• Journal of the Korean Ceramic Society
• /
• v.32 no.2
• /
• pp.257-269
• /
• 1995

The TiC-Co/Al reaction-sintered products were prepared by the infiltration of various Co/Al metal mixture into the preform, and their microstructure, phases, and mechanical properties were investigated. With increasing the atomic ratio of Co/Al, tiC grain shape was changed from spherical to platelet particles, and the grain size increased. The crystalline phases found in the liquid matrix formed by the infiltration of Co/Al metal mixture were determined to be Al5Co2 and AlCo by EDS and XRD, and the two crystalline phases were located dominantly between TiC grains, when the Co/Al atomic ratio was lower than an unity. There was a tendency that the density, bending strength and fracture toughness increase with Co/Al atomic ratio until the infiltrated metal was 100% Co. The maximum value was achieved by the composition containing 100% Co infiltrated metal. The Vickers hardness decreased as Co/Al atomic ratio increased.

• Journal of the Korean Society for Heat Treatment
• /
• v.21 no.1
• /
• pp.3-9
• /
• 2008

Al-Co-N thin films, Al-Co-N/Al-N and Al-Co-N/Al-Co multilayers containing various amounts of Co content were deposited by using a two-facing targets type dc sputtering (TFTS) system. The films were also annealed successively and isothermally at different annealing temperatures. Irrespective of Co content and preparation methods, all the as-deposited films were observed non-magnetized. It was found that annealing conditions can control the magnetic and electrical properties as well as the microstructure of the films.

• Clean Technology
• /
• v.21 no.1
• /
• pp.68-75
• /
• 2015

In this study, we investigated the structure and properties of a highly heat conductive metal-ceramic core-shell CoAl₂O₄@Al micro-composite for heterogeneous catalysts support. The CoAl₂O₄@Al was prepared by hydrothermal surface oxidation of Al metal powder, which resulted in the structure with a high heat conductive Al metal core encapsulated by a high surface area CoAl₂O₄ shell. For comparison, CoAl₂O₄ was also prepared by co-precipitation method and also utilized for a catalyst support. Rh catalysts supported on CoAl₂O₄@Al and CoAl₂O₄ were prepared by incipient wetness impregnation and characterized by N₂ adsorption, X-ray diffraction (XRD), scanning electron microscopy (SEM), CO chemisorption, and temperature-programmed reduction (TPR). The properties of catalysts were investigated for glycerol steam reforming reaction for hydrogen production at 550 ℃. Rh/CoAl₂O₄@Al exhibited about 2.8 times higher glycerol conversion turnover frequency (TOF) than Rh/CoAl₂O₄ due to facilitated heat transport through the core-shell structure. The CoAl₂O₄@Al and CoAl₂O₄ also showed some catalytic activities due to a partial reduction of Co on the support, and a higher catalytic activity was also found on the CoAl₂O₄@Al core-shell than CoAl₂O₄. These catalysts, however, displayed deactivation on the reaction stream due to carbon deposition on the catalysts surface.

• Applied Microscopy
• /
• v.30 no.3
• /
• pp.249-254
• /
• 2000

We investigated the microstructure, electrical property, and magnetic property of Co/Al multilayer after annealing treatment. CoAl was formed during depositing Co/Al multilayer due to the interfacial reaction. After annealing treatment, $Co_2Si$ was formed at the Co/Si interface. The sheet resistance of Co 2 nm/Al 2 nm multilayer have the lowest value and the Rs of multilayer decreased with the increase of annealing temperature due to the formation of $Co_2Si$ phase. The Ms of 2 nm Co/2 nm Al multilayer have the lowest value and the Ms of multilayer increased with the increase of film thickness.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.2
• /
• pp.79-90
• /
• 1996

Transmission electron microscopy(TEM) investigation on the phase decomposition of B2-ordered (Ni,Co)Al supersaturated with Ni and Co has revealed the precipitation of $(Ni,Co)_2Al$ which has not been expected from the reported equilibrium phase diagram. The $(Ni,Co)_2Al$ phase has a hexagonal struture and takes a rod-like shape with the long axis of the rod parallel to the <111> directions of the B2 matrix. By aging at temperatures below 873 K, a long period Superlattice Structure appears in the hexagonal $(Ni,Co)_2Al$ Phase. The orientation relationship between the $(Ni,Co)_2Al$ Precipitates and the B2-(Ni,Co)Al matrix is found to be$(0001)_p$ // $(111)_{B2}$ and $[\bar{1}2\bar{1}0]_P$ // $[\bar{1}10]_{B2}$, Where the suffix p and B2 denote the $(Ni,Co)_2Al$ precipitate and the B2-(Ni,Co)Al matrix, respectively. (Ni,Co)Al hardens appreciably by the fine precipitation of the $(Ni,Co)_2Al$ phase. Energy dispersive spectroscopy was used to analyze the compositions of each phase formed in B2-(Ni,Co)Al.

• Journal of Electrochemical Science and Technology
• /
• v.12 no.2
• /
• pp.230-236
• /
• 2021

Ionic conduction mechanism of Mg-Al layered double hydroxides (LDHs) intercalated with CO₃^2- (Mg-Al CO₃^2- LDH) was studied. The electromotive force for the water vapor concentration cell using Mg-Al CO₃^2- LDH as electrolyte showed water vapor partial pressure dependence and obeyed the Nernst equation, indicating that the hydroxide ion transport number of Mg-Al CO₃^2- LDH is almost unity. The ionic conductivity of Mg(OH)₂, MgCO₃ and Al₂(CO₃)₃ was also examined. Only Al₂(CO₃)₃ showed high hydroxide ion conductivity of the order of 10^-4 S cm^-1 under 80% relative humidity, suggesting that Al₂(CO₃)₃ is an ion conducting material and related to the generation of carrier by interaction with water. To discuss the ionic conduction mechanism, Mg-Al CO₃^2- LDH having deuterium water as interlayer water (Mg-Al CO₃^2- LDH(D₂O)) was prepared. After the adsorbed water molecules on the surface of Mg-Al CO₃^2- LDH(D₂O) were removed by drying, DC polarization test for dried Mg-Al CO₃^2- LDH(D₂O) was examined. The absorbance attributed to O-D-stretching band for Mg-Al CO₃^2- LDH(D₂O) powder at around the positively charged electrode is larger than that before polarization, indicating that the interlayer in Mg-Al CO₃^2- LDH is a hydroxide ion conduction channel.

• Applied Chemistry for Engineering
• /
• v.26 no.2
• /
• pp.138-144
• /
• 2015

Effects of Co/Al and Si/Al molar ratios of cobalt incorporated SAPO-34 catalysts (CoAPSO-34) on their catalytic lifetime were investigated in dimethyl to olefin (DTO) reaction. The property of CoAPSO-34 catalysts was characterized using XRD, SEM, $^{29}Si$ MAS NMR, and $NH_3$-TPD techniques. First, the lifetime of CoAPSO-34 prepared by varying Co/Al molar ratios was improved than that of using the SAPO-34 catalyst, and the optimal Co/Al molar ratio was 0.0025. The total acid site amounts increased from 0.432 to 1.111 mmol/g with increasing Si/Al molar ratios from 0.05 to 0.20 while fixing a Co/Al molar ratio of 0.0025. However, the catalysts with too high acid site amounts were deactivated rapidly with blockages of the pores due to the fast accumulation of polycyclic aromatic hydrocarbons in the cage. Therefore, the CoAPSO-34 catalyst with a proper Si/Al molar ratio of 0.10 was the most superior in terms of the lifetime, which was improved by about 87% as compared with that of the SAPO-34 catalyst.

• Clean Technology
• /
• v.17 no.2
• /
• pp.166-174
• /
• 2011

The xAl-yCe oxide catalysts with different mol ratios of Al/(Al+Ce) were prepared by a co-precipitation method and Pt supported on xAl-yCe oxide catalysts were synthesized by an incipient wetness impregnation method. The catalysts were characterized by X-ray Diffraction (XRD), $N_2$ sorption, and $H_2$/CO-temperature programmed reduction ($H_2$/CO-TPR) to correlate with catalytic activities in co oxidation. Among the catalysts studied here, Pt/1Al-9Ce oxide catalyst showed the highest activity in dry and wet reaction conditions and the catalytic activity showed a typical volcano-shape curve with respect to Al/(Al+Ce) mol ratio. When the presence of 5% water vapor in the feed, the temperature of $T_{50%}$ was shifted ca. $30^{\circ}C$ to lower temperature region than that in dry condition. From CO-TPR, the desorption peak of $CO_2$ on Pt/1Al-9Ce oxide catalyst showed the highest value and well correlated the catalytic performance. It indicates that the Pt/1Al-9Ce oxide catalyst has a large amount of active sites which can be adsorbed by co and easy to supplies the needed oxygen. In addition, the amount of pentacoordinated $Al^{3+}$ sites obtained through $^{27}Al$ NMR analysis is well correlated the catalytic performance.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.4
• /
• pp.154-159
• /
• 2001

(Li,Al)$MnO_2(OH)_2$:Co compound was synthesized by hydrothermal method. $MnO_2$, LiOH.$H_2$O, $Co_3O_4$ and $Al(OH)_3$ were used as starting materials and the optimum conditions for synthesis of monolithic (Li,Al)$MnO_2(OH)_2$:Co compound were as follows : reaction temperature; $200^{\circ}C$, reaction time; 3 days, hydrothermal solvent; 3M-KOH solution, reaction apparatus; seesaw type, atomic ratio of Li:Al:Mn;Co = 1:2.1:2.5~2:0.5~1. Monolithic(Li,Al)$MnO_2(HO)_2$:Co compound synthesized in this work had a god crystallinity and excellent color forming effect as a blue pigment compatible with natural mineral. The particles of the synthesized (Li,Al)$MnO_2(OH)_2$:Co compound have hexagonal plate shape with the size of 0.5~1 $\mu\textrm{m}$.

• Journal of the Korean Vacuum Society
• /
• v.3 no.2
• /
• pp.227-233
• /
• 1994

CuAlGeSe4 및 CuAlGeSe4 ; Co2+ 결정을 고순도의 성분원소로부터 합성하고 서냉법으로 결정을 성장시켰다. 이들결정은 chalcopyrite 결정구조를 갖고 있으며 직접전이형 energy gap 구조를 갖고 286K에서 energy gap은 CuAlGeSe4 결정의 경우는 2.394eV이며 CuAlGeSe4 ; Co2+ 결정의 경우는 2.302 eV로 주어졌다. CuAlGeSe4 : Co2+ 결정에서 cobalt에 의한 불순물 광흡수 peak들은 12243, 7002, 3890 cm-1에서 나타났으며 이 peak들은 CuAlGeSe4 : Co2+ 결정의 Td symmetry site에 위치한 Co2+ ion의 energy 준위사이의 전자전이에 의한 optical absorption임을 규명했다.