• Journal of the Semiconductor & Display Technology
• /
• v.21 no.3
• /
• pp.105-109
• /
• 2022

For the realization of higher reliable transition metal dichalcogenide layer, molybdenum disulfide was formed on sapphire substrate by direct current sputtering and subsequent rapid thermal annealing process. Unlike RF sputtered MoS₂ thin films, DC sputtered showed no irregular holes and protrusions after annealing process from scanning electron microscope images. From atomic force microscope results, it was possible to investigate that surface roughness of MoS₂ thin films were more dependent on DC sputtering power then annealing temperature. On the other hand, the Raman scattering spectra showed the dependency of significant E¹_2g and A¹_g peaks on annealing temperatures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.6
• /
• pp.439-444
• /
• 2012

For the application of photo-detector as active layer, we have studied how to deposit SiGe thin film using an independent Si target and Ge target, respectively. Both targets were synthesized by purity of 99.999%. Plasma generators were generated by radio frequency (rf, 13.56 MHz) and direct current (dc) power. When Ge and Si targets were sputtered by dc and rf power, respectively, we could observe the growth of highly crystalline Ge thin film at the temperature of $400^{\circ}C$ from the result of raman spectroscopy and X-ray diffraction method. However, SiGe thin film did not deposit above method. Inversely, we changed target position like that Ge and Si targets were sputtered by rf and dc power, respectively. Although Ge crystalline growth without Si target sputtering deteriorated considerably, the growth of SiGe thin film was observed with increase of Si dc power. SiGe thin film was evaluated as microcrystalline phase which included (111) and (220) plane by X-ray diffraction method.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.554-557
• /
• 2001

Indium Tin Oxide(ITO) thin films have been fabricated by the dc magnetron sputtering technique with a target of a mixture $In_{2}O_{3}$(90mol%) and $SnO_{2}$(10mol%). We prepared ITO thin films with substrate temperature 200 to $400^{\circ}C$ and annealing temperature 200 to $500^{\circ}C$. Good polycrystalline-structured ITO films with a low electrical resistivity of $3.4{\times}10^{-4}\Omega{\cdot}cm$ have been obtained. The visible light transmittance of all obtained films was over 80 %.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.554-557
• /
• 2001

Indium Tin Oxide(ITO) thin films have been fabricated by the dc magnetron sputtering technique with a target of a mixture In$_2$O$_3$(90mo1%) and SnO$_2$(10mo1%). We prepared ITO thin films with substrate temperature 200 to 400$^{\circ}C$ and annealing temperature 200 to 500$^{\circ}C$ food polycrystalline-structured ITO films with a low electrical resistivity of 3.4${\times}$10$\^$-4/ Ω$.$cm have been obtained. The visible light transmittance of all obtained films was over 80 %.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2014.11a
• /
• pp.274-274
• /
• 2014

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.60-61
• /
• 2007

IAZO (indium aluminium zinc oxide) anode films were co-sputtered on glass substrate using a dual target DC magnetron sputtering system. For preparation of IATO films, at constant DC power of IZO (indium zinc oxide) target of 100 W, the DC power of AZO (Aluminum zinc oxide) target was varied from 0 to 100 W. To analyze electrical and optical properties of IAZO anode, Hall measurement examination and UV/V is spectrometer were performed, respectively. In addition, structure of IAZO anode film was examined by X-ray diffraction (XRD) method. Surface smoothness was investigated by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). From co-sputtered IAZO anode, good conductivity($2.32{\times}10^{-4}{\Omega}.cm$) and high transparency(approximately 80%) in the visible range were obtained even at low temperature deposition. Finally, J-V-L characteristics of phosphorescent OLED with IAZO anode were studied by Keithley 2400 and compared with phosphorescent OLED with conventional ITO anode.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.2
• /
• pp.55-71
• /
• 2017

Transparent Conductive Oxide (TCO), especially Indium Tin Oxide (ITO) films are almost prepared by DC magnetron sputtering because of the advantage of obtaining homogeneous large area coatings with high reproducibility. The purpose of this report is describe a detailed investigation of key factors dominating electrical and structural properties of sputtered ITO films. It was confirmed that crystallinity and electrical properties of ITO films were strongly depend on the sputtering pressure and kinetic energy of sputtered particles which are expected to have a close relation with the transport processes between target and substrate. And also, nodule formation on the ITO target was suppressed by both $CaCO_3$ addition and decreasing micro-pore in the target. On the other hand, we focused on the characteristics of amorphous TCO film to use as transparent electrode for various applications. To realize high thermoelectric performance, it was tried to control both high electrical conductivity and low thermal conductivity for the amorphous IZO:Sn films.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.249-249
• /
• 2015

Silver films have been of considerable interest for years due to their better performance relative to other metal films for engineering applications. A series of multi-layer silver coatings with different thickness (i.e. 0.3 um to 1.5 um) were prepared on Aluminium substrate containing copper undercoat by direct current (DC) magnetron sputtering method. For the comparative purpose, similar thickness silver coatings were prepared by electrolytic deposition method. Microstructural, morphological, and mechanical characteristics of the silver coatings were evaluated by means of scanning electron microscope (SEM), X-ray diffraction (XRD), Surface roughness test, microhardness test and nano-scratch test. From the results, it has been elucidated that the silver films prepared by DC magnetron sputtering method has superior properties in comparison to the wet coating method. On the other hand, DC magnetron sputtering method is relatively easier, faster, eco-friendly and more productive than the electrolytic deposition method that uses several kinds of hazardous chemicals for bath formulation. Therefore, a New Work Item Proposal (NWIP) for the test methods standardization of DC magnetron sputtered silver coatings has recently been proposed via KATS, Korea and a NP ballot is being progressed within a technical committee "ISO/TC107-metallic and other inorganic coating".

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.1
• /
• pp.44-48
• /
• 2013

Niobium oxide($Nb_2O_5$) films were deposited on p-type Si wafers at room temperature using in-line pulsed-DC magnetron sputtering system with various frequencies. The different duty ratios were obtained by varying the frequency of pulsed DC power from 100 to 300 kHz at the fixed reverse time of $1.5{\mu}s$. From the thickness of the sputtered $NbO_x$ films, it was possible to obtain much higher deposition rate in case of pulsed-DC sputtering than RF sputtering. However, the similar leakage currents and structural characteristics were obtained from the metal-insulator-semiconductor(MIS) structure fabricated with the $NbO_x$ films and the x-ray photoelectron spectroscopy(XPS) results in spite of the different deposition rates. From the experimental results, the $NbO_x$ films sputtered by pulsed-DC sputtering are expected to be used in the fabrication process instead of RF sputtering.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.14 no.6
• /
• pp.277-280
• /
• 2004

p-ZnO films have been grown on (0001) sapphire substrates by RF-DC magnetron co-sputtering. The p-ZnO single crystalline thin films of the thickness about 120 nm were grown successfully. The dopant (Aluminum) was sputtered simultaneously from Al metal target by DC sputtering during rf-magnetron sputtering of ZnO at the substrate temperatures of $400^{\circ}C$ and $600^{\circ}C$ respectively. The crystallinity and optical properties of as-grown P-ZnO films have been characterized.