• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.98-103
• /
• 2006

[$Bi_2Sr_2Ca_1Cu_2O_x$](BSCCO 2212) tubes were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted in a Pt crucible and solidified in a rotating steel mold. The BSCCO 2212 tube samples separated from steel mold were heat-treated at $800^{\circ}C\;and\;810^{\circ}C$ in oxygen flow. The critical current($I_c$) of the samples was measured by transport measurement at 77K, and the microstructure was investigated by scanning electron microscope. The $J_c$ at 77K of the tubes heated treated at $800^{\circ}C\;and\;810^{\circ}C$ were 197 and 240 $A/cm^2$, respectively. It was observed that the plate like grains in BSCCO 2212 tube was more developed in the sample heat treated at $810^{\circ}C\;and\;800^{\circ}C$ heated tube. It is found that the critical current($I_c$) of the BSCCO 2212 sample was dependent on the heating schedule regarding the growth of the BSCCO 2212 grains.

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.103-107
• /
• 2009

$Bi_2Sr_2Ca_1Cu_2O_x$(BSCCO 2212) superconductors for current lead were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted at $1200^{\circ}\C$ in a resistance furnace using a Pt crucible and poured in a rotating cylindrical mold preheated at $550^{\circ}\C$ for 2 hour. The solidified BSCCO-2212 samples were heat-treated by partial melting process in oxygen atmosphere. The current-voltage curves at 77 K of the samples were obtained by transport measurement, and the microstructure was investigated by scanning electron microscope. The $J_c$ values at 77 K of the tubes partially melted at $840^{\circ}C,\;860^{\circ}C\;and\;880^{\circ}C$ were 492, 430 and 398 $A/cm^2$, respectively. It was observed that the plate-like grains in BSCCO 2212 tube was more developed in the sample heat-treated at $840^{\circ}C$. It was found that the critical current of the BSCCO 2212 samples was dependent on the partial melting schedule regarding the grain shape and size of the BSCCO 2212.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.179-183
• /
• 2006

As a material for SFCL(Superconducting Fault Current Limiter), BSCCO tube with metal stabilizer is a promising candidate, assuring the stability and large power capacity, For the application, the proper soldering technique, which overcome the difficulties of the joining between BSCCO and metal stabilizer, is required. In this study, after soldering In-Bi solder and In-Sn solder with BSCCO superconductor, welding properties between BSCCO and solders were investigated. Because ceramic materials is difficult to weld, Ag electro-plating on BSCCO 2212 is used for intermetallic layer. To find out the best welding condition for superconductor, soldering is tested in the maximum temperature from $155^{\circ}C\;to\;165^{\circ}C$ in the reflow oven. By investigating the composition and thickness of IMC (lntermetallic Compound) created in the reaction of Ag with solder, we analyzed the welding properties of High-Tc superconductor from a micro point of view.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.267-267
• /
• 2006

전력에 큰 손실을 초래하는 고장전류를 차단하기 위한 한류기(FCL) 소재로서 고온 초전도체인 BSCCO 2212가 사용된다. 고온에서 용융된 BSCCO 2212 분말은 원심성형법에 의해 한류기용 튜브로 제조되었다. BSCCO 튜브의 기계적 특성을 높이고 용융온도를 낮추기 위해 $SrSO_4$(10wt-%)를 첨가하였다. 용탕은 $1200^{\circ}C$에서 완전히 용융되어 금속 몰드로 주입되었고 원심성형에 사용되는 금속 몰드는 $550^{\circ}C$ 온도로 2시간 예열 후 1020 ~ 2520 RPM으로 회전시켰다. 원심력에 의해 성형된 BSCCO 튜브는 약 48시간 동안 로에서 서냉 후 금속 몰드로부터 분리하였다. 튜브의 용이한 분리를 위해 이형제로서 BSCCO 2212 powder를 사용하였고 임계전류측정을 고려하여 Ag tape 단자를 튜브 끝단에 부착하였다. BSCCO 제조 공정에 있어서 몰드의 예열온도, 용융온도, 몰드 회전속도 등의 변수를 조절하여 최적의 조건을 확립하였다. 제조한 BSCCO 튜브의 임계전류($I_c$)와 임계전류밀도($J_c$)는 77K에서 536A와 $205A/cm^2$ 이었다. 본 연구에서는 BSCCO 2212 튜브를 제조하는 공정조건 변화와 각 조건에서 제조된 BSCCO 2212 튜브의 전기적 특성 및 그에 따른 분석에 대해 기술하였다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.134-134
• /
• 2005

• Progress in Superconductivity
• /
• v.9 no.2
• /
• pp.193-198
• /
• 2008

We fabricated BSCCO-2212(2212) bulk superconductors by using a casting process and evaluated the superconducting properties. The effects of annealing conditions on microstructure and critical properties were studied. It was found that the homogeneous and uniform microstructure improved the critical properties and the microstructures of ingot and annealed rods were different with the size of 2212 rod and tube. The critical current($I_c$) of rods increased with increasing annealing time, probably due to increased grain size of 2212. Annealing time of the highest $I_c$ for the smaller rod(diameter of 10 mm) was shorter(150 hr) than that of the larger rod(diameter of 16 mm, 400 hr). This size effect seems to be related to different grain sizes of the intermediate phases such as 2201 and secondary phases in the ingot. In addition, we fabricated 2212 tubes from the rod by removing the center region which contained inhomogeneous microstructures. The $I_c$ of 2212 tube with the outer diameter of 16 mm and the thickness of 2 mm was measured to 844 A, which corresponds to the critical current density of $1017\;A/cm^2$ at 77 K.

• Proceedings of the Korea Institute of Applied Superconductivity and Cryogenics Conference
• /
• 2001.02a
• /
• pp.25-28
• /
• 2001

Bi-2212 HTS tube was fabricated by centrifugal forming process(CFP). As a variation of melt casting process(MCP) or centrifugal casting technique, the centrifugal forming process is a flexible method for manufacturing Bi-2212 bulk tubes and has been optimized to achieve smooth surface and uniform thickness. At this process, the slurry was prepared in the mixing ratio of 10:1 between Bi-2212 powder and binder and initially charged into the rotating mold under the speed of 300~450 rpm Heat-treatment was performed at the temperature ranges of 860 ~ $890^{\circ}C$ in air for partial melting. The HTS tube fabricated by centrifugal forming process at $890^{\circ}C$ under the rotating speed of 450 rpm was highly densified and the plate-like grains with more than 20$\mu$m were well oriented along the rotating axis. The measured Tc and Jc at 10K were around 85K and 3,000A/cm2 respectively.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.24-27
• /
• 2008

For the development of superconducting fault current limiters(SFCLs) having large current capacity, we fabricated an SFCL element that consists of Bi-2212 superconductor and Cu-Ni alloy tubes. First, Ag was plated on the surface of the Bi-2212 for the enhancement of soldering process. On the Ag-plated Bi-2212 tube, a Cu-Ni alloy tube was soldered using optimized solders and soldering conditions. The BSCCO/Cu-Ni composite was processed mechanically to have a helical shape for the improvement of the SFCL characteristics. The total current path of the SFCL element was 1330 mm long with 12 turns, and had critical current of 340 A at 77 K. Finally, we carried out the fault test using the fabricated SFCL element. It showed successful current limiting performance under the fault condition of 50 $V_{rms}$ and 5.5 kA. From the results, the rated voltage of the SFCL element was decided to be 0.4 V/cm, and the power capacity was 12 kVA at 77 K. The fabrication process of the SFCL and the fault test results will be presented.

• 한국초전도학회:학술대회논문집
• /
• 2008.08a
• /
• pp.78-78
• /
• 2008

• Progress in Superconductivity
• /
• v.7 no.1
• /
• pp.97-101
• /
• 2005

Bi-22l2 tubes for fault current limiter (FCL) were fabricated by centrifugal melting process. $SrSO_4$ ($10\;wt.\;\%$) was added to Bi-2212 powder to lower the melting point of Bi-22l2 and to improve the mechanical properties. The BSCCO powder was completely melted at $1300\;^{\circ}C$ using the RF furnace and then poured into rotating steel mold. The steel mold, preheated at $450\;{\circ}C{\sim}550^{\circ}C$ for 2 hour was rotated at $1020{\sim}2520\;RPM$. The solidified BSCCO tube was cooled down to room temperature in the furnace for 48 hours and separated from the mold between Bi-2212 and the mold. $ZrO_2$ solution was used to separate it easily from the mold and Ag tape was attached in the mold inner wall of the mold to analysis electrical property. Bi-22l2 tube was often cracked when the cooling rate was high. BSCCO tubes with $70{\Phi}{\times}100\;mm,\;50{\Phi}{\times}100\;mm$ and $30{\Phi}{\times}150\;mm$ size were fabricated by centrifugal melting process. The $J_{c}s$ of tubes with $50{\Phi}{\times}100\;mm{\times}4.0\;t$ and $50{\Phi}{\times}100\;mm{\times}4.l\;t$ were 178 and $74.2\;A/cm^2$ at 77K, respectively. The processing condition for Bi-2212 tube fabrication was investigated using XRD and SEM analyses.