• Journal of the Korean Wood Science and Technology
• /
• 제22권3호
• /
• pp.17-25
• /
• 1994

This study was carried out to compare the properties of Com-Ply Boards with those of OSBs. These two kinds of boards were made of same flakes. Com-Ply Boards were covered with three different thickness veneers, such as 4mm, 3mm, and 2.5mm. All manufactured Com-Ply Boards and OSBs were 12mm thick. In MOR, all Com-Ply Boards were higher than OSB, and especially 3mm-veneer and 2.5mm-veneer Com-Ply Board were highest. But OSB showed 420kg/$cm^2$. 3mm-veneer Com-Ply Board showed the highest internal bonding 7.0kg/$cm^2$ and then 2.5mm-veneer showed 6.8kg/$cm^2$, and OSB showed 6.6kg/$cm^2$. Screw holding strength showed the high value 23.9kg/$cm^2$, 25.5kg/$cm^2$, and 29.3kg/$cm^2$ respectively at 3mm-veneer, 2.5mm-veneer Com-Ply Board and OSB. Thickness swelling of Com-Ply Boards was lower than that of OSB, but Water absorption of OSB was lower. Finally it was very encouraging that all properties of OSB without veneer, whose cost is higher than flake and whose properties is better, were not worse than those of Com-Ply Board with veneer. It seems That more researches on OSB will be required.

• 한국산림과학회지
• /
• 제96권1호
• /
• pp.54-57
• /
• 2007

요소수지접착제를 합판제조용 접착제와 유사하게 실험실에서 합성하고, 합성한 요소수지접착제를 증량제, 충전제, 산경화촉매제와 혼합하였다. 요소수지접착제 혼합물의 고형분량은 56.1%이고, 물은 43.9%였다. 국산재와 요소수지접착제 혼합물로 5종류의 Com-Ply를 제조하고, KS F 3101 보통합판의 인장 전단 접착력 시험 및 KS F 3104 파티클보드의 휨파괴계수 시험을 수행했다. 성능 평가된 결과는 제조된 5종류의 Com-Ply에서 모두 적합한 결과를 보여줬다. 이런 결과는 본 연구에서 사용된 요소수지접착제 혼합물이 국산재 Com-Ply제조에 적합하다는 것이다.

• Journal of the Korean Wood Science and Technology
• /
• 제20권3호
• /
• pp.29-37
• /
• 1992

This research was carried out to investigate the effects of cyclic humidification on the dimensional stability of particleboard manufactured according the three specific gravity levels and com-ply fabricated with a core of particleboard and veneer or plywood as the face and back materials. Both the particleboard and com-ply were subjected to four cycles of 50-90-50% relative humidity. The results are summarized as follows: Particleboard and com-ply followed a clear pattern of increasing dimensions and weight on the adsorption cycle and decreasing dimensions and weight on the humidification cycle. After the fourth cycle, the dimensions and weight of both particleboard and com-ply were greater than those originally measured. The greater part of increase in occurred during the first humidification cycle. The specific gravity of particleboard has a significant effect thickness and volume change. The dimensional stability of com-ply was better than that of particleboard. In addition, the dimensional stability of com-ply bonded with plywood was better than that of com-ply bonded with veneer.

• Journal of the Korean Wood Science and Technology
• /
• 제48권6호
• /
• pp.907-916
• /
• 2020

This research was conducted to investigate the linear expansion and resistance properties of a composite board (com-ply). This board was made of medium-density fiberboard (MDF) laminated using avocado (Persea americana), mahogany (Swietenia mahogani), and pine (Pinus merkusii) veneers. These three types of veneers were laminated on both surfaces of the MDF using adhesives, namely, epoxy and isocyanate. Glue (250 g·m^-2) was spread on the surface, followed by cold press for 3 h with an applied pressure of 15 kg·cm^-2. The research result revealed that com-ply exhibited an increased dimensional stability compared with MDF, indicated by reduction in water absorption, thickness swelling, and linear expansion. The com-ply made of the pine veneer and isocyanate adhesive exhibited high density, water absorption, thickness swelling, and screw withdrawal load. The com-ply that exhibited the strongest resistance to drywood termite attacks was the one made of the mahogany veneer and isocyanate adhesive. Moreover, the com-ply that exhibited the biggest weight loss (3.6 %) was made of the pine veneer and epoxy adhesive. The results of this research may facilitate in manufacturing com-ply using the selected veneer and adhesive without the application of hot press.

• Journal of the Korean Wood Science and Technology
• /
• 제47권2호
• /
• pp.239-248
• /
• 2019

This research presents an improvement of the physical and mechanical properties of composite board (com-ply) made of Oriented Strand Board (OSB) coated with wood veneer of Pine (Pinus merkusii), Avocado (Persea Americana) and Mahogany (Swietenia mahogany). 1.5 mm thick veneers of those three wood types were adhered to the surface of OSB using two adhesive types: epoxy and isocyanate. The adhesive with the glue spread of $250g\;m^{-2}$ applied using single glue line was spread and then cold pressed with the pressure of $15kg\;cm^{-2}$ for 3 hours. The research result showed an improving dimension stability of com-ply, but not found on all parameters of physical property test. The moisture content seemed to be influenced by the com-ply type, yet not related to its thickness swelling, water absorption and linear expansion. The exception took place in the parallel linear expansion when immersed for 2 hours. The highest to the lowest increases of MOE and MOR were consecutively found on OSB coated with wood veneer of Pine, Mahogany and Avocado. However, the increases were statistically insignificant. The highest increasing screw hold power was found at the com-ply type AE (avocado veneer and epoxy adhesive) that was by 28%.

• Journal of the Korean Wood Science and Technology
• /
• 제41권1호
• /
• pp.33-41
• /
• 2013

본 연구에서는 최근 파티클보드(Particle Board ; 이하 PB)의 원재료로 재활용되고 있는 목재 폐기물 중 합판공장의 부산물을 원재료로 사용하고 비포름알데히드계 EMDI접착제의 적용을 통한 제조조건을 최적화하여 재활용 원재료의 효과적인 활용을 통한 고(高)내수성 PB의 개발과 그에 대한 물리 기계적 특성을 규명하고자 하였다. 그 결과, (1) 베니어 적층 복합보드에 EMDI수지를 사용하였을 경우 휨 강도가 섬유방향 57.7 $N/mm^2$, 섬유 직각방향 25.1 $N/mm^2$의 강도를 나타내었다. (2) 두께팽윤율과 수분흡수율은 U형, M형, P형 실험에서 EMDI수지가 UF수지보다 높은 수준의 내수성을 나타내었다. (3) 잔존 포름알데히드의 양을 줄이고자 실행하였던 72시간 수침전처리는 파티클보드의 포름알데히드 방산량을 증가시키는 결과를 초래하였다.

• 펄프종이기술
• /
• 제37권4호통권112호
• /
• pp.38-43
• /
• 2005

Natural Com Starch(NCS) spray system has been widely used In multiply board mill for the better bonding strength between board layers. However the unsuitable NCS spray system could lead to a drop in plybond efficiency of multiply board. It could also result in the accumulation of unretained-starch in the white water system, which could not only rise in BOD and COD level but also reduce the effects of rosin-alum sizing system and other additives. In this study, the simple and rapid method by UV-spectroscopy for measuring the starch contents in the white water was proposed, and the quantitative analysis for dissolved starch content in white water was carried out in two kinds of board production process. It could be confirmed that about 150 ppm of oxidized starch was retained in white water dewatered from undertop ply of multiply board process, and about 470 ppm of natural starch was dissolved in white water originated from unsuitable spraying system in the multiply board production lines for cup base paper.