Abstract
This research has been performed for the fabrication of high quality ferrite plastic magnet. The magnetic properties of S $r_{5.9}$F $e_2$ $O_3$ ferrite bonded magnets by injection moulding with a variety of applied magnetic field were investigated. 0.3wt% CaCO3, 0.2wt% $SiO_2$, 0.5wt% $Al_2$ $O_3$and 0.5wt% N $a_2$ $SiO_3$are added in order to improve the magnetic properties of Sr-ferrite plastic magnets during the powder fabrication. For carbon coating on chemical compound specimen, 5wt% polyvinyl alcohol is added, and then calcinated under $N_2$ environment of 12$25^{\circ}C$. The particle size is distributed from 0.9~1.2${\mu}{\textrm}{m}$ which approximates to the single domain. The obtained Sr ferrite powder is well mixed with silane coupling and calcium stearate of 1wt%. Nest, the specimen is pelleted after kneading each of them with polyamidel2 as a binder. When the temperature of injection and mould were 25$0^{\circ}C$ and 8$0^{\circ}C$ respectively at injection pressure of 200kgf/$\textrm{cm}^2$, the degree of orientation was 85.3% under the applied magnetic field of 12kOe. As the results, when the packing density of Sr ferrite powder was 90wt%, the magnetic properties of Sr ferrite bonded magnet were follows : $_{B}$ $H_{c}$=2.41kOe, Br=3.1kG, (BH)$_{max}$=2.21MgOe. Especially, the Sr-ferrite bonded magnet with 10wt% N $d_2$F $e_{14}$B additive were as follows : $_{B}$ $H_{c}$=2.57kOe, Br=3.14kG and (BH)$_{max}$=2.39MGOe.GOe.GOe.GOe.e.