• The Journal of Natural Sciences
• /
• v.7
• /
• pp.19-25
• /
• 1995

In this study, the Mossbauer effect of the $NiAl_0.8Fe_1.2O_4$ was investigated in the temperature range of 77K-1000K. The spectra were composed of two component, one is sixtet and the other doublet, at low temperature. From the temperature dependence of Mossbauer spectum, it is appeared that the magnetic properties of $NiAl_0.8Fe_1.2O_4$ varies from ferrimagnetism to paramagnetism as the increasing tempereture. And the magnetic relaxation patterns of the $NiAl_0.8Fe_1.2O_4$ were shown superparamagnetic effect.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.313.2-313.2
• /
• 2013

본 연구에서는 기존에 연구된 Solar Cell 보다 구조 및 제작이 단순한 $Al/Al_2O_3/Si$(100) Solar cell을 제작하여 평가하였다. 기판으로는 p-type Si(100), 0.5~2 ${\Omega}{\cdot}cm$을 사용하여 chemical cleaning 후 ALD(Atom Layer Deposition)법으로 Al2O3 터널링 절연막을 증착하였으며, 박막의 두께를 1~10 nm로 변화시켜 MIS 커패시터의 터널링 효과를 평가하였다. MIS 커패시터의 전기적 특성평가를 위해 누설전류 밀도-전계 특성은 pA meter/DC Voltage source를 사용하였고, 커패시턴스-전압특성, D-factor 특성은 precision LCR meter를 사용하였다. $Al/Al_2O_3/Si$(100) Solar cell의 특성평가를 위해 300~1100nm 파장영역에 따른 양자 효율을 평가하기 위해 Quantum Efficiency system (QE)을 사용하였고, Stanard Test Conditions 100 $mW/cm^2$, AM1.5, $25^{\circ}C$ 조건의 Voc, Isc, Jsc, FF (Fill Factor) 및 Efficiency(%)를 평가하기 위해 Solar simulator를 이용하였다.

• Journal of Surface Science and Engineering
• /
• v.48 no.5
• /
• pp.233-237
• /
• 2015

In order to investigate the potassium (K) gettering, Al-1%Si/$SiO_2$/PSG multilevel thin films were fabricated. Al-1%Si thin films and $SiO_2$/PSG passivations were deposited by using DC magnetron sputter techniques and APCVD (atmosphere pressure chemical vapor deposition), respectively. Heat treatment was carried out at $300^{\circ}C$ for 5 h in air. SIMS (secondary ion mass spectrometry) depth profiling analysis was used to determine the distribution of K, Al, Si, P, and other elements throughout the $SiO_2$/PSG passivated Al-1%Si thin film interconnections. Potassium peaks were observed throughout the $SiO_2$/PSG passivation layers, and especially the interface gettering at the $SiO_2$/PSG and at the Al-1%Si/$SiO_2$ interfaces was observed. Potassium gettering in Al-1%Si/$SiO_2$/PSG multilevel thin films is considered to be caused by a segregation type of gettering.

• Korean Chemical Engineering Research
• /
• v.61 no.3
• /
• pp.479-486
• /
• 2023

In this study, we investigated the effect of the Ce_xZr_1-xO₂ (CZ) addition onto Ni/Al₂O₃ catalysts on the catalytic performance in methane steam reforming. In the reaction results, the CZ-added Ni/Al₂O₃ catalyst showed higher CH₄ conversion and H₂ yield under the same reaction conditions than Ni/Al₂O₃. From the characterization data, the two catalysts had similar support porosity and Ni dispersion, confirming that the two properties could not determine the catalytic performance. However, the oxygen vacancy over the CZ-added Ni/Al₂O₃ catalyst induced an efficient steam activation at low reaction temperatures, resulting in an increase in the catalytic activity and H₂ yield.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.7
• /
• pp.394-399
• /
• 2000

The mechanical and electrical properties of pressed and annealed $\beta-SiC-TiB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of $Al_2O_3+Y_2O_3$. Phase analysis of composites by XRD revealed $\alpha$-SiC(6H), TiB2, and (Al5Y3O12). Reaction between Al2O3 and $Y_2O_3$ formed YAG but the relative density decreased with increasing $Al_2O_3+Y_2O_3$ contents. The Flexural strength showed the value of 458.9 MPa for composites added with 4 wt% $Al_2O_3+Y_2O_3$ additives at room temperatures. Owing to crack deflection and crack bridging, the fracture toughness showed 6.2, 6.0 and 6.6 MPa.m1/2 for composites added with 4, 8 and 12 wt% Al2O3+Y2O3 additives respectively at room temperature. The resistance temperature coefficient showed the value of $3.6\times10^{-3},\; 2.9\times10^{-3}\; and\; 3.0\times10^{-3} /^{\circ}C$$^{\circ}C$ for composite added with 4, 8 and 12 wt% $Al_2O_3+Y_2O_3$additives respectively at room temperature. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) in the temperature range of $25^{\circ}C\; to\; 700^{\circ}$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.9
• /
• pp.516-522
• /
• 2000

The mechanical and electrical properties of the hot-pressed and annealed $\beta-SiC-ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of$Al_2O_3+Y_2O_3$ Phase analysis of composites by XRD revealed $\alpha-SiC(6H) ZrB_2\; and YAG(Al_5Y_3O_{12})$ The relative density of composites were increased with increased Al2O3+Y2O3 contents. The Flexural strength showed the highest value of 390.6MPa for composites added with 20wt% Al2O3+Y2O3 additives at room temperature. Owing to crack deflection crack bridging phase transition and YAG of fracture toughness mechanism the fracture toughness showed the highest value of 6.3MPa.m1/2 for composites added with 24wt% Al2O3+Y2O3 additives at room temperature. The resistance temperature coefficient showed the value of$ 2.46\times10^{-3}\;, 2.47\times10^{-3},\; 2.52\times10^{-3}/^{\circ}C$ for composite added with 16, 20, 24wt% Al2O3+Y2O3 additives respectively. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) in the temperature range of $256{\circ}C\; to\; 900^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.933-938
• /
• 1998

The hydration for the system of fluorogypsum and 20wt% blast furnace slag was investigated at liquid/soild ratio of 0.45 for 1, 3, and 7 days by using 3 kinds of accelerators such as K2SO4 Al2(SO4)3 $.$16-18H2O and AlK(SO4)2$.$12H2O After curing the hardened specimen was characterized by the compressive strength the content of combined water XRD, DTA and SEM It was found that the activating effect was increased in the order of K2SO4

• Proceedings of the KIEE Conference
• /
• 1998.11c
• /
• pp.853-855
• /
• 1998

The electrical resistivity and mechanical properties of the hot-pressed and annealed ${\beta}$-SiC+39vol.%$ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of $Al_{2}O_{3}+Y_{2}O_{3}$(6:4wt%). In this microstructures. no reactions were observed between $\beta$-SiC and $ZrB_2$, and the relative density is over 97.6% of the theoretical density. Phase analysis of composites by XRD revealed mostly of a $\alpha$-SiC(6H, 4H), $ZrB_2$ and weakly $\beta$-SiC(15R) phase. The fracture toughness decreased with increased $Al_{2}O_{3}+Y_{2}O_{3}$ contents and showed the highest for composite added with 4wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives. The electrical resistivity increased with increased $Al_{2}O_{3}+Y_{2}O_{3}$ contents because of the increasing tendency of pore formation according to amount of liquid forming additives $Al_{2}O_{3}+Y_{2}O_{3}$. The electrical resistivity of composites is all positive temperature coefficient resistance(PTCR) against temperature up to $700^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.552-560
• /
• 1994

A composite of TiB2-Al2O3 system was successfully prepared from a mixture of TiO2, B2O3, and Al by self-propagating high temperature synthesis (SHS) with a novel characteristic, utilizing the internal oxidation heat of aluminium metal of the mixture, instead of by a conventional technique, externally heating a mixture of Ti, B and Al2O3. From a mixture with B/Ti molar ratio of =2.0, pure two phases of TiB2 and $\alpha$-Al2O3 with good crystallinity and small, uniform sizes were formed. However, when the B/Ti molar ratio of the mixture goes to a value less than 2.0, in addition to the above main minerals, a small smounts of metastable phases such as TiB and Ti3B4 were formed. It was found that about 60%, the optimum green density of compacts gave their highest reaction rate and temperature during SHS process. TiB2-Al2O3 system composite with B/Ti molar ratio of =2.0 could be pressurelessly sintered even at 190$0^{\circ}C$ under Ar gas flows without any addition of sintering aids, showing their good properties such as 91.2% in relative density, 2750 kgf/$\textrm{mm}^2$ in Vickers hardness and 2620 kgf/$\textrm{cm}^2$ in flexural strength.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.42-42
• /
• 1996