• Korean Journal of Materials Research
• /
• v.13 no.10
• /
• pp.640-644
• /
• 2003

NiCr thin films were fabricated by rf magnetron sputtering for applying to both the top electrode and absorption layer on Pb(Zr, Ti)O$_3$(PZT) thin films for infrared sensors. The rms roughness and resistivity of NiCr films prepared with Ni power of 80 W and Cr power of 50 W showed the most stable oxidation resistance after annealing at $600^{\circ}C$ for 5 min in oxygen ambient. The rms roughness and resistivity of NiCr films annealed at $V^{\circ}C$ in oxygen ambient were about 2$0\AA$ and $70 \mu$Ω-cm, respectively. As-deposited Ni/PZT/Pt and NiCr (Ni 80 W, Cr 50 W)/PZT/Pt structures showed well saturated hysteresis loops. However, in case of the samples annealed at $500^{\circ}C$ in oxygen ambient, only NiCr/PZT/Pt showed saturated loops having a remanent polarization of 20$\mu$C/$\textrm{cm}^2$. Ultra-thin NiCr films showed a possibility as a top electrode for infrared sensors.

• Proceedings of the IEEK Conference
• /
• 2000.06b
• /
• pp.24-27
• /
• 2000

Ferroelectric P $b_{0.99}$〔(Z $r_{0.6}$S $n_{0.4}$)$_{0.9}$ $Ti_{0.1}$〕$_{0.98}$N $b_{0.02}$ $O_3$(PNZST) thin films were deposited by a RF magnetron sputtering on (L $a_{0.5}$S $r_{0.5}$)Co $O_3$(LSCO)/Pt/Ti/ $SiO_2$/Si substrate using a PNZST target with excess PbO of 10 mole％. The thin films deposited at the substrate temperature of 500 $^{\circ}C$ were crystallized to a perovskite phase after rapid thermal annealing(RTA) The thin films annealed at 650 $^{\circ}C$ for 10 seconds in air exhibited the good crystal structures and ferroelectric properties. The remanent polarization and coercive field of the PNZST capacitor were about 20 $\mu$C/$\textrm{cm}^2$ and 50 kV/cm, respectively. The reduction of the polarization after 2.2$\times$10$^{9}$ switching cycles was less than 10 ％.0 ％.％.0 ％.0 ％.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.967-976
• /
• 1995

The possiblity of the existence of a spontaneous relaxor-normal ferroelectric transition was proposed and examined using 1~5 mol% PbZrO3-doped Pb(Ni1/3Nb2/3)O3-PbTiO3 (PNN-PT) systems having tetragonal symmetry at rom temperature. On cooling, the system with 60mol% Pb(Ni1/3Nb2/3)O3 underwent a spontaneous transition from a relaxor to a normal ferroelectric state. A microscopic examination demonstrates that the relaxornormal ferroelectric transition corresponds to a micro-macro domain switching accompanied with thermoelastic martensitic transformation. The long-range macrodomains below the transition temperature were characterized by twinlike 90$^{\circ}$macrodomains with tetragonal symmetry. The relaxor-normal ferroelectric transition was further correlated with the rhombohedral-tetragonal first-order structural transition.

• Journal of the Korean Ceramic Society
• /
• v.42 no.4
• /
• pp.219-223
• /
• 2005

A promising capacitor, which has conformable step coverage and good uniformity of thickness and composition, is needed to manufacture high-density non-volatile FeRAM capacitors with a stacked cell structure. In this study, ferroelectric $Bi_{3.61}Nd_{0.39}Ti_3O_{12}$ (BNdT) thin films were prepared on $Pt(111)/TiO_2/SiO_2/Si$ substrates by the liquid delivery system MOCVD method. In these experiments, $Bi(ph)_{3}$, $Nd(TMHD)\_{3}$ and $Ti(O^iPr)_{2}(TMHD)_{2}$ were used as the precursors and were dissolved in n-butyl acetate. The BNdT thin films were deposited at a substrate temperature and reactor pressure of approximately $600^{\circ}C$ and 4.8 Torr, respectively. The microstructure of the layered perovskite phase was observed by XRD and SEM. The remanent polarization value (2Pr) of the BNdT thin film was $31.67\;{\mu}C/cm^{2}$ at an applied voltage of 5 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.1084-1087
• /
• 2001

The (Sr$\sub$0.85/Ca$\sub$0.15/)TiO$_3$(SCT) thin films are deposited on Pt-coated electrode(Pt/TiN/SiO$_2$/Si) using RF sputtering method. The crystallinity of SCT thin films is increased with increase of substrate temperature in the temperature range of 100[$^{\circ}C$]∼500[$^{\circ}C$]. Also, the crystallinity of SCT thin films are obtained at the substrate temperature above 400[$^{\circ}C$]. SCT thin films had (111) preferred orientation. The dielectric constant changes almost linearly in temperature ranges of-80∼+90[$^{\circ}C$]. The temperature properties of the dielectric loss have a stable value within 0.1. SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200[kHz].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.566-569
• /
• 2002

The $(Sr_{0.9}Ca_{0.1})TiO_3$(SCT) thin films are deposited on Pt-coated electrode (Pt/TiN/$SiO_2$/Si) using RF sputtering method. The maximum dielectric constant of SCT thin film is obtained by annealing at $600[^{\circ}C]$. The temperature properties of the dielectric loss have a value within 0.02 in temperature ranges of $-80{\sim}+90[^{\circ}C]$. The capacitance characteristics had a stable value within ${\pm}4[%]$. The drastic decrease of dielectric constant and increase of dielectric loss in SCT thin films is observed above 200[kHz].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.325-329
• /
• 1998

In this paper, the (Sr$_{1-x}$ Ca$_{x}$)TiO$_3$(SCT) thin films were deposited at various substrate temperature using RF magnetron sputtering method on optimized Pt-coated electrodes (Pt/TiN/SiO$_2$/Si). An influence of substrate temperature and annealing temperature on the structural and dielectric properties are investigated. The substrate temperature changed from 100[$^{\circ}C$] to 500[$^{\circ}C$] and crystalline SCT thin films were deposited abode 400[$^{\circ}C$]. All thin films had (111) preferred orientation, the (100) oriented films were obtained at the substrate temperature above 400[$^{\circ}C$]. The dielectric constant changes almost linearly in the temperature region of -80~+90[$^{\circ}C$], the temperature characteristics of the dielectric loss exhibited a stable value within 0.1, then not affected by substitutional contents. The capacitance characteristics appears a stable value within $\pm$5[%].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.295-299
• /
• 1999

The (S $r_{1-x}$C $a_{x}$)Ti $O_3$(SCT) thin films are deposited on Pt-coated electrode(Pt/TiN/ $SiO_2$/ Si) using RF sputtering method with substitutional contents of Ca. The maximum grain of thin films is obtained by substitution of Ca at 15[mol%]. The dielectric constant was increased with increasing the substitutional contents of Ca, while it was decreased if the substitutional contents of Ca exceeded over 15[mo1%]. The dielectric constant changes almost linearly in temperature ranges of -80~ +90[$^{\circ}C$]. The temperature properties of the dielectric loss have a stable value within 0.02 independent of the substitutional contents of Ca. All SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200(kHz).)..

• Proceedings of the KIEE Conference
• /
• 1992.07b
• /
• pp.759-761
• /
• 1992

$0.10Pb(Sb_{1/2}Sn_{1/2})O_3-0.25PbTiO_3-0.65PbZrO_3+MnO_2(0.18mol%)$, NiO(0.15mol%) temary compound ceramics won fabricated by the mixed-oxide method. Noise properties of the pyroelectric infrared sensor were investigated with particle size of the raw materials and gain size of the specimens. Particle size were decreased and sintered density, voltage resposivity were increased with increasing the ball-mill times. The specimen ball-milled for a 80[hr] showed a good pop-corn noise properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.04b
• /
• pp.80-83
• /
• 2000

The post-annealing treatments on rf magnetron sputtered PZT($Pb_{1.05}(Zr_{0.52},\;Ti_{0.48})O_3$) thin films($4000{\AA}$) have been investigated for a structure of PZT/Pt/Ti/Coming glass(1737). Crystallization properties of PZT films were strongly dependent on RTA(Rapid Thermal Annealing) annealing temperature and time. We were able to obtain a perovskite structure of PZT at $650^{\circ}C$ and 10min. P-E curves of Pd/PZT/Pt capacitor demonstrate typical hysteresis loops. The measured values of $P_r$, $E_c$ were $8.1[{\mu}C/cm^2]$, 95[kV/cm] respectively. Polarization value decrease about 25% after $10^9$ cycles.