• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.11
• /
• pp.1014-1019
• /
• 2006

The influence of the number of solution coatings on the densification of the PZT thick films was studied. PZT powder and PZT precursor solution was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were (A) PZT(80/20)/PZT(20/80), (B) PZT(70/30)/PZT(30/70) and (C) PZT(60/40)/PZT(40/60), (D) PZT(52/48)/PT. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 moth and the number of coating was repeated from 0 to 6. The porosity of the thick films was decreased with increasing the number of coatings and the PZT thick films with 6-times coated showed the dense microstructure and thickness of about $60{\mu}m$. A grain size was increased with increasing the coating number. All PZT thick films showed the typical XRD patterns of a typical perovskite polycrystalline structure. The relative dielectric constant of PZT thick films was improved 30-100% as the number of coatings.

• Tribology and Lubricants
• /
• v.32 no.4
• /
• pp.125-131
• /
• 2016

In recent years, thick ta-C coating has attracted considerable interest owing to its existing and potential commercial importance in applications such as automobile accessories, drills, and gears. The thickness of the ta-C coating is an important parameter in these applications. However, the biggest problems are achieving efficient coating and uniformity over a large area with high-speed deposition. Feasibility is confirmed for the ta-C coating thickness of up to 9.0 µm (coating speed: 3.0 µm/h, fixed substrate) using a single FCVA cathode. The thickness was determined using multiple coating cycles that were controlled using substrate temperature and residual stresses. In the present research, we have designed a coating system using FCVA plasma and produced enhanced thick ta-C coating. The system uses a specialized magnetic field configuration with stabilized DC arc plasma discharge during deposition. To achieve quality that is acceptable for use in automobile accessories, the magnetic field, T-type filters, and 10 pieces of a multi-cathode are used to demonstrate the deposition of the thick ta-C coating. The results of coating performance indicate that uniformity is ±7.6 , deposited area is 400 mm, and the thickness of the ta-C coating is up to 5.0 µm (coating speed: 0.3 µm/h, revolution and rotation). The hardness of the coating ranges from 30 to 59 GPa, and the adhesion strength level (HF1) ranges from 20 to 60 N, depending on the ta-C coating.

• Journal of Powder Materials
• /
• v.18 no.5
• /
• pp.423-429
• /
• 2011

Thermoelectric-thick films were fabricated by using a screen printing process of n and p-type bismuth-telluride-based pastes. The screen-printed thick films have approximately 30 ${\mu}m$ in thickness and show rough surfaces yielding an empty gap between an electrode and the thick film. The gap might result in an increase of an electrical resistivity of the fabricated thick-film-type thermoelectric module. In this study, we suggest a conductive metal coating onto the surfaces of the screen-printed paste in order to reduce the contact resistance in the module. As a result, the electrical resistivity of the thermoelectric module having a gold coating layer was significantly reduced up to 30% compared to that of a module without any metal coating. This result indicates that an introduction of conductive metal layers is effective to decrease the contact resistivity of a thick-film-typed thermoelectric module processed by screen printing.

• Korean Journal of Oriental Medicine
• /
• v.13 no.3
• /
• pp.119-124
• /
• 2007

Introduction: In Oriental medicine, the status of tongue is the important indicator to diagnose one's health, because it represents physiological and clinicopathological changes of inner parts of the body. The method of tongue diagnosis is not only convenient but also non-invasive, so tongue diagnosis is most widely used in Oriental medicine. By the way, since tongue diagnosis is affected by examination circumstances a lot, its performance depends on a light source, degrees of an angle, a medical doctor's condition etc. Therefore, it is not easy to make an objective and standardized tongue diagnosis. In order to solve this problem, in this study, we tried to design a discriminant function for thick and thin coating with color vectors of preprocessed image. Method: 52 subjects, who were diagnosed as white-coated tongue, were involved. Among them, 45 subjects diagnosed as thin coating and 7 subjects diagnosed as thick coating by oriental medical doctors, and then their tongue images were obtained from a digital tongue diagnosis system. Using those acquired tongue images, we implemented two steps: Preprocessing and image analyzing. The preprocessing part of this method includes histogram equalization and histogram stretching at each color component, especially, intensity and saturation. It makes the difference between tongue substance and tongue coating was more visible, so that we can separate tongue coating easily. Next part, we analyzed the characteristic of color values and found the threshold to divide tongue area into coating area. Then, from tongue coating image, it is possible to extract the variables that were important to classify thick and thin coating. Result : By statistical analysis, two significant vectors, associated with G, were found, which were able to describe the difference between thick and thin coating very well. Using these two variables, we designed the discriminant function for coating classification and examined its performance. As a result, the overall accuracy of thick and thin coating classification was 92.3%. Discussion : From the result, we can expect that the discriminant function is applicable to other coatings in a similar way. Also, it can be used to make an objective and standardized diagnosis.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.211-214
• /
• 2002

Properties of 52/48 PZT films with various thicknesses for piezoelectric micro-electro mechanical systems (MEMS) devices fabricated by multi-coating method on $Pt(3500{\AA})/Ti(400{\AA})/SiO_2(3000{\AA})/Si$(525$\mu\textrm{m}$) substrates were investigated. PZT films were deposited by spin-coating process at 3500 rpm for 30 sec, followed by pyrolysis at 45$0^{\circ}C$ for 10 min producing the thickness of about 120nm. These processes were repeated 4, 8, 12, 16 and 20 times in order to have various thicknesses, respectively. Finally, they were crystallized at $650^{\circ}C$ for 30 min. All thick PZT films showed dense and homogeneous surface microstructures. Thick PZT films showed crystalline structures of random orientations with increasing thickness. Dielectric constants of thick PZT films were increased with increasing film thickness and reached 800 at 100kHz for 2.3$\mu\textrm{m}$ thick PZT film. $P_r\; and\; E_c$ of 2.3$\mu\textrm{m}$ thick PZT films were about 20$\mu$C/$\textrm{cm}^2$ and 63kV/cm. Depth profile analysis by Auger Electron Spectroscopy (AES) of 4800 $\AA$ thick PZT film showed the formation of the perovskite phase on Pt layer by Pb diffusion behavior. It was considered that Pb-Pt intermediate layer promoted PZT (111) columnar structures.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.35-36
• /
• 2006

The influence of the concentration of precursor solution and the number of solution coatings on the densification of the Pb($Zr_xTi_{1-x}$)$O_3$(PZT) thick films was studied. PZT powder and PZT precursor solution were prepared by sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The powder and solution of composition were PZT(70/30) and PZT(30/70), respectively. The coating and drying procedure was repeated 4 times. And then the PZT precursor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5 to 2.0 mol/L[M] and the number of coating was repeated from 0 to 6. The relative dielectric constant of the PZT thick film was increased with increasing the number of solution coatings and the thick films with 15M, 6-time coated showed the 698. The remanent polarization of the 1.5M, 6-time coated PZT thick films was 38.3 ${\mu}C/cm^2$.

• Journal of Surface Science and Engineering
• /
• v.31 no.5
• /
• pp.286-296
• /
• 1998

Galvannealing is becomming the main stream of the coating technology applied to automobile outer and inner panels due to its low cost and easy application applied to automobile outer and inner panels due to its low cost and easy application in thick Zn coating, compared to electro galvanizing. Despite of filed up data with an experience in this field, galvannealing in thick Zn coating is getting more difficult because of the absence of Fe deposition in Zn coating. As a result, it exhibits, with different steel sheet and grain size there is a proper temperature range which is good for the tarket coating thickness of galvannealing. In case of 1,200mm wide and 0.77 mm thick extra low carbon steel with 20$mu extrm{m}$ grain size, its proper temperature range for galvannealing of one side 60g/$\textrm{m}^2$ is 470-$480^{\circ}C$.

• Journal of Welding and Joining
• /
• v.7 no.4
• /
• pp.46-55
• /
• 1989

Zirconia coatings are performed by the plasma spraying on the substrate of Al-Si alloy. In case of plasma sprayed ceramic coatings, it is important to control properly residual stress occurred during cooling process. Residual stress in coating layer varies with sprayed conditions and is influenced greatly by the coating layer thickness. Surface residual stress due to coating layer thickness is measured by X-ray diffraction method and the residual stress in coating layer is estimated by the deflection of coating layer when the restraint force in substrate was removed. When zirconia was coated on the substrate, tensile residual stress remains on zirconia coated surface layer. The tensile stress is increased to 0.35mm thickness and after 0.45mm thickness it is decreased abrouptly. A thick bond and composite coating reduce the zirconia surface stress and composite coating controls effectively the thick zirconia surface stress.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.144.2-144.2
• /
• 2016

Diamond-like carbon (DLC) coatings have been widely applied to the mechanical components, cutting tools due to properties of high hardness and wear resistance. Among them, hydrogenated amorphous carbon (a-C:H) coatings are well-known for their low friction properties, stable production of thin and thick film, they were reported to be easily worn away under high temperature. Non-hydrogenated tetrahedral amorphous carbon (ta-C) is an ideal for industrial applicability due to good thermal stability from high $sp^3$-bonding fraction ranging from 70 to 80 %. However, the large compressive stress of ta-C coating limits to apply thick ta-C coating. In this study, the thick ta-C coating was deposited onto Inconel alloy disk by the FCVA technique. The thickness of the ta-C coating was about $3.5{\mu}m$. The tribological behaviors of ta-C coated disks sliding against $Si_3N_4$ balls were examined under elevated temperature divided into 23, 100, 200 and $300^{\circ}C$. The range of temperature was setting up until peel off observed. The experimental results showed that the friction coefficient was decreased from 0.14 to 0.05 with increasing temperature up to $200^{\circ}C$. At $300^{\circ}C$, the friction coefficient was dramatically increased over 5,000 cycles and then delaminated. These phenomenon was summarized two kinds of reasons: (1) Thermal degradation and (2) graphitization of ta-C coating. At first, the reason of thermal degradation was demonstrated by wear rate calculation. The wear rate of ta-C coatings showed an increasing trend with elevated temperature. For investigation of relationship between hardness and graphitization, thick ta-C coatings(2, 3 and $5{\mu}m$) were additionally deposited. As the thickness of ta-C coating was increased, hardness decreased from 58 to 49 GPa, which means that graphitization was accelerated. Therefore, now we are trying to increase $sp^3$ fraction of ta-C coating and control the coating parameters for thermal stability of thick ta-C at high temperatures.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.9
• /
• pp.429-433
• /
• 2006

PZT(80/0) powder was prepared by a sol-gel method and PZT thick films were fabricated by the screen-printing method on the alumina substrates. The coating and drying procedure was repeated 4 times. And then the PZT(20/80) precusor solution was spin-coated on the PZT thick films. A concentration of a coating solution was 0.5mol/L and the number of coating was varied from 0 to 6. The porosity decreased and the grain size increased with increasing the number of coatings. The thickness of the PZT-6(6: number of coatings) films was about $60{\mu}m$. The relative dielectric constant increased and the dielectric loss decreased with increasing the number of PZT(20/80) sol coatings. The relative dielectric constant and dielectric loss of the PZT-6 thick film were 275 and 3.5%, respectively. The remanent polarization, coercive field and breakdown strength of the PZT-6 film were $19.8{\mu}C/cm^2$, 13.7kV/cm and 130kV/cm, respectively.