• Korean Journal of Materials Research
• /
• v.16 no.9
• /
• pp.578-583
• /
• 2006

We studied the physical properties of Ni-Zn ferrites by adding different chemicals such as $SO_4$, Cl, and $NO_3$. Specimens were prepared by the coprecipitation method and sintered at temperatures $950^{\circ}C,\;1,150^{\circ}C,\;and\;1,350^{\circ}C$, respectively. X-ray diffractions showed a spinel structure and the optical microscopy revealed grain size of 0.3 to 0.6 ${\mu}m$. The optimum sintering temperature to obtain fine, sintered microstructure depended on the additive : Cl and $NO_3\;at\;950^{\circ}C\;and\;SO_4\;at\;1,150^{\circ}C$. According to particle size analysis, higher magnetic permeability and magnetization value were observed with Cl and $NO_3\;than\;SO_4$. As sintering temperature was raised from $950^{\circ}C$ to $1,350^{\circ}C$, the average grain diameter, initial permeability and the magnetic moment also increased.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.260-260
• /
• 2015

본 연구는 높은 인장력, 좋은 내마모성, 열전도성, 경도와 자성 등의 특성을 가진 니켈 코발트 합금 도금액 개발에 있어 첨가제를 첨가하여 피막 특성을 관찰하였다. Ni-Co 합금 도금액 개발을 위해 니켈 염으로 썰파민산 니켈 혹은 황산 니켈을 이용하여 황산코발트를 50g/L 혼합하여 $5A/dm^2$의 전류를 가할 경우 약 $40{\mu}m/hr$의 도금속도를 나타내었으며 코발트의 공석량은 50~55wt.% 였다. 도금액에 Leveler 및 wetter를 첨가하여 도금피막 특성을 관찰하였으며 이때 도금피막에 작용하는 내부응력을 관찰한 결과 썰파민산 니켈을 사용한 도금액의 내부응력이 낮음을 확인할 수 있었다.

• Journal of Surface Science and Engineering
• /
• v.37 no.1
• /
• pp.28-39
• /
• 2004

The effect of trace metallic additives on microstructure, surface appearance and hardness of zinc electrodeposits was investigated by using sulfate bath and flow cell system. The preferred orientation of Zn deposit with Fe additive was (103)(104)+(002) mixed texture and that of Zn deposits with both Fe-Ni and Fe-Co additives was (10 1), while Zn deposits with Fe-Cr additives had (002) preferred orientation. The surface morphology of the zinc deposits was closely related to the preferred orientation of the deposits. The glossiness of Zn deposit with Fe-Ni additives was higher than that of pure Zn deposit, while the glossiness of Zn deposits with both Fe-Co and Fe-Cr additives was lower than that of pure Zn deposit. The hardness of Zn deposits with both Fe-Ni and Fe-Co additives was noticeably higher than that of Zn-Fe deposit, while that of Zn deposit with Fe-Cr additives was similar to that of Zn-Fe deposit.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.218-219
• /
• 2012

Carbon coils could be synthesized using $C_2H_2/H_2$ as source gases and $SF_6$ as an incorporated additive gas under thermal chemical vapor deposition system. Prior to the carbon coils deposition reaction, two kinds of samples having different combination of Ni catalyst and substrate were employed, namely a commercially-made $Al_2O_3$ ceramic boat with Ni powders and a commercially-made $Al_2O_3$ substrate with Ni layer. By using a commercially-made $Al_2O_3$ ceramic boat, the production yield of carbon coils could be enhanced as much as 10 times higher than that of $Al_2O_3$ substrate. Furthermore, the dominant formation of the microsized carbon coils could be obtained by using $Al_2O_3$ ceramic boat.

• Journal of Hydrogen and New Energy
• /
• v.24 no.1
• /
• pp.1-11
• /
• 2013

Additives such as glycerol, methanol, acetone, and ethanol were used to prevent $NaBO_2$ from precipitation, and their effects on hydrogen generation properties of $NaBH_4$ hydrolysis were investigated. When the concentration of additives was 5 wt%, the additives such as methanol, acetone, and ethanol could not prevent $NaBO_2$ precipitation. Although glycerol prevented $NaBO_2$ precipitation, conversion efficiency decreased to 78.0% due to its viscosity. Based on test results, hydrogen generation tests were also performed at various concentration of glycerol and methanol to investigate the concentration effects on hydrogen generation properties. As the concentration of glycerol increased from 1 wt% to 3 wt%, conversion efficiency increased owing to additive effect. When its concentration increased to 5 wt%, conversion efficiency decreased due to its viscosity. As the concentration of methanol increased from 5 wt% to 10 wt%, conversion efficiency increased owing to additive effect. When its concentration increased to 15 wt%, conversion efficiency decreased due to $NaB(OCH_3)_4$ precipitate. Although conversion efficiency decreased about 1% when 3 wt% glycerol was added, $NaBO_2$ precipitation was prevented. Consequently, addition of 3 wt% glycerol to $NaBH_4$ solution improves stability of hydrogen generation system.

• Journal of Environmental Science International
• /
• v.30 no.11
• /
• pp.945-956
• /
• 2021

In this study, the effects of single and binary heavy metals toxicity on the growth and phosphorus removal ability of Bacillus sp.. known as be a phosphorus-removing microorganism, were quantitatively evaluated. Cd, Cu, Zn, Pb, Ni were used as heavy metals. As a result of analysis of variance of the half of inhibition concentration and half of effective concentration for each single heavy metal treatment group, the inhibitory effect on the growth of Bacillus sp. was Ni < Pb < Zn < Cu < Cd. And the inhibitory effect on phosphorus removal by Bacillus sp. was Ni < Pb < Zn < Cu < Cd. When analyzing the correlation between growth inhibition and phosphorus removal efficiency of a single heavy metal treatment group, a negative correlation was found (R² = 0.815), and a positive correlation was found when the correlation between IC₅₀ and EC₅₀ was analyzed (R² = 0.959). In all binary heavy metal treatment groups, the interaction was an antagonistic effect when evaluated using the additive toxicity index method. This paper is considered to be basic data on the toxic effects of heavy metals when phosphorus is removed using phosphorus removal microorganisms in wastewater.

• Korean Journal of Environmental Agriculture
• /
• v.35 no.1
• /
• pp.79-86
• /
• 2016

BACKGROUND: This study was initiated to quantitatively evaluate the effects of five heavy metals on the growth and P removal efficiencies of Alcaligenes sp., known as the Phosphorus Accumulating Organisms (PAOs). It was cultivated in the batch system with five heavy metals, such as Cd, Cu, Zn, Pb and Ni, added in single and binary mixtures, respectively.METHODS AND RESULTS: IC₅₀ (half of inhibition concentration of bacterial growth) and EC₅₀ (half of effective concentration of phosphorus removal Efficiencies) were used to quantitatively evaluate the effects of heavy metals on the growth and phosphorus removal Efficiencies of Alcaligenes sp. In addition, Additive Index Value (A.I.V.) method was used to evaluate the interactive effects between Alcaligenes sp. and heavy metals. As a result, as the five heavy metals were singly added to Alcaligenes sp., the greatest inhibitory effects on the growth and P removal efficiencies of each bacteria was observed in the cadmium (Cd). In the binary mixture treatments of heavy metals, the treatments of lowest IC₅₀ and EC₅₀ were the Cd + Cu treatment. Based on the IC₅₀ and EC₅₀ of the binary mixtures of heavy metals treatments, most interactive effects between the heavy metals were found to be antagonistic.CONCLUSION: Based on the results obtained from this study, it appears that they could provide the basic information about the toxic effects of the respective treatments of single and binary mixtures of heavy metals on the growth and P removal efficiencies of Alcaligenes sp. through further study about the characterization of functional proteins involved in toxic effects of heavy metals.

• Journal of the Microelectronics and Packaging Society
• /
• v.30 no.4
• /
• pp.61-68
• /
• 2023

In this study, Sn-3.5Ag-15.0Fe composite solder was manufactured and applied to TLP bonding to change the entire joint into a Sn-Fe IMC(intermetallic compound), thereby applying it as a high-temperature solder. The FeSn₂ IMC formed during the bonding process has a high melting point of 513℃, so it can be stably applied to power modules for power semiconductors where the temperature rises up to 280℃ during use. As a result of applying ENIG surface treatment to both the chip and substrate, a multi-layer IMC structure of Ni₃Sn₄/FeSn₂/Ni₃Sn₄ was formed at the joint. During the shear test, the fracture path showed that cracks developed at the Ni₃Sn₄/FeSn₂ interface and then propagated into FeSn₂. After 2hours of the TLP joining process, a shear strength of over 30 MPa was obtained, and in particular, there was no decrease in strength at all even in a shear test at 200℃. The results of this study can be expected to lead to materials and processes that can be applied to power modules for electric vehicles, which are being actively researched recently.

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.241-248
• /
• 2003

We controlled the amount of Y$_2$O$_3$additives, 8 mol% and 10 mol%, and the type of carbon pore former, activated carbon and carbon black, to improve the strength of porous NiO-YSZ anode materials for solid oxide fuel ceil. The 3-point flexural strength, porosity and electrical conductivity were evaluated. As a result, the strength of anode materials with the addition of carbon black was markedly improved. The strength of NiO-10 mol%YSZ sintered at relatively higher temperature was higher than that of NiO-8 mol%YSZ materials. The electrical conductivity of NiO-10 mol%YSZ with carbon black was evaluated as much as 10$^2$∼10$^3$S/cm at 700$^{\circ}C$∼1000$^{\circ}C$ in reducing atmosphere.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1624-1626
• /
• 2004

This study was to measure the minuteness structure, piezoelectric properties of (0.3-x)PMN- xPSS -0.7PZT+0.5[wt%]NiO+0.5(wt%)$MnO_2$ (x=0.05, 0.10, 0.15, 0.20, 0.25)ceramics according to sintering temp- erature and PSS(mol%) after manufacturing the specimens with a general method. the results of this study were gotten such as follows. The crystal structure of ceramic has the rombohedral structure in XRD. It appeared that addition of Ni, Mn additive was helpful to the formation of stable structure. The electrome- chanical coupling coefficient(kp) showed good properites on the whole, showed its maximum value 25.94[%] in specimens sintered at 1100[$^{\circ}C$], x=0.25mol. The mechanical quality coefficient(Qm) showed its maximum value 272.42 in specimens sintered at 1150[$^{\circ}C$], x=0.05mol. and was decreased by increasing PSS[mol%] The temperature coefficient of the resonant frequency(TCFr) showed stable properties in all sintering temperature with x=0.05mol. Especially good stability of 0.0054[%/$^{\circ}C$] showed in specimens sintered at 1100$^{\circ}C$, x=0.05mol.