• Journal of the Semiconductor & Display Technology
• /
• v.21 no.1
• /
• pp.103-107
• /
• 2022

Scaffolds are the structures that safely protect sensors in various parts of the body. Because of scaffolds must protect sensors from load, the tensile strength of the scaffolds must be higher than 750 kgf/cm². Currently, the tensile strength of scaffolds made with the 3d printer is 714 kgf/cm². We confirm that the tensile strength of the scaffolds increase using air with high nitrogen concentration. In this study, we conducted experiments to find nitrogen concentrations in which the tensile strength of the specimen is higher than 750 kgf/cm². The nitrogen control device and the nitrogen concentration sensor were installed in the chamber type 3d printer. The nitrogen concentration inside the 3d printer was changed by 5 % from 80 % to 100 %. Specimens of ASTM D 638 standard were produced under changed nitrogen concentration. We measured the tensile strength of specimens. We compared the tensile strength of specimens produced under each nitrogen concentration. We confirmed that when air with nitrogen concentration of 90 % was used, the tensile strength of scaffolds were 762 kgf/cm².

• Journal of the Semiconductor & Display Technology
• /
• v.20 no.4
• /
• pp.177-181
• /
• 2021

Scaffolds protect the sensor in the body. Scaffolds are made of a bioabsorbable polymer. The polymer process is sensitive to humidity. Inside of the 3D printer has been improved to control the humidity. Specimens were produced by injection molding and 3D printer. 3D printed specimens were printed under various humidity conditions. We measured tensile strength of the injection-molded specimen and tensile strength of the 3d printing specimen. We compared tensile strength of the injection-molded specimen and tensile strength of the 3d printing specimen. Tensile strength of the injection-molded specimen is 557 kgf/cm². We confirmed tensile strength of the specimen was highest at 741 kgf/cm² when the humidity was 10 %. We confirmed lower the humidity, higher tensile strength of the polymer product.

• Journal of the Korean Chemical Society
• /
• v.50 no.3
• /
• pp.224-231
• /
• 2006

agents used for enhancing mechanical properties of porous natural scaffolds, reduces biocompatability of the scaffolds, due to their inherent cytotoxicity. In this study, scaffolds which was composed of chitosan, alginate and gelatin were cross-linked by using heat treatment instead of cross-linking agent and mechanical properties of the cross-linked scaffold were investigated. Fourier transform infrared spectroscopy (FT-IR) analysis confirmed that cross-linking of heat-treated scaffold was formed via amide or ester linkage between the polymer chains. The heat-treated scaffold had interconnected pores with mean diameter of 100~200 m and showed more than two fold increase of water uptake in comparison with chemically cross-linked scaffold. Tensile strength of the heat-treated scaffold increased up to 130% compared to non cross-linked scaffold and average maximum elongation was 11.3%. The porous cross-linked scaffold with the improved mechanical property may be suitable as a biocompatable scaffold for tissue engineering.

• Macromolecular Research
• /
• v.14 no.5
• /
• pp.552-558
• /
• 2006

Biodegradable nanofibrous poly(L-lactic acid) (PLLA) scaffold was prepared by an electrospinning process for use in tissue regeneration. The nanofiber scaffold was treated with oxygen plasma and then simultaneously in situ grafted with hydrophilic acrylic acid (AA) to obtain PLLA-g-PAA. The fiber diameter, pore size, and porosity of the electrospun nanofibrous PLLA scaffold were estimated as $250\sim750nm,\;\sim30{\mu}m$, and 95%, respectively. The ultimate tensile strength was 1.7 MPa and the percent elongation at break was 120%. Although the physical and mechanical properties of the PLLA-g-PAA scaffold were comparable to those of the PLLA control, a significantly lower contact angle and significantly higher ratio of oxygen to carbon were notable on the PLLA-g-PAA surface. After the fibroblasts were cultured for up to 6 days, cell adhesion and proliferation were much improved on the nanofibrous PLLA-g-PAA scaffold than on either PLLA film or unmodified nanofibrous PLLA scaffold. The present work demonstrated that the applications of plasma treatment and hydrophilic AA grafting were effective to modify the surface of electrospun nanofibrous polymer scaffolds and that the altered surface characteristics significantly improved cell adhesion and proliferation.

• Journal of Biosystems Engineering
• /
• v.32 no.1 s.120
• /
• pp.57-62
• /
• 2007

The objectives of this study were to prepare a new artificial eardrum patch using water-insoluble chitosan for healing the tympanic membrane perforations and to investigate biomechanical properties and cyotoxicity of the chitosan patch scaffold (CPS). Tensile strength and elongation at the rupture point of CPSs were 2.49-74.05 MPa and 0.11-107.06%, respectively. As the biomechanical properties or CPSs varied with the concentration of chitosan and glycerol, the proper conditions for the CPS were found out. SEM analysis showed very smooth and uniform surface of CPSs without pores at x1000. The result of MTT test showed that CPSs had no cytotoxicity.

• Journal of Biomedical Engineering Research
• /
• v.38 no.5
• /
• pp.248-255
• /
• 2017

Polyurethane/polyethylene glycol(PU/PEG) hybrid scaffolds with various concentrations of PEG (0 to 50wt%) were prepared by electrospinning to evaluate the mechanical properties and the biocompatibility of the PU/PEG blend scaffolds. The 12wt% PU/PEG polymers were studied due to the absence of beads. The ultimate tensile strength of 12wt% PU was $8.2{\pm}0.5MPa$. The strength increased to $9.2{\pm}0.7MPa$ when 10% PEG was added to PU. However, the dry and the wet strength of PU/PEG scaffolds began to decrease dramatically when the PEG content was more than 10wt%. No cytotoxicity was observed for all the PU/PEG scaffolds investigated, indicating that the PU/PEG hybrid scaffolds are clinically safe and effective to small-diameter vascular grafts. In addition, the L-929 cells attached and proliferated well on the PU/PEG hybrid scaffolds.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.51.2-51.2
• /
• 2011

A novel electrospun nanofiber membrane was fabricated using combined poly (vinylphosphonic acid) (PVPA) and polyvinyl alcohol (PVA) intended for bone tissue engineering applications. PVPA is a proton-conducting polymer used as primer for bone implants and dental cements to prevent corrosion and brush abrasion. The phosphonate groups of PVPA have the ability to crosslink and attach itself to the hydroxyapatite surface facilitating faster integration of the biomaterial to the bone matrix. PVA was combined with PVPA to provide hydrophilicity, biocompatibility and improve its spinnability. To improve its mechanical strength, PVPA/PVA and neat PVA mixtures were combined to produce a multilayer scaffold. The physical and chemical properties of the of the fabricated matrix was investigated by SEM and TEM morphological analyses, tensile strength test, XRD, FT-IR spectra, swelling behavior and biodegradation rates, porosity and contact angle measurements. Biocompatibility was also examined in vitro by cytotoxicity and cell proliferation studies with MTT assay and cell adhesion behavior by SEM and confocal microscopy.

• Journal of Adhesion and Interface
• /
• v.24 no.1
• /
• pp.17-25
• /
• 2023

In this study, waste polyethylene terephthalate (PET) was recycled to produce a support and then polyetherimide (PEI) was used for environmentally friendly organic solvent nanofiltration. The prepared composite membrane was first prepared by electrospinning a PET support, then casted on the support using PEI having excellent solvent resistance, and organic solvent nanoparticles using a Non-solvent Induced Phase Separation (NIPS) method. A filtration membrane was prepared. First, the fiber diameter and tensile strength of the PET scaffold prepared prior to membrane fabrication were identified through morphology analysis, and the optimal scaffold for the organic solvent nanofiltration membrane was identified. Afterward, the PET/PEI composite membrane prepared was checked for the DEA removal rate of Congo red having a molecular weight of 697 g/mol in ethanol to understand the performance as an organic solvent nanofiltration membrane according to the concentration of PEI. Finally, the removal rate of Congo red was 90% or more.

• Maxillofacial Plastic and Reconstructive Surgery
• /
• v.11 no.1
• /
• pp.117-129
• /
• 1989

The commercial availability of processed heterogenous bone has provided the surgeons with almost unlimited supply, avoidance of additional operation and prevention of the postoperative complications. In addition to these merits, unnecessary bone bank, easy availibility and storage have been achieved. The purpose of this study was to compare and examine the healing capacity of Kiel bone, Pyrost and Osteovit which used as the processed heterografts for the reconstruction of bony defect. Twenty rabbits weighing about 1.7-2.0 Kg were selected and divided into two groups. In experimental group A, the left mandibular defect was allowed to fill with blood, and the right defect was filled with Kiel bone. In experimental group B, the left defect was grafted with Pyrost, and the right with Osteovit. The experimental animals were sacrified after 1, 2, 4 and 8 weeks and the grafted site was studied histologically. To evaluate the strength of healed bone, 2 rabbits from each experimental group and a nonoperated control were sacrified at the 6th week after implantation and used for biometric testing on universal testing machine. The results obtained were as follows : 1. It was considered that these heterogenous bone grafts has feeble or absent immunogenicity since all of them appeared to evoke little inflammatory or forign body reaction. 2. In all experimental groups, new bone formation began from the adjacent region of host bone and extended progressively into the defect sites. New bone was partly formed within the intertrabecular space of the implant and gradually united with the bone that formed at the margin of the host bone. 3. With Pyrost bone formation was rapid and prominent comparing with other graft materials. 4. Osteovit was begun to be absorbed from 2 weeks, and Kiel bone from 4 weeks, however Pyrost was remained to be intact until the end of 8 weeks. 5. As the results of tensile test, the mean values of maximum tensile stress were 1.11${\uparrow}$ $Kgf/mm^{2}$ in Pyrost implanted specimens, 0.85 $Kgf/mm^{2}$ in Osteovit, 0.42 $Kgf/mm^{2}$ in Kiel bone, 0.66 $Kgf/mm^{2}$ in blood filled specimens and 1..13 $Kgf/mm^{2}$ in control. These results indicate that heterogenous bones grafted have little antigenicity to the host tissue, and that they mediate effectively osteoconduction by providing the scaffold for the bone formation. Pyrost and Osteovit appeared to be suitable for the clinical use.