• Journal of the Korean Electrochemical Society
• /
• v.16 no.3
• /
• pp.162-168
• /
• 2013

$Li_2MnO_3-LiMO_2$(M=Ni, Co, Mn) nano-composite is a promising cathode material for xEV application due to its high theoretic capacity. However high voltage operating system of $Li_2MnO_3-LiMO_2$(M=Ni, Co, Mn) has worked as a hurdle in its application because of the inherent demerits, such as cycle life degradation and gas evolution. In order to enhance cell performance of $Li_2MnO_3-LiMO_2$(M=Ni, Co, Mn)/graphite cell, we examined electrolyte mainly composed of FEC, fluroalkyl ether and $LiPF_6$ (F-based EL). F-based EL showed much better discharging retention ratio than 1.3 M $LiPF_6$ EC/EMC/DMC (3/4/3, v/v/v) (STD). Furthermore gas evolution, especially CO and $CO_2$ during $60^{\circ}C$ storage for 30 days was dramatically reduced owing to thermal stable SEI formation effect of F-based EL.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.826-829
• /
• 2002

$MoO_3$ thin films were deposited on electrode and heater screen-printed alumina substrates in en atmosphere by RF reactive sputtering. The deposition was performed at $300^{\circ}C$ with 350W of a forward power in an $Ar-O_2$ atmosphere. The working pressure was maintained at $3{\times}10^{-2}$mtorr and all deposited films were annealed at $500^{\circ}C$ for 5hours. The surface morphology of films was observed by using a SEM and crystalline phases were analyzed by XRD. The sensing properties were investigated in term of gas concentration under exposure of reducing gases such as $H_2$, $NH_3$ and CO.

• Korean Chemical Engineering Research
• /
• v.57 no.6
• /
• pp.891-897
• /
• 2019

In this study, heteropoly acid PVMo catalysts were supported on activated carbon with various composition of phosphoric acid ($H_3PO_4$), vanadium (V) pentoxide ($V_2O_5$) and molybdenum (VI) trioxide ($MoO_3$). Catalytic performance was examined at $140^{\circ}C$ for 1hour in vapor formaldehyde. XRD and BET analyses were carried with the catalysts before and after the reaction. Formaldehyde conversion was increased with decreasing Mo and $H_3PO_4$ content and increasing $V_2O_5$ content. Acidity of the catalysts was investigated with $NH_3-TPD$. Crystallinity of the catalysts was relatively low, and surface area was decreased after the reaction. In $NH_3-TPD$ result, the ratio of strong acid site corresponding to $NH_3$ desorption between $400^{\circ}C$ and $500^{\circ}C$ was increased by decreasing $MoO_3$ and $H_3PO_4$ content and increasing $V_2O_5$ content. Therefore, it was found that the strong acid site could affect the catalytic reactivity in vapor formaldehyde conversion.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.12
• /
• pp.3675-3678
• /
• 2010

In-situ X-ray absorption spectroscopy (XAS) was used to elucidate the structural variation of $\alpha-MoO_3$ electrode upon discharge/charge reaction in a lithium ion battery. According to the XAS analysis, hexavalent Mo atoms in $\alpha-MoO_3$ framework are reduced as the amount of intercalated lithium ions increases. As lithium de-intercalation proceeds, most of pre-edge peaks are restored again. However, according to the Fourier transforms of the extended X-ray absorption fine structure (EXAFS) spectra, lithium de-intercalation reaction is partially irreversible upon the charge reaction, which is one of the main reasons why the capacity of $\alpha-MoO_3$ electrode decreases upon successive discharge/charge cycles.

• Nano
• /
• v.13 no.10
• /
• pp.1850115.1-1850115.10
• /
• 2018

A novel sensor material of Au nanoparticles (NPs) functionalized 1D ${\alpha}-MoO_3$ nanobelts (NBs) was fabricated by a facile lysine-assisted approach. The obtained $Au/{\alpha}-MoO_3$ product was characterized by means of X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM) and energy dispersive X-ray (EDX), and X-ray photoelectron spectra (XPS). Then, in order to investigate the gas sensing performances of our samples, a comparative gas sensing study was carried out on both the ${\alpha}-MoO_3$ NBs before and after Au NPs decoration by using ethanol vapor as the molecular probe. The results turned out that, after the functionalization of Au NPs, the sensor exhibited improved gas-sensing characteristics than the pure ${\alpha}-MoO_3$, such as response and recovery time, optimal operating temperature (OT) and excellent selectivity. Take for example 200 ppm of ethanol, the response/recovery times were 34 s/43 s and 5.7 s/10.5 s, respectively, while the optimal operating temperature (OT) was lower to $200^{\circ}C$ rather than $250^{\circ}C$. Besides, the functionalized sensor showed a higher response to ethanol at $200^{\circ}C$, and response was 1.6 times higher than the pure $MoO_3$. The mechanism of such improved sensing properties was interpreted, which might be attributed to the spillover effect of Au NPs and the electronic metal-support interaction.

• Applied Science and Convergence Technology
• /
• v.27 no.3
• /
• pp.52-55
• /
• 2018

We reported a new method to enhance the photoluminescence (PL) properties of $Eu^{3+}$ ions doped $Gd_2Mo_4O_{15}$ phosphors via cation substitution. With the aid of conventional sol-gel method, a series of $Eu^{3+}$ ions doped $Gd_{2(1-x)}Y_{2x}Mo_4O_{15}$ phosphors were prepared. The prepared samples emitted red light when excited at 393 nm. Moreover, when part of the $Gd^{3+}$ ions was substituted by the $Y^{3+}$ ions, the PL emission intensity of the studied samples was enhanced and the optimal doping concentration for $Y^{3+}$ ions was 30 mol%. The calculated CIE coordinate (0.663,0.337) was situated in the red region. Furthermore, the thermal quenching behaviors of the synthesized $Eu^{3+}$ ions doped $Gd_{2(1-x)}Y_{2x}Mo_4O_{15}$ phosphors were studied. At last, we also packaged a red-emitting light-emitting diode device by integrating the obtained phosphors and a near-ultraviolet chip to verify the applications of the $Eu^{3+}$ ions doped $Gd_{2(1-x)}Y_{2x}Mo_4O_{15}$ phosphors for indoor lighting.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1994.11a
• /
• pp.25-26
• /
• 1994

• Korean Chemical Engineering Research
• /
• v.54 no.4
• /
• pp.560-567
• /
• 2016

In this study, we characterized steam reforming reactions and surface of $Ni/Al_2O_3$ catalysts. Ni-Mo based catalysts were prepared by loading Mo as the co-catalyst and reaction activities of the Ni-Mo based catalysts were compared with those of Ni-based catalysts. Through the $H_2$-TPR and XPS analysis it was confirmed that this characteristic efficiency. $O_2$-TPO analysis was performed to examine the deposition characteristics, bonding structures and evaporation characteristics of carbon deposited on the surface of catalysts after long run experiments were performed for steam reforming reactions. As the results, it was found that durability was improved in Ni-Mo based catalysts inhibiting formation of graphitic carbon species which reduced reaction activities of the catalysts by strongly interacting with Ni in the steam reforming reaction.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.436-439
• /
• 2000

Change of dielectric loss of use in high relative permitivity capacitor BaTiO$_3$ ceramic depends on Mn doping have been investigated. The powders used in this study were commercial BaTiO$_3$, TiO$_2$and, MnCO$_3$. Sample was fabricated by conventional ceramic process. The quantity of Mn was changed gradually from 0.lmol% to 10mo1%. The sintering densities were reduced with increasing amount of MnCO$_3$. This result is because of increase of low density second phase BaMnO$_3$. When the samples were doped by over 0.2mol% of MnCO$_3$, average grain sizes were enlarge to several tens ${\mu}{\textrm}{m}$. The dielectric losses were reduced by Mn doping to lmol% but, increased from lmol% to 10mo1% gradually.

• Korean Journal of Materials Research
• /
• v.17 no.9
• /
• pp.484-488
• /
• 2007

Mo(Ti) alloy and pure Cu thin films were subsequently deposited on $SiO_2-coated$ Si wafers, resulting in $Cu/Mo(Ti)/SiO_2$ structures. The multi-structures have been annealed in vacuum at $100-600^{\circ}C$ for 30 min to investigate the outdiffusion of Ti to Cu surface. Annealing at high temperature allowed the outdiffusion of Ti from the Mo(Ti) alloy underlayer to the Cu surface and then forming $TiO_2$ on the surface, which protected the Cu surface against $SiH_4＋NH_3$ plasma during the deposition of $Si_3N_4$ on Cu. The formation of $TiO_2$ layer on the Cu surface was a strong function of annealing temperature and Ti concentration in Mo(Ti) underlayer. Significant outdiffusion of Ti started to occur at $400^{\circ}C$ when the Ti concentration in Mo(Ti) alloy was higher than 60 at.%. This resulted in the formation of $TiO_2/Cu/Mo(Ti)\;alloy/SiO_2$ structures. We have employed the as-deposited Cu/Mo(Ti) alloy and the $500^{\circ}C-annealed$ Cu/Mo(Ti) alloy as gate electrodes to fabricate TFT devices, and then measured the electrical characteristics. The $500^{\circ}C$ annealed Cu/Mo($Ti{\geq}60at.%$) gate electrode TFT showed the excellent electrical characteristics ($mobility\;=\;0.488\;-\;0.505\;cm^2/Vs$, on/off $ratio\;=\;2{\times}10^5-1.85{\times}10^6$, subthreshold = 0.733.1.13 V/decade), indicating that the use of Ti-rich($Ti{\geq}60at.%$) alloy underlayer effectively passivated the Cu surface as a result of the formation of $TiO_2$ on the Cu grain boundaries.