• Restorative Dentistry and Endodontics
• /
• v.16 no.2
• /
• pp.18-32
• /
• 1991

The purpose of this study was to observe characteristic properties of amalgam through the polarization curves and SEM images from 4 type amalgams (Amalcap, Shofu spherical. Dispersalloy and Tytin) with 3 different surface finish procedures (polishing, burnishing and carving) by using the potentiostats (EG & GPARC) and SEM (Jeol JSM-35). After each amalgam alloy and Hg was triturated as the direction of the manufacturer by means of mechanical amalgamator (Samki), the triturated mass was inserted into the cylndrical metal mold which was 12 mm in diameter and 10 mm in height and was pressed with $100kg/cm^2$. 4 specimens of each type amalgam were burnished with egg burnisher and another 4 specimens of each type amalgam were carved with Hollenback carver. Above 8 specimens and remaining untreated 4 specimens were stored at room temperature for about 7 days. Untreated 4 specimens of each type amalgam were polished with abrasive papers (Deer) from #400 to #1200 and finally on the polishing cloth with $0.5{\mu}m$ and $0.06{\mu}m$ $Al_2O_3 $ powder suspended water. Anodic polarization measurements was employed to compare the corrosion behaviours of the amalgams in 0.9% saline solution at $37^{\circ}C$. The open circuit potential was determined after 30 minutes immersion of specimen in electrolyte. The scan rate was 1 mV/sec and the surface area of amalgam exposed to the solution was $0.64cm^2$ for each specimen. All the potentials reported are with respect to a saturated calomel electrode (SCE). SEM images of each specimen were taken after + 800 mV (SCE) polarization. The results were as follows: 1. The corrosion potential of high copper amalgam was more anodic than that of low copper amalgam. 2. The polished amalgam were more resistant to corrosion than any other burnished and carved amalgam. 3. In the case of polishing, current density of high copper amalgam was lower than that of low copper amalgam.

• Tribology and Lubricants
• /
• v.31 no.3
• /
• pp.79-85
• /
• 2015

RC delay is a critical issue for achieving high performance of ULSI devices. In order to minimize the RC delay time, we uses the CMP process to introduce high-conductivity Cu and low-k materials on the damascene. The low-k materials are generally soft and fragile, resulting in structure collapse during the conventional high-pressure CMP process. One troubleshooting method is electrochemical mechanical polishing (ECMP) which has the advantages of high removal rate, and low polishing pressure, resulting in a well-polished surface because of high removal rate, low polishing pressure, and well-polished surface, due to the electrochemical acceleration of the copper dissolution. This study analyzes an electrochemical state (active, passive, transpassive state) on a potentiodynamic curve using a three-electrode cell consisting of a working electrode (WE), counter electrode (CE), and reference electrode (RE) in a potentiostat to verify an electrochemical removal mechanism. This study also tries to find optimum conditions for ECMP through experimentation. Furthermore, during the low-pressure ECMP process, we investigate the effect of current density on surface roughness and removal rate through anodic oxidation, dissolution, and reaction with a chelating agent. In addition, according to the Faraday’s law, as the current density increases, the amount of oxidized and dissolved copper increases. Finally, we confirm that the surface roughness improves with polishing time, and the current decreases in this process.

• Journal of Electrochemical Science and Technology
• /
• v.11 no.4
• /
• pp.346-351
• /
• 2020

The removal characteristics of copper (Cu) from electrochemical surface by voltage-activated reaction were reviewed to assess the applicability of electrochemical-mechanical polishing (ECMP) process in three types of electrolytes, such as HNO₃, KNO₃ and NaNO₃. Electrochemical surface conditions such as active, passive, transient and trans-passive states were monitored from its current-voltage (I-V) characteristic curves obtained by linear sweep voltammetry (LSV) method. In addition, the oxidation and reduction process of the Cu surface by repetitive input of positive and negative voltages were evaluated from the I-V curve obtained using the cyclic voltammetry (CV) method. Finally, the X-ray diffraction (XRD) patterns and energy dispersive spectroscopy (EDS) analyses were used to observe the structural surface states of a Cu electrode. The electrochemical analyses proposed in this study will help to accurately control the material removal rate (MRR) from the actual ECMP process because they are a good methodology for predicting optimal electrochemical process parameters such as current density, operating voltage, and operating time before performing the ECMP process.

• Transactions on Electrical and Electronic Materials
• /
• v.5 no.6
• /
• pp.233-236
• /
• 2004

Copper metallization has been used in high-speed logic ULSI devices instead of the conventional aluminum alloy metallization. One of the key issues in copper CMP is the development of slurries that can provide high removal rates. In this study, the effects of slurry chemicals and pH for slurry dispersion stability on Cu CMP process characteristics have been performed. The experiments of copper slurries containing each different alumina and colloidal silica particles were evaluated for their selectivity of copper to TaN and $SiO_{2}$ films. Furthermore, the stability of copper slurries and pH are important parameters in many industries due to problems that can arise as a result of particle settling. So, it was also observed about several variables with various pH.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.434-437
• /
• 2005

Chemical Mechanical Polishing (CMP) has become an essential step in the overall semiconductor wafer fabrication technology. In general, CMP is a surface planarization method in which a silicon wafer is rotated against a polishing pad in the presence of slurry under pressure. The polishing pad, generally a polyurethane-based material, consists of polymeric foam cell walls, which aid in removal of the reaction products at the wafer interface. It has been found that the material removal rate of any polishing pad decreases due to the so-called 'pad glazing' after several wafer lots have been processed. Therefore, the pad restoration and conditioning has become essential in CMP processes to keep the urethane polishing pad at the proper friction coefficient and to allow effective slurry transport to the wafer surface. Diamond pad conditioner employs a single layer of brazed bonded diamond crystals. Due to the corrosive nature of the polishing slurry required in low pH metal CMP such as copper, it is essential to minimize the possibility of chemical interaction between very low pH slurry (pH <2) and the bond alloy. In this paper, we report an exceptional protective coated conditioner for in-situ pad conditioning in low pH Cu CMP process. The protective Cr-coated conditioner has been tested in slurry with pH levels as low as 1.5 without bond degradation.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.10a
• /
• pp.77-77
• /
• 2003

• Applied Microscopy
• /
• v.34 no.2
• /
• pp.95-102
• /
• 2004

The TEM samples prepared by ion milling have the advantage that thin area can be obtained from almost any materials. However, it has the disadvantage that the amount of thin area can often be quite limited. For the cross-sectioned samples and grossly heterogeneous materials, the thickness of less than $0.1{\mu}m$ can be achieved by mechanical grinding and polishing (tripod polisher) and then the TEM samples may be ion-milled for final thinning or cleaning. These approaches were described in this paper. Examples of TEM observations were taken from cross-section samples of thin films on silicon and sapphire, from diffusion layers between $Mo_5Si_3\;and\;Mo_2B$, and from rapidly solidified 304 stainless steel powders embedded in electroplated copper.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.2
• /
• pp.94-103
• /
• 2007

The transition of interconnection metal from aluminum alloy to copper has been introduced to meet the requirements of high speed, ultra-large scale integration, and high reliability of the semiconductor device. Since copper, which has low electrical resistivity and high resistance to degradation, has different electrical and material characteristics compared to aluminum alloy, new related materials and processes are needed to successfully fabricate the copper interconnection. In this review, some important factors of multilevel copper damascene process have been surveyed such as diffusion barrier, seed layer, organic additives for bottom-up electro/electroless deposition, chemical mechanical polishing, and capping layer to introduce the related issues and recent research trends on them.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.7
• /
• pp.569-573
• /
• 2012

We investigated the speed change of the diamond spherical abrasive during the substrate surface polishing under the pad compression by using classical molecular dynamics modeling. We performed three-dimensional molecular dynamics simulations using the Morse potential functions for the copper substrate and the Tersoff potential function for the diamond abrasive. As the compressive pressure increased, the indented depth of the diamond abrasive increased and then, the speed of the diamond abrasive along the direction of the pad moving was decreased. Molecular simulation result such as the abrasive speed decreasing due to the pad pressure increasing gave important information for the chemical mechanical polishing including the mechanical removal rate with both the pad speed and the pad compressive pressure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.537-537
• /
• 2008

Copper (Cu) has been widely used for interconnection structure in intergrated circuits because of its properties such as a low resistance and high resistance to electromigration compared with aluminuim. Damascene processing for the interconnection structure utilizes 2-steps chemical mechanical polishing(CMP). After polishing, the removal of abrasive particles on the surfaces becomes as important as the polishing process. In the paper, buffing process for the removal of colloidal silica from polished Cu wafer was proposed and demonstrated.