• Journal of the Korean Wood Science and Technology
• /
• v.35 no.1
• /
• pp.36-43
• /
• 2007

Elemental analysis, SEM-EDX, X-ray diffraction (XRD) and IR analysis were adopted to examine the quality of charred woods excavated from the underground of the Daewoongjeon Hall of Youngguksa Temple, Youngdong-gun, Chungbuk, Korea. A large amount of calcium was detected in SEM-EDX analysis. The analyses of chemical elements suggested that completely charred wood was carbonized at about $500^{\circ}C$. The XRD results indicated the destruction of cellulose crystalline region. The IR analysis exhibited that thermal degradation of wood component was different depending upon the carbonization temperature. It can be suggested from the results that PEG with different molecular weights should be used for the conservation of excavated charred woods.

• Fire Science and Engineering
• /
• v.28 no.5
• /
• pp.58-63
• /
• 2014

Fire-resistance paints are supposed to become intumescent and diminish heat transfer along the steel frames in case of a fire. If unsatisfactory fire-resistance paints which do not satisfy their standard specification are used, it may result in a severe disaster. Because satisfactory fire-resistance paints are hardly discriminated from the unsatisfactory ones by a simple visual inspection, more reliable and convenient onsite evaluation methods are necessary. Here we report the preliminary study result on the fire safety testing method for fire-resistance paints using an X-ray analysis method. It was found that the existence and quantity of effective constituents in fire-resistance paints can be detected by the X-ray analysis method. X-ray fluorescence (XRF) analyses showed that P and Cl elements are much more enriched in fire-resistance paints, compared to normal paints. X-ray diffraction (XRD) analyses showed that ammonium polyphosphate is present as the main crystalline material in fire-resistance paints, but absent in normal paints. The X-ray analysis method is expected to be used for the onsite inspection of fire-resistance paints with the upcoming availability of portable XRF and XRD instruments.

• Cement
• /
• s.126
• /
• pp.65-71
• /
• 1992

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.2
• /
• pp.1-9
• /
• 2002

The intermetallic formation between Sn-Ag-(Cu) solders and metal pads in a real BGA package was characterized using SEM, EDS, and XRD. The intermetallic phase formed in the interface between Sn-Ag-Cu and Au/Ni/Cu pad is likely to be ternary compound of $(Cu,Ni)_6Sn_5$ from EDS analysis High concentration of Cu was observed in the solder/Ni interface. XRD analysis confirmed that $\eta -Cu_6 Sn_5$ type was intermetallic phase formed in the interface between Cu containing solders and Ni substrates and $Ni_3$Sn_4$ intermetallic was formed in the Sn-Ag solder/Ni interface. The thickness of intermetallic phase increased with the reflow times and Cu concentration in solder.

• Journal of the Korean Ceramic Society
• /
• v.34 no.2
• /
• pp.209-215
• /
• 1997

Aluminum nitride(AIN) thin films were deposited by reactive single ion beam sputtering using N2 or NH3 as reactive gas. The structural, compositional and optical properties of AIN thin films were characterized by XRD, GAXRD, TEM, SEM, XPS UV/VIS spectrophotometer, and FT-IR. All the deposited AIN thin films were amorphous by the analysis fo XRD and GAXRD. However, TEM analysis showed that AIN nano-crystallites were uniformly distributed in the films. The presence of Al-N bonds were also confirmed by FT-IR and XPS analyses. The optical bandgap of AIN films increased up to 6.2 eV and the transmittance was a-bout 100% in visible range with approaching the stoichimetric composition. Irrespective of using N2 or NH3 as reactive gas, the deposited AIN thin films had very smooth surface morphologies. Their refractive index ranged from 1.6 to 1.7.

• Journal of the Mineralogical Society of Korea
• /
• v.24 no.2
• /
• pp.119-131
• /
• 2011

The asbestos contents in some representative building materials were analyzed using JIS (Japanese Industrial Standard) X-ray diffraction (XRD) method. The changes in mineral composition during analysis process and problems in JIS method were also examined. XRD analysis of some representative domestic building materials used for roof, wall, ceiling, and floor indicates that slate have the highest asbestos content having 6.87~6.93% of chrysotile. Other building materials analyzed in this study also have 1.35~3.98% of chrysotile contents. The XRD analysis results of asbestos contents in some domestic building materials are presented in this study. This method is very effective for the asbestos content evaluation of building materials according to newly modified asbestos content regulation (Law of Industrial Safety and Health, 2007-26) that limits asbestos content less than 0.1% by Ministry of Employment and Labor. Small amount of tremolite as well as chrysotile were also observed in some samples. With consideration of crystal shape, contents and geological occurrence, it is considered that tremolite is an associated mineral of chrysotile and is not intentionally added. Complemental analyses with optical microscope and SEM/EDS are also necessary because XRD method cannot distinguish asbestiform from non-asbestiform. The XRD method applied in this study is very effective in the asbestos content analysis of building materials, specially building materials showing high asbestos concentration in residues due to the high loss rate with ashing and acid dissolution procedure.

• Journal of the Korean GEO-environmental Society
• /
• v.12 no.10
• /
• pp.5-12
• /
• 2011

Recently, NDS(Natural and Durable Stabilizer)method and other similar methods are composed of inorganic accelerating agent and the ultra-super fine cement have been studied as the ground improvement material in Korea. However, in the existing research, the chemical changing process of NDS in the strength development mechanism with the elapsed curing time and the principles of strength development did not give an explanation. For the popularization of the inorganic grout material, it determined that the mechanism verifying of the curing process had to be clearly preceded. Therefore, unconfined compression test, SEM and XRD analysis were performed by the elapsed curing time and were analyzed. In addition, the same trial for SGR method, that is the representative example of the water glass grout material, was selected as comparative target in order to distinguish properties of NDS more clearly. The result of experiment, the strength development mechanism of NDS could be investigated through the close correlation of the unconfined compression strength - SEM - XRD analysis, and excellence of a performance was confirmed.

• Polymer(Korea)
• /
• v.29 no.1
• /
• pp.87-90
• /
• 2005

In this study, we have examined the exfoliation behavior of layered clay during in-situ polymeriztion with styrene by using real-time XRD analysis. The 4C1 beam line at the Pohang Accelerator Laboratory (PAL) was used for this study. Different exfoliation behaviors have been shown to depend on the cation exchange capacity (CEC) of clay and the chemical structure of organic modifiers. For 10A-MMT and 15A-MMT having high CEC, no peak shifts were observed on real-time XRD analysis during polymerization. However, 2$\theta$ for 25A-MMT and VDAC-MMT, each having low CEC’s as well as aromatic benzene moieties and vinyl groups, respectively, decreased as polymerization time increased.

• Applied Chemistry for Engineering
• /
• v.28 no.3
• /
• pp.286-289
• /
• 2017

Synthesis of zeolite 4A was carried out to optimize the nanoparticle synthesis process using statistical experimental design method. The zeolite 4A was synthesized by controlling the concentration of the silicon precursor, sodium metasilicate (SMS), and characterized by XRD, SEM and nitrogen adsorption. In particular, the property of zeolite 4A can be determined by XRD analysis. Using the general factor analysis in the design of experiments, we analyzed main effects and interactions according to the reactor, reaction temperature and reaction time. The optimum reaction condition for the synthesis of zeolite 4A crystallinity was using an autoclave for 3 hours at $110^{\circ}C$. Furthermore, the optimal synthesis conditions of zeolite 4A with various crystallinity using Ludox as a silicon precursor were presented of what using both the surface and contour plot.

• Resources Recycling
• /
• v.21 no.3
• /
• pp.28-38
• /
• 2012

The purpose of this paper is to develop the alkali-activated concrete which uses 100% fly ash as a binder without any cement. The compressive strength of the mortar was examined depending on the chemical change in alkali-activator through SEM and SEM/EDS observations and the XRD analysis. It was found from the test that the higher molar concentration induced the greater effect on the initial strength, and that $Si^{4+}$ and $Al^{3+}$ were eluted relative to the compressive strength of mortar. In addition, it was confirmed that Al and Si were determined to be most influential ingredients on the microstructural development of the mortar, and that the different ingredient of the activator was almost no change in solidity from the XRD analysis.