• Journal of Welding and Joining
• /
• v.23 no.6
• /
• pp.87-92
• /
• 2005

It has been well hewn that ductile fracture of steels is accelerated by triaxial stresses. The characteristics of ductile crack initiation in steels are evaluated quantitatively using a two-parameters criterion based on equivalent plastic strain and stress triaxiality. The present study focuses on the effects of strength mismatch, which can elevate plastic constraint due to heterogeneous plastic straining, on the critical condition for ductile fracture initiation usinga two-parameter criterion. Fracture initiation testing has been conducted under static loading using notched round bar specimens which had different notch locations. This study provides the fundamental clarification of the effect of strength mismatching and effect of notch location on the critical condition to ductile crack initiation from notch root using fuite element method and ultrasonic-mechatronics system. The critical condition of ductile crack initiation from notch root of strength mismatched tensile specimens under static loading appeared to be almost the same as those of homogeneous tensile specimens with circumferential sharp notch specimen. Also, the effect of notch location in mismatched specimens was estimated using finite element(FE) analyses.

• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.6-9
• /
• 2012

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.20-22
• /
• 2005

In this study, deformation of flange of pedestal crane due to Lug welding and lifting. Thermo elasto-plastic analysis was performed using commercial FE code MSC/MARC. The accuracy control of roundness is critical to the final product assembly. Deformation is mainly occurs during Lug welding. So, we determine welding sequence and Lug space in order to reduce deformation. And we also investigate safety of lifting Lug during crane lifting.

• Proceedings of the KWS Conference
• /
• 1996.05a
• /
• pp.145-148
• /
• 1996

• Proceedings of the KWS Conference
• /
• 1992.10a
• /
• pp.210-212
• /
• 1992

• International Journal of Korean Welding Society
• /
• v.1 no.2
• /
• pp.51-60
• /
• 2001

A prediction method for determining the welding residual stress by artificial neural network is proposed. A three-dimensional transient thermo-mechanical analysis has been performed for the $CO_2$ arc welding using the finite element method. The first part of numerical analysis performs a three-dimensional transient heat transfer analysis, and the second part then uses the results of the first part and performs a three-dimensional transient thermo-elastic-plastic analysis to compute transient and residual stresses in the weld. Data from the finite element method are used to train a back propagation neural network to predict the residual stress. Architecturally, the fully interconnected network consists of an input layer for the voltage and current, a hidden layer to accommodate the failure mechanism mapping, and an output layer for the residual stress. The trained network is then applied to the prediction of residual stress in the four specimens. It is concluded that the accuracy of the neural network predicting method is fully comparable with the accuracy achieved by the traditional predicting method.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.10a
• /
• pp.195-196
• /
• 2006

• Journal of Welding and Joining
• /
• v.2 no.1
• /
• pp.41-48
• /
• 1984

Recrystallization technique was applied to analyze plastic strain at the notch tip of coarse grain HAZ in mild steel (SB 41) and high strength steel (SA 588). The notch tip of specimen was deformed by three point bending. Accumulated displacement (Crack Opening Displacement ${delta}t$) by the monotonic and cyclic loading under room temperature and hot strain embrittlement temperature ($250^{\circ}C$) was 0~1.0mm. Recrystallization heat treatment conditions were $650^{circ}C{ imes}3hr$ for SB 41 and $700^{circ}C{ imes}3hr$ for SA 588. The experimental results obtained were as follows ; 1) Distribution of the effective plastic strain at plastic zone was appeared by the function of crack opening displacement, and plastic zone or the effective plastic strain increased with crack opening displacement. 2) Plastic strain at notch tip of HAZ due to accumulated hot strain calculated as follows. .epsilon. over bar $_{p}$ = .epsilon. over bar $_{cr}$ (x/ $R_{x}$ ) $^{m}$ (m=0.25) 3) Work hardending ratio of notch tip for hot strain was linearly increased with .epsilon. over bar $_{max}$ and dependent upon the material types.s.

• Journal of Welding and Joining
• /
• v.18 no.6
• /
• pp.83-88
• /
• 2000

Variation of welded-joint hardness and tensile strength of a accelerated-cooled fine-grained ferritic-pearlitic steel with heat input was investigated. In a weld heat-affected zone, a softened zone was formed and it had lower hardness than that of a base metal. While the width of a softened zone increased continuously with an increase of heat input up to 100kJ/cm. the minimum hardness in a softned zone was almost constant after a continuos decrease up to 60KJ/cm. Because of a softened zone, the welded-joint was fractured in the HAZ and its maximum reduction of tensile strength was about 20%. Measured welded-joint tensile strength and calculated minimum tensile strength in a welded-joint was almost same, which means that the plastic restraint of a softened zone did not occur in this experiment. It is believed that as a softened zone width-to-specimen thickness ratio is as high as 2~6 in this experiment, the plastic restraint effect does not occur. Theoretical analysis shows that the plastic restraint effect occurs only when the ratio is below 0.5.

• Journal of Welding and Joining
• /
• v.15 no.2
• /
• pp.64-71
• /
• 1997

In order to define the effects on shapes of welding joint, during Post Welding Heat Treatment (PWHT), we have carried out numerical analysis on the several test pieces by using computer program which was based on thermal-elasto-plastic-creep theories for the study. And then, welding residual stresses after PWHT were measured same test-pieces to compare with the results of numerical analysis. The main results obtained from this study is as follows: 1) The distribution modes of welding residual stresses are same on the all test pieces after and during PWHT by the both sides (measurement and numerical analysis). 2) The mechanical difference for change the thickness of plate and bevel angle are not appeared. 3) In a mechanical point of view (like material quality test, welding deformation etc.), manimum bevel angle (40$^{\circ}$.) is more suitable than maximum bevel angle (70$^{\circ}$).