• Journal of the Korea Institute of Building Construction
• /
• 제17권6호
• /
• pp.527-534
• /
• 2017

Accordingly, this study, in order to use powder of recycled aggregate from production of recycled aggregate as an activator of ground granulated blast furnace slag, the influence of added recycled aggregate powder on physical properties of concrete induced ground granulated blast furnace slag were analyzed by hydration stages. The results of the study are summarized as follows: Except for samples eluted powder of recycled aggregate 1%, all the samples were high alkali suspensions with higher than pH 12.0. In particular, when eluted time was 5 hours, the sample eluted powder of recycled aggregate 3% showed about 15 mg/l of calcium hydroxide that was not different from the amount of calcium hydroxide in the mixing water eluted powder of recycled aggregate 5%. Hence, from this results, it can be considered that optimal eluted powder of recycled aggregate was 3% in this study. When using mixing water eluted with powder of recycled aggregate, compared to use of ordinary mixing water, it showed greater compressive strength in the entire ages, and in the sample replaced with ground granulated blast furnace slag by 50%, its compressive strength was greater than that of the OPC. As use of mixing water eluted with powder of recycled aggregate in concrete used with large amount of ground granulated blast furnace slag was more effective for improving compressive strength than ordinary mixing water, it is verified that powder of recycled aggregate had an effect of activator.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 한국건축시공학회 2012년도 춘계 학술논문 발표대회
• /
• pp.257-258
• /
• 2012

With regard to the carbon reduction that has become an international problem, we have examined the effects of compressive strength of the ground granulated blast-furnace slag mortar with the curing temperature. Also, we evaluated the mechanical properties of steel slag powder produced during the steelmaking process in order to examine the possibility as admixture.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 한국건축시공학회 2013년도 춘계 학술논문 발표대회
• /
• pp.78-79
• /
• 2013

As a part of study to maximize the amount used of the ground granulated blast-furnace slag, the study deals with setting properties of paste that is mixed the ground granulated blast-furnace slag with CaO-Al₂O₃ based inorganic blinder. The results of the experiment show that the setting time is most fast in the mix of 25% rate of CaO-Al₂O₃ based inorganic blinder. It is generally needed 2 hours for work time in precast concrete products. In this study, this requirement is achieved when using the retarder of 0.5%.

• Geomechanics and Engineering
• /
• 제19권4호
• /
• pp.361-368
• /
• 2019

This study aims to evaluate the applicability of a grout material that is mixed with carbon fiber, biogrout, ground granulated blast furnace slag (GGBS) powder and cement. Uniaxial compressive strength tests were performed on homo-gel samples at days of 1, 3, 7, 14 and 28. In addition, the variation of permeability with the mixing ratios was measured. Based on the uniaxial compressive strength test, it was confirmed that the uniaxial compressive strength increased by 1.2times when carbon fiber increased by 1%. In addition, as a result of the permeability test, it was found that when the GGBS increased by 20%, the permeability coefficient decreased by about 1.5times. Therefore, the developed grout material can be used as a cutoff grouting material in the field due to its strength and cut-off effect.

• Proceedings of the Korea Concrete Institute Conference
• /
• 한국콘크리트학회 1999년도 학회창립 10주년 기념 1999년도 가을 학술발표회 논문집
• /
• pp.191-194
• /
• 1999

Recently in Korea, may workers have reported the effects of the granulated blast furnace slag[BFS] of high fineness on the strength development of slag cement. We have studied the effect of slag fineness on the strength development of mortar with curing conditions, in order to get the basic data of high strength concrete using BFS. In this paper, we discussed the effects of slag fineness and porosity of mortar and the reaction of slag in hardened slag cement.

• Proceedings of the Korea Concrete Institute Conference
• /
• 한국콘크리트학회 1998년도 가을 학술발표논문집(II)
• /
• pp.275-280
• /
• 1998

In this study, to increase fluidity and resistance of segregation of materials, the effect of each of the materials, which have effects on high performance concrete from investigating the properties of strength and drying shrinkage of high performance concrete made by the basic mix proportion used fly-ash and ground granulated blast-furnace slag after hardening, has been checked. By the results of this experiment, fluidity on W/C=34% was satisfied within slump-flow 65$\pm$5cm and U-type self-compacting difference 5cm. On the properties of strength, high performance concrete produced compressive strength over 400kg/$\textrm{cm}^2$ in 28days when powder was replaced by 40% of fly-ash and 60% of ground granulated blast-furnace slag. And compressive strength was taken over 600kg/$\textrm{cm}^2$ equal to non-replacement in 91days. Also, the length change of concrete with the addition of fly-ash was smaller than that without it. Therefore, it may be effective on the decrease of drying shrinkage volume.

• Journal of the Korea Concrete Institute
• /
• 제16권1호
• /
• pp.1-9
• /
• 2004

This paper represents the permeability of chloride ions and the corrosion performance in the concrete blended with granulate blast furnace slag exposed to chloride environment. An ordinary cement (type I ) and sulfate resisting cement(type V) were used for the experiment. The two cements were combined with $0\%$, $25 \%$, $40\%$, and $55\%$ of the granulated blast furnace slag. The accelerated permeability tests of chloride ions were performed in accordance with ASTM C1202, and the accelerated corrosion tests of steel were carried out by using the method of immersion/drying cycles. After water curing 28 days, 56 days and 91 days, these tests were conducted until 30 cycles. In every cycle, test specimens were wetted in $3\%$ NaCl solution for three days and dried again in $60^{\circ}C$ air for four days. As an experimental results, the diffusion coefficient of chloride ions of the ordinary cement Concrete Combined granulated blast furnace slag was much lower than that of non granulated blast furnace slag concrete. Moreover, the diffusion coefficient of chloride ions of sulfate resisting cement concrete was higher than that of ordinary cement concrete. On the basis of the results of accelerated corrosion tests, corrosion resistance of the concrete mixed with granulated blast furnace slag shows good to corrosion resistance, however, the concrete with sulfate resisting cement shows bad to corrosion resistance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• 제10권1호
• /
• pp.9-14
• /
• 2022

Most of the existing research on ferronickel slag has focused on its potential as aggregate and fine aggregate, this study was conducted focusing on the potential of ferronickel slag powder as a concrete admixture. For concrete, which fly ash, blast furnace slag, and FSP were mixed with each 10 % type the reactivity was evaluated by applying ASTM C 1260 of the United States. As a result, compared with the control group, the expansion rate of fly ash decreased by 8.43 % and that of fine blast furnace slag powder decreased by 14.46 %, while the expansion rate of ferronickel slag decreased by 49.40 %. it was confirmed that ferronickel slag can sufficiently be replaced existing supplementary cementitious admixtures such as fly ash and blast furnace slag in terms of suppressing the reactivity of aggregates. However as a result of SEM analysis, ettringites were generated, and additional research about how it affects concrete is needed.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 한국건축시공학회 2019년도 추계 학술논문 발표대회
• /
• pp.19-20
• /
• 2019

This study investigated the possibility of strength development by incorporating the slighly coarser soda-lime glass powder (GP) with 0-100 wt.% of Ground Granulated Blast Furnace Slag (GGBS) to synthesis GGBS based geopolymer. Compressive strength, water absorption & apparent porosity, were experimentally determined. To determine the homogeneity of mix, the microstructure & elemental composition of samples were studied using SEM-EDS. Study reveals the improvement in strength and reduction in porosity for the samples containing up to 30% GP. Furthermore, the microstructure analyses confirmed the development of denser and compact structure with the incorporation of glass powder up to 30%.

• Computers and Concrete
• /
• 제20권1호
• /
• pp.77-84
• /
• 2017

Shirasu, a pyroclastic flow deposit, showed considerable performance as aluminosilicate source in geopolymer, based on past research. However, the polymerization reactivity was somewhat lower compared to the traditional fly ash based geopolymer even though the long-term strength was fairly good. The present study concentrates on the development of higher initial strength performance of Shirasu based geopolymer by utilizing ground granulated blast furnace slag as an admixture. Mortars with various mix proportions were adopted to study the effect of parametric changes on strength development along with the addition of slag in different percentages. A combination of sodium hydroxide and sodium silicate was used as alkaline activators considering parameters like molar ratios of alkali to geopolymer water and silica to alkali molar ratio. The mortars were cured at elevated temperatures under different curing conditions to analyze the effect on strength development. Compressive strength test, mercury intrusion porosimetry and X-ray powder diffraction were carried out to assess the strength performance and microstructure of slag-Shirasu based geopolymer. Based on the experimental study, it was observed that the initial and long-term strength development of Slag-Shirasu geopolymer were improved by the addition of slag.