In this paper, we are proposed the antennas for RFID tag operated at UHF band which are inserted ground plane easy to mount the RFTD chips at the antenna surfaces. In order to implemented antenna for RFID tag which the size is same as conventional name card, the structure of the antenna is meander type, matching method for improvement characteristics of the antenna use T matching method, ground plane is inserted at the antenna substrate fer mounting RFID chips. The substrate size of implementation is $100\times60\;mm^2$ and the FR4 substrate is used. Results of the experiment, the center frequency of the implemented antenna is 427 MHz, -10 dB return loss bandwidth is 8 MHz, maximum return loss is 21 dB, the radiation pattern is omnidirectional. From these results, we are conformed application for UHF RFID tag antenna.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.56-59
• /
• 2004

The stochiometric composition of $AgGaS_2$ polycrystal source materials for the $AgGaS_2/GaAs$ epilayer was prepared from horizontal furnace. From the extrapolation method of X-ray diffraction patterns it was found that the polycrystal $AgGaS_2$ has tetragonal structure of which lattice constant $a_0$ and $c_0$ were 5.756 ${\AA}$ and 10.305 ${\AA}$, respectively. $AgGaS_2/GaAs$ epilayer was deposited on throughly etched GaAs (100) substrate from mixed crystal $AgGaS_2$ by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $590^{\circ}C$ and $440^{\circ}C$ respectively. The crystallinity of the grown $AgGaS_2/GaAs$ epilayer was investigated by the DCRC (double crystal X-ray diffraction rocking curve). The optical energy gaps were found to be 2.61 eV for $AgGaS_2/GaAs$ epilayer at room temperature. The temperature dependence of the photocurrent peak energy is well explained by the Varshni equation, then the constants in the Varshni equation are given by ${\alpha}=8.695{\times}10^{-4}eV/K$, and $\beta$=332 K. From the photocurrent spectra by illumination of polarized light of the $AgGaS_2/GaAs$ epilayer, we have found that crystal field splitting $\Delta$ Cr was 0.28 eV at 20 K. From the PL spectra at 20 K, the peaks corresponding to free and bound excitons and a broad emission band due to D-A pairs are identified. The binding energy of the free excitons are determined to be 0.2676 eV and 0.2430 eV and the dissociation energy of the bound excitons to be 0.4695 eV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.04b
• /
• pp.7-7
• /
• 2009

Lead telluride (PbTe) is a very promising thermoelectric material due to its narrow band gap (0.31 eV at 300 K), face-centered cubic structure and large average excitonic Bohr radius (46 nm) allowing for strong quantum confinement within a large range of size. In this work, we present the thermoelectric properties of individual single-crystalline PbTe nanowires grown by a vapor transport method. A combination of electron beam lithography and a lift-off process was utilized to fabricate inner micron-scaled Cr (5 nm)/Au (130 nm) electrodes of Rn (resistance of a near electrode), Rf (resistance of a far electrode) and a microheater connecting a PbTe nanowire on the grid of points. A plasma etching system was used to remove an oxide layer from the outer surface of the nanowires before the deposition of inner electrodes. The carrier concentration of the nanowire was estimated to be as high as $3.5{\times}10^{19}\;cm^{-3}$. The Seebeck coefficient of an individual PbTe nanowire with a radius of 68 nm was measured to be $S=-72{\mu}V/K$ at room temperature, which is about three times that of bulk PbTe at the same carrier concentration. Our results suggest that PbTe nanowires can be used for high-efficiency thermoelectric devices.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.4
• /
• pp.298-303
• /
• 2012

$Y_{1-x}VO_4:Eu_x^{3+}$ red phosphors were synthesized with changing the mol ratios of $Eu^{3+}$ ions by using the solid-state reaction method. The crystalline structure of phosphors was found to be a tetragonal system with the maximum diffraction intensity at $25.02^{\circ}$. The grain particles showed the truncated hexagonal patterns with a very homogeneous size distribution at 0.05 mol of $Eu^{3+}$ ion. The excitation spectra of the phosphor ceramics were composed of a broad band centered at 303 nm and weak narrow multilines peaked in the range of 360-420 nm. The dominant emission spectrum was the strong red emission centered at 619 nm due to the $^5D_0{\rightarrow}^7F_2$ electric dipole transition. The experimental results suggest that the optimum doping mol ratio of $Eu^{3+}$ ions for preparing the red phosphors is 0.10 mol with the asymmetry ratio of 5.21.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.386-391
• /
• 2003

Sing1e crystal $CuAlSe_2$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at $410^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $CuAlSe_2$source at $680^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence(PL) and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $CuAlSe_2$ thin films measured with Hall effect by van der Pauw method are $9.24{\times}10^{16}\;cm^{-3}$ and $295\;cm^2/V{\cdot}\;s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CuAlSe_2$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)\;=\;2.8382\;eV\;-\;(8.86\;{\times}\;10^{-4}\;eV/K)T^2/(T\;+\;155K)$. After the as-grown single crystal $CuAlSe_2$ thin films were annealed in Cu-, Se-, and Al-atmospheres, the origin of point defects of single crystal $CuAlSe_2$ thin films has been investigated by PL at 10 K. The native defects of $V_{Cd}$, $V_{Se}$, $Cd_{int}$, and $Se_{int}$ obtained by PL measurements were classified as donors or accepters. And we concluded that the heat-treatment in the Cu-atmosphere converted single crystal $CuAlSe_2$ thin films to an optical n-type. Also, we confirmed that Al in $CuAlSe_2/GaAs$ did not form the native defects because Al in single crystal $CuAlSe_2$ thin films existed in the form of stable bonds.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.5
• /
• pp.467-475
• /
• 2004

ZnO epilayer were synthesized by the pulsed laser deposition(PLD) process on $Al_2$ $O_3$substrate after irradiating the surface of the ZnO sintered pellet by the ArF(193 nm) excimer laser. The epilayers of ZnO were achieved on sapphire(A $l_2$ $O_3$) substrate at a temperature of 400 $^{\circ}C$. The crystalline structure of epilayer was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of ZnO epilayer measured with Hall effect by van der Pauw method are 8.27${\times}$$10^{16}$$cm^{-3}$ and 299 $\textrm{cm}^2$/Vㆍs at 293 K, respectively. The temperature dependence of the energy band gap of the ZnO obtained from the absorption spectra was well described by the Varshni's relation, $E_{g}$(T)= 3.3973 eV - (2.69 ${\times}$ 10$_{-4}$ eV/K) $T^2$(T＋463k). After the as-grown ZnO epilayer was annealed in Zn atmospheres, oxygen and vaccum the origin of point defects of ZnO atmospheres has been investigated by the photoluminescence(PL) at 10 K. The native defects of $V_{Zn}$ , $V_{o}$ , Z $n_{int}$, and $O_{int}$ obtained by PL measurements were classified as a donors or accepters type. In addition, we concluded that the heat-treatment in the oxygen atmosphere converted ZnO thin films to an optical p-type. Also, we confirmed that vacuum in ZnO/A $l_2$ $O_3$did not form the native defects because vacuum in ZnO thin films existed in the form of stable bonds.s.s.s.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.10
• /
• pp.871-880
• /
• 2003

Single crystal CuAlSe$_2$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at 410 C with hot wall epitaxy (HWE) system by evaporating CuAlSe$_2$ source at 680 C. The crystalline structure of the single crystal thin films was investigated by the photoluminescence(PL) and double crystal X -ray diffraction (DCXD). The carrier density and mobility of single crystal CuAlSe$_2$ thin films measured with Hall effect by van der Pauw method are 9.24${\times}$10$\^$16/ cm$\^$-3/ and 295 cm$^2$/V $.$ s at 293 K, respectively. The temperature dependence of the energy band gap of the CuAlSe$_2$ obtained from the absorption spectra was well described by the Varshni's relation, Eg(T) = 2.8382 eV - (8.86 ${\times}$ 10$\^$-4/ eV/K)T$^2$/(T + 155K). After the as-grown single crystal CuAlSe$_2$ thin films were annealed in Cu-, Se-, and Al-atmospheres, the origin of point defects of single crystal CuAlSe$_2$ thin films has been investigated by PL at 10 K. The native defects of V$\_$cd/, V$\_$se/, Cd$\_$int/, and Se$\_$int/ obtained by PL measurements were classified as donors or acceptors. And we concluded that the heat-treatment in the Cu-atmosphere converted single crystal CuAlSe$_2$ thin films to an optical n-type. Also, we confirmed that Al in CuAlSe$_2$/GaAs did not form the native defects because Al in single crystal CuAlSe$_2$ thin films existed in the form of stable bonds.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.76-77
• /
• 2005

Single crystal $CuAlSe_2$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at 410$^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $CuAlSe_2$ source at $680^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence(PL) and double crystal X-ray diffraction (DCXO). The temperature dependence of the energy band gap of the $CuAlSe_2$ obtained from the absorpt ion spectra was wel1 described by the Varshni's relation, $E_g$(T) = 2.8382 eV - ($8.86\times10^{-4}$ eV/H)$T_2$/(T + 155K). After the as-grown single crystal $CuAlSe_2$ thin films were annealed in Cu-, Se-, and Al-atmospheres, the origin of point defects of single crystal $CuAlSe_2$ thin films has been investigated by PL at 10 K. The native defects of $V_{cd}$, $V_{se}$, $Cd_{int}$, and $Se_{int}$ obtained by PL measurements were classified as donors or acceptors. And we concluded that the heat-treatment in the Cu-atmosphere converted single crystal $CuAlSe_2$ thin films to an optical n-type. Also. we confirmed that hi in $CuAlSe_2$/GaAs did not form the native defects because Al in single crystal $CuAlSe_2$ thin films existed in the form of stable bonds.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.280-280
• /
• 2010

Semiconductor quantum dots are of great interest for both fundamental research and industrial applications due to their unique size dependant properties. The most promising application of colloidal semiconductor nanocrystals (quantum dots or QDs) is probably as emitters in biomedical labeling, LEDs, lasers etc. As compared to II-VI quantum dots, III-V have attracted greater interest owing to their less ionic lattice, larger exciton diameters and reduced toxicity. Among the III-V semiconductor quantum dots, Indium Phosphide (InP) is a popular material due to its bulk band gap of 1.35 (eV) which is responsible for the photoluminescence emission wavelength ranging from blue to near infrared with change in size of QDs. Nevertheless, in recent years, the exact type of collective properties that arise when semiconductor quantum dots (QDs) are assembled into two- or three-dimensional arrays has drawn much interest. The term "uantum dot solids" is used to indicate three-dimensional assemblies of semiconductor QDs. The optoelectronic properties of the quantum dot solids are known to depend on the electronic structure of the individual quantum dot building blocks and on their electronic interactions. This paper reports an efficient and rapid method to produce highly luminescent and monodisperse quantum dots solution and solid through fabrication of InP thin films. By varying the molar concentration of Indium to Ligand, QDs of different size were prepared. The absorption and emission behaviors were also studied. Similar measurements were also performed on InP quantum dot solid by fabricating InP thin films. The optical properties of the thin films are measured at different curing temperatures which show a blue shift with increase in temperature. The dielectric properties of the thin films were also investigated by Capacitance-voltage(C-V) measurements in a metal-insulator-semiconductor (MIS) device.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.5
• /
• pp.386-389
• /
• 2009

The electrical characteristics and annealing effects of tunneling dielectrics stacked with $SiO_2$ and $Si_{3}N_{4}$ were investigated. I-V characteristics of band gap engineered tunneling gate stacks consisted of $Si_{3}N_{4}/SiO_2/Si_{3}N_{4}$ (NON), $SiO_2/Si_{3}N_{4}/SiO_2$ (ONO) dielectrics were evaluated and compared with $SiO_2$ single layer using the MOS (metal-oxide-semiconductor) capacitor structure. The leakage currents of engineered tunneling barriers (ONO, NON stacks) are lower than that of the conventional $SiO_2$ single layer at low electrical field. Meanwhile, the engineered tunneling barriers have larger tunneling current at high electrical field. Furthermore, the increased tunneling current through engineered tunneling barriers related to high speed operation can be achieved by annealing processes.