• Journal of Powder Materials
• /
• v.11 no.2
• /
• pp.143-148
• /
• 2004

In the present study, $TiO_2$ imbedded composite powders have been successfully prepared from the (Cu. Zn)/$TiO_2$ composite salt solution. The composite (Cu, Zn)/$TiO_2$ powders were formed by drying the solution at 200~$600^{\circ}C$ in the hydrogen atmosphere. Photocatalytic characteristics was evaluated by detecting the decomposition ratio of aniline blue with UV-visible spectrophotometer(Shimazu Co., UV-1601). Phase analysis of (Cu, Zn)/$TiO_2$ composite powders was carried out by XRD and DSC, and powder size was measured with TEM. The mean particle size of composite powders was about 100mm. As the reduction temperature increases, a few zinc sulfide and oxide phases was formed and copper oxide phase was reduced. The decomposition ratio of aniline blue was about 80％ under the UV irradiation by the TiO$_2$ phase in the composite (Cu, Zn)/$TiO_2$ powders and similar decomposition ratio of 80％ was obtained at the UV lightless condition by virtue of Cu and Zn compounds.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.4
• /
• pp.65-69
• /
• 2012

Composite coating can be manufactured during the electroplating with the bath containing a suspension of particles: ceramic, polymer, nanopowders. Improvement of hardness, wear resistance, corrosion resistance and lubrication properties are well-known advantage of composite coating. In this study, nano $TiO_2$ powder dispersed Ni composite plating was investigated. The improvement of surface hardness and photo decomposition effects can be expected in this coating. Zeta potential was measured with pH. The effect of ultrasonication time and types of ultrasonicator were studied to minimize the agglomeration of $TiO_2$ nanopowders in the electrolyte. Optimum conditions for nano $TiO_2$ dispersed Ni composite coating were $40mA/cm^2$ of current density, pH 3.5, and $50^{\circ}C$. At these conditions, $TiO_2$ nanoparticles contents in the Ni deposit was 15-20 at.%.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.9
• /
• pp.561-564
• /
• 2015

Nano-size $BaTiO_3$ powder was synthesized by relatively simple hydrothermal reaction method. Finely dispersed Ti hydroxide precursor was first precipitated using $Ti(SO_4)_2$ and NaOH solution by applying ultrasonic power and washed thoroughly to remove $SO_4{^{2-}}$ and $Na^+$ ion. Then hydrothermal reaction was done at $160^{\circ}C$ for 6 hrs using solution prepared by washed Ti hydroxide precursor slurry and $Ba(OH)_2{\cdot}8H_2O$ with Ti:Ba mole ratio of 1:1. 200 ~ 500 nm size and uniform size distributed $BaTiO_3$ powder was synthesized by relatively low temperature and simple process.

• Textile Coloration and Finishing
• /
• v.20 no.6
• /
• pp.1-7
• /
• 2008

The effects of $TiO_2$ contents and UV irradiation treatment on the surface properties of PLA films embedded with $TiO_2$ nanoparticle were investigated. Whereas UV irradiation decreased reflectance of the treated PLA films proportionally with increasing UV energy, the reflectance of PLA/$TiO_2$ films increased with increasing UV energy. The UV irradiation treatment caused PLA/$TiO_2$ blend films more polar as indicated in the generation of new carbonyl group and decrease in zeta potentials, which was more pronounced with the introduction of $TiO_2$. Upon UV irradiation, $TiO_2$ particles appeared on the film surface as observed in SEM images. The PLA/$TiO_2$ blend films showed photocatalytic properties such as photobleaching of methylene blue, deodorization of ammonia and antimicrobial activity in comparison with pure PLA films.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.172-173
• /
• 2021

With the development of nano-reinforcement technology and the increasing concern for environmental issues, TiO₂ nanomaterials have received wide attention as an additive besides carbon nanomaterials that can be used to enhance the mechanical properties of cement-based materials. Also, TiO₂-based materials can allow cement-baned materials with photocatalytic capability, providing a potentially effective approach to reduce environmental problems. In this work, compressive strength, splitting tensile strength, and degradation of methylene blue solution were used as target to assess the effect of TiO₂ nanotubes on the mechanical strength and photocatalytic effect of hardened cement paste at different curing time. According to the strength results, the optimum amount of TiO₂ was identified as 0.5% of the weight of cement. Meanwhile, the TiO₂ nanotubes-reinforced specimen exhibited better photocatalytic effect in the early stage of curing.

• Journal of Photoscience
• /
• v.12 no.1
• /
• pp.17-23
• /
• 2005

Application of a new photocatalyst has been attempted to improve the efficiency and rates of photocatalytic degradation of azo dyes by using a model dye such as Methyl Orange. As a new photocatalyst, $TiO_2$ encapsulated EFAL-removed zeolite Y ($TiO_2$ /EFAL-removed zeolite Y) has been synthesized by ion-exchange in the mixture of EFAL-removed zeolite Y with 0.05 M aqueous [$(NH_4)_2 TiO(C_2O_4)_2.H_2O$] [$TiO(C_2O_4)_2.H_2O$]. This new photocatalyst has been characterized by measuring XRD, IR and reflectance absorption spectra as well as ICP analysis, and it was found that the framework structure of $TiO_2$ /EFAL-removed zeolite Y is not changed by removing the extra-framework aluminum (EFAL) from the normal zeolite Y and the $TiO_2$ inside the photocatalyst exists in the form of $(TiO^{2+})_n$ nanoclusters. Based on the ICP analysis, the Si/Al ratio of the $TiO_2$ /EFAL-removed zeolite Y and the weight of $TiO_2$ were determined to be 23 and 0.061g in 1.0g photocatalyst, respectively. It was also found that adsorption of the azo dye in the $TiO_2$ /EFAL-removed zeolite is very effective (about 80 % of the substrate used). This efficient adsorption contributes to the synergistic photocatalytic activities of the $TiO_2$ /EFAL-removed zeolite by minimizing the required flux diffusion of the substrate. Thus, the photocatalytic reduction of methyl orange (MO) was found to be 8 times more effective in the presence of $TiO_2$ /EFAL-removed zeolite Y than in the presence of $TiO_2$ /normal zeolite Y. Furthermore, the photocatalytic reduction of MO by using 1.0 g of the $TiO_2$ /EFAL-removed zeolite Y containing 0.061g of $TiO_2$ is much faster than that carried out by using 1.0 g of Degussa P-25.

• Korean Chemical Engineering Research
• /
• v.46 no.3
• /
• pp.479-485
• /
• 2008

Porous $TiO_2$ nanostructured particles containing both mesopores and macropores were fabricated by utilizing an aerosol templating method from two kinds of starting materials (colloidal mixture of $TiO_2$ nanoparticles and PS particles, and that of TTIP solution and PS particles). The effects of mixing ratio of PS to $TiO_2$ and reactor temperature on the particle properties were investigated. When $TiO_2$ nanoparticles were used as starting materials, the increase of macropores number was observed by SEM and the specific surface area and total pore volume were increased from $31.6m^2/g$ to $39.1m^2/g$ and $0.068cm^3/g$ to $0.089cm^3/g$, respectively, by increasing the weight mixing ratio of $PS/TiO_2$ from 0.79 to 1.31. When TTIP was used as precursor, the specific surface area and mesopore volume of particles prepared at same condition decreased by 67% and 75%, respectively.

• Rapid Communication in Photoscience
• /
• v.1 no.1
• /
• pp.13-15
• /
• 2012

New porous $TiO_2$ nanostructures with shapes of pearl and rice were synthesized by hydrothermal treatment of $TiO_2$-liposome nanocomposites in acid and base solutions, respectively, as identified by scanning electron microscopy (SEM), transmission electron microscopy (TEM) images and large Brunauer-Emmett-Teller (BET) surface areas. The x-ray diffraction (XRD) patterns and selected area electron diffraction proved them to be well-defined anatase crystals. Their UV-visible reflectance absorption spectra were observed to have low band gap energy (3.03 and 3.07 eV, respectively), exhibiting surface absorption band in the visible range from 400 to 600 nm. The degradation of methylene blue (MB) over the $TiO_2$ nanostructures was observed upon visible-light irradiation, which was found to be very efficient as compared with any other conventional visible-light responsive $TiO_2$ nanostructures.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1152-1153
• /
• 2008

본 연구에서는 Ketjen black을 이용한 DSCs (Dye-sensitized solar cells)용 다공질의 $TiO_2$ nano-powder 제작기술을 제안한다. $TiO_2$ powder는 sol-gel법에 의해 Ti-isopropoxide와 2-propanol을 사용하여 제작되었으며, Ketjen black의 함량(0g$\sim$2g)을 달리하여 제작된 $TiO_2$ nano-powder의 다공성과 입자의 크기, 결정성등의 특성을 고찰하였다. 또한 이러한 $TiO_2$ powder를 paste로 만들어 다른 열처리 온도($100^{\circ}C{\sim}600^{\circ}C$)에서 $TiO_2$ 박막을 이용한 DSCs를 제작한 후 그 효율을 측정하였다. 그 결과 Ketjen black 1g을 함유시켜 만들어진 $TiO_2$ powder의 다공성과 입자 크기가 가장 우수한 것으로 FE-SEM의 측정결과 나타났으며, 500$^{\circ}C$의 열처리 공정을 거쳐 제작된 셀의 효율이 가장 높은 효율인 5.46%를 나타내고 있음을 확인할 수 있었다.

• Current Photovoltaic Research
• /
• v.4 no.2
• /
• pp.42-47
• /
• 2016

Increasing the efficiency of dye-sensitized solar cells (DSSCs) by the fabrication of new photoelectrodes (PEs) is an important challenge. This study examined the photovoltaic parameters of DSSCs composed of a $TiO_2$ PE with $WO_3$ nanoparticles (NPs). A number of PEs with the same thickness but different concentrations of $WO_3$ NPs in the $TiO_2PE$ were prepared. The morphology and structural properties of the prepared PEs were examined by field-emission scanning electron microscopy and X-ray diffraction, respectively. The effects of the $WO_3$ NPs mixing concentration on the efficiency of DSSCs were investigated under simulated solar light irradiation.