• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.4
• /
• pp.83-88
• /
• 2018

The electromigration (EM) tests were performed at $150^{\circ}C$ with $1.5{\times}10^5A/cm^2$ conditions in order to investigate the effect of non-conductive film (NCF) trap on the electrical reliability of Cu/Ni/Sn-Ag microbumps. The EM failure time of Cu/Ni/Sn-Ag microbump with NCF trap was around 8 times shorter than Cu/Ni/Sn-Ag microbump without NCF trap. From systematic analysis on the electrical resistance and failed interfaces, the trapped NCF-induced voids at the Sn-Ag/Ni-Sn intermetallic compound interface lead to faster EM void growth and earlier open failure.

• Journal of Powder Materials
• /
• v.13 no.1 s.54
• /
• pp.18-24
• /
• 2006

The brazing adhesion properties of Ag coated W-Ag electric contact on the Cu substrate have been investigated in therms of microstructure, phase equilibrium and adhesion strength. Precoating of Ag layer ($3{\mu}m$ in thickness) on the $W-40\%Ag$ contact material was done by electro-plating method. Subsequently the brazing treatment was conducted by inserting BCuP-5 filler metal (Ag-Cu-P alloy) layer between Ag coated W-Ag and Cu substrate and annealing at $710^{\circ}C$ in $H_2$ atmosphere. The optimum brazing temperature of $710^{\circ}C$ was semi-empirically calculated on the basis of the Cu atomic diffusion profile in Ag layer of commercial electric contact produced by the same brazing process. As a mechanical test of the electric contact after brazing treatment the adhesion strength between the electric contact and Cu substrate was measured using Instron. The microstructure and phase equilibrium study revealed that the sound interlayer structure was formed by relatively low brazing treatment at $710^{\circ}C$. Thin Ag electro-plated layer precoated on the electric contact ($3{\mu}m$ in thickness) is thought to be enough for high adhesion strength arid sound microstructure in interface layer.

• Composites Research
• /
• v.24 no.3
• /
• pp.17-24
• /
• 2011

The EAM simulation of nanoindentation was performed to investigate misfit dislocation slip in the Ag/Cu. The film layer, whose thickness in the range of 2-5nm, was indented by a spherical indenter with the N$\'{o}$se-Hoover thermostat condition. The simulation shows that the indentation position relative to misfit dislocation (MFD) has the effect on the dislocation, glide up or cross slip, for Ag film layer thickness less than 4 nm. Elastic energy variation during MFDs slip was revealed to be a key factor for the softening of Ag/Cu. The critical film layer thickness was evaluated for each case of Ag/Cu according to the spline extrapolation technique.

• Composites Research
• /
• v.22 no.3
• /
• pp.9-17
• /
• 2009

Nanoindentation behaviours on the films of softer Ag film/harder Cu substrate structure were studied by the molecular dynamics method. As a result, it was shown that the stiffness and hardness of films were strongly dependent on the thickness of films. The stiffness and hardness increased with the thickness of film within a critical range as an inverse Hall-Petch relation. The stiffness and hardness of Cu substrate with Ag film less than 5 nm were observed to be lower than those of bulk silver. In particular, the flower-like dislocation loop was created on the interface by the interaction between dislocation pile-up and misfit dislocation during the indentation of Ag film/Cu substrate with film thickness less than 4 nm, which seemed to be associated with the drop of load in the indentation load versus displacement curve.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.226-226
• /
• 2008

지난 10여년 동안 Sn-3.0Ag-0.5(wt%)Cu 합금은 대표 무연솔더 조성으로 다양한 전자제품의 실장 및 접합에 적용되어 왔으며, 그 신뢰성 역시 충분히 검증된 바 있다. 그러나 최근 Ag 가격의 급격한 상승과 솔더 접합부의 내 충격 신뢰성을 보다 향상시키고자 하는 업계의 동향은 Ag의 함량이 낮은 무연솔더 조성의 적용 확대를 유도하고 있다. 이에 따라 본 연구자들은 저 Ag 함유 무연슬더로 Sn-1.2Ag-0.5Cu-0.4In 조성을 제안한 바 있는데, 이는 Sn-3.0Ag-0.5Cu 조성 이상의 solderability를 가지면서도 그 금속원료 가격이 약 20% 가량 저렴한 특징을 가진다. 또한 열 싸이클링 (cycling) 테스트를 통한 슬더 조인트의 신뢰성을 평가한 결과, Sn-3.0Ag-0.5Cu에 크게 뒤떨어지지 않는 양호한 특성이 관찰되었다. 따라서 본 연구에서는 열 싸이클링 테스트와 더불어 최근 그 중요성이 지속적으로 커지고 있는 내 충격 신뢰성 평가 시험을 실시하여 개발된 4원계 무연솔더 조성의 기계적 특성을 기존 무연솔더 조성과 비교, 분석해 보았다. 각 솔더 조성은 솔더 볼 형태로 제조되어 CSP(Chip Scale Package) 상에 범핑 (bumping)되었으며, CSP를 PCB(Printed Circuit Board) 상에 실장하는 공정에서도 Sn-3.0Ag-0.5Cu 및 Sn-1.2Ag-0.5Cu-0.4In의 두 종류의 솔더 페이스트가 사용되었다. 본 연구에서의 내 충격 신뢰성 시험에는 자체 제작한 rod drop 시험기를 사용하였는데, 고정된 CSP 실장 board의 후면 부위를 일정한 높이에서 추를 반복적으로 자유 낙하시켜 급격한 충격을 주는 방식으로 실험을 실시하였다. 이 때 추의 무게는 30g, 낙하 높이는 10cm 였으며, 추의 낙하 시 측정된 board 의 휨 변위량은 약 0.7mm로 측정되었다. 사용된 CSP와 PCB 는 모두 daisy chain 방식으로 연결되어 있기 때문에 저항측정기를 사용한 간단한 실시간 저항 측정 방법으로 시험 이력에 따른 파단부의 발생 시점과 대략의 위치를 손쉽게 확인할 수 있었다. 솔더 조인트의 파단 기준 저항값으로 $1000\Omega$을 설정하였으며. 각 조건 당 5 개 이상의 샘플에 대해 평가를 실시한 후 그 평균값을 조사하였다. 시험 결과 제안된 Sn-1.2Ag-0.5Cu-0.4In 조성은 대표적인 저 Ag 함유 조성인 Sn-1.0Ag-0.5Cu에 비해서는 떨어지는 내 충격 신뢰성을 나타내었지만, 우수한 연성에 기인하여 Sn-3.0Ag-0.5Cu 조성에 비해서는 약 2 배 이상 우수한 신뢰성이 관찰되었다. 또한 CSP의 실장 시 Sn-3.0Ag-0.5Cu보다 Sn-1.2Ag-0.5Cu-0.4In 조성 솔더 페이스트를 적용한 경우에서 보다 우수한 내 충격 신뢰성을 나타내어 기본적으로 개발된 Sn-1.2Ag-0.5Cu-0.4In 솔더 페이스트가 Sn-3.0Ag-0.5Cu 조성의 기존 솔더 페이스트 보다 내 충격 신뢰성이 우수함을 검증할 수 있었다. 각 조성의 솔더 조인트를 $150^{\circ}C$ 에서 500시간 aging한 후 실시한 내 충격 신뢰성 평가에서는 모든 조성에서 그 신뢰성이 급감하는 경항을 나타내었으나, Sn-1.2Ag-0.5Cu-0.4In가 Sn-l.0Ag-0.5Cu보다도 그 상대적인 신뢰성이 우수한 것으로 관찰되었다. 이와 같이 aging 후 실시하는 충격시험은 가장 실제적인 상황과 유사한 조건이므로 상기의 실험 결과는 매우 고무적이었으며, 이에 대한 보다 면밀한 분석이 요청되었다. 마지막으로 파면 및 미세조직 관찰을 통하여 각 조성에서의 충격 파단 특성을 비교, 분석해 보았다.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.2
• /
• pp.59-64
• /
• 2022

Effects of film stack structure and peeling rate on the peel strength of screen-printed (SP) Ag/polyimide (PI) systems were investigated by a 90° peel test. When PI film was peeled at PI/SP-Ag and PI/SP-Ag/electroplated (EP) Cu structures, the peel strength was nearly constant regardless of the peeling rate. When EP Cu was peeled at EP Cu/SP-Ag/PI structure, the peel strength continuously increased as peeling rate increased. Considering uniaxial tensile test results of EP Cu/SP-Ag film with respect to loading rate, the increase of 90° plastic bending energy and peel strength was attributed to increased flow stress and toughness. On the other hand, viscoelastic PI film showed little variation of flow stress and toughness with respect to loading rate, which was assumed to result in nearly constant 90° plastic bending energy and peel strength.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.6
• /
• pp.549-554
• /
• 2003

The purpose of this paper is to investigate the solder properties by the change of P mass percentage. Tension test, wetting balance test, spread test, and analysis of intermetallic compound after isothermal aging of Sn-2.5Ag-0.7Cu-0.005P, Sn-2.5Ag-0.7Cu-0.01P, Sn-2.5Ag-0.7Cu-0.02P, Sn-0.7Cu-0.005P were performed. Adding P in the solder alloys resulted in improvement of tensile strength, reduction of intermetallic compound growth, reduction of oxidization in fusible solders under wave soldering. After comparing solder alloy containing P with tin-lead eutectic solder alloy, P contained solders alloys showed much better solder properties than eutectic solder alloy. Furthermore, this solder alloy presented remarkable properties than any other lead-free solder alloy.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2008.10a
• /
• pp.313-316
• /
• 2008

This work sought to examine the suitability of twin roll strip casting for Ag-27%Cu-25%Zn-3%Sn brazing alloy (BAg-7A) and to investigate the mechanical properties and microstructure of the strip. The effect of aging heat treatment on the properties was also studied,. This new manufacturing process has applications in the production of the brazing alloy. XRD and microstructural analysis of the Ag-27%Cu-25%Zn-3%Sn strip represented eutectic microstructure of a Cu-rich phase and a Ag-rich matrix regardless of heat treatment. The results of mechanical tests showed tensile strength of 470MPa, a significant enhancement, and an 18% elongation of the twin roll casted strip, due mainly to the solid solution strengthening of Zn atoms (${\sim}20%$) in the Cu-rich phases. Tensile results showed gradually decreasing strengths and increasing elongation with aging heat treatment. Microstructural evolution and fractography were also investigated and related to the mechanical properties.

• Proceedings of the KWS Conference
• /
• 2006.05a
• /
• pp.218-220
• /
• 2006

Sn-3.0Ag-0.5Cu solder is widely used as micro-joining materials of flip chip package(FCP) because of the fact that it causes less dissolution and has good thermal fatigue property. However, compared with ternary electroplating in the manufacturing process, binary electroplating is still used in industrial field because of easy to make plating solution and composition control. The objective of this research is to fabricate Sn-3.0Ag-0.5Cu solder bumping having accurate composition. The ternary Sn-3.0Ag-0.5Cu solder bumping could be made on a Cu pad by sequent binary electroplating of Sn-Cu and Sn-Ag. Composition of the solder was estimated by EDS and ICP-OES. The thickness of the bump was measured using SEM and the microstructure of intermetallic-compounds(IMCs) was observed by SEM and EDS. From the results, contents of Ag and CU found to be at $2.7{\pm}0.3wt%\;and\;0.4{\pm}0.1wt%$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.640-644
• /
• 2000

The microstructure, wettability, shear strength and aging effect of Sn-3.5Ag/Cu and Alloy42 lead-frame solder joints were measured for comparison. In the case of Sn-3.5Ag/Cu, Ag$_3$Sn and Cu$\sub$6/Sn$\sub$5/ phases in the matrix Sn and 1∼2$\mu\textrm{m}$ thick Cu$\sub$6/Sn$\sub$5/ Phase at the interface of solder/lead-frame were formed. In the case of Sn-3.5AAg/A11oy42, only Ag$_3$Sn Phase of low density in the matrix Sn and 0.5∼1.5$\mu\textrm{m}$ thick FeSn$_2$phase at the interface of solder/lead-frame were formed. Comparing to Cu, Alloy42 shear strength of Alloy 42 solder joints was smaller than that of Cu and all declined after aging. After aging at 180$^{\circ}C$ for 1 week, η-Cu$\sub$6/Sn$\sub$5/ layer was formed on Cu lead-frame, while AgSn$_3$ phase in the matrix and thickened FeSn$_2$at the interface were formed on Alloy42 lead-frame.