• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.179-180
• /
• 2023

The adhesion performance of PCCs for crack repair of RC structures was greater in the case of using ultra high-early strength cement than in the case of using ordinary Portland cement, and the effect of mixing silica fume was higher in the case of ordinary Portland cement than that of ultra high-early strength cement. On the other hand, 130% of W/C was more fluid than 80% of W/C in the same P/C 80%, which increased the fillability and improved the strength, but the strength improvement effect was the greatest in adhesion in flexure. Through this study, the basic characteristics of the adhesion performance of PCCs were identified, and based on this, it is necessary to induce an optimal mixing design that can increase adhesion performance through various mixing designs.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.39-40
• /
• 2023

Recently, due to the advancement of buildings, finishing methods using stone are increasing. However, finishing methods are not standardized and rely on workers' arbitrary methods. In stone finishing, many building defects occur due to adhesion performance, so the adhesion performance of stones attached with epoxy is important. Therefore, in this study, the adhesion performance of stones attached with epoxy was evaluated by exposing them to various environments. As a result of the experiment, the test specimens exposed to thermal shock showed only 20% of the standard test specimens' adhesion performance, and the test specimens cured at high and low temperatures showed the standard test specimens. It was expressed in 65-80% of the test specimens. Therefore, the adhesion performance of stone using epoxy was found to be vulnerable to repeated harsh environments.

• 대한기계학회논문집A
• /
• 제29권6호
• /
• pp.804-808
• /
• 2005

A pneumatic tire is made up of many flexible filaments of high modulus cord of natural textile, synthetic polymer, glass fiber, or fine hard drawn steel embedded in and bonded to a matrix of low modulus polymetric material. Adhesion property of these materials is very important in tire durability safety because belt-leaving-belt tread separation reduces the ability of a driver to control a vehicle, whether or not the separation is accompanied by a loss of air. In this study adhesion test of carcass-belt-tread is conducted on material properties of 5 PCR tire model, which are on sale in domestic market and analyzed adhesion properties. For those tire models FMVSS 109 indoor high speed durability test is conducted to analyze the correlation between adhesion force and high speed performance of tires and found the correlation between the two test results.

• Journal of the Korean Wood Science and Technology
• /
• 제38권2호
• /
• pp.117-123
• /
• 2010

The objective of this research was executed to investigate the effect of molar ratio of formaldehyde to urea and melamine (F/(U+M)) of urea-melamine-formaldehyde (UMF) resin on bonding high and low moisture content veneers. For that purpose, UMF resin types with 5 different F/(U+M) molar ratios (1.45, 1.65, 1.85, 2.05, and 2.25) synthesized were used in present study. First, their curing behavior was evaluated by differential scanning calorimetry. Second, their adhesion performance in bonding high and low moisture content veneers was evaluated by probe tack and dry and wet shear strength tests. Curing temperature and reaction enthalpy decreased with the increase of F/(U+M) molar ratio. And the dry and wet shear strengthsof plywood manufactured from low moisture content veneers were higher than thoseof plywood manufactured from high moisture content veneers. Also, the maximum initial tack force on the low moisture content veneer was higher than that on the high moisture content veneer.

• 대한전기학회논문지:전기기기및에너지변환시스템부문B
• /
• 제51권1호
• /
• pp.40-47
• /
• 2002

This paper describes a re-adhesion control method for the Korean High-Speed Train (KHST) with parallel induction motor drive. To keep a traction efficiency and to improve vehicle maintenance, the adhesion characteristics between wheel and rail are analyzed. Also the re-adhesion controller is designed as the subsystem of induction motor vector control. In order to verify performance of the proposed control techniques, the simulation is executed by train model and a downscaled re-adhesion control simulator is utilized. Both simulation and running test results show that good re-adhesion characteristics are obtained.

• 센서학회지
• /
• 제33권2호
• /
• pp.86-92
• /
• 2024

Flexible electronic devices are exposed to repeated mechanical deformation; therefore, electrode performance is an important element. Recently, a new technology has been developed to improve the adhesion strength between polymer substrates and metal thin films through the cross-linking reaction of bovine serum albumin (BSA) bioconjugation proteins; however, additional performance evaluation as an electrode is necessary. Therefore, in this study, we investigated the effect of adhesive strength between a flexible substrate and a metal thin film on the performance of a flexible electrode. Cracks and changes in the electrical resistance of the electrode surface were observed through outer bending fatigue tests and tensile tests. As a result of a bending fatigue test of 50,000 cycles and a tensile test at 10% strain, the change in the electrical resistance of the flexible electrode with a high adhesion strength was less than 40%, and only a few microcracks were formed on the surface; thus, the electrical performance did not significantly deteriorate. Through this study, the relationship between the adhesion strength and electrical performance was identified. This study will provide useful information for analyzing the performance of flexible electrodes in the commercialization of flexible electronic devices in the future.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.181-182
• /
• 2023

This study is a study on the flexural adhesion performance of polymer cement composites(PCCs) repair section according to the crack depth, and the flexural adhesion strength was obtained through a flexural strength test of cement mortar that was filled into cracks and repaired to a certain thickness using PCCs made of ultra high-early strength cement and polymer dispersion of EVA. As a result of the study, the flexural adhesion performance according to the crack width and crack depth was expected to decrease the flexural adhesion strength as the crack depth increased at the crack width 3.0mm, but the crack width 2.0mm and 1.5mm did not show any tendency according to the crack depth. In addition, even in the final destruction, the fact that the cracks and bottoms filled with PCCs were not cut or dropped proves that PCCs have excellent adhesion and rich toughness.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2009년도 춘계 학술논문 발표대회 학계
• /
• pp.225-229
• /
• 2009

It has been found that existing detects at the junction between waterproofing layer as well as the material and the surfaces of the construction when waterproofing sheet is employed in the currently used unground structures waterproofing technology, causing a series of problems such as the high cost to the maintenance for leakage and the durability. The purpose of this study is about reducing the waterpoofing defects in underground structures. consequently, the homogeneous sheet which has some quality such as the unvulcanizate, high-adhesion and high-elastic was examined on physical properties. As a test result, it was confirmed to have satisfied performance about the ks. However, it must be continued to study through mock-up test for confirming of site application.

• Journal of Industrial and Engineering Chemistry
• /
• 제68권
• /
• pp.387-392
• /
• 2018

Various technical approaches and concepts have been proposed to develop conductive super-hydrophobic (SH) surfaces. However, most of these approaches are not usable in practical applications because of insufficient adhesion and cost issues. Additionally, durability and uniformity issues are still in need of improvement. The goal of this research is to produce a large-area conductive SH surface with improved adhesion performance and uniformity. To this end, carbon nanotubes (CNT) with a high aspect ratio and elastomeric polymer were utilized as a conductive filler and matrix, respectively, to form a coating layer. Additionally, nanoscale silica particles were utilized for stable implementation of the conductive SH surface. To improve the adhesion properties between the SH coating layer and substrate, pretreatment of the substrate was conducted by utilizing both wet and dry etching processes to create specific organic functional groups on the substrate. Following pretreatment of the surface, a zirco-aluminate coupling agent was utilized to enhance adhesion properties between the substrate and the SH coating layer. Raman spectroscopy revealed that adhesion was greatly improved by the formation of a chemical bond between the substrate and the SH coating layer at an optimal coupling agent concentration. The developed conductive SH coating attained a high electromagnetic interference (EMI) shielding effectiveness, which is advantageous in self-cleaning EMI shielding applications.

• 대한건축학회논문집:구조계
• /
• 제34권9호
• /
• pp.19-26
• /
• 2018

The focus of this study was centered around 15 common injection type water leakage repair materials (3 different types for each; synthetic polymer, cementitious, acrylic, epoxy, urethane) used in concrete structures of Korea and analyzing their wet surface adhesion performance in accordance to the ISO TS 16774 Test Method for Repair Materials for Water-leakage Cracks in Underground Concrete Structures, Part 4: Test Method for Adhesion on Wet Concrete Surface, and the results of this study was taken to be place under a comparative analysis with the results of the preceeding study on response to substrate movement performance study. The results of this comparative study showed that other than 1 specimen of 1 type of the acrylic and 3 specimens of 1 type of the synthetic polymer type materials, all of the 93% of the specimens used in this study showed stable adhesion on wet substrate surface, and we were able to determine that materials that have proper response properties against substrate movement are highly flexible and have high adhesion properties, but their adhesion properties on wet substrate would change based on their viscosity.