• Journal of the Korean Electrochemical Society
• /
• v.14 no.1
• /
• pp.16-21
• /
• 2011

$Li_4Sn_xTi_{5-x}O_{12}$ was manufactured by high energy ball milling (HEBM) and used as an anode material for lithium ion battery. Various amount of $SnO_2$was added to $Li_4Ti_5O_{12}$ and heated at different temperatures. The purpose of this research was to see the effect of $SnO_2$ addition into $Li_4Ti_5O_{12}$. Manufactured samples were analyzed by TGA, XRD, SEM, PSA. Battery cycler was used to test the charge/discharge properties of active materials. Heat treatment temperature of $800^{\circ}C$ was needed to make a stable structure of $Li_4Sn_xTi_{5-x}O_{12}$ and the particle size distribution was $0.2{\sim}0.6\;{\mu}m$. Charge/discharge process was repeated for 50 cycles at room temperature. The initial capacity was 168mAh/g and the voltage plateau was observed at 1.55V(Li/$Li^+$).

• Journal of Powder Materials
• /
• v.22 no.4
• /
• pp.283-288
• /
• 2015

Two sintering methods of a pressureless sintering and a spark-plasma sintering are tested to densify the Fe-TiC composite powders which are fabricated by high-energy ball-milling. A powder mixture of Fe and TiC is prepared in a planetary ball mill at a rotation speed of 500 rpm for 1h. Pressureless sintering is performed at 1100, 1200 and $1300^{\circ}C$ for 1-3 hours in a tube furnace under flowing argon gas atmosphere. Spark-plasma sintering is carried out under the following condition: sintering temperature of $1050^{\circ}C$, soaking time of 10 min, sintering pressure of 50 MPa, heating rate of $50^{\circ}C$, and in a vacuum of 0.1 Pa. The curves of shrinkage and its derivative (shrinkage rate) are obtained from the data stored automatically during sintering process. The densification behaviors are investigated from the observation of fracture surface and cross-section of the sintered compacts. The pressureless-sintered powder compacts show incomplete densification with a relative denstiy of 86.1% after sintering at $1300^{\circ}C$ for 3h. Spark-plasma sintering at $1050^{\circ}C$ for 10 min exhibits nearly complete densification of 98.6% relative density under the sintering pressure of 50 MPa.

• Journal of Powder Materials
• /
• v.16 no.2
• /
• pp.91-97
• /
• 2009

Nanopowders of $Co_3O_4$ and FeAl were fabricated by high energy ball milling. Dense 4.25 $Co_{0.53}Fe_{0.47}-Al_2O_3$ composite was simultaneously synthesized and consolidated by high frequency induction heated combustion method within 2 min from mechanically activated powders. Consolidation was accomplished under the combined effects of a induced current and mechanical pressure of 80 MPa.

• Korean Journal of Metals and Materials
• /
• v.50 no.5
• /
• pp.369-374
• /
• 2012

Nanopowders of Mo, Ta and Si were made by high-energy ball milling. A dense nanostructured $MoSi_2-TaSi_2$ composite was sintered by the high-frequency induction heated combustion method within 2 minutes from mechanically activated powder of Mo, Ta and Si. A highly dense $MoSi_2-TaSi_2$ composite was produced under simultaneous application of a 80 MPa pressure and the induced current. Mechanical properties and microstucture were investigated. The hardness and fracture toughness of the $MoSi_2-TaSi_2$ composite were $1200kg/mm^2$ and $3.5MPa.m^{1/2}$, respectively. The mechanical properties were higher than those of monolithic $MoSi_2$.

• Korean Journal of Metals and Materials
• /
• v.49 no.9
• /
• pp.715-719
• /
• 2011

Nanopowders of $Fe_3N$ and Si were fabricated by high-energy ball milling. A dense nanostructured $12Fe-Si_3N_4$ composite was simultaneously synthesized and consolidated using a high-frequency induction-heated sintering method for 2 minutes or less from mechanically activated powders of $Fe_3N$ and Si. Highly dense $12Fe-Si_3N_4$ with a relative density of up to 99% was produced under simultaneous application of 80 MPa pressure and the induced current. The microstructure and mechanical properties of the composite were investigated.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.340-341
• /
• 2005

Lithium titanium oxide as anode material for energy storage prepared by novel synthesis method. $Li_4Ti_5O_{12}$ based spinel-framework structures are of great interest material for lithium-ion batteries. We describe here $Li_4Ti_5O_{12}$ a zero-strain insertion material was prepared by novel sol-gel method and by high energy ball milling (HEBM) of precursor to from nanocrystalline phases. According to the X-ray diffraction and scanning electron microscopy analysis, uniformly distributed $Li_4Ti_5O_{12}$ particles with grain sizes of 100nm were synthesized. Lithium cells, consisting of $Li_4Ti_5O_{12}$ anode and lithium cathode showed the 173 mAh/g in the range of 1.0 $\sim$ 3.0 V. Furthermore, the crystalline structure of $Li_4Ti_5O_{12}$ didn't transfer during the lithium intercalation and deintercalation process.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.5C no.3
• /
• pp.119-123
• /
• 2005

Lithium titanium oxide as anode material for energy storage prepared by novel synthesis method. Li$_{4}$Ti$_{5}$O$_{12}$ based spinel-framework structures are of great interest material for lithium-ion batteries. We describe here Li$_{4}$Ti$_{5}$O$_{12}$ a zero-strain insertion material was prepared by novel sol-gel method and by high energy ball milling (HEBM) of precursor to from nanocrystalline phases. According to the X-ray diffraction and scanning electron microscopy analysis, uniformly distributed Li$_{4}$ Ti$_{5}$O$_{12}$ particles with grain sizes of 100nm were synthesized. Lithium cells, consisting of Li$_{4}$ Ti$_{5}$O$_{12}$ anode and lithium cathode showed the 173 mAh/g in the range of 1.0 $\~$ 3.0 V. Furthermore, the crystalline structure of Li$_{4}$ Ti$_{5}$O$_{12}$ didn't transform during the lithium intercalation and deintercalation process.

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1989-1991
• /
• 2005

Lithium titanium oxide as anode material for energy storage prepared by novel synthesis method. $Li_4Ti_5O_{12}$ based spinel-framework structures are of great interest material for lithium-ion batteries. We describe here $Li_4Ti_5O_{12}$ a zero-strain insertion material was prepared by novel sol-gel method and by high energy ball milling (HEBM) of precursor to from nanocrystalline phases. According to the X-ray diffraction and scanning electron microscopy analysis, uniformly distributed $Li_4Ti_5O_{12}$ particles with grain sizes of 100nm were synthesized. Lithium cells, consisting of $Li_4Ti_5O_{12}$ anode and lithium cathode showed the 173 mAh/g in the range of $1.0{\sim}3.0V$. Furthermore, the crystalline structure of $Li_4Ti_5O_{12}$ didn't transfer during the lithium intercalation and deintercalation process.

• Journal of Powder Materials
• /
• v.17 no.2
• /
• pp.107-112
• /
• 2010

Carbon-nanotube-embedded bismuth telluride (CNT/$Bi_2Te_3$) matrix composites were fabricated by a powder metallurgy process. Composite powders, whereby 5 vol.% of functionalized CNTs were homogeneously mixed with $Bi_2Te_3$ alloying powders, were successfully synthesized by using high-energy ball milling process. The powders were consolidated into bulk CNT/$Bi_2Te_3$ composites by spark plasma sintering process at $350^{\circ}C$ for 10 min. The fabricated composites showed the uniform mixing and homogeneous dispersion of CNTs in the $Bi_2Te_3$ matrix. Seebeck coefficient of CNT/$Bi_2Te_3$ composites reveals that the composite has n-type semiconducting characteristics with values ranging $-55\;{\mu}V/K$ to $-95\;{\mu}V/K$ with increasing temperature. Furthermore, the significant reduction in thermal conductivity has been clearly observed in the composites. The results showed that CNT addition to thermoelectric materials could be useful method to obtain high thermoelectric performance.

• Proceedings of the KIEE Conference
• /
• 1994.07b
• /
• pp.1333-1335
• /
• 1994

The nitrification of pure iron powders is found to occur even at room temperature by high energy ball milling in $NH_3$ gas atmosphere. The powders of metastable iron nitrides ($0<at.%N{\le}23.3$) thus produced are identified as the super-saturated bee structure for the N content below 14.9 at.%N and the high temperature phase of the hcp structure above 19.4 at.%N. The atomic volume of Fe in the bcc phase is found to be smaller than that of the N-martensite reported in the literature. Magnetization at room temperature gradually decreases with increasing the N concentration in contrast to the enhancement reported for the bet nitrides. Neutron diffraction experiment also provide detailed information about the local structure surrounding the nitrogen atom. The coordination number of Fe atom around a nitrogen atom for the iron nitride containing 9.5 at.%N turns out to be 3.9 atoms.