Abstract
In this study were carried out basic experiments mainly to investigate important reaction mechanism, the reaction temperature, time and the addition amount of Zn in recycling of waste cemented carbide by the zinc bath process. As a result, it was required that the Zn bath reaction was heated more than at 800℃ to accelerate reaction of melted Zn and Co inside of wasted cemented carbide. Furthermore, thickness of the waste cemented carbide was reduced linearly according to increase of reaction time at 700℃ for 0.5~2h in the zinc bath reaction. Also the zinc bath reaction was examined that heating in lower than at 800℃ for 3h and then heated more than at 900℃ for 1h(above 3.0×10 torr-2 vaccum) was suitable to reduce vapour loss amount of Zn in the zinc bath process.
본 연구에서는 zinc bath 프로세스에 의한 폐초경합금의 재활용 시 중요한 반응온도, 시간 및 아연의 첨가량 등 반응 메카니즘을 조사하기 위해 기초실험을 수행하였다. 그 결과, zinc bath 반응은 용융 아연(Zn)과 폐초경합금 내측의 코발트(Co)의 반응을 촉진시키기 위해 800℃ 이상에서 가열하는 것이 요구되었다. 또한 폐초경합금의 두께는 800℃에서 0.5~2시간 동안의 zinc bath 프로세스에 있어서 반응시간의 증가에 따라 선형적으로 감소하였으며, 아연의 증발 감소량을 줄이기 위해서는 800℃이하에서 3시간 가열된 후에 2.0×10 torr-2이상의 진공분위기로 900℃이상에서 1시간 동안 가열하는 것이 적합한 것으로 조사되었다.