• Journal of Fisheries and Marine Sciences Education
• /
• v.10 no.1
• /
• pp.69-78
• /
• 1998

Thermal sprayed Cu-Ni alloy coating on the carbon steel was carried out impingement erosion-corrosion test and electrochemical corrosion test in the marine environment. The impingement erosion-corrosion behavior and electrochemical corrosion characteristics of substrate(SS400) and thermal sprayed Cu-Ni coating was investigated, and the corrosion control efficiency of Cu-Ni coating to substrate was estimated quantitatively. Main results obtained are as follows : 1) The weight loss rate of Cu-Ni coating layer by the impingement erosion-corrosion compared with substrate was smaller in high specific resistance solution than in low specific resistance solution. 2) The corrosion potential of Cu-Ni coating layer spray coating in the marine environment became more noble than that of substrate. 3) With the lapse of time, corrosion current density of Cu-Ni coating layer became stable, but that of substrate was increased. 4) As the corrosion control efficiency of Cu-Ni coating layer in the marine environment was over 90%, its anti-corrosion characteristics was excellent.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.3
• /
• pp.128-136
• /
• 2014

In the present study, we successfully developed an eco-friendly chemical etching solution and proper condition for plating on ABS material. The mechanism of forming Ni plating layer on ABS substrate is known as following. In general, the etching solution used for the etching process is a solution of chromic acid and sulfuric acid. The etching solution is given to the surface resulting in elution of butadiene group, so-called anchor effect. Such a rough surface can easily adsorb catalyst resulting in the increase of adhesion between ABS substrate and Ni plating layer. However a use of chromic acid is harmful to environment. It is, therefore, essential to develop a new alternative solution. In the present study, we proposed an eco-friendly etching solution composed of potassium permanganate, sulfuric acid and phosphoric acid. This solution was testified to observe the surface microstructure and the pore size of electrical Ni plating layer, and the adhesive correlation between deposited layers fabricated by electro Ni plating was confirmed. The result of the present study, the newly developed, eco-friendly etching solution, which is a mixture of potassium permanganate 25 g/L, sulfuric acid 650ml/L and phosphoric acid 250ml/L, has a similar etching effect and adhesion property, compared with the commercially used chromium acid solution in the condition at $70^{\circ}C$ for 5 min.

• Proceedings of the KIEE Conference
• /
• 1991.07a
• /
• pp.217-220
• /
• 1991

Ni-Zn ferrite powders in the few hundred angstrum size range and up have been synthesized by a wet direct method. The coprecipitate were prepared by adding alkaline solution into the constituent metal ions solution. and subsequent calcined at various temperature. At 95, the particles were ultrafine spherical shaped particles of about 500(A) in diameter.

• Corrosion Science and Technology
• /
• v.15 no.1
• /
• pp.13-17
• /
• 2016

The aim of this study was to evaluate the use of iron-nickel oxide ($Fe_2O_3$.NiO) nanopowder (FeNi) as an anti-corrosion pigment for a different application. The corrosion protection ability and the mechanism involved was determined using aqueous solution of FeNi prepared in a corrosive solution containing 3.5 wt.% NaCl. Anti-corrosion abilities of aqueous solution were determined using electrochemical impedance spectroscopy (EIS) on line pipe steel (API 5L X-80). The protection mechanism involved the adsorption of metallic cations on the steel surface forming a protective film. Analysis of EIS spectra revealed that corrosion inhibition occurred at low concentration, whereas higher concentration of aqueous solution produced induction behavior.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.45-45
• /
• 2003

• Korean Journal of Materials Research
• /
• v.26 no.7
• /
• pp.393-399
• /
• 2016

Flower-like nickel oxide (NiO) catalysts were coated on NiCrAl alloy foam using a hydrothermal method. The structural, morphological, and chemical bonding properties of the NiO catalysts coated on the NiCrAl alloy foam were investigated by field-emission scanning electron microscopy, scanning electron microscopy-energy dispersive spectroscopy, X-ray diffraction, and X-ray photoelectron spectroscopy, respectively. To obtain flower-like morphology of NiO catalysts on the NiCrAl alloy foam, we prepared three different levels of pH of the hydrothermal solution: pH-7.0, pH-10.0, and pH-11.5. The NiO morphology of the pH-7.0 and pH-10.0 samples exhibited a large size plate owing to the slow reaction of the hydroxide ($OH^-$) and nickel ions ($Ni^+$) in lower pH than pH-11.5. Flower-like NiO catalysts (${\sim}4.7{\mu}m-6.6{\mu}m$) were formed owing to the fast reaction of $OH^-$ and $Ni^{2+}$ by increased $OH^-$ concentration at high pH. Thus, the flower-like morphology of NiO catalysts on NiCrAl alloy foam depends strongly on the pH of the hydrothermal solution.

• Resources Recycling
• /
• v.28 no.4
• /
• pp.30-36
• /
• 2019

In this study, Li powder was recovered from the by-product of LNO ($Li_2NiO_2$) process, which is the positive electrode active material of waste lithium ion battery, through the $CO_2$ thermal reaction process. In the process of recovering Li powder, the $CO_2$ injection amount is 300 cc/min. The $Li_2NiO_2$ award was phase-separated into the $Li_2CO_3$ phase and the NiO phase by holding at $600^{\circ}C$ for 1 min. After this, the collected sample:distilled water = 1:50 weight ratio, and after leaching, the solution was subjected to vacuum filtration to recover $Li_2CO_3$ from the solution, and the NiO powder was recovered. In order to increase the purity of Ni, it was maintained in $H_2$ atmosphere for 3 hours to reduce NiO to Ni. Through the above-mentioned steps, the purity of Li was 2290 ppm and the recovery was 92.74% from the solution, and Ni was finally produced 90.1% purity, 92.6% recovery.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.13 no.4
• /
• pp.410-414
• /
• 2013

We report the wet etching of titanium nickel (TiNi) films for the production of nano-electro-mechanical (NEM) device. $SiO_2$ and $Si_3N_4$ have been selected as sacrificial layers of TiNi metal and etched with polyethylene glycol and hydrofluoric acid (HF) mixed solution. Volume percentage of HF are varied from 10% to 35% and the etch rate of the $SiO_2$, $Si_3N_4$ and TiNi are reported here. Within the various experiment results, 15% HF mixed polyethylene glycol solution show highest etch ratio between sacrificial layer and TiNi metal. Especially $Si_3N_4$ films shows high etch ratio with TiNi films. Wet etching results are measured with SEM inspection. Therefore, this experiment provides a novel method for TiNi in the nano-electro-mechanical device.

• Journal of Powder Materials
• /
• v.14 no.4
• /
• pp.238-244
• /
• 2007

The electrophoretic deposition process of Ni nano-particles in organic suspension was employed for self-repairing of heat exchanger tubes. For this purpose, Ni nano-particles prepared by levitational gas condensation method were dispersed into the solution of ethanol with the addition of dispersant Hypermer KD2. For electrophoretic deposition of Ni nano-particles on the Ni alloy specimen, constant electric fields of 20 and 100 V $cm^{-1}$ were applied to the specimen in Ni-dispersed solution. It was found that as electrophoretic deposition proceeds, the size of the pit or crack remarkably decreased due to the agglomeration of Ni nano-particles at the pit or crack. This strongly suggests that the electrophoretic mobility of the charged particles is larger for the damaged part with a higher current value rather than outer surfaces with a lower current value.

• Korean Journal of Metals and Materials
• /
• v.50 no.6
• /
• pp.419-425
• /
• 2012

The purpose of this research was to develop a low Ni austenitic cast iron through replacing Ni by Cu and Mn because they are cheaper than Ni. The effect of the Cu content (6-12 wt%) on the microstructure characteristics was investigated in Fe-3%C-16%(Ni+Cu+Mn) cast iron. Contrary to general effect of the Cu on cast iron, the result of the microstructure analysis indicated that bainite and cementite were formed in high Cu content (>8 wt%Cu). A crystallized Cu-solution (Cu-Mn) phase and MnS in the Cu-solution were formed. The quantity of those phases increased as the Cu content increased. Consequently, the high Cu content in the composition ratio (Ni+Cu+Mn=16%) caused the formation of Cu-Mn/MnS and those phases decreased the effect of Cu and Mn on austenite formation. For this reason, bainite and cementite were formed in high Cu content.