• Journal of the Korean Wood Science and Technology
• /
• 제48권4호
• /
• pp.503-512
• /
• 2020

Using Na₂CO₃ versus NaCl as chemical activator, we compared the quality of activated carbon produced from oil palm fronds as raw material. These activators were selected for comparison because both are readily available and are environmentally friendly. In the manufacturing, we used Indonesian National Standard (SNI 06-3730-1995) parameters. For the quality comparison, we determined activated-carbon yield, moisture, ash, volatiles, and fixed-carbon contents; and adsorption capacity of iodine. The best characteristics, assessed by morphological surface analysis and Fourier transform infrared (FTIR) spectral analysis, were observed in the carbon activated by Na₂CO₃ at an activator concentration of 10% and carbonization temperature of 400 ℃. The results were as follows: activated-carbon yield, 84%; water content, 8.80%; ash content, 2.20%; volatiles content, 14.80%; fixed-carbon content, 68.60%; and adsorption capacity of iodine, 888.51 mg/g. Identification using the FTIR spectrophotometer showed the presence of the functional groups O-H, C=O, C=C, C-C, and C-H in the Na₂CO₃-activated carbon.

• Journal of the Korean Wood Science and Technology
• /
• 제48권6호
• /
• pp.907-916
• /
• 2020

This research was conducted to investigate the linear expansion and resistance properties of a composite board (com-ply). This board was made of medium-density fiberboard (MDF) laminated using avocado (Persea americana), mahogany (Swietenia mahogani), and pine (Pinus merkusii) veneers. These three types of veneers were laminated on both surfaces of the MDF using adhesives, namely, epoxy and isocyanate. Glue (250 g·m^-2) was spread on the surface, followed by cold press for 3 h with an applied pressure of 15 kg·cm^-2. The research result revealed that com-ply exhibited an increased dimensional stability compared with MDF, indicated by reduction in water absorption, thickness swelling, and linear expansion. The com-ply made of the pine veneer and isocyanate adhesive exhibited high density, water absorption, thickness swelling, and screw withdrawal load. The com-ply that exhibited the strongest resistance to drywood termite attacks was the one made of the mahogany veneer and isocyanate adhesive. Moreover, the com-ply that exhibited the biggest weight loss (3.6 %) was made of the pine veneer and epoxy adhesive. The results of this research may facilitate in manufacturing com-ply using the selected veneer and adhesive without the application of hot press.

• Journal of the Korean Wood Science and Technology
• /
• 제48권2호
• /
• pp.136-153
• /
• 2020

In this paper, the influence of initial formaldehyde/urea (F/U) molar ratios on the performance of low molar ratio (1.0) urea-formaldehyde (UF) resin adhesives has been investigated. Two initial F/U molar ratios, i.e., the first and second initial molar ratios were used for the alkaline addition reaction. Three levels of the first initial F/U molar ratios (2.0, 3.0, and 4.0) and two levels of the second initial molar ratios (2.0 and 1.7) were employed to prepare a total of six UF resins with an identical final molar ratio (1.0). The basis properties, functional groups, molecular weight, crystallinity, and thermal curing properties of the UF resins were characterized in detail. Higher levels (3.0 and 4.0) of the first initial F/U molar ratio provided the UF resins with better properties (non-volatile solids content, viscosity, gelation time, pH, and specific gravity) than those of the resins prepared with the conventional level F/U molar ratio of 2.0. Statistical analysis suggested that combining the first and second initial molar ratio of 4.0 with 1.7 would result in UF resins with greater adhesion strength and lower formaldehyde emission than those of the resins prepared with other molar ratios. The results showed that higher levels of the first initial molar ratio resulted in a more branched structure, as indicated by GPC, FTIR, DSC, XRD, and greater adhesion strength than those of the other UF resins with an identical final molar ratio of 1.0.

• Journal of the Korean Wood Science and Technology
• /
• 제44권2호
• /
• pp.172-183
• /
• 2016

Densification of the inner part of oil palm trunk (OPT) by the close system compression (CSC) method was performed in this study. The effects of the compression temperature and time on the anatomical, physical and mechanical properties of OPT were evaluated. The inner part of OPT with an initial average density of $0.3g/cm^3$ was used as samples. Oven-dried samples were immersed in water and vacuumed until fully saturated and then compressed by CSC at 120, 140, 160 or $180^{\circ}C$ for 10, 20, 30 or 40 min. The anatomical characteristics of transverse and radial sections before and after compression were compared by optical microscopy. The physical and mechanical properties, including the density, recovery of set (RS), modulus of elasticity (MOE), modulus of rupture (MOR), and compression parallel to grain were examined. It was observed that the anatomical characteristic of the inner part of OPT (i.e., vascular bundles, vessels, and parenchyma tissue) became flattened, fractured, and collapsed after compression by CSC. The RS decreased with increasing compression temperature and time. The lower RS indicated high dimensional stability. The physical and mechanical properties (i.e., density, MOR, MOE, and compressive strength) of the inner part of OPT increased with increasing compression temperature and time. Compression by the CSC method at $160^{\circ}C$ for 40 min was the optimum treatment.

• 한국미생물·생명공학회지
• /
• 제43권3호
• /
• pp.241-248
• /
• 2015

Tuak is a traditional alcoholic beverage, one of the most widely known in the North Sumateran region of Indonesia. It is produced by a spontaneous fermentation process through the application of one or more several kinds of wood bark or root, called raru (Xylocorpus wood bark or a variety of forest mangosteen), into the sap water of sugar palm (Arenga pinnata) for 2−3 days. In this research, yeast that are potentially useful for ethanol production was isolated from Tuak and identified. Based on analysis of D1/D2 domain sequence of LSU (large subunit) rRNA genes, those isolated yeast strains, HT4, HT5, and HT10 were identified as Candida tropicalis. Fermentation test of these C. tropicalis isolates displayed an ability to produce 6.55% (v/v) and 4.58% ethanol at 30℃ and 42℃, respectively. These results indicated C. tropicalis isolates more rapidly utilize glucose and obtain higher levels of the production of ethanol at the higher temperature of 42℃ than S. cerevisiae, a common yeast used for bioethanol fermentation.

• Journal of the Korean Wood Science and Technology
• /
• 제46권2호
• /
• pp.155-165
• /
• 2018

The objective of the research was to evaluate the effect of particle pre-treatment on physical, mechanical, and durability of jatropha fruit hulls (JFH) particleboard. The pre-treatments included were immersing in cold water, hot water, and acetic acid solution. After each treatment, the particles were dried up to 3% moisture content. Urea-formaldehyde (UF) resin was used to fabricate particleboards with board size, thickness and density target of 25 cm by 25 cm, 0.80 cm, and $0.70g/cm^3$, respectively. Board pressed at $130^{\circ}C$ for 10 minutes, and $25kg/cm^2$ pressure. The evaluation of particleboard followed the JIS A 5908-2003. Whilist their resistance to subterranean termite test (mass loss, mortality, antifeedant value and feeding rate) refers to the Indonesian standard (SNI 01.7207-2006). The physical and mechanical properties of particleboards showed that all pre-treatments decreased the pH of particles. Overall, all particle immersing treatments resulted of better physical and mechanical properties of particleboard than those of untreated ones. The acetic acid treatment resulted the best physical and mechanical properties of particleboard. Based on the mass loss of JFH particleboard, hot water and acetic acid treated particleboards were classified into weak resistance to subterranean attack. The other two treatments were classified into very weak resistance. Hot water treated particleboard provided the highest mortality and antifeedant as much as 87.40% and 34.20%, respectively. Based on antifeedant classification, hot water treated particleboards were classified into moderately strong resistance, while other treatments were categorized into weak resistance. The lowest feeding rate value ($45.30{\mu}g/termite/day$) was attained by hot water treatment.

• 한국주거학회논문집
• /
• 제25권6호
• /
• pp.111-121
• /
• 2014

The purpose of the study is to understand the unique characteristics of decoration style in traditional Javanese houses. Reviewing literature and visiting site were applied as the research method. Javanese House can be divided into three parts; roof, wall and floor. First, the roof of the traditional Javanese House is the most unique and important decorative element. The roofs are covered with roof-tiles and have clay carving ornaments on top. Usually there are no ceilings, just exposed to the oblique shape roof, which are made of wood to enable air ventilation. Joglo roof is the outstanding and representative roof type of Javanese houses. There is artistic and constructive roof structure named as tumpang sari in Joglo roof. The decoration on tumpang sari is the most colorful and symbolic ornaments. Secondly, the most unique element in the wall is the gebyok. Gebyok is made of wood and full of carved ornament, which has an artistic appearance, and also important function. The top part of doors are designed as perforated woodcarving, which give both aesthetic and ventilation purposes. Last, the stratified floor is begin with ground yard, then veranda that made from hardened clay, and main room constituted with a wood scaffold to provide air circulation and remove the humidity of the ground. The decorations of the column stand (umpak) are unique, where usually lotus flower is carved into black stone or lime stone. The outside of the buildings in Java Houses is not decorated by colors or symbols, whereas colors are only used in temples, pavilion or in royal housings. Instead they have carvings and decorations on important structural elements such as columns and beams inside. The ornaments and colors of decorations symbolize their god, ancestors and piece.

• Journal of the Korean Wood Science and Technology
• /
• 제44권6호
• /
• pp.842-851
• /
• 2016

The objective of this study was to improve physical and mechanical properties of soft-inner part of oil palm trunk (S-OPT) after impregnation with phenol formaldehyde (PF) resin and densification by close system compression (CSC) method. Effect of different methods of PF resin impregnation (i.e., no vacuum-pressure, vacuum, and vacuum-pressure) was evaluated. The results showed that PF resin impregnation and CSC significantly improved the physical and mechanical properties of S-OPT up to: (1) 176% in density; (2) 309% in modulus of rupture (MOR); (3) 287% modulus of elasticity (MOE); and (4) 191% in the compressive strength. Physical and mechanical properties of S-OPT showed their best performances when PF resin impregnated with vacuum-pressure method as shown by higher weight gain, density, MOR, MOE, compressive strength, and lower recovery of set due to better penetration of PF resin into S-OPT. Combining PF resin impregnation and densification by CSC method could be a good method to improve physical and mechanical properties of S-OPT.

• Journal of the Korean Wood Science and Technology
• /
• 제43권6호
• /
• pp.768-776
• /
• 2015

본 연구에서는 인도네시아 조림지에서 생장한 4수종의 효율적 활용방안을 마련하기 위해 콘칼로리미터법에 의해 연소특성을 조사하였다. 그 결과, 평균열방출량($HRR_{mean}$)은 비중에 비례하였으며, 총열방출량(THR) 및 연소시간(FT) 등열관련 계수도 같은 경향을 나타냈다. Albizia는 열방출 시간이 짧았고, Mindi는 4수종 중 점화시간(TTI)과 연소시간(FT)이 길어져 4수종 중 연소속도가 늦었고, 열방출 시간도 가장 길게 이어져 결국은 Mangium 수종과 비슷한 총열방출률을 나타내는 것을 확인할 수 있었다. Albizia는 공시수종 중 가장 높은 비소화면적 값을 나타내어 연기발생비율이 높았고, 반대로 Mindi는 가장 낮은 비소화면적 값을 나타내 연기발생비율이 낮았다. 초기 연기방출률은 Albizia가 높았으나 이후에는 Gmelina와 Mangium 의 연기방출률이 높아져 총연기발생량이 높게 나타났다. Gmelina는 불완전연소로 인해 연소기간 중 가장 많은 일산화탄소 연기를 생성하였고, $CO/CO_2$ 비율은 다른 수종에 비해 3배 이상 높았다.

• Journal of the Korean Wood Science and Technology
• /
• 제43권2호
• /
• pp.248-257
• /
• 2015

This research focused on the natural durability of twenty one lesser known tropical wood species planted in West Java, Indonesia against subterranean termite (Coptotermes curvignathus). It was observed that both heartwood and sapwood of Kiara payung (Filicium decipiens); heartwoods of Nangka (Arthocarpus heterophyllus), Mahoni (Swietenia macrophylla) and Simpur (Dillenia grandifolia); and sapwood of Bungur (Lagerstroemia speciosa) were rated as resistant (natural durability class II) according to Indonesian standard SNI 01.7207.2006 (BSN 2006). Both heartwood and sapwood of Salam (Syzigium polyanthum), Pasang (Lithocarpus sundaicus), Bisbul (Diospyros discolor), Rukam (Flacourtia rukam) and Trembesi (Samanea saman); heartwood of Puspa (Schima walichii), Bungur, Tanjung (Mimusops elangi) and Angsana (Pterocarpus indicus) were rated as moderately resistant (natural durability class III). Both heartwood and sapwood of Sungkai (Peronema canescens), Pine (Pinus merkusii), Mangium (Acacia mangium) and Afrika (Maesopsis eminii); sapwoods of Mahoni, Puspa and Tanjung were rated as poorly resistant (natural durability class IV). Both heartwood and sapwood of Agathis (Agathis dammara), Durian (Durio zibethinus), Ki sampang (Evodia latifolia) and Jabon (Anthocephalus cadamba); sapwoods of Nangka and Angsana were rated as very poorly resistant (natural durability class V). This reserach showed that woods with lower resistance against C. curvignathus attack (natural durability class IV and V) tend to have lower termite mortality values compared to woods with higher resistance against C. curvignathus attack (natural durability class II and III). Results of the study will provide some valuable information on termite resistance of twenty one lesser known tropical wood species planted in Indonesia.