• Korean Journal of Materials Research
• /
• v.24 no.2
• /
• pp.67-72
• /
• 2014

Nanocrystalline materials have received much attention as advanced engineering materials with improved physical and mechanical properties, including high strength, high hardness, excellent ductility and toughness. In this study, nanopowders of $Al_2O_3$, MgO and $TiO_2$ were prepared as starting materials by high energy ball milling for the simultaneous synthesis and sintering of the nanostructured compound $Mg_4Al_2Ti_9O_{25}$ by high-frequency induction heating process. The highly dense nanostructured $Mg_4Al_2Ti_9O_{25}$ compound was produced within one minute by the simultaneous application of 80MPa pressure and induced current. The sintering behavior, grain size and mechanical properties of the $Mg_4Al_2Ti_9O_{25}$ compound were evaluated.

• Journal of Powder Materials
• /
• v.11 no.3
• /
• pp.247-252
• /
• 2004

Recently, it has been found that mechanical alloying (MA) facilitates the nanocomposites formation of metal-metal oxide systems through solid-state reduction during ball milling. In this work, we studied the MA effect of Fe$_{3}$O$_{4}$-M (M = Al, Ti) systems, where pure metals are used as reducing agents. It is found that composite powders in which $Al_{2}$O$_{3}$ and TiO$_{2}$ are dispersed in $\alpha$-Fe matrix with nano-sized grains are obtained by mechanical alloying of Fe$_{3}$O$_{4}$ with Al and Ti for 25 and 75 hours, respectively. It is suggested that the large negative heat associated with the chemical reduction of magnetite by aluminum is responsible for the shorter MA time for composite powder formation in Fe$_{3}$O$_{4}$-Al system. X-ray diffraction results show that the reduction of magnetite by Al and Ti if a relatively simple reaction, involving one intermediate phase of FeAl$_{2}$O$_{4}$ or Fe$_{3}$Ti$_{3}$O$_{10}$. The average grain size of $\alpha$-Fe in Fe-TiO$_{2}$ composite powders is in the range of 30 nm. From magnetic measurement, we can also obtain indirect information about the details of the solid-state reduction process during MA.

• Korean Journal of Metals and Materials
• /
• v.50 no.5
• /
• pp.369-374
• /
• 2012

Nanopowders of Mo, Ta and Si were made by high-energy ball milling. A dense nanostructured $MoSi_2-TaSi_2$ composite was sintered by the high-frequency induction heated combustion method within 2 minutes from mechanically activated powder of Mo, Ta and Si. A highly dense $MoSi_2-TaSi_2$ composite was produced under simultaneous application of a 80 MPa pressure and the induced current. Mechanical properties and microstucture were investigated. The hardness and fracture toughness of the $MoSi_2-TaSi_2$ composite were $1200kg/mm^2$ and $3.5MPa.m^{1/2}$, respectively. The mechanical properties were higher than those of monolithic $MoSi_2$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.4
• /
• pp.129-134
• /
• 2004

In this study, we investigated the effect of a nitrogen atom on the amorphization of V-Fe alloy through solid-gas reaction during mechanical alloying (MA). MA by planetary ball mill of $V_{70}Fe_{30}$ elemental powders was carried out under the nitrogen gas atmosphere. Amorphization has been observed after 160 hours of ball milling in this case. The DSC spectrum for the mechanically alloyed ($V_{70}Fe$_{30}$)_{0.89}N_{0.11}$ powders exhibits a sharp exothermic peak due to crystallization at about $600^{\circ}C$. Structural transformation from the bcc crystalline to amorphous states was also observed through X-ray and neutron diffractions. We take a full advantage of a negligibly small scattering length of the V atom in the neutron diffraction measurement. During amorphization process the octahedral unit, which is typical of a polyhedron formed in any crystal structures, was preferentially destroyed and transformed into the tetrahedral unit. Futhermore, neutron diffraction measurements revealed that a nitrogen atom is selectively situated at a center of the polyhedron formed by V atoms.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.4
• /
• pp.189-194
• /
• 2013

Single phase crystalline powders of $Mg_3Sb_2$ and $Mg_3Bi_2$ were prepared by mechanical alloying Mg, Sb and Bi metals with planetary ball milling for 24~48 h. The compositions of starting raw materials for single phase $Mg_3Sb_2$ and $Mg_3Bi_2$ were 3Mg : 1.8Sb and 3Mg : 1.6Bi, respectively. Two types of mechanically alloyed powders obtained were mixed at some ratios for the fabrication of $Mg_3Sb_2-Mg_3Bi_2$ composites and then hot pressed under uniaxial pressure of 70 MPa at 723 K for 1 h. The main phase of composites was a stable phase similar to $Mg_3Bi_2$ phase with a small amount of Bi phase. The distributions of Sb and Bi elements on EDS mapping images were discontinuous and their compositional contours were clear, which means that the hot pressed specimens were composites composed of two compounds of $Mg_3Sb_2$ and $Mg_3Bi_2$.

• Korean Journal of Materials Research
• /
• v.11 no.4
• /
• pp.294-299
• /
• 2001

Effects of the surface fluorination on the electrochemical charge-discharge properties of $Mg_2$Ni electrode in Ni-MH batteries fabricated by mechanical alloying were investigated. After 20h ball milling, Mg and Ni powder formed nanocrystalline $Mg_2$Ni. Discharge capacity of this alloy increased greatly at first one cycle, but due to the formation of Mg(OH)$_2$ passive layer, it showed a rapid degradation in alkaline solution within 10cyc1es. In case of 6N KOH +xN KF electrolyte (x = 0.5, 1, 2), a continuous and stable fluorinated layer formed by adding excess F$^{[-10]}$ ion, increased durability of $Mg_2$Ni electrode greatly and high rate discharge capability(90-100mAh/g). 2N KF addition led to the highest durability of all tested here. The reason of the improvement is due to thin MgF$_2$, which can prevent the $Mg_2$Ni electrode from forming Mg(OH)$_2$layer that is the main cause of degradation.

• Journal of Hydrogen and New Energy
• /
• v.5 no.2
• /
• pp.73-79
• /
• 1994

The hydrogenation behavior of Ti-Ni powders prepared by mechanical alloying in a high energy ball mill have been investigated by P-C isotherm curves, DSC(differential scanning calorimetry), X-ray diffractometer, SEM(scanning electron microscope). Amorphous TiNi phase was formed after 10 milling hours. The hydrogen storage capacity gradually decreased as a function of mechanical alloying time. There appears the DSC endothermic peak due to hydrogen evolution of amorphous hydride phase.

• Journal of Powder Materials
• /
• v.16 no.1
• /
• pp.16-21
• /
• 2009

Nanostructured $ReSi_{1.75}$ was synthesized to have high density via rapid and cost effective process named as high-frequency induction heated combustion synthesis(HFIHCS) method. For the process, mechanically activated Re-Si powder was used, which had been prepared by mechanical ball milling of Re and Si powders with mixing ratio of 1:1.75. Both combustion synthesis and densification were accomplished simultaneously by applying electric current and mechanical pressure of 80 MPa during the process. The average grain size, hardness, and fracture toughness of the compound were 210 nm, 1085 $kg/mm^2$ and 4 $MPa{\cdot}m^{1/2}$, respectively. The experimental results show that HFIHCS is a promising process for synthesis of nanostructured $ReSi_{1.75}$ which has a potential for both high temperature and thermo-electric applications.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1992.05b
• /
• pp.126-126
• /
• 1992

Solid and liquid sintering behaviors of mechanically alloyed 75W-25Cu powders have been studied by using a dilatometry technique. The sintering was performed under hydrogen atmosphere of 1 atm with a heating rate of 3 $^{\circ}C$/min. The mechanically alloyed 75W-25Cu powders were prepared by high energy ball milling process under argon atmosphere of 1 atm with alloying times of 0 to 400 h. To compare with the sintering behaviors of mechanically alloyed powders, pure Cu and W powders were also sintered under the above conditions, As the mechanical alloying time increased from 0 to 400 h, the shrinkage behavior of the alloyed powders was enhanced during the sintering, and staring temperature of liquid sintering decreased from 1083 to 1068 $^{\circ}C$. The saturation temperature, above which the shrinkage was completed, of liquid phase sintering decreased from 1248 to 1148 $^{\circ}C$ with increasing mechanical alloying time from 200 to 400 h. The residual stress of the mechanically alloyed powder was measured by X-raydiffractometer. The microstructure of sintered spcimen was observed by optical and scanning electron microscope. From these results, variations of solid and liquid sintering behaviors with mechanical alloying time were discussed in terms of the amount of residual stress and the distribution of W and Cu powders in the mechanically alloyed powder.

• Korean Journal of Metals and Materials
• /
• v.50 no.1
• /
• pp.39-44
• /
• 2012

Nanopowders of TiCo were synthesized from Ti and Co by high energy ball milling. Highly dense nanostructured TiCo compounds were consolidated at low temperature by pulsed current activated sintering within 3 minutes from the mechanical synthesis of the powders (TiCo) and horizontal milled Ti+Co powders under 100 Mpa pressure. This process allows very quick densification to near theoretical density and prohibits grain growth in nanostructured materials. The grain sizes of the TiCo compounds were calculated. Finally, the average hardness values of the nanostructured TiCo compounds were investigated.