• 접착 및 계면
• /
• 제8권4호
• /
• pp.23-31
• /
• 2007

고분자 소재에 평판형 플라즈마 전처리 방식을 적용시켜 표면의 접촉각 및 접착력을 향상시켰다. 분위기 기류를 질소로 하고 유량을 30~100 mL/min, 반응시간은 0~30초로 하여 PU 소재를 주 물질로 하여 EVA foam, Leather (Action), Rubber, Unwoven 소재에 대하여 각 조건별로 플라즈마 처리시켜 처리 전후의 각 소재별 접촉각과 접착박리강도 측정을 통한 소재의 물성변화와, SEM분석을 이용한 처리 전후의 표면 변화를 측정하여 플라즈마 처리의 영향과 효과를 산출하였다. 대기압 평판형 플라즈마 반응기를 이용하여 최적 조건인 기체유량 100 mL/min, 전처리시간 10초에서 EVA foam, Leather (Action) 및 Rubber 소재의 접촉각 감소와 접착력 향상을 확인하였다.

• The Journal of Advanced Prosthodontics
• /
• 제5권3호
• /
• pp.341-350
• /
• 2013

PURPOSE. To evaluate adherence of human gingival fibroblasts (HGFs) to transmucosal abutment of dental implant with different surface conditions with time and to investigate the roles of focal adhesion linker proteins (FALPs) involved in HGFs adhesion to abutment surfaces. MATERIALS AND METHODS. Morphologies of cultured HGFs on titanium and ceramic discs with different surface were observed by scanning electron microscopy. Biocompatibility and focal adhesion were evaluated by ultrasonic wave application and cell viability assay. FALPs expression levels were assessed by RT-PCR and western blot. RESULTS. There seemed to be little difference in biocompatibility and adhesion strength of HGFs depending on the surface conditions and materials. In all experimental groups, the number of cells remaining on the disc surface after ultrasonic wave application increased more than 2 times at 3 days after seeding compared to 1-day cultured cells and this continued until 7 days of culture. FALPs expression levels, especially of vinculin and paxillin, also increased in 5-day cultured cells compared to 1-day cultured fibroblasts on the disc surface. CONCLUSION. These results might suggest that the strength of adhesion of fibroblasts to transmucosal abutment surfaces increases with time and it seemed to be related to expressions of FALPs.

• 접착 및 계면
• /
• 제16권1호
• /
• pp.22-28
• /
• 2015

본 연구에서는 수분산 폴리우레탄의 내가수분해성 및 접착력을 향상시키기 위하여 polyester polyol, epoxy resin, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), dimethylol propionic acid (DMPA)를 사용하여 epoxy를 함유한 수분산 폴리우레탄을 합성하였다. 또한 합성된 수분산 폴리우레탄의 물성은 DSC, UTM, adhesion test 등을 통해 평가하였다. 합성된 수분산 폴리우레탄의 Tg는 $-50^{\circ}C$ 부근에서 나타났으며, epoxy resin의 함량이 증가함에 따라 Tg도 상승하는 결과를 나타내었다. Epoxy resin의 함량이 증가함에 따라 인장강도는 증가하였고, 신율은 감소하였다. 또한 접착력 및 내가수분해 접착력은 polyol : epoxy = 99 : 1에서 최고값을 나타내었다.

• 접착 및 계면
• /
• 제4권3호
• /
• pp.21-32
• /
• 2003

본 원고에서는 전에 발표된 동반 논문[한국 접착 및 계면학회지, 3권4호(2002)]과 연관된 여러 가지 접착력 측정방법에 관하여 살펴보았다. 먼저 이상적인 접착력 측정방법에 관하여 살펴보았고, 그 다음으로 기계적 방법, 비기계적 방법 그리고 기타 방법의 3가지로 종류의 접착력 측정방법들을 소개하였다.

• 폴리머
• /
• 제37권3호
• /
• pp.373-378
• /
• 2013

폴리카보네이트(PC) 필름을 유연기판으로 사용하기 위해서는 $SiO_x$ 증착에 의한 베리어 특성 개선이 필요하며 이때 베리어 층과 PC 계면 접착력이 매우 중요하다. 본 연구에서는 언더 코팅, UV/$O_3$ 및 저온 플라즈마와 같은 다양한 표면 처리 방법에 의하여 PC 필름 표면을 개질하여 표면의 물리적 화학적 변화가 증착된 베리어 층 계면 접착력에 미치는 영향을 살펴보았다. 표면 처리 전의 PC 필름은 표면 거칠기 및 표면 에너지가 매우 낮아 $SiO_x$ 베리어 층과의 접착력이 현저히 떨어짐을 알 수 있었다. PC 필름을 저온 플라즈마로 표면 처리한 결과, 표면의 거칠기 증가와 극성 관능기 생성에 의하여 극성 표면 에너지가 향상되는 반면 UV/$O_3$ 처리의 경우, 표면 거칠기 변화 없이 표면에 생성된 극성 관능기에 의해 극성 표면 에너지가 증가됨을 알 수 있었다. 이러한 표면의 변화는 베리어층과 PC 기판의 계면 접착력 증가에 기여함을 알 수 있었다. 표면 처리 방법으로 언더 코팅을 사용하는 경우 표면에 에너지를 가하지 않아도 코팅제의 아크릴산과 $SiO_x$의 접착력 향상에 의하여 PC 필름과의 계면 접착력이 증가되며 유무기 하이브리드 다층 구조에 의한 베리어 특성 개선이 함께 일어남을 알 수 있었다.

• 접착 및 계면
• /
• 제8권2호
• /
• pp.15-21
• /
• 2007

광기능성시트 보호용 점착제를 제조하기 위하여 천연고무와 DCPD계 점착부여수지, 세 종류의 지방족 점착부여수지를 이용하여 천연고무계 점착제를 제조하였다. 또한, 천연고무의 낮은 응집력을 대체하기 위하여 점착부여수지의 함량이 고정된 상태에서 SIS 블록공중합체를 함량비에 따라 첨가하여 점착제를 제조하였다. 제조한 점착제의 점착물성을 초기점착력과 박리강도로써 평가하였다. 천연고무/점착부여수지의 초기점착력은 점착부여수지의 함량이 증가함에 따라 증가하다 최대값을 보이고 감소하였다. 또한, 지방족계 점착부여수지의 연화점이 증가함에 따라 초기점착력이 다소 증가하였다. 점착부여수지의 함량이 50 wt%까지는 박리강도가 증가하였으나 그 이상의 함량에서는 혼합파괴 현상을 보였다. SIS가 블랜드된 점착제의 초기점착력은 지방족계 점착부여수지의 함량이 20~40 wt%에서 최대값을 보였으나 20 wt%에서 fibrillation 현상을 나타내었고 박리강도는 40 wt%에서 최대값을 나타내었다.

• 대한치과보철학회지
• /
• 제35권2호
• /
• pp.330-343
• /
• 1997

Extraoral maxillofacial prostheses are essential for restoring facial structures that are lost as a result of congenital missing, injuries from accidents, surgical treatments of head and neck cancer. Recently, silicone is the most useful material for this purpose and is more advantageous than other maxillofacial prosthetic materials. However, there are some problems for long-term usage of silicone prostheses due to tear and color change. These are major contributing environmental factors to those problems that are such as ultraviolet light, cleansing agents, changes in humidity and successive adhesion and removal. The aim of this study is to evaluate the physical properties and color changes of maxillofacial prosthetic silicone material by those environmental factors using A-2186 silicone material (Factor II, USA) and two pigments, cadmium yellow medium and cosmetic red. Aluminium molds were fabricated according to the ASTM No. D412 & D624 specifications and resulted specimens from molds were fabicated and treated as follows. Control group and experimental I group were fabricated with 0.1% wt. pigment mixing in silicone elastomer and II-1 group, II-2 group of experimental II group were fabricated with 0.2%, 0.3% wt. pigment mixing in silicone elastomer, respectively. Control group was kept in darkroom at room temperature, I-1 group was kept under natural sunlight during 1week, I-2 group was soaked in 20% soap water during 1wk. I-3 group was successively adhered and removed 200 times on inner region of arm using Daro adhesive-33. Experimental II groups were kept in darkroom at room temperature. Instron universal testing machine was used to measure the % elongation, tensile strength, tear strength of control, experimental I, II groups and reflectance spectrophotometer(COLOR EYE-3000, Macbeth, USA) was used to measure the color differences between control group and experimental I group. The results were as follows : 1. When compared with control group, natural weathering group and 20% soap-water soaking group had no significant differences in % elongation(p>0.05). 2. 200 times successive adhesion and removal group, 0.2% wt. pigment group and 0.3% wt. pigment group had significant decreases in % elongation(p<0.05). 3. Natural weathering group, 20% soap-water soaking group and 200 times successive adhesion and removal group had no significant differences in tensile strength (p>0.05). 4. 0.2%, 0.3% wt. pigment groups had significant decreases in tensile strength(p<0.05). 5. Values of all experimental groups were decreased in tear strength. and 200 times successive adhesion and removal group had significant decrease in tear strength(p<0.05). 6. Natural weathering group and 20% soap-water soaking group had significant color differences(${\Delta}E$) and it could be detectable to naked eye(p<0.05). 7. Color differences between control group and 200 times adhesion and removal group were not detectable to the naked eye (${\Delta}E<1.0$).

• 한국임상수의학회지
• /
• 제25권4호
• /
• pp.263-267
• /
• 2008

This study was performed to compare the efficacy of carboxymethylchitosan fabric (CMCF) with that of the combination of CMCF and low molecular weight heparin (LMWH) for the prevention of postoperative uterine adhesion in rats. Adhesions were induced by suturing both the uterine serosa and peritoneum abrased until petechial bleeding occurred. Fourteen days later, adhesions were evaluated clinically and histopathologically. The mean tensile strength was significantly decreased in the CMCF and CMCF+LMWH groups compared to that of control group, and the CMCF+LMWH group had the lowest tensile strength. The distance of adhesion site was highest in the CMCF group and slightly decreased in the CMCF+LMWH group comparing to that of control group. The inflammatory cell infiltration and neovascularization of the CMCF group were significantly lower than those of the control group. It was observed that the damage at intestinal serosa was significantly decreased in the CMCF+LMWH group comparing to that of control group. Therefore, it was concluded that CMCF and LMWH may be useful to prevent postoperative uterine adhesion in rats.

• 한국추진공학회지
• /
• 제24권4호
• /
• pp.33-40
• /
• 2020

접착 보조제 종류에 따른 고체 추진제, 라이너 그리고 내열재의 접착 특성에 대한 연구를 수행하였다. 추진제/라이너/내열재 간의 가소제 또는 경화제의 이동을 막기 위하여 접착 보조제를 사용하였다. 접착 보조제의 종류는 Isocyanate계를 사용하였으며, 한 분자 내에 Isocyanate의 개수, 분자량에 대하여 접착 특성을 확인하였다. 시험 결과, -NCO기가 많을수록, 접착 보조제의 분자량이 클수록 접착력이 증가하는 것으로 확인하였다. 또한 접착 보조제를 도포한 후 가사시간에 따른 접착력을 비교한 결과, 가사시간이 짧을수록 접착력이 증가하는 것으로 확인되었다.

• 한국추진공학회지
• /
• 제24권5호
• /
• pp.84-90
• /
• 2020

본 논문은 이종추진제(1차 추진제/2차 추진제) 접착에 필요한 코팅제에 대해 기술하였다. 코팅제는 유기용매, 고분자 경화제, 경화촉매로 구성되어 있다. 경화촉매인 FeAA를 0.14 wt% 이상 적용한 코팅제는 2차 추진제 경화 직후 시험한 결과 접착계면이 아닌 추진제가 파단되는 결과를 확인하였으며, 0.10 wt% 이하에서는 접착계면이 파단되었다. 경화촉매는 2차 추진제 경화 직후 접착계면이 파단되는 결과를 확인하였다. 또한 TPB 경화촉매를 적용한 코팅제의 경우 시간이 경과함에 따라 1차 추진제와 2차 추진제간의 접착력이 증가하는 결과를 확인하였다.