• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.265-272
• /
• 2011

Even though concrete is the most important material for building structures, its intrinsic gray color degrades urban esthetics. In order to improve this problem, coloring methods of mixing pigment in concrete batch and painting the surface of concrete surface have been tried. However, applications of the coloring methods in construction field are difficult due to high cost and low durability. Recently, acid stain agent is emerging as a new coloring method for concrete. It is able to apply a remarkably thin colored layer on a concrete surface from chemical reaction between acid and alkaline solutions. This study has examined the changes and variations of the surface layer of mortar specimen from chemical reaction of acid stained agents. The colors were changed into natural irregular stains according to aging. After the staining, no shape change was found from visible inspections. Microstructure of the colored surface applied with acid stained agent was much rougher than that of original mortar. When the colored layer was compared to original surface, crystals of hydrate such as $Ca(OH)_2$ and C-S-H gel were observed. Surface hardness was same or slightly higher in the colored layer. The value of pH was reduced by approximately 10%, weight contents of elements such as Ca, Si, and Al were low. In the chemical composition of the colored layer, the non-cement based elements of Mn, Cr, and Cu increased. Also, Fe and alkali elements of K and Na increased.

• Journal of Korean Elementary Science Education
• /
• v.25 no.4
• /
• pp.352-362
• /
• 2006

Many misconceptions regarding biology and evolution have been reported by students prior to being exposed to a formal education program of evolution which challenged them. This study sought to investigate and to analyze the misconception formation process of evolution originating from TV animation and science books for children. Firstly, to identify TV animation's influence on students' misconceptions of evolution, a questionnaire including TV animation characters was constructed and administered to 146 elementary school students, 161 middle school students, and 156 high school students. The data collected was analyzed. Secondly, 17 science books for children were sampled and the contents related to evolution were selected and analyzed in terms of five evolutionary explanations: creationism internal will explanation, teleological explanations, explanations of use and disuse, mutation and finally, natural selection. Children have understood 'growth' and 'metamorphosis' on TV animation as 'evolution'. The processes by which characters on TV animation undergo some forms of change, which are in fact a kind of metamorphosis has often been understood as 'evolution'. Many respondents have defined evolution incorrectly as the process of growing and changing shape. On the other hand, some science books fur children contained descriptions of evolution including' mutation and finally natural selection explanation'; however, most of the science books fur children sampled in this study were written through the perspectives of alternative evolutionary views such as 'teleology view', 'internal will view', and 'use and disuse view'. It is apparent that TV animation and science books fur children influence the formation of various misconceptions regarding evolution by children.

• Journal of the Korean Electrochemical Society
• /
• v.7 no.4
• /
• pp.173-178
• /
• 2004

Silicon thin film were synthesized from silane and argon gas mixture directly on copper foil by rf PECVD and then lithium ion batteries were prepared from them employed as the negative electrodes without any further treatment. In the present study, two different kinds of silicon thin films, amorphous silicon and copper silicide were prepared by changing deposition temperature. Amorphous silicon film was prepared below $200^{\circ}C$, but copper silicide film with granular shape was formed by the reaction between silicon radical and diffused copper ions under elevating temperature above $400^{\circ}C$. The amorphous silicon film gives higher capacity than copper silicide, but the capacity decreases sharply with charge-discharge cycling. This is possibly due to severe volume changes. The cyclability is improved, however, by employing the copper silicide as a negative electrode. The copper silicide plays an important role as an active material of the electrode, which mitigates volume change cause by the existence of silicon and copper chemical bonding and provides low electrical resistance as well.

• The korean journal of orthodontics
• /
• v.34 no.2 s.103
• /
• pp.109-119
• /
• 2004

This study aimed at investigating the skeletal, dentoalveolar, and soft tissue changes of Class III malocclusion cases treated by second molar extraction. The lateral cephalograms of 15 subjects with moderate Class III malocclusion by average ANB $-1.4^{\circ}\;and\;IMPA\;85^{\circ}$ were traced and the computerized superimposition of average craniofacial change was made. The data was gathered and statistically analyzed. The results were as follows: 1 Lower anterior facial height/anterior facial height increased by 0.6%(P<0.01), mandibular plane increased by $1.5^{\circ}$(P<0.05). 2. There was a slightly downward & backward rotation of the mandible. 3. Lower first molar tipped distally by 4.nm(P<0.001), lower anterior teeth lingually tipped by $3.2^{\circ}$(P<0.05). 4. Retracted lower lip improved facial profile. This study may suggest that second molar extraction could be effective for a moderate Class III malocclusion to make distalization of the lower first molar easier and avoid severe lingual tipping of the lower incisor, if the lower third molar has a normal shape, good direction of eruption and adequate time for lower second molar extraction

• Journal of Korean Society of Forest Science
• /
• v.102 no.2
• /
• pp.305-308
• /
• 2013

This study was conducted to describe the external morphology of Platypus-koryoensis Murayama in immature stage, to determine each instar based on larvae head-capsule, and to measure individual and local variations in the number of mycangia of adult. Egg of P. koryoensis, had oval shape and lengths of the major and minor axis were $0.67{\pm}0.051$ mm and $0.41{\pm}0.053$ mm, respectively. Body colour of $5^{th}$ instar was gloss white with well-developed mandible. Larvae of P. koryoensis grew up to $5^{th}$ instar and each instar was clearly classified by head capsule width. Head capsule width for $1^{st}$, $2^{nd}$, $3^{rd}$, $4^{th}$, and $5^{th}$ instar larvae were $0.35{\pm}0.004$ mm, $0.45{\pm}0.010$ mm, $0.67{\pm}0.039$ mm, $0.94{\pm}0.069$ mm and, $1.12{\pm}0.007$ mm, respectively. The colour of pupa was pale yellow and its length was $4.64{\pm}0.044$ mm. The number of mycangia per female had individual variations from 5 to 12 and 83% of the adults had from 6 to 8 mycangia. There was no significant difference in number of mycangia collected from between Namyangju region and Honchen region.

• Journal of Korean Academy of Oral and Maxillofacial Radiology
• /
• v.28 no.1
• /
• pp.47-58
• /
• 1998

The purpose of this study was to investigate an influence of the change of central panoramic curves on the image reconstruction in the dental implant CT. The author designed three experimental groups according to the location of central panoramic curve. In group A, central panoramic curve was determined as the curve connecting the center of roots from the first premolar to the first molar. In group B, central panoramic curve was determined as the line connecting the lingual cortical plate at the level of the mesial aspect of the first premolar with the buccal cortical plate at the level of the mesial aspect of the first molar. In Group C, central panoramic curve was determined as the line connecting the buccal cortical plate at the level of the mesial aspect of the first premolar with the lingual cortical plate at the level of the mesial aspect of the first molar. Twenty four reformatted CT images was acquired from four mandibles embedded in the resin block and twenty four contact radiographs of dog specimens were acquired. Each Image was processed under Adobe Photoshop program analysed by MSPA(mandible/maxilla shape pattern analysis) variables such as MXVD, MXHD, UHD, MHD, and LHD. The obtained results were as follows ; 1. The mean of MXVD variable was 19.9, 20.2, and 20.0 in group A, B, and C, respectively, which were smaller than actual value 20.5. But, there was no significant difference among 3 groups (p>0.05). 2. The mean of MXHD, UHD, MHD, and LHD variables in group A, B, and C was 11.9, 12.2, and 12.3; 9.3, 9.5, and 9.6; 10.0, 10.3, and 10.3; 9.2, 9.3, and 9.4 respectively which were equal to or greater than the actual value 11.8, 9.3, 10.0, and 9.2. But, there was no significant difference among 3 groups (p>0.05). 3. The number of noneffective observations with difference over or under 1 mm with comparison to the actual value was 24(20％), 58(48.3％), and 52(43.3％), respectively, in group A, B, and C. 4. In group A, the number of observations over 1 mm and under 1 mm was 9 and 15, respectively, but in group Band C, the number of observations over 1 mm was more than under 1 mm.

• Clean Technology
• /
• v.14 no.1
• /
• pp.1-6
• /
• 2008

Removal of paraffin wax from a ceramic injection mold using supercritical $CO_2$ has been studied. The paraffin wax is used as a binder in the ceramic injection molding process. The effects of pressure, temperature and flow rate of supercritical $CO_2$ on the removal of the paraffin wax were investigated. The removal rates were measured with various flow rates of $CO_2$ in the range of 328.15 - 348.15 K and 15 - 30 MPa. The removal rate of paraffin wax increased as the pressure increased. In the effect of temperature, the paraffin wax was effectively removed over 329.15K (melting point of paraffin wax), however, the efffct of temperature was not significant when the temperature was further increased. The increase of $CO_2$ flow rate also affected the removal of paraffin wax. However, the effect of flow rate was not observed when the flow rate reached a certain value. Propane was used as a co solvent in order to remove the paraffin wax effectively. When the propane was added to the $CO_2$, the removal efficiency was improved. The paraffin wax was completely removed from the ceramic injection mold without any change in their shape and the structure.

• Clean Technology
• /
• v.22 no.4
• /
• pp.308-315
• /
• 2016

$SiO_x/ZnO$ composites were prepared from sol-gel method for excellent cycle life characteristics. The composites were coated by PVC as a carbon precursor. ZnO removal to create a void space therein was able to buffer the volume change during charge and discharge. To determine the crystal structure and the shape of the synthesized composite, XRD, SEM, TEM analysis was performed. The carbon contents in the composites were confirmed by TGA. The pore structure and pore size distribution of the composite was measured with the BET specific surface area analysis and BJH pore size distribution. Enhanced electric conductivity by carbon addition was determined from powder resistance measurement. Electrochemical properties were measured with the AC impedance and the charge and discharge cycle life characteristics. When carbon was coated on the $SiO_x/ZnO$ sample, the electrical conductivity and the discharge capacity were increased. After removal of ZnO with HCl the surface area of the sample was increased, but the discharge capacity was decreased. $SiO_x/ZnO$ sample without acarbon coating showed very low discharge capacity, and after carbon coating the sample showed high discharge capacity. For cycle life characteristics, $C-SiO_x/ZnO$ composite (Zn : Si : C = 1 : 1 : 8) with a capacity of $815mAh\;g^{-1}$ at 50 cycle and 0.2 C has higher capacity than existing graphite-based anode materials.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.119-124
• /
• 2009

Statement of problem: The increasing demand for esthetic restorations has been required developing new materials for tooth colored restoration. Ceromer(Ceramic Optimized Polymer) has some advantages over porcelain, and has gained increasing popularity in restorative dentistry. However, there is little information on the dimensional changes in a clinical restoration in moist conditions. Purpose: This study examined the dimensional changes in Ceromer restorations with a clinical crown shape that were fabricated in a clinical manner. Material and methods: The crowns for the maxillary central incisor were fabricated with two Ceromers($BelleGlass^{(R)}$ and $Targis^{(R)}$) using a similar clinical restoration manufacturing technique. A total of twenty specimens were prepared and immersed in distilled water at room temperature to allow for water absorption. The weight, height and width were measured at 24, 72 and 168 hours. The accumulated ratios of the changes were calculated and evaluated using a paired t-test and an independent independent t-test. Results: The dimensions and weight increased with increasing soaking time. $Targis^{(R)}$ showed significant differences in height and weight between 24 hours and the other times(P<.05). $BelleGlass^{(R)}$ showed significant differences in width and weight between 24 hours and the other times. The two materials showed different changing patterns of the dimensions but there were no statistically significant differences between them. Conclusion: The dimensions and weight of the Ceromer restorations were changed by water absorption. The clinical crown shaped specimen showed more complicated dimensional changes than the simplified specimens.

• Journal of the Korean Magnetics Society
• /
• v.17 no.4
• /
• pp.156-161
• /
• 2007

To develop array magnetic sensors, specular-type giant magnetoresistive- spin valve (GMR-SV) film of Glass/Ta(5)MiFe(7)/IrMn(10)NiFe(5)/$O_2$/CoFe(5)/Cu(2.6)/CoFe(5)/$O_2$/NiFe(7)/Ta(5)(nm) was deposited by using a high-vacuum sputtering system. One of 15 way sensors in the area of $8{\times}8mm^2$ was Patterned a size of $20{\times}80{\mu}m^2$ in multilayer sample by Photo-lithography. All of 15 sensors with Cu electrodes were measured a uniform magnetic properties by 2-probe method. The highest magnetic sensitivity of MR and output voltage measured nearby an external magnetic field of 5 Oe were MS = 0.5%/Oe and ${\triangle}$V= 3.0 mV, respectively. An easy-axis of top-free layers of $CoFe/O_2/NiFe$ with shape anisotropy was perpendicular to one of bottom-pinned layers $IrMn/NiFe/O_2/CoFe$. When the sensing current increased from 1 mA to 10 mA, the output working voltage uniformly increased and the magnetic sensitivity was almost stable to use the nano-magnetic devices with good sensitive properties.