We prepared the ITO/Ag multilayer thin films on soda-lime glass substrate by the Facing Target Sputtering System (FTS) at room temperature. To confirm the effect of Ag layer in ITO/Ag multilayer thin films, we have prepared various range of Ag layer in its thickness and investigated prior to the setting of ITO/Ag multilayer thin films. The thickness of Ag layer was controlled by the sputtering deposition time. Properties of as-prepared samples were investigated by using a four-point probe, UV-Visual spectrometer with a spectral visual range (400 - 800 nm) and X-ray diffractometer (XRD). As a result, the transmittance of as-prepared samples turned out to be very low in the visible range due to light-scattering on the surface of thin film as the thickness of Ag layer got increased. However, reduction of phenomenon of light-reflection in visual range was observed around 20nm of Ag thickness. We prepared the ITO/Ag multilayer thin film with a resistivity of about $8{\times}10^{-5}[{\Omega}-cm]$ and a transmittance of more than 80 % at 550 nm.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.385-386
• /
• 2007

We prepared the Al doped ZnO coating Ag multilayer thin films on glass without substrate heating using FTS system. The structure of multilayer thin films has Al doped ZnO/Ag/Al doped ZnO(AZO/Ag/AZO). The thickness of top and bottom AZO thin films were fixed to 50 nm, respectively and controlled the thickness of Ag thin films with deposition time. As-doped multilayer thin films were prepared at 1mTorr and input power (DC) of 100W at room temperature. To investigate the film properties, we employed four-point probe, UVNIS spectrometer, X-ray diffractometer (XRD), scanning electron microscopy (SEM), Hall Effect measurement system and Atomic Force Microscope (AFM).

• 한국전기전자재료학회논문지
• /
• 제26권7호
• /
• pp.510-514
• /
• 2013

In order to prevent heat loss that occurs through the glass, low-emissivity (Low-E) coating methods with good insulating properties and high transmittance were used. InGaZnO/Ag/InGaZnO (IGZO/Ag/IGZO) multilayer thin films have been deposited on XG glass substrate by RF magnetron sputtering. Depending on the different thickness of Ag in multilayer films, the structural and optical properties of Low-E multilayer films were analyzed. By XRD analysis results, the multilayer thin films were observed to be amorphous structure regardless of Ag thickness. According to the AFM results, surface morphology of the multilayer films was observed and compared. Using UV-VIS spectroscopy, low emissivity property has been observed clearly with the transmittance of higher than 85% at visible range and lower than 30% at IR range.

• Journal of Magnetics
• /
• 제4권2호
• /
• pp.69-72
• /
• 1999

Magnetic properties and crystallographic structure of e-beam evaporated Co/Cr and Co/Mo multilayer thin films were investigated using VSM and XRD. Co/Cr and Co/Mo multilayer thin films are confirmed as an alternating layered structure. The structure of films with thicker Co layers than Cr and Mo layers are found to be a hcp structure with the c-axis perpendicular to the film plane. The direction of the film plane is the easy magnetization one. There is a no significant difference in shape of hysteresis loops between Co/Cr and Co/Mo multilayer films. It is found that Mo layer is more effective than Cr for preparing Co layer with c-axis normal to the film plane.

• Macromolecular Research
• /
• 제16권8호
• /
• pp.725-733
• /
• 2008

Polyimide (PI) multilayer thin films were prepared by spin-coating from a poly(amic acid) (PAA) and poly(amic acid) ammonium salt (PAAS). PI was prepared from pyromellitic dianhydride (PMDA) and 4,4'-oxydianiline (ODA) PAA. Different compositions of PAAS were prepared by incorporating triethylamine (TEA) into PMDA-ODA PAA in dimethylacetamide. PI multilayer thin films were spin-coated from PMDA-ODA PAA and PAAS. The PAAS comprising cationic and anionic moieties were spherical with a particle size of $20{\sim}40\;nm$. Some particles showed layers with ammonium salts, despite poor ordering. Too much salt obstructed the interaction between the polymer chains and caused phase separation. A small amount of salt did not affect the interactions of the interlayer structure but did interrupt the stacking between chains. Thermogravimetric analysis (TGA) showed that the average decomposition temperature of the thin films was $611^{\circ}C$. All the films showed almost single-step, thermal decomposition behavior. The nanostructure of the multilayer thin films was confirmed by X -ray reflectivity (XRR). The LF 43 film, which was prepared with a 4:3 molar ratio of PMDA and ODA, was comprised of uniformly spherical PAAS particles that influenced the nanostructure of the interlayer by increasing the interaction forces. This result was supported by the atomic force microscopy (AFM) data. It was concluded that the relationship between the uniformity of the PAAS particle shapes and the interaction between the layers affected the optical and thermal properties of PI layered films.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.19-19
• /
• 2009

TiNxOy/TiNx multilayer thin films with a high resistance (~ k$Omega$) were deposited on SiO2/Si substrates at room temperature by sputtering. The TiNx thin films show island and smooth surface morphology in samples prepared by dc and rf magnetron sputtering, respectively. TiNxOy/TiNx multilayer has been developed to control temperature coefficient of resistance (TCR) by the incorporation of TiNx layer (positive TCR) inserted into TiNxOy layers(negative TCR). Electrical and structural properties of sputtered TiNxOy/TiNx multilayer films were investigated as a function of annealing temperature. In order to achieve a stable high resistivity, multilayer films were annealed at various temperatures in oxygen ambient. Samples annealed at 700 oC for 1 min exhibit a good TCR value and a stable high resistivity.

• Journal of Electrochemical Science and Technology
• /
• 제2권4호
• /
• pp.193-197
• /
• 2011

The influences of the thickness and microstructure of Fe layer on the electrochemical performances of Fe/Si multilayer thin film anodes were investigated. The Fe/Si multilayer films were prepared by electron beam evaporation, in which Fe layer was deposited with/without simultaneous bombardment of Ar ion. The kinetics of Li insertion/extraction reactions in the early stage are slowed down with increasing the thickness of Fe layer, but such a slowdown seems to be negligible for thin Fe layers less than about $500{\AA}$. When the Fe layer was deposited with ion bombardment, even the $300{\AA}$ thick Fe layer significantly suppress Li diffusion through the Fe layer. This is attributed to the dense microstructure of Fe layer, induced by ion beam assisted deposition (IBAD). It appears that the Fe/Si multilayer films prepared with IBAD show good cyclability compared to the film deposited without IBAD.

• 한국전기전자재료학회논문지
• /
• 제30권11호
• /
• pp.740-744
• /
• 2017

Herein we studied the electrical and optical properties of indium tin oxide ITO/Ag/ITO multilayer thin films for application in transparent conducting electrodes. The ITO and Ag thin films were deposited onto soda lime glass (SLG) using radiofrequency and DC-sputtering methods, respectively. The as-synthesized ITO/Ag/ITO multilayer thin films were analyzed using 4-point probe, UV-Visible spectroscopy, and Hall measurement. We observed a rapid increase in electron concentration with increasing Ag thickness. However, electron mobility decreased with increasing Ag thickness. Finally, ITO/Ag/ITO multilayer thin films showed a characteristic low sheet resistance of $18{\Omega}/sq$ and high optical transmittance value (80%) with variation of Ag thickness (5~10 nm).

• 한국기계가공학회지
• /
• 제17권3호
• /
• pp.51-58
• /
• 2018

In this paper, the organic material Poly(methyl methacrylate) PMMA is used with inorganic $Al_2O_3$ to fabricate organic-inorganic multilayer barrier thin films. The organic thin films are developed using a roll-to-roll electrohydrodynamic atomization system, whereas the inorganic are grown using a roll-to-roll low-temperature atmospheric pressure atomic layer deposition system. For the first time, these two technologies are used together to develop organic-inorganic multilayer barrier thin films in atmospheric condition. The films are grown under optimized parameters and classified into three classes based on the layer structures, when the total thickness of the barrier is maintained at ~ 160 nm. All classes of barriers show good morphological, optical and chemical properties. The $Al_2O_3$ films with a low average arithmetic roughness of 1.58 nm conceal the non-uniformity and irregularities in PMMA thin films with a roughness of 5.20 nm. All classes of barriers show a notably good optical transmission of ~ 85 %. The hybrid organic-inorganic barriers show water vapor and oxygen permeation in the range of ${\sim}3.2{\times}10^{-2}g/m^2/day$ and $0.015cc/m^2/day$ at $23^{\circ}C$ and 100% relative humidity. It has been confirmed that it can be mass-produced and used as a low-cost barrier thin film in various printing electronic devices.

• E2M - 전기 전자와 첨단 소재
• /
• 제8권6호
• /
• pp.795-805
• /
• 1995

A novel thin film processing technique has been developed for the fabrication of ultrathin films of conducting polymers with molecular-level control over thickness and multilayer architecture. This new self-assembly process opens up vast possibilities in applications which require large area, ultrathin films of conducting polymers and more importantly in applications that can take advantage of the unique interactions achievable in the complex, supermolecular architectures of multilayer films.