Effect of Annealing Conditions on Properties of BSCCO-2212 Bulk

열처리조건이 BSCCO-2212 벌크의 특성에 미치는 영향

  • Kim, Kyu-Tae (Neutron Science Division, Korea Atomic Energy Research Institute) ;
  • Kim, Chan-Joong (Neutron Science Division, Korea Atomic Energy Research Institute) ;
  • Lim, Jun-Hyung (School of Advanced Materials Science and Engineering, Sungkyunkwan University) ;
  • Park, Eui-Cheol (School of Advanced Materials Science and Engineering, Sungkyunkwan University) ;
  • Park, Jin-Hyun (School of Advanced Materials Science and Engineering, Sungkyunkwan University) ;
  • Joo, Jin-Ho (School of Advanced Materials Science and Engineering, Sungkyunkwan University) ;
  • Hyun, Ok-Bae (Power System Laboratory, Korea Electric Power Research Institute) ;
  • Kim, Hye-Rim (Power System Laboratory, Korea Electric Power Research Institute)
  • Published : 2008.04.30
Download PDF
⟨ Previous Next ⟩

Abstract

We fabricated BSCCO-2212(2212) bulk superconductors by using a casting process and evaluated the superconducting properties. The effects of annealing conditions on microstructure and critical properties were studied. It was found that the homogeneous and uniform microstructure improved the critical properties and the microstructures of ingot and annealed rods were different with the size of 2212 rod and tube. The critical current($I_c$) of rods increased with increasing annealing time, probably due to increased grain size of 2212. Annealing time of the highest $I_c$ for the smaller rod(diameter of 10 mm) was shorter(150 hr) than that of the larger rod(diameter of 16 mm, 400 hr). This size effect seems to be related to different grain sizes of the intermediate phases such as 2201 and secondary phases in the ingot. In addition, we fabricated 2212 tubes from the rod by removing the center region which contained inhomogeneous microstructures. The $I_c$ of 2212 tube with the outer diameter of 16 mm and the thickness of 2 mm was measured to 844 A, which corresponds to the critical current density of $1017\;A/cm^2$ at 77 K.