• E2M - 전기 전자와 첨단 소재
• /
• 제10권5호
• /
• pp.440-446
• /
• 1997

This research has been performed for the fabrication of high quality ferrite plastic magnet. The magnetic properties of S $r_{5.9}$F $e_2$ $O_3$ ferrite bonded magnets by injection moulding with a variety of applied magnetic field were investigated. 0.3wt% CaCO3, 0.2wt% $SiO_2$, 0.5wt% $Al_2$ $O_3$and 0.5wt% N $a_2$ $SiO_3$are added in order to improve the magnetic properties of Sr-ferrite plastic magnets during the powder fabrication. For carbon coating on chemical compound specimen, 5wt% polyvinyl alcohol is added, and then calcinated under $N_2$ environment of 12$25^{\circ}C$. The particle size is distributed from 0.9~1.2${\mu}{\textrm}{m}$ which approximates to the single domain. The obtained Sr ferrite powder is well mixed with silane coupling and calcium stearate of 1wt%. Nest, the specimen is pelleted after kneading each of them with polyamidel2 as a binder. When the temperature of injection and mould were 25$0^{\circ}C$ and 8$0^{\circ}C$ respectively at injection pressure of 200kgf/$\textrm{cm}^2$, the degree of orientation was 85.3% under the applied magnetic field of 12kOe. As the results, when the packing density of Sr ferrite powder was 90wt%, the magnetic properties of Sr ferrite bonded magnet were follows : $_{B}$ $H_{c}$=2.41kOe, Br=3.1kG, (BH)$_{max}$=2.21MgOe. Especially, the Sr-ferrite bonded magnet with 10wt% N $d_2$F $e_{14}$B additive were as follows : $_{B}$ $H_{c}$=2.57kOe, Br=3.14kG and (BH)$_{max}$=2.39MGOe.GOe.GOe.GOe.e.

• 공업화학
• /
• 제17권4호
• /
• pp.420-425
• /
• 2006

Propylene oxide (PPO)를 gelation agent로 한 졸-겔법으로 입자가 균일하고 자기적 특성이 우수한 $MO{\cdot}Fe_{12}O_{18}$ (M/Ba and Sr)의 구조식을 가지는 M-type hexagonal ferrite를 제조하였다. 본 방법으로 얻은 졸-겔용액은 매우 안정적인 분산상태를 보이며, $Fe^{3+}$의 겔화가 진행되고, 생성된 $Fe_2O_3$의 표면에서 $Ba^{2+}$ 또는 $Sr^{2+}$의 겔화가 진행되는 것으로 설명될 수 있어서, +3가 이하의 금속이라도 +3가 이상의 금속 존재 하에는 겔화가 가능한 것을 확인하였다. 또한, 기존 방법과 비교하여 값싼 원료를 사용하며, 반응 시간도 1 min 이내로 짧아지는 장점이 있다. 본 제조법으로 얻어진 분말은 기왕에 발표된 문헌 값과 비교하면 $150^{\circ}C$ 이상 낮은 열처리 온도에서 최고의 자기적 특성을 나타냈으며, 향상된 자기적 특성을 보였다. Sr-ferrite의 경우 최대포화자화 값 74.4 emu/g, 보자력 값 6198 Oe을, Ba-ferrite의 경우도 최대포화자화 값 68.1 emu/g, 보자력 값 5155 Oe을 보였다. 이들은 기존에 발표된 문헌 값과 비교하면 각각 10%와 5% 이상 증가된 보자력 값을 나타내어, 고밀도 자기기록재료에 적합함을 확인하였다. 제조된 분말은 1차 건조 분말의 경우 3~5 nm의 입자들이 응집된 50 nm 정도의 구형입자가 생성되고, 열처리 후에는 500 nm 정도의 고른 크기를 가진 육각판상형 입자가 생성된다.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권3호
• /
• pp.324-331
• /
• 1995

0.36[wt%l $SiO_{2}$ and 0.1[wt%] $H_{3}$B $O_{3}$ were added to strontium ferrite magnets of the magnetoplumbite phase SrO.5.7F $e_{2}$ $O_{3}$ to hinder grain growth and accelerate sintering, respectively. This experiment was carried out to investigate effect of particle size distribution as a function of milling time(20, 30, 40, 50, 60, 70 hours) on the magnetic properties of SrO.5.7F $e_{2}$ $O_{3}$ ferrite magnet. The B-H curve, density and the degree of orientation were measured. And the microstructure of ferrite magnets was examined with a SEM. The optimal conditions and properties of the typical sample are the following : The milling time was 60 hours. Magnetic and physical properties are $B_{r}$=4, 000[G], $_{b}$ $H_{c}$=3, 330[Oe], (BH)max=3.786[MGOe], $_{I}$ $H_{c}$=3, 525[Oe], density=5.0063[g/c $m^{3}$] and orientation factor f=0.813.0.813.3.3.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1990년도 하계학술대회 논문집
• /
• pp.239-242
• /
• 1990

The effect of $CaCo_3$, $SrCo_3$, $SiO_2$ and $H_3BO_3$ in the range of 0.1-1.0 wt% on strontium ferrites consisting of the magnetoplumbite phase $SrO-5.7Fe_2O_3$ were investigated. The hysteresis loop, density, demagnetization curve and the intrinsic coercive force were measured on anisotropic ferrite. The particle diameter and 0.5(wt%) of second additive $CaCo_3$ is particularly important for the properties of anisotropic ferrite. When the particle diameter is decreased from 1.98(${\mu}m$) to 1.07(${\mu}m$), the remance is increased from 2900 to 4010(G) and the coercive force from 2150 to 2850(Oe) at a sintering temperature 1230 ($^{\circ}C$). Remance Br(G), coercleve force(Oe) and maximum energy product of sample A-16 are87(%), 56(%), 67(%) of S-W model theoretical value.

• 한국자기학회지
• /
• 제26권6호
• /
• pp.196-200
• /
• 2016

크기가 서로 다른 Sr-페라이트 분말에 대한 활성화 부피의 자기장 의존성을 조사하였다. 그 결과, 입자의 크기가 큰 시료 C2 는 낮은 자기장 영역에서는 활성화 부피가 컸으나 자기장이 증가할수록 감소하였으며, 크기가 작은 시료 C3의 경우는 보자력과 거의 같은 고착 자기장에서 최대를 보이다가 감소하는 경향을 보였다. 이와 같은 현상은 자화 역전 현상을 설명하는 자구생성 및 자벽고착 자기장의 상대적 위치 그리고 쌍극자 상호작용의 세기에 밀접하게 관련되는 것으로 판단된다.

• 한국자기학회지
• /
• 제8권2호
• /
• pp.86-92
• /
• 1998

플라스틱 자석에는 균일한 자장분포와 높은 자기특성을 얻기 위해서는 균질화된 혼합물이 요구되며, 이를 위해서는 적절한 혼합경로와 혼합물의 균질도 평가방법이 필수적이다. 본 연구에서는 Sr-ferrite/EVA 플라스틱 자석에서 혼합균질도의 평가방법과 혼합균질도가 자기특성에 미치는 영향을 조사하였다. 회분식 혼합기와 단축압출기를 이용하여 균질도가 서로 다른 혼합균질도를 조사하였다. 토크센서를 이요한 혼합시 토크변화 측정방법은 임계분말충전율 결정에는 효과적인데 반해 혼합균질도 평가에는 적합하지 않았다. 이그이방성 플라스틱 자석의 분말이방화율을 이용한 균질도 평가방법은 정밀도는 높으나, 시편제조와 측정에 고가의 장비와 필요하고 자성분말 혼합물 이외에는 이용될수 없다. 모세관 레오미터를 이용한 압출압력변화 측정방법은 정밀도가 높고 측정이 간편하여 효과적이었다. 혼합물의 균질도가 증가함에 따라 분말이방화율이 증가하였으며, 분말이방화율의 증가에 따라 잔류자속밀도는 직선적으로 증가하였다.