• Journal of the Korean institute of surface engineering
• /
• v.32 no.1
• /
• pp.31-42
• /
• 1999

The effect was investigated that aluminium in the zinc bath has on the coating adhesion of Hot-rolled Galvanized Iron(HGI) manufactured without pickling process. It is thought that the coating adhesion of HGI manufactured without pickling process is good due to the fact that increasing aluminium content in the zinc bath makes zinc and aluminium diffuse to the cracks or pores in the scale formed through the reduction heat treatment, and Fe-Zn-Al compound with good ductility is formed in the scale layer and plays a role of anchor between zinc coating and substrate. It is possible that HGI with the good coating adhesion was produced without pickling treatment in the zinc bath with more that 3wt% of Al content even at the $550^{\circ}C$ of conventional reduction heating temperature. In creasing the temperature of heating section and aluminium content in the zinc bath prevents the Zn-Fe alloy. The corrosion resistance of HGI manufactured without pickling process is excellent because of the mixed reaction of zinc sacrifice and aluminium passivity film.

• Journal of Power System Engineering
• /
• v.5 no.2
• /
• pp.71-78
• /
• 2001

Using sodium hypophosphite as reducing agent, bath composition and plating condition of electroless copper plating on plating rate have been studied. The followings were determined as optimum, bath composition; $CuSO_4\;0.025M,\;NiSO_4\;0.002M,\;NaH_2PO_2\;0.4M$, sodium citrate 0.06M, $H_3BO_3$ 0.6M, thiourea or 2-MBT $0.2mg/{\ell}$, and operation conditions; pH $9{\sim}10$ at bath temperature rage of $60{\sim}70^{\circ}C$. A small amount of nickel ion($Ni^{2+}/Cu^{2+}$=0.002/0.025) to the hypophosphite reduced solution promotes autocatalysis and continuous plating. An additive such as thiourea or 2-MBT of a small amount($0.2mg/{\ell}$) can be used to stabilize the solution without changing plating rate much. The attivation energy between $20^{\circ}C\;and\;70^{\circ}C$ were calculated to be 11.3kcal/mol for deposition weight. Plating reaction had been ceased by the adjustment of pH above 13, temperature higher than $90^{\circ}C\;and\;under\;20^{\circ}C$. Deposited surface became worse in the case of increment of bath temperature above $80^{\circ}C$.

• Proceedings of the KSME Conference
• /
• 2007.05b
• /
• pp.2654-2659
• /
• 2007

Fluid flow and temperature distribution inside a molten zinc bath were investigated by computational fluid dynamics method. Modeling the channel inductor where alternating current of 60Hz was applied, Lorentz force and generated heat were obtained and later supplemented as source terms to momentum and heat equations. The present work validates CFD technique is effectively adopted when the inductor hardware modification or its configuration is considered for the optimum flows.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.4
• /
• pp.137-143
• /
• 2011

The internal stress and magnetic properties (coercivity and squareness) of Ni-Fe nano thin film synthesized by electrodeposition method were studied as a function of acidic chloride bath conditions (composition and temperature) and current density. Fe deposition patterns were different depending on the temperature of the solution, the stress of film decreased with increasing the solution temperature, and the depending on the amount of Fe deposition showed a parabolic shape. The grain size of film was inversely proportional to stress of thin film. The internal stress of thin film and magnetic properties were deeply relevant, and the stress of thin film had a relationship with bath conditions and grain size of the thin film surface.

• Journal of Fashion Business
• /
• v.23 no.3
• /
• pp.23-34
• /
• 2019

The aim of this study is to explore the possibility utilizing Rhododedron brachycarpum as a new natural dye resource. It was dyed in silk fabric according to different dyeing conditions such as dye concentration, dye bath temperature, dyeing time and dye bath pH. The effect of the mordanting conditions were estimated as dyeability and color changes. Additionally, the colorfastness, antibacterial property, ultraviolet protection properties of the dyed and mordanted silk fabrics were examined. The water-soluble dye of Rhododedron brachycarpum extracted with distilled water was expressed as Yellow Red color. The dye-abilities of silk generally increased depending on the increasing values of dye concentration, dye bath temperature and dyeing duration. The highest K/S values were obtained at a dye concentration of 100% (v/v), a dye bath temperature of $90^{\circ}C$, a dyeing duration 120 minutes and a dyeing of pH 2. The light fastness of dyed and Cu mordanted silk fabrics were found to be 4 grade while Al, Fe mordanted silk fabrics were found to be 2~3 grade. The dry cleaning and rubbing fastness were excellent or good. The fade of washing fastness was not good, however, the stain of washing fastness was excellent. The dyed and Al, Cu mordanted silk fabrics indicated 99.9% reduction rate. The dyed and the mordanted fabrics showed very good ultraviolet protection factors.

• Journal of Fashion Business
• /
• v.23 no.4
• /
• pp.100-111
• /
• 2019

In this study, the dyeing properties and functionalities of Crataegi fructus extract were investigated for the purpose of application to new natural dye resources. The effects of dyeing conditions(concentration of dye, dye bath temperature, dyeing duration and dye bath pH) and mordanting on dye uptake and color changes were also examined. The study also estimated the colorfastness, antibacterial properties, and ultraviolet protection properties of the dyed and mordanted silk fabrics. The dye uptake increased in tandem with the dye concentration and dye bath temperature. The highest K/S values were obtained at the following conditions: a dye concentration of 100%(v/v), a dyeing period of 60 minutes, a dye bath temperature of $90^{\circ}C$, and a dyeing pH of 3. The colorfastness of the material when dry cleaned or rubbed ranged from good to excellent and fastness to light was rated at grade 2-3. The change in the color grade when exposed to washing was not good; however, the stain of washing fastness was good at a range of 4-5. In regards to the functional property aspects, the dyed and mordanted fabrics exhibited excellent results with a 99.9% reduction rate, and excellent ultraviolet protection factors.

• Journal of Sericultural and Entomological Science
• /
• no.11
• /
• pp.63-68
• /
• 1970

The induction of polyhedroses in the silkworm, Bambyx mari L., was investigated treating the 5th instar larvae just after eodysis with high temperature (hot water bath at 40$^{\circ}C$ for 5 minutes or dry heat shock at 40$^{\circ}C$ for 30 minutes) and low temperature (5$^{\circ}C$ for 24 hours). The results obtained were as follows; 1. Comparing between the frequency of nuclear and cytoplasmic polyhedroses induced by cold and heat treatments (hot water bath at 40$^{\circ}C$ for 5 minutes), the induction ratio of the former is clearly less than that of the latter. But if the larvae tested with cold were left at room temperature (25$^{\circ}C$) for 30-120 minutes till the next hot water bath (40$^{\circ}C$) for 5 minutes and water bath (20$^{\circ}C$) for 5 minutes, treatments, the frequency of induced cytoplasmic polyhedrosis was more than that in the case of cold or hot water bath treatment alone. 2. The frequency of nuclear and cytoplasmic polyhedrosis induced by cold and successive heat (dry heat shock at 40$^{\circ}C$ for 30 minutes), left at room temperature (25$^{\circ}C$) ti11 the second treatment, the frequency of nuclear polyhedrosis was less than that of cytoplasmic polyhedrosis. 3. The reaction of nuclear polyhedra to stains also differs sharply from that of the cytoplasmic type. In a smear of nuclear polyhedra on a slide staining with Giemsa solution remains unstained against a stained back ground, in contrast to this, the cytoplasmic polyhedra take up stain readly.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1999.05a
• /
• pp.97-97
• /
• 1999

Dross formation in the zinc bath is inevitable under any condition as long as coating process on steel strip continues. Thus, bath aluminum and temperature are precisely managed to suppress the increase of dross. Also, excessive dross for normal coating process is generally eliminated physically by bubbling and skimming. Total amount of dross in the bath can be sometimes high enough to cause coating defect. On the other hand, local concentration of dross can make coating defect even with satisfactory level of total amount of dross. Reduction of dross in the bath was attempted by using ceramic foam filter made of mainly alumina. Dross in molten zinc was almost reduced to the levels of solubility of iron and aluminum in molten zinc at $450~460^{\circ}C$. Their solubility levels were confirmed by thermodynamic calculations or DEAL program. Two kinds of filters were tested for dross reduction. One was #20 ppi, porous per inch, and the other #30 ppi filter. Both were effective in reducing the bath dross to the solubility levels at the static state. Bath iron was reduced by 24 wt% and 19 wt% with #20 filter, and by 35 wt% and 29 wt% with #30 filter for GI and GA pot, respectively. Also, ceramic foam filter did not make any harm to the zinc bath composition after filtering test.

• Korean Journal of Food Science and Technology
• /
• v.51 no.2
• /
• pp.103-108
• /
• 2019

This study was conducted to select the optimal extraction method of codonopsis lanceolata saponin. To investigate the lancemasides content depending on each extraction method, various extractions were performed: reflux (methanol and butanol), hot water, as well as ultrasonic bath (40 kHz; continuous irradiation/interval irradiation) and ultrasonicator (20 kHz) extractions. From the result, the overall lancemasides content were the highest in ultrasonic bath (MeOH; continuous irradiation) extraction, followed by ultrasonic bath (water; continuous irradiation)>ultrasonic bath (MeOH; interval irradiation)>ultrasonicator (MeOH)>hot water>MeOH reflux>BuOH reflux extractions in that order. Sample drying method prior to ultrasonic bath extraction was more effective shade drying than freeze drying. Effective duration and temperature of extraction was 2 hr at $64^{\circ}C$. And ingredient change diverted from aster saponin Hb to lancemasides was identified by extraction condition such as extraction time and temperature.

• Resources Recycling
• /
• v.29 no.6
• /
• pp.35-40
• /
• 2020

In this study were carried out basic experiments mainly to investigate important reaction mechanism, the reaction temperature, time and the addition amount of Zn in recycling of waste cemented carbide by the zinc bath process. As a result, it was required that the Zn bath reaction was heated more than at 800℃ to accelerate reaction of melted Zn and Co inside of wasted cemented carbide. Furthermore, thickness of the waste cemented carbide was reduced linearly according to increase of reaction time at 700℃ for 0.5~2h in the zinc bath reaction. Also the zinc bath reaction was examined that heating in lower than at 800℃ for 3h and then heated more than at 900℃ for 1h(above 3.0×10 torr-2 vaccum) was suitable to reduce vapour loss amount of Zn in the zinc bath process.