• Transactions on Electrical and Electronic Materials
• /
• v.7 no.6
• /
• pp.279-282
• /
• 2006

[ $Pb(Zr_{0.4}Ti_{0.6}O_{3}\;and\;Pb(Zr_{0.6}Ti_{0.4})O_{3}$ ] paste were made and alternately screen-printed on the $Al_{2}O_{3}$ substrates. We have introduced a press-treatment to obtain a good densification of screen printed films. The porosity of the thick films was decreased with increasing the applied pressure and the thick films pressed at 60 MPa showed the dense microstructure and thickness of about $76\;{\mu}m$. The remanent polarization and coercive field increased with increasing applied pressure and the values for the PZT thick films pressed at 60 MPa were $17.04{\mu}C/cm^{2}$ and 78.09 kV/cm, respectively.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1301-1302
• /
• 2007

The multilayered $Pb_{1.1}(Zr_{0.4}Ti_{0.6})O_{3}$/$Pb_{1.1}(Zr_{0.6}Ti_{0.4})O_{3}/Pb_{1.1}(Zr_{0.4}Ti_{0.6})O_{3}$[PZT(4060)/(6040)/(4060)] thin films were deposited by RF sputtering method on the Pt/TiO2/SiO2/Si substrate. We investigated the effects of deposition conditions on the structural and electrical properties of the multilayered PZT thin films. All the multilayered PZT thin films showed dense and homogeneous structure without the presence of the rosette structure. The dielectric properties such as dielectric constant, loss, remanent polarization of the multilayered PZT thin film were superior to those of single composition PZT(4060) and PZT(6040) films, and those values for the multilayered PZT(10/20/10) thin film were 903, 1.01% and $25.60{\mu}C/cm^2$. This study suggests that the design of the multilayered PZT thin films capacitor with tetragonal and rhombohedral phase should be an effective method to enhance the dielectric and ferroelectric performance in devices.

• Journal of the Korean Vacuum Society
• /
• v.8 no.3A
• /
• pp.231-237
• /
• 1999

$SrBi_{22.4}Ta_2O_9$ (SBT) thin films of 70~150 nm thickness were prepared on platinized silicon substrates by Liquid Source Misted Chemical Deposition (LSMCD) process, and their microstructure, feroelectric and leakage current characteristics were investigated. By annealing at $800^{\circ}C$ for 1 hour in oxygen ambient, SBT films were fully crystallized to the Bi layered perovskite structure without preferred orientation. The grain size of the LSMCD- derived SBT films was about 100nm, and was not varied with the film thickness. $2P_r$ and $E_c$ of the SBT films increased with decreasing the film thickness, and the 70nm-thick SBT film exhibited $2P_r$ of 17.8 $\mu$C/$\textrm{cm}^2$ and $E_c$ of 74kV/cm at applied voltage of 5V. Within the film thickness range of 70~150nm, the relative dielectric permittivity of the LSMCD-derived SBT film decreased with decreasing the film thickness. Leakage current densities lower than $10^{-7}\textrm{A/cm}^2$ at 5V were observed in the SBT films thicker than 125nm.

• The Korean Journal of Ceramics
• /
• v.6 no.1
• /
• pp.64-67
• /
• 2000

Reactively sputtered $Pb(Zr,Ti)O_3$(PZT) films on $IrO_2$and Ir were evaluated with particular consideration on interface properties. The $IrO_2$and Ir were previously annealed at $650^{\circ}C$ in $O_2$or $N_2$atmosphere, respectively. There was no appreciable roughening in the interface of the $PZT/IrO_2$respective to that of the PZT/Ir; the rms roughness of $IrO_2$and Ir was about 3nm and 10nm, respectively. The ferroelectric properties of the $PZT/IrO_2$were found to be better than that of the PZT/Ir; however, the leakage current of the $PZT/IrO_2$was slightly larger than that of the PZT/Ir. The $PZT/IrO_2$thin films did not exhibit any fatigue up to $10^{11}$ cycles; the $P^*\;_r-P^r$ value decreased only from 16.6 to 14$\mu$C/$\textrm{cm}^2$ until $10^{12}$ polarization reversals. On the other hand, although thin $IrO_2$layer was formed between PZT and Ir, the PZT/Ir thin films began to undergo fatigue after $10^9$ polarization reversals.

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.279-285
• /
• 2003

Ferroelectric S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$ thin films with 200 nm thicknesses were deposited on Pt/Ti $O_2$/ $SiO_2$/Si Substrates by a sol-gel method. In these experiments, Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$ and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. After UV-irradiation and RTA processes, the remanent polarization value (2 $P_{r}$) of SBTN thin films with annealed at $650^{\circ}C$ was 8.49 and 11.94 $\mu$C/$\textrm{cm}^2$ at 3 V and 5 V, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.817-820
• /
• 2004

The $Sr_{0.7}Bi_{2.6}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode($Pt/TiO_2/SiO_2/Si$) using a RF magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing time were studied. In the SEM images, Bi-layered perovskite phase was crystallized at 10min and grains largely grew with annealing tune. SBT thin films are transformed from initial amorphous phase to the fully formed layer-structured perovskite. During the annealing process at $750^{\circ}C$, we found that an fluorite-like stage is formed after 3min. In the XRD pattern, the SBT thin films after 3min annealing time had (105) orientation. The ferroelectric properties of SBT capacitor with annealing time represent a favorable properties at 60 min. The maximum remanent polarization and the coercive electric field with 60 min are $12.40C/cm^2$ and 30kV/cm, respectively. The leakage current density with 60min is $6.81{\times}10^{-10}A/cm^2$.

• Proceedings of the IEEK Conference
• /
• 2004.06b
• /
• pp.363-366
• /
• 2004

PZT thin films were formed by rf-magnetron sputtering on $Pt/Ti/SiO_2/Si$ substrate. Bulk PZT target containing $5\%$ excess PbO was used. They were formed with in-situ process at $650^{\circ}C$ as total thickness of 175 and 250 nm after the depositing of thin PZT films at room temperature, i. e. 2-step Sputtering. It was found that the ferroelectric perovskite phase is formed at $650^{\circ}C$ by XRD and the interface between room temp.-layer and $650^{\circ}C$ -layer is not existent. In the samples undergoing 2-step sputtering the dielectric constant was 600 or more and the leakage current density was $2{\times}10^{-7}A/cm^2$. So, we found that the room temp.-layer on the bottom electrode stabilize the underlaid layers.

• Journal of the Korean Ceramic Society
• /
• v.26 no.5
• /
• pp.670-676
• /
• 1989

The PbTiO3 is well known materials having remarkable ferroelectric, piezoelectric, and pyroelectric properties. PbTiO3 thin films with a perovskite structure were successfully fabricated on titanium substrate by chemical vapor deposition. These films were characterized according to composition, crystal structure, and electrical properties. Semi-quantitative compositional analysis of the deposited films was made by Auger Electron Spectroscopy(AES). The PbTiO3 film deposited on titanium substrate at the deposition temperature 75$0^{\circ}C$, the Ti(C2H5O)4 fraction 0.15, and O2 partial pressure 0.06atm, has a columnar structure and grows with(001) preferred orientation, and has stoichiometric composition. A clear dielectric transition and offset in the dc conductivity near the transition temperature(48$0^{\circ}C$) were observed in the deposited lead titanate film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.709-712
• /
• 2001

The effects of post annealing temperature by the Rapid Thermal Annealing(RTA) on the electrical properties of Pb(Zr,Ti)O$_3$(PZT) thin film were investigated. Analyses by the RTA treatments reveled that the leakage current of PZT thin films strongly depend on heating temperature and time. It was found that leakage current properties of PZT capacitor were changed by heating temperature during the RTA annealing. On Pt/Ti/Si substrates, PZT films are deposited at 350 $^{\circ}C$ by rf magnetron sputtering. The X-ray diffusion (XRD) was confirmed the formation of PZT thin film. Leakage current characteristics were improved with decreasing the post annealing temperature of PZT thin film. RTA annealed film on the 700$^{\circ}C$ shows ferroelectric and electrical properties with a remanent polarization of 12.4${\mu}$C/$\textrm{cm}^2$ coercive field of 117kV/cm, leakage current J= 6.2${\times}$10$\^$-6/ A/$\textrm{cm}^2$

• Journal of the Korean Ceramic Society
• /
• v.31 no.2
• /
• pp.171-176
• /
• 1994

The spin-casted PLZT(9/65/35) thin films through polymeric sol-gel process were prepared on Pt substrate. The crack-free, uniform and dense films were obtained by post-annealing at the temperature between 35$0^{\circ}C$ and $700^{\circ}C$. The composite structure mixed together with large grains called "rosette" and surrounding small grains were observed on the films annealed over $600^{\circ}C$. Pyrochlore phase was completely changed to perovskite phase above $600^{\circ}C$ with the increase of annealing temperature. Dielectric constant (k) was larger with the increase of film thickness and annealing temperature. from the measurements of dielectric constant as a function of measuring temperature, it was also observed that Curie temperature was shifted to higher temperature with the increase of film thickness and annealing temperature. The pyroelectric coefficient(P) of 10 times coated film annealed at $700^{\circ}C$ was 65 $\mu$C/$\textrm{cm}^2$.K.$.K.