• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.05a
• /
• pp.27-28
• /
• 2018

Deterioration of reinforced concrete structures due to salt corrosion is a phenomenon that can be easily seen, and the main reason for deterioration is chloride ion. Therefore, researches are actively conducted to control chlorine ion penetration worldwide. The purpose of this study is to evaluate the chloride ion fixation capacity of Portland cement paste containing Hydrotalcite. For this purpose, cement paste containing 0%, 2.5%, and 5% of Hydrotalcite was sealed and cured for 28 days, and the cured cement paste was crushed. Chloride ion solution was prepared at a concentration of 0.5M using NaCl, and the powdered cement paste was reacted for a specific time in aqueous chloride ion solution. After the reaction, the concentration of the chloride ion aqueous solution was measured using a silver nitrate potentiometric titrator, and the reacted cement paste was analyzed using XRD and FT-IR.

• Journal of the Korean Ceramic Society
• /
• v.44 no.11
• /
• pp.633-638
• /
• 2007

The setting time of alkali activated slag cement tends to be much faster than ordinary Portland cement, and its compressive strength had been higher from the 1 day but became lower than that of the cement on the 28 days. According to the results of the surface observation, weight loss, compressed strength, and erosion depth tests on the sulphuric acid solution. It has been drawn that alkali activated slag cement has a higher sulphate resistance than ordinary Portland cement, and in particular, the alkali activated slag cement added 5 wt% alumina cement has little deterioration on the sulphuric acid solution. The reason why the alkali activated slag cement has higher sulphate resistance than other hardened cement pastes is that it has no $Ca(OH)_2$ reactive to sulphate ion, and there is little $CaSO_4{\cdot}2H_2O$ production causing volume expansion, unlike other pastes. And it is supposed that $Al(OH)_3$ hydrates with high sulphate resistance, which is produced by adding the alumina cement increases the sulfate resistance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.103-111
• /
• 2012

One of the basic physical properties of the hardened cement paste, the rigidity, is deteriorated during concrete matrix forming, depending on the replacement rate of the crushed stone powder, and due to drying shrinkage. Therefore, the concrete containing crushed stone powder has been limitedly used as non-structural construction material. To improve these disadvantages, a hydrothermal reaction employing method can be considered. High-temperature and high-pressure water is involved in the hydrothermal reaction in the mixing with specific materials. The rigidity improving mechanism is related to the synthesis of calcium silicate. The calcium silicate is produced through reaction between calcium compounds and the silicic acid. Various kinds of calcium silicate can be produced depending on the CaO/$SiO_2$ mole ratio, the temperature of the hydrothermal synthesis, the pressure, and the reaction time. The product of the synthesis mechanism, tobermorite crystal, plays a pivotal role for the rigidity reinforcement. The crushed stone powder, analyzed in this study, contains 50 to 60% of $SiO_2$ and 10 to 20% $Al_2O_3$. The composite rate is appropriate to create the tobermorite crystal through formation of hardened cement matrix under the hydrothermal synthetic conditions and with the CaO in the cement. Moreover, further reinforcement was promoted using the property of material under the identical density through promoting the formation of tobermorite crystal.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1989.10a
• /
• pp.21-24
• /
• 1989

The effect of superplasticizing agents on the mechanical properties in hardened concrete have been analyzed and investigated under various mix proportions of water cement ratio of 0.40, 0.50, 0.60 and 0.70, Superplasticizing agents of NL-4000, and Rheobuild-716, and addition rate of sp. agents of 0.0, 0.5, 1.0, 1.5 and 2.0 in the practical range. It is the aim of this study to provide the fundamental data on the compressive strength, dynamic and static modulus of elasticity, stress and strain curve of hardened concrete comparing with base concrete and conventional concrete for the practical use and research data accumulation of superplasticized concrete in the side of development of concrete construction technology and management.

• Korean Journal of Agricultural Science
• /
• v.6 no.1
• /
• pp.45-55
• /
• 1979

This study made to find the variation of strengths of briquette ash which were hardened into cement. The briquette ash were mixed with the cement, ((cement (90%)+slaked lime (10%)) and ((cement (80%)+fly ash (20%)) in the ratio of 1:2, 1:3, 1:4, 1:5, 1:7 and 1:9, respectively, and these were compared with the one made of cement plus standard sand in the strengths of compression, tension and bending at the ages of 7 days and 28 days. The results from the study conducted preliminary without studying the economical aspects or duration of the products are summarized as follows: 1. The compressive strengths of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash and (cement+fly ash) to briquette ash were 84%, 90% and 75% at the age of 7 days and 84.9%, 73.5% and 69.8%, respectively of those of Korean Standard values. 2. The compressive strength s of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash and (cement+fly ash) to briquette ash were 69.3%, 75.1% and 41.3% at the age of 7 days and 56.4%, 49%, and 46.5% at the age of 28 days, respectively of the mortar made of standard sand. 3. The tension strengths of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash, and (cement+fly ash) to briquette ash were 64.4%, 47.1% and 35.4% at the age of 7days and 69.6%, 64.8%, and 57.3%, respectively of that of the mort ar produced with standard sand. 4. The bending strengths of mortar made of 1 to 2 ratios of cement to briquette ash, (cement+slaked lime) to briquette ash, and (cement+fly ash) to briquette ash were 46.3%, 65.9% and 39.1% at the age of 7 days and 89.9%, 96.7%, and 85.1%, respectively of that of mortar produced with standard sand. 5. The bending strength of the mortar was lower than that of cement mortar, when the briquette ash were harqened into cement. However, the mortar produced by such method seemed to be used as the secondary products of cement or concrete. The additional usefullness of the hardened biquette ash can be found in contributing toward the solving the various pollution problems, the saving the labor costs needed to clean-up waste materials, and the saving the construction materials.

• Magazine of the Korea Concrete Institute
• /
• v.8 no.4
• /
• pp.161-169
• /
• 1996

Styrene-maleic anhydride copolymers with different composition (1:1SMA. 5:1SMA) were synthesized and further reacted with sulfuric acid to obtain water soluble copolymers (1:1SSMA, 5:1SSM.4). In the flow experiments of cement mortar mixed with copolymers, 5:1SSMA showed higher fluidity than 1:1SSMA. The cement mortar mixed with 1% 5:1SSMA maintained 95% of original flow after 60 min. On the other hand, the compressive strength of the hardened cement mortars containing 0.5% copolymers after 28 days curing was also examined. The compressive strength of hardened cement mortar containing 5:1SSMA was increased up to 41% compared to the plain while 1:1SSMA was increased up to 29%. As the results, the 5:1SSMA used in this study are greatly expected as a new high range water reducers for the concrete.

• Journal of the Korean Society of Safety
• /
• v.16 no.1
• /
• pp.65-72
• /
• 2001

Portland cement concrete is made with coarse aggregate, fine aggregate, portland cement, water and, in some cases, selected chemical admixture such as air-entraining agents, water reducer, superplasticizer, and so on, and mineral admixture such as fly ash, silica fume, slags, etc. Typically, in the concrete, the coarse aggregate and fine aggregate will occupy approximately 80 percent of the total volume of the finished mixture. Therefore, the coarse and fine aggregates affect to the properties of the portland cement concrete. As the deposits of natural sands have slowly been depleted, it has become necessary and economical to produce crushed sand(manufactured fine aggregate). It is reported that crushed sand differs from natural sands in gradation, particle shape and texture, and that the content of micro fines in the crushed sand affect to the quality of the portland cement concrete. Therefore, the purpose of this paper is to investigate the characteristics of fresh and hardened concrete with higher micro fines. This study provides a firm data to apply crushed sand with higher micro fines.

• Magazine of the Korea Concrete Institute
• /
• v.6 no.5
• /
• pp.149-157
• /
• 1994

보통 포틀랜드 시멘트와 수용성 고분자 물질인 hydroxy propyl methyl cellulose(HPMC), 미세골재 및 혼화재료를 사용하여 W/C=0.1이 되도록 물을 첨가하고 twin roll mill로 혼합 성형한 후 60일간 양생하여 고강도 시멘트 경화체를 제조하였다. 이 경화체에 대한 휨강도 및 파괴인성을 검토하였다. SiC 분말 및 백색시멘트를 첨가한 경우 휨강도는 약 100MPa정도, 탄성계수는 80-95GPa의 값을 나타내었다. 실리카흄을 첨가한 경우 휨강도는 80MPa, 탄성계수는 60GPa의 값을 나타내었다.

• Journal of Environmental Science International
• /
• v.18 no.9
• /
• pp.993-1000
• /
• 2009

The development of a new type of soil-cement concrete pavement using volcaniclastic is the main purpose of this study. Various mixture ratios, specimens' penetration resistance, time of setting, slump flow of fleshly mixed concrete, compressive strength and color characteristics of hardened concrete were studied. It was concluded that the optimum weight ratio of cement:volcaniclastic to produce good properties of soil-cement concrete is 1:3 and the use of volcaniclastic as main aggregate can improve the concrete surface color that is warm earth-tone road color. Therefore, commercial development for soil-cement concrete pavement using volcaniclastic is highly promising.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1999.04a
• /
• pp.437-442
• /
• 1999

Corrosion of steel reinforcment is the most significant factor of deterioration in reinforced concrete structures. Chloride ion is considered one of the most common culprits on the corrosion of steels in concrete. This study is effect of cement hydraulic degree on the chloride binding in hardened cement pastes. With increasing the cement hydration, cement products such as CSH and Ca(OH)2 were increased, and the part of added chloride were binded with them. With respect to A type, in first, the additional contents of chloride of 27.08mM/L in pore solution were reduced as 4.3mM/L at 3 days, 4.0mM/L at 7 days, 3.6mM/L at 28 days.