A STUDY ON THE SHEAR BOND STRENGTHS AND MICROLEAKAGES OF THREE BONDING AGENTS ON DENTIN

상아질 접착제의 전단결합강도와 미세누출에 관한 연구

New bonding agent systems have been supplied which operators can simply apply to conditioned tooth surfaces. The purpose of this study was to evaluate the shear bond strengths and the microleakages of three bonding agents and composite resins to dentin. Seventy-five extracted human maxillary and mandibular molar teeth were used in this study. For the shear bond strength test, the entire occlusal dentin surfaces of thirty teeth were exposed with Diamond Wheel Saw and smoothed with Lapping and Polishing Machine (South Bay Technology Co., U.S.A). For the microleakage test, Class V cavities were prepared in the buccal surfaces of fourtyfive teeth. They were randomly assigned into 3 groups according to dentin bonding agents ($Scotchbond^{TM}$ Multi-Purpose plus, ONE-$STEP^{TM}$ and Prime & $Bond^{TM}$)and composite resins (Z-100, $Aelitefil^{TM}$ and TPH $Spectrum^{TM}$) to be used. Bonding agents and composite resins were bonded to exposed dentin surfaces of the tooth crown and to Class V cavities on the buccal surfaces respectively according to manufacturer's directions. The shear bond strengths were measured by universal testing machine($U^{TM}$ AGS-100, Japan). In addition, the degree of micro leakage at the occlusal and gingival margin was examined by 2 % methylene blue and stereomicroscope(Olymous SZH 10, Japan). The results were as follows: 1. The shear bond strength to dentin was the highest value in SBMP-Plus group($16.68{\pm}7.38$ MPa) and the lowest value in Prime & Bond group($11.61{\pm}5.82$ MPa), but there was no significant difference of shear bond strength among three groups. 2. The degree of microleakage at both occlusal and gingival margin was showed the lowest in SBMP-Plus group and the highest in ONE-STEP group. 3. At both occlusal and gingival margin, there was significant difference of microleakage between SBMP-Plus and ONE-STEP/ Prime & Bond groups(p<0.05), but no significant difference of microleakage between ONE-STEP and Prime & Bond group(p>0.05).