• Analytical Science and Technology
• /
• v.5 no.3
• /
• pp.327-332
• /
• 1992

Mn-Zn ferrite single crystals show some fluctuations in composition along the direction of growth by the conventional Bridgman method. The single crystal with a uniform composition was obtained by maintaining the liquid composition content. For example, two batches of powder were prepared : one is consisted of 52 mol% of $Fe_2O_3$, 30 mol% of MnO, and 18 mol% Zn(Composition A), and the other 53 mol% of $Fe_2O_3$, 28.5 mol% of MnO, and 18.5 mol% ZnO(Composition B). Crack-free single crystals with the uniform composition B were grown in a size of 60mm diameter, 300mm long by melting the pellets of composition A and followed by supplying the composition B as tablets. Initial permeabilities were obtained above 600 at 5 MHz in the region of 30~270 mm along the direction of growth.

• Resources Recycling
• /
• v.11 no.5
• /
• pp.34-38
• /
• 2002

To minimize the size of transformer volume, the operating frequency of ferrites cores increasing. The power loss of Mn-Zn ferrites comprises hysteresis loss, eddy current loss and residual loss. In the range more then 500 KHz, the total power loss is mainly due to the residual loss. The power loss increase with the frequency 3rd power. To minimize residual loss as well as eddy current loss, the microstructure should have small grain and high density, It should be noted that as the product of resonance frequency and static permeability increase, the power loss decrease at high frequency region.

• Proceedings of the Korea Electromagnetic Engineering Society Conference
• /
• 2003.11a
• /
• pp.622-629
• /
• 2003

Generally, a silicone rubber and a chloride polyethylene(CPE) have been used for the development of high-performance composite EM(ElectroMagnetic) wave absorber. In this study, the EM wave absorption abilities for natural lacquer which is newly suggested in this study as a binder for composite EM wave absorber were investigated to develop an improved EM wave absorber In addition, MnZn ferrite composite EM wave absorber mixed with the natural lacquer were prepared and their absorption ability was also investigated. MnZn ferrite composite EM wave absorber which employs the natural lacquer as a binder showed an improved EM wave absorption characteristics in comparison with the conventional binder such as a silicone rubber and a chloride polyethylene(CPE). The matching frequency and the absorption ability of EM wave absorber mixed with natural lacquer can be controled the change of the thickness of them.

• Resources Recycling
• /
• v.7 no.4
• /
• pp.50-54
• /
• 1998

In order to obtain desired electromagnetic propertieι high initial permeability and good frequency dependance of initial p permeability, the adding effects of sevral seeds were experimented in Mn-Zn ferrite system. As adding seed grams, calcined at sintering temperature, abnormal grains were disappeared clearly but the density and the initial permcability of sintered Mn-Zn ferrite body were decreased. On the contrary, in case of adding seed rains which were calcined below the calcination temperatnre of matrix particle, abnormal grains remained but the initial permeability was increas$\xi$d with proper s$\xi$ed content. W With proper seed content, the initial permeability was increased by 10-20% but tbe $\alpha$ltoff frequency was not changed.

• Korean Journal of Materials Research
• /
• v.5 no.2
• /
• pp.239-245
• /
• 1995

Mn-Zn ferrite thin films were deposited on $SiO_2(1000 \AA)/Si(100)$ by ion beam sputtering using a single ion source. A mosaic target consisting of a single crystal(ll0) Mn-Zn ferrite with a Fe metal strip on it was used. As-deposited films without oxygen gas flow have a wiistite structure due to oxygen deficiencies, which originated from the extra metal atoms sputtered from the metal strips during deposition. The as-deposited films with oxygen gas flow, however, have a spinel structure with (111) preferred orientation. The crystallization of thin films was maximized at the ion beam extraction voltage of 2.lkV, at which the deposited films are bombarded appropriately by the energetic secondary ions reflected from the target. As the extraction voltage increased or decreased from the optimum value, the crystallinity of thin films becomes poor owing to a weak and severe bombardment of the secondary ions, respectively. Crystallization due to the bombardment of the secondary ions was also maximized at the beam incidence angle of $55^{\circ}$. The as-deposited ferrite thin films with a spinel structure showed ferrimagnetism and had an in-plane magnetization easy axis.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.96-100
• /
• 2003

평면형 자심재료용으로 응용하기 위한 Mn-Zn 페라이트에서 저손실 조성의 전자기적 특성과 분위기 조건에 따른 특성변화를 관찰하였다. $Fe_{2}O_{3}$ : MnO : ZnO 의 물비가 53 : 36 : 11 일 때, 가장 우수한 특성을 나타내었으며, $SiO_{2}$와 CaO는 입계 저항층 형성을 통한 손실은 감소시키고, 이로 인해 성능지수는 증가하여 100kHz ~ 200kHz 범위에서 최대값을 나타내어 전자기적 효율이 극대화되었다. 산소분압의 제어는 승온과정부터 산소분압을 제어시켜주어야만 Zn-loss 현상의 증가와 $Fe^{2+}$이온 농도의 감소 및 $Fe^{2+}-Fe^{3+}$ 이온간의 호핑(hoping)현상 등에 의한 손실을 최소화 할 수 있으며, 높은 투자율을 얻을 수 있었다. 그리고 소결 또는 냉각 중 평형 산소분압이 유지되지 못하면 다량의 결함이 출현하게 되고, 특히 $600^{\circ}C$이하에서 스피넬 상의 분해-산화반응이 일어나면서 미세구조 상에 결함으로 남게 되어 전자기적 특성이 저하되었다.

• The Journal of Korean Institute of Electromagnetic Engineering and Science
• /
• v.15 no.4
• /
• pp.406-413
• /
• 2004

In this study, we investigated the reflection coefficient of absorbers fur mobile phone on average Particle size and preparation temperature of specimens. We used recycled MnZn ferrite with initial permeability of 2,500 and 10,000 as starting materials. Absorption ability increased at 1.8 ㎓ which is frequency fur mobile phones with increasing average particle size. We developed a sheet type electromagnetic wave absorber with the thickness of 1 mm which showed reflection coefficient of -3.8 ㏈ at 1.8 ㎓.

• Proceedings of the Korean Magnestics Society Conference
• /
• 1996.05a
• /
• pp.82-83
• /
• 1996

• Proceedings of the Korean Magnestics Society Conference
• /
• 1994.03a
• /
• pp.52-53
• /
• 1994

• Proceedings of the Korean Magnestics Society Conference
• /
• 1994.03a
• /
• pp.54-55
• /
• 1994