• Proceedings of the Korea Concrete Institute Conference
• /
• 1997.10a
• /
• pp.375-380
• /
• 1997

The purpose of this study is to examine the properties of polymer-modified mortars using asphalt emulsion. The polymer-modified mortars using asphalt emulsion with various asphalt-cement ratios are prepared, and tested for flexural and compressive strengths, water absorption and permeability, carbonation, Cl ion penetration and chemical resistance. From the test results, the flexural and compressive strengths, water absorption and permeability, carbonation and Cl ion penetration depths of polymer-modified mortars using asphalt emulsion tend to be decreased with increasing asphalt-cement ratio, and chemical resistance is improved. It is evident that polymer-modified mortars using asphalt emulsion having an excellent properties as a waterproof and finish materials can be produced.

• Journal of Korean Foot and Ankle Society
• /
• v.17 no.4
• /
• pp.283-287
• /
• 2013

Purpose: To evaluate the result of arthroscopic modified Brostrom procedure with suture anchor for chronic lateral ankle instability. Materials and Methods: Fifty-two patients with chronic lateral ankle instability were analyzed, who underwent arthroscopic modified Brostrom procedure between December 2010 and May 2012. Clinical evaluation was performed using AOFAS scroring and Sefton grading system. Results: The average AOFAS hind foot score increased from preoperative 61.9 to 88.8 at the last follow up. There were 35 excellent, 9 good, 4 fair, 4 poor results according to Sefton grading system. For one patient, lateral ankle instability recurred. Conclusion: Arthroscopic modified Brostrom procedure is considered to be an effective and satisfactory technique.

• Fibers and Polymers
• /
• v.5 no.4
• /
• pp.259-263
• /
• 2004

Rubber-modified epoxy resins have been employed as adhesive and matrix materials for glass and corbon-fiber composites. The behavior of fracture around a crack tip for rubber-modified epoxy resin is investigated through the acoustic emission (AE) analysis of compact tension specimens. Damage zone and rubber particles distributed around a crack tip were observed by a polarized optical microscope and an atomic force microscope (AFM). The damage zone in front of pre-crack tip in rubber-modified specimen $(15wt\%\; rubber)$ began to form at about $13\%$ level of the fracture load and grew in size until $57\%$ load level. After that, the crack propagated in a stick-slip manner. Based on time-frequency analysis of AE signals and microscopic observation of damage zone, it was thought that AE signals with frequency bands of 0.15-0.20 MHz and 0.20­0.30 MHz were generated from cavitation in the damage zone and crack propagation, respectively.

• Transactions on Electrical and Electronic Materials
• /
• v.18 no.4
• /
• pp.203-206
• /
• 2017

The effect of the content of microsilica and nanosilica continuously modified with hydroxy silane and epoxy-modified silicone in cycloaliphatic epoxy/microsilica/nanosilica composites (EMNCs) on the mechanical and water repellent properties was evaluated. Surface-modified micro- and nanosilica was well-mixed with a cycloaliphatic epoxy resin in the presence of polyester-modified polydimethylsiloxane (PEM-PDMS) as a dispersing agent using an ultrasonicator. Tensile and flexural tests were carried out using a universal testing machine (UTM). The water repellent property was evaluated by contact angle measurements of water on the composite surface. Tensile strength of the composite could be enhanced by 32.2% up to 91.4 MPa, and the flexural strength was raised to 122.0 MPa, which is 38.8% higher than that of neat epoxy. The contact angle of water on the composite was as high as $104.1^{\circ}$.

• Industry Promotion Research
• /
• v.9 no.1
• /
• pp.31-38
• /
• 2024

In this study, evaluated the properties of layered silicate-based nanocomposite sensitive film. For the fabrication of nanocomposite materials, we selected organically modified layered silicate materials, specifically Cloisite^® and Bentone^®, which were treated with quaternary ammonium salts. The impedance of the humidity sensors containing organically modified montmorillonite/hectorite clay decreased with increasing relative humidity(RH%). In the case of the Cloisite^® humidity sensor exhibited slightly better impedance linearity and hysteresis compared to the Bentone^® 38 humidity sensor. Additionally the impedance of the sensor with Bentone^® 38 addition was the lowest when compared to the Cloisite^®-modified sensor. Comparing the Cloisite^®-modified sensors individually, we observed different moisture absorption characteristics based on the hydrophilic properties of the organic-treated materials. The response speed of Cloisite^® 93A tended to be slower due to differences in moisture evaporation rates influenced by the hydrophilic organic components. Based on these results, moisture barriers utilizing organically modified layered silicate materials may exhibit slightly lower moisture absorption properties compared to conventional polymer-based moisture barriers. However, their excellent stability, simple processing, and cost-effectiveness make them suitable for humidity sensor applications.

• Elastomers and Composites
• /
• v.50 no.1
• /
• pp.62-67
• /
• 2015

The surface modification of microfibriled cellulose (MFC) was carried out through the hydrolysis-condensation reaction using (3-aminopropyl)triethoxysilane (APS) and 3-glycidyloxypropyltriethoxysilane (GPS) and then the modified cellulose was compounded with bio-degradable poly(lactic acid) (PLA). Also, pristine MFC was compounded with PLA as a control groups. The confirmation of surface modification for the pristine MFC was characterized by FT-IR and SEM/EDX. The thermal and mechanical properties of the PLA/MFC composites depended on the content of MFC and the type of silane coupling agents. From the thermal, morphological and mechanical behaviors of the PLA/MFC composites, it was found that GPS-MFC was more successful to improve the interface adhesion between PLA matrix and the surface of MFC than that of APS-MFC.

• The korean journal of orthodontics
• /
• v.45 no.5
• /
• pp.268-272
• /
• 2015

Clear thermoplastic retainers have been widely used in daily orthodontics; however, they have inherent limitations associated with thermoplastic polymer materials such as dimensional instability, low strength, and poor wear resistance. To solve these problems, we developed a new type of clear orthodontic retainer that incorporates multi-layer hybrid materials. It consists of three layers; an outer polyethylenterephthalate glycol modified (PETG) hard-type polymer, a middle thermoplastic polyurethane (TPU) soft-type polymer, and an inner reinforced resin core. The resin core improves wear resistance and mechanical strength, which prevent unwanted distortion of the bucco-palatal wall of the retainer. The TPU layer absorbs impact and the PETG layer has good formability, optical qualities, fatigue resistance, and dimensional stability, which contributes to increased support from the mandibular dentition, and helps maintain the archform. This new type of vacuum-formed retainer showed improved mechanical strength and rate of water absorption.

• Journal of Information Display
• /
• v.13 no.3
• /
• pp.107-111
• /
• 2012

An almost pure phase of $Ba_3Si_6O_{12}N_2$ doped with $Eu^{2+}$ was successfully synthesized through the ammonia nitridation of an oxide precursor prepared through an aqueous-solution method, using propylene- glycol-modified silane. The emission peak intensity of the obtained $Ba_3Si_6O_{12}N_2:Eu^{2+}$ was -2.2 times higher than that of the sample prepared through a solid-state reaction method.

• Macromolecular Research
• /
• v.17 no.1
• /
• pp.37-43
• /
• 2009

To fabricate dental nanocomposites containing finely dispersed silica nanoparticles, nearly monodispersed silica nanoparticles smaller than 25 nm were synthesized without forming any aggregates via a modified sol-gel process. Since silica nanoparticles synthesized by the Stober method formed aggregates when the particle size is smaller than 25 nm, the synthetic method was modified by changing the reaction temperature and adding poly(1-vinyl-2-pyrrolidinone) (PVP) to the reaction mixture. The size of the formed silica nanoparticles was reduced by increasing the reaction temperature or adding PVP. Furthermore, the formation of aggregates with primary silica nanoparticles smaller than 25 nm was prevented by increasing the amount of PVP added to the reaction mixture. To enhance the dispersion of the silica particles in an organic matrix, the synthesized silica nanoparticles were treated with 3-methacryloxypropyltrimethoxysilane ($\gamma$-MPS). A dental nanocomposite containing finely dispersed silica nanoparticles could be produced by using the surface-treated silica nanoparticles.

• Journal of the Microelectronics and Packaging Society
• /
• v.20 no.3
• /
• pp.11-18
• /
• 2013

Interest in copper nanoparticles has increased as an alternative for substituting silver nanoparticles because of its lower cost and less electromigration effect than silver. In this paper, the recent research trends and main results in wet-chemical synthesis of sub-100 nm Cu nanoparticles were summarized. The characteristics of synthesis were discussed with a classification such as modified polyol synthesis, modified hydrothermal synthesis, solvothermal synthesis, and the others, focussing on effects of capping agents, reductants, and pH. Information on the oxidation of synthesized copper nanoparticles were additionally commented.