• The Journal of Advanced Prosthodontics
• /
• v.5 no.3
• /
• pp.305-311
• /
• 2013

PURPOSE. Over the past years, the adhesion of fiber posts luted with simplified adhesive systems has been a matter of great interest. The aim of this study was to assess the post retentive potential of a self-adhesive resin cement using different adhesive systems to compare the push-out bond strengths of fiber posts. MATERIALS AND METHODS. The post spaces of 56 mandibular premolar roots were prepared and divided into 4 experimental groups and further divided into 2 subgroups according to testing time (n=7). The fiber posts (Rely X Fiber Post) were luted with a self-adhesive resin cement (RelyX Unicem) and one of the following adhesive systems: no adhesive, a total-etch adhesive resin (Single Bond), a two-step self-etch adhesive resin (Clearfil SE Bond) and a one-step self-etch adhesive resin (Clearfil S3 Bond). Each root was cut horizontally, and 1.5 mm thick six root segments were prepared. Push-out tests were performed after one week or three months (0.5 mm/min). Statistical analysis were performed with three-way ANOVA (${\alpha}$=.05). RESULTS. Cervical root segments showed higher bond strength values than middle segments. Adhesive application increased the bond strength. For one week group, the total-etch adhesive resin Single Bond showed higher bond strength than the self-adhesive resin cement RelyX Unicem applied without adhesive resin at middle region. For 3 months group, the two-step self-etch adhesive resin Clearfil SE Bond showed the highest bond strength for both regions. Regarding the time considered, Clearfil SE Bond 3 months group showed higher bond strength values than one week group. CONCLUSION. Using the adhesive resins in combination with the self-adhesive resin cement improves the bond strengths. The bond strength values of two-step self-etch adhesive resin Clearfil SE Bond improved as time passes.

• Journal of Welding and Joining
• /
• v.17 no.2
• /
• pp.104-111
• /
• 1999

The interfacial microstructure and bond strength were examined for WC-Co/Cu/SM45C steel join using a nickel-plated copper in vacuum at 1323K for 0.6ks∼3.6ks. After bonding, microstructure in bonding interface was observed by OM(Optical Microscopy), SEM(Scanning Electron Microscopy) and EPMA(Eelectron Probe Micro Analyzer). The oil cooling was carried out at 353K, the cooling rate in air and furnace was 22K/s and 4.4K/s. respectively. It was found that dendritic widths increased with the content of cobalt and bonding times at 1323K. As a whole, bond strength values at the same bonding condition decreased in this order: WC-13wt.%Co/SM45Csteel. WC-8wt.%Co/SM45Csteel and WC-4wt.%Co/SM45Csteel. The bond strength of WC-13wt.%Co/S45C steel joint in oil cooling was 273MPa. This value was greatly higher than those of 125MPa in furnace cooling and 93MPa in air cooling at 1323K for 0.6ks. The bond strength values were found to be closely associated with the content of cobalt in WC-Co and cooling rate.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.4
• /
• pp.407-418
• /
• 2007

Purpose: The objective of this study was to evaluate the effects of hydrofluoric acid concentration & etching time on the shear bond strength between IPS Empress 2 ceramic and resin cement. Material and methods: Thirty three rectangular shape ceramic specimens($20{\times}12{\times}5mm$ size, IPS Empress 2 core materials) were used for this study. The ceramic specimens divided into ten experimental groups with three specimens in each group and were etched with hydrofluoric acid(4%, 9%) according to different etching times(30s, 60s, 90s, 120s, 180s). Etched surfaces of ceramic specimens were bonded with resin cement(Rely X Unicorn) using acrylic glass tube. All cemented specimens were tested under shear loading until fracture on universal testing machine at a crosshead speed of 0.5mm/min and the maximum load at fracture(kg) was recorded. Collected shear bond strength data were analyzed with one way ANOVA and Duncan tests. All etched ceramic surfaces were examined morphologically using SEM(scanning electron microscopy). Results: Shear bond strength of etching group$(35.89{\sim}68.01MPa)$ had four to seven times greater than no-etching group$(9.53{\pm}2.29MPa)$. The ceramic specimen etched with 4% hydrofluoric acid for 60s showed the maximum shear bond strength$(68.01{\pm}11.78MPa)$. Ceramic surface etched with 4% hydrofluoric acid for 60s showed most retentive surface texture. Conclusion: It is considered that 60s etching with 4% hydrofluoric acid is optimal etching methods for IPS Empress 2 ceramic bonding.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.3
• /
• pp.296-305
• /
• 2002

The main disadvantage of cement-retained implant restorations is their difficulty in retrievability. Advocates of cemented implant restorations frequently state that retrievability of the restoration can be maintained if a provisional cement is used. The purpose of this study was to find the optimal properties of provisional luting cements and the surface treatment of abutments in single implant abutment system. 30 prefabricated implant abutments, height 8mm, diameter 6mm, 3-degree taper per side, with light chamfer margins were obtained. Three commercially available provisional luting agents which were all zinc oxide eugenol type ; Cavitec, TempBond and TempBond NE were evaluated. No cement served as the control. TempBond along with vaseline, a kind of petrolatum (2:1 ratio) was also evaluated. Ten out of thirty abutments were randomly selected and abutment surfaces were sandblasted with $50{\mu}m$ aluminum oxide. Another ten abutments were sandblasted with $250{\mu}m$ aluminum oxide. A vertical groove, 1 mm deep and 5mm long was cut in each twenty abutments. Ten of them were sandblasted with $50{\mu}m$ aluminum oxide. The full coverage casting crowns were cemented to the abutments with the designated provisional luting agent. Specimens were stored in distilled water at $37^{\circ}C$ for 24 hours. Each specimen was attached to a universal testing machine. A crosshead speed of 0.5mm/min was used to apply a tensile force to each specimen. Within the limitations of this in vitro study, the following conclusions were drawn: 1. Tensile bond strength of provisional luting cements in no surface treatment decreased with the sequence of TempBond NE, TempBond, Cavitec, TempBond with vaseline, no cement. 2. Tensile bond strength more increased by surface treatment. Sandblasting with $250{\mu}m$ aluminum oxide exhibited the highest tensile bond strength in the abutment cemented with TempBond NE and sandblasting with $50{\mu}m$ aluminum oxide exhibited the highest tensile bond strength in cemented with TempBond. 3. In the aspect of a groove formation, tensile bond strength significantly increased in TempBond with vaseline only and the others had no significant effect on tensile bond strength.

• The korean journal of orthodontics
• /
• v.40 no.4
• /
• pp.267-275
• /
• 2010

Objective: The aim of this study was to evaluate and compare the shear bond strength (SBS) and failure-mode of orthodontic buttons bonded to erupted and unerupted teeth with conventional and self-etching adhesive systems. Methods: Eighty-four erupted and 84 unerupted, human third-molar teeth were used. For both groups, the buccal surfaces of each tooth were assigned one of the following type of adhesive systems (n = 12). A, Conventional systems: 1, Transbond XT (3M Unitek, Monrovia, CA, USA); 2, Prime & Bond NT (Dentsply/Caulk, Milford, USA); 3, Single Bond (3M ESPE, Minnesota, USA); and B, Self-etching adhesives; 4, Clearfil SE Bond (Kuraray, Okayama, Japan); 5, Transbond Plus (3M Unitek, Monrovia, CA, USA); 6, Clearfil S3 (Kuraray, Tokyo, Japan); 7, G Bond (GC, Tokyo, Japan). The SBSs of the attachments and the adhesive remnant index (ARI) scores were recorded. Data were analyzed with analysis of variance (ANOVA), independent-sample t-test and chi-square tests. Results: When the SBSs of erupted and unerupted teeth were compared, only the Clearfil-SE Bond and G-Bond were significantly different. Bond strengths of all adhesive systems were higher in unerupted teeth than erupted teeth, except the Single-Bond system. Conclusions: When using conventional adhesives, bonding to erupted and unerupted teeth may not be significantly different. However, clinicians need to take into consideration the types of self-etching systems before usage.

• International Journal of Concrete Structures and Materials
• /
• v.6 no.2
• /
• pp.123-134
• /
• 2012

There is significant concern in the engineering community regarding the safety and effectiveness of fiber-reinforced polymer (FRP) strengthening of RC structures because of the potential for brittle debonding failures. In this paper, previous research programs conducted by other researchers were reviewed in terms of the debonding failure of FRP laminates externally attached to concrete. This review article also discusses the influences on bond strength and failure modes as well as the existing experimental research and developed equations. Based on the review, several important conclusions were re-emphasized, including the finding that the bond transfer strength is proportional to the concrete compressive strength; that there is a certain bond development length that has to be exceeded; and that thinner adhesive layers in fact lower the chances of a concrete-adhesive interface failure. It is also found that there exist uncertainty and inaccuracy in the available models when compared with the experimental data and inconsistency among the models. This demonstrates the need for continuing research and compilation of data on the topic of FRP's bond strength.

• Computers and Concrete
• /
• v.24 no.3
• /
• pp.237-247
• /
• 2019

The key issue for the finite element analysis (FEA) of section steel reinforced concrete (SRC) structure is how to consider the bond-slip performance. However, the bond-slip performance is hardly considered in the FEA of SRC structures because it is difficult to achieve in the finite element (FE) model. To this end, the software developed by Python can automatically add spring elements for the FE model in ABAQUS to considering bond-slip performance. The FE models of the push-out test were conducted by the software and calculated by ABAQUS. Comparing the calculated results with the experimental ones showed that: (1) the FE model of SRC structure with the bond-slip performance can be efficiently and accurately conducted by the software. For the specimen with a length of 1140 mm, 3565 spring elements were added to the FE model in just 6.46s. In addition, different bond-slip performance can also be set on the outer side, the inner side of the flange and the web. (2) The results of the FE analysis were verified against the corresponding experimental results in terms of the law of the occurrence and development of concrete cracks, the stress distribution on steel, concrete and steel bar, and the P-S curve of the loading and free end.

• Journal of Industrial Technology
• /
• v.28 no.A
• /
• pp.195-198
• /
• 2008

Graphite and $MoS_2$ were added respectively to the Cu/Sn bond materials of the same composition as a lubricant in order to find out the effect of lubricants on the mechanical properties and the increase in density of the sintered products for microblades. The addition of $MoS_2$ as a lubricant was more beneficial to strength, fracture toughness, and hardness as well as densification than graphite. $MoS_2$ seemed to be more effective in reducing the friction between the metallic powders and die wall during hot pressing process. Due to the better wettability of MoS2 with bond metal alloy, less amount of interfacial defects which is detrimental to mechanical properties use observed.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.27 no.3
• /
• pp.444-456
• /
• 2000

To test the shear bond strength of a new "one-bottle adhesive" system to primary dentin two commercially available one-bottle adhesives (Prime & Bond NT, Single bond) and conventional three step system(Scotchbond Multi-Purpose Plus) were included for comparison. And We observe the interfacial morphology by scanning electron microscope. 90 primary molar teeth were embedded in acrylic and buccal and lingual surface were polished to 320 grit to create standardized dentin surface for testing. After bonding of composite resin to sample surfaces according to the manufacturer s direction and 1000 times thermocycling in dwell time 30 second, Shear bond strengths of adhesives to dentin were determined using universal testing machine and analyzed by ANOVA test. Another groups of specimens were treated by hydrochloric acid to secure the resin only and those tags were evaluated under SEM for their length and forms and the morphology of the bonding sites were also observed. The result are as follows. 1. Group I(Prime & Bond NT) showed higher shear bond strength than group iI(Single Bond) and III(Scotchbond Multi Purpose Plus) but no statistically significant difference was founded between groups(p>.05). 2. Relating long resin tags of $70-120{\mu}m$ were observed in samples of all groups under SEM. We could observed hybrid layer, resin tag and many lateral branches in every group. But, we observed in group III rare lateral branched than other two group and discontinuous hybrid layer.

• Restorative Dentistry and Endodontics
• /
• v.22 no.2
• /
• pp.680-692
• /
• 1997

New bonding agent systems have been supplied which operators can simply apply to conditioned tooth surfaces. The purpose of this study was to evaluate the shear bond strengths and the microleakages of three bonding agents and composite resins to dentin. Seventy-five extracted human maxillary and mandibular molar teeth were used in this study. For the shear bond strength test, the entire occlusal dentin surfaces of thirty teeth were exposed with Diamond Wheel Saw and smoothed with Lapping and Polishing Machine (South Bay Technology Co., U.S.A). For the microleakage test, Class V cavities were prepared in the buccal surfaces of fourtyfive teeth. They were randomly assigned into 3 groups according to dentin bonding agents ($Scotchbond^{TM}$ Multi-Purpose plus, ONE-$STEP^{TM}$ and Prime & $Bond^{TM}$)and composite resins (Z-100, $Aelitefil^{TM}$ and TPH $Spectrum^{TM}$) to be used. Bonding agents and composite resins were bonded to exposed dentin surfaces of the tooth crown and to Class V cavities on the buccal surfaces respectively according to manufacturer's directions. The shear bond strengths were measured by universal testing machine($U^{TM}$ AGS-100, Japan). In addition, the degree of micro leakage at the occlusal and gingival margin was examined by 2 % methylene blue and stereomicroscope(Olymous SZH 10, Japan). The results were as follows: 1. The shear bond strength to dentin was the highest value in SBMP-Plus group($16.68{\pm}7.38$ MPa) and the lowest value in Prime & Bond group($11.61{\pm}5.82$ MPa), but there was no significant difference of shear bond strength among three groups. 2. The degree of microleakage at both occlusal and gingival margin was showed the lowest in SBMP-Plus group and the highest in ONE-STEP group. 3. At both occlusal and gingival margin, there was significant difference of microleakage between SBMP-Plus and ONE-STEP/ Prime & Bond groups(p<0.05), but no significant difference of microleakage between ONE-STEP and Prime & Bond group(p>0.05).