-500, Instron Corporation, Kyonggi, Korea). Data were statistically analyzed using independent t-test and two-way ANOVA(${\alpha}=0.05$). The ceramic-resin cement bonding strength was affected by hydrofluoric acid etching treatment(p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in hydrofluoric acid etching treatment with treated zirconia and hybrid zirconia groups.