Abstract
0.36[wt%l $SiO_{2}$ and 0.1[wt%] $H_{3}$B $O_{3}$ were added to strontium ferrite magnets of the magnetoplumbite phase SrO.5.7F $e_{2}$ $O_{3}$ to hinder grain growth and accelerate sintering, respectively. This experiment was carried out to investigate effect of particle size distribution as a function of milling time(20, 30, 40, 50, 60, 70 hours) on the magnetic properties of SrO.5.7F $e_{2}$ $O_{3}$ ferrite magnet. The B-H curve, density and the degree of orientation were measured. And the microstructure of ferrite magnets was examined with a SEM. The optimal conditions and properties of the typical sample are the following : The milling time was 60 hours. Magnetic and physical properties are $B_{r}$=4, 000[G], $_{b}$ $H_{c}$=3, 330[Oe], (BH)max=3.786[MGOe], $_{I}$ $H_{c}$=3, 525[Oe], density=5.0063[g/c $m^{3}$] and orientation factor f=0.813.0.813.3.3.