• Korean Journal of Materials Research
• /
• v.25 no.1
• /
• pp.16-20
• /
• 2015

In this study, in order to improve the efficiency of n-type monocrystalline solar cells with an Alu-cell structure, we investigate the effect of the amount of Al paste in thin n-type monocrystalline wafers with thicknesses of $120{\mu}m$, $130{\mu}m$, $140{\mu}m$. Formation of the Al doped $p^+$ layer and wafer bowing occurred from the formation process of the Al back electrode was analyzed. Changing the amount of Al paste increased the thickness of the Al doped $p^+$ layer, and sheet resistivity decreased; however, wafer bowing increased due to the thermal expansion coefficient between the Al paste and the c-Si wafer. With the application of $5.34mg/cm^2$ of Al paste, wafer bowing in a thickness of $140{\mu}m$ reached a maximum of 2.9 mm and wafer bowing in a thickness of $120{\mu}m$ reached a maximum of 4 mm. The study's results suggest that when considering uniformity and thickness of an Al doped $p^+$ layer, sheet resistivity, and wafer bowing, the appropriate amount of Al paste for formation of the Al back electrode is $4.72mg/cm^2$ in a wafer with a thickness of $120{\mu}m$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.6
• /
• pp.282-288
• /
• 2017

In this paper, GaAs/AlGaAs multi-layer structure was grown by liquid phase epitaxy with graphite sliding boat, which can be used as a device structure of a photocathode image sensor. The multi-layer structure was grown on an n-type GaAs substrate in the sequence as follows: GaAs buffer layer, Zn-doped p-type AlGaAs layer as etching stop layer, Zn-doped p-type GaAs layer, and Zn-doped p-type AlGaAs layer. The Characteristics of GaAs/AlGaAs structures were analyzed by using scanning electron microscope (SEM), secondary ion mass spectrometer (SIMS) and hall measurement. The SEM images shows that the p-AlGaAs/p-GaAs/p-AlGaAs multi-layer structure was grown with a mirror-like surface on a whole ($1.25mm{\times}25mm$) substrate. The Al composition in the AlGaAs layer was approximately 80 %. Also, it was confirmed that the free carrier concentration in the p-GaAs layer can be adjusted to the range of $8{\times}10^{18}/cm^2$ by hall measurement. In the result, it is expected that the p-AlGaAs/p-GaAs/p-AlGaAs multi-layer structure grown by the LPE can be used as a device structure of a photoelectric cathode image sensor.

• Proceedings of the KIEE Conference
• /
• 2005.11a
• /
• pp.27-29
• /
• 2005

ZnO and phosphorus doped ZnO thin films (ZnO:P) are deposited by pulsed laser deposition grown on (001) $Al_{2}O_{3}$. ZnO/ZnO:P/ZnO/$Al_{2}O_{3}$ (multi-layer) structure was used for phosphorus doped ZnO fabrication. This multi-layer structure thin film was annealed at $400^{\circ}C$ for 40 min. The electron concentration of that was changed from $10^{19}$ to $10^{16}/cm^{-3}$ after annealing. ZnO thin films with encapsulated structure showed the enhanced structural and optical properties than phosphorus doped ZnO without encapsulated layer. In this study, encapsulated ZnO structure was suggested to enhance electrical, structural and optical properties of phosphorus doped ZnO thin film and it was identified that encapsulated structure could be used to fabricate high quality phosphorus doped ZnO thin film.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.1
• /
• pp.6-10
• /
• 2009

In this paper, a selective area growth (SAG) of a GaN/AlGaN double heterostructure (DH) has been performed on r-plane sapphire substrate by using the mixed-source hydride vapor phase epitaxy (HVPE) with multi-sliding boat system. The SAG-GaN/AlGaN DH consists of GaN buffer layer, Te-doped AlGaN n-cladding layer, GaN active layer, Mg-doped AlGaN p-cladding layer, and Mg-doped GaN p-capping layer. The electroluminescence (EL) characteristics show an emission peak of wavelength, 439 nm with a full width at half maximum (FWHM) of approximately 0.64 eV at 20 mA. The I-V measurements show that the turn-on voltage of the SAG-GaN/AlGaN DH is 3.4 V at room temperature. We found that the mixed-source HVPE method with a multi-sliding boat system was one of promising growth methods for III-Nitride LEDs.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.8 no.5
• /
• pp.1057-1061
• /
• 2007

In this study, we investigated the properties of ZnO thin films prepared by layer-by-layer method in RF magnetron sputtering system using AlAs and ZnO targets. Effects of $H_2O_2$ dip prior to thermal treatment were studied as well. Either n-type or p-type films were observed in our study depending on the annealing conditions. It thus indicates the feasibility of arbitrarily modifying the conductivity type. At the same time, it also implies the thermal instabilities of the film properties. Property measurements after stressing the films up to 144 hours showed that thermal variations of properties nay be suppressed by pre-treatment in 30% $H_2O_2$ for 1 min.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.3
• /
• pp.89-92
• /
• 2009

High-quality Al-N doped p-type ZnO thin films were deposited on Si and buffer layer/Si by DC magnetron sputtering in a mixture of $N_2$ and $O_2$ gas. The target was ceramic ZnO mixed with $Al_2O_3$ (2 wt%). The p-type ZnO thin films showed a carrier concentration in the range of $1.5{\times}10^{15}{\sim}2.93{\times}10^{17}\;cm^{-3}$, resistivity in the range of 131.2${\sim}$2.864 ${\Omega}cm$, mobility in the range of 3.99${\sim}$31.6 $cm^2V^{-1}s^{-l}$, respectively. It was easier to dope p-type ZnO films on Si substrates than on buffer layer/Si. The film grown on Si showed the highest quality of photoluminescence (PL) characteristics. The Al donor energy level depth $(E_d)$ of Al-N codoped ZnO films was reduced to about 50 meV, and the N acceptor energy level depth $(E_a)$ was reduced to 63 meV.

• Journal of Electrochemical Science and Technology
• /
• v.10 no.4
• /
• pp.424-432
• /
• 2019

Planar BiVO₄ and 3 wt% Mo-doped BiVO₄ (abbreviated as Mo:BiVO₄) film were prepared by the facile spin-coating method on fluorine doped SnO₂(FTO) substrate in the same precursor solution including the Mo precursor in Mo:BiVO₄ film. After annealing at a high temperature of 450℃ for 30 min to improve crystallinity, the films exhibited the monoclinic crystalline phase and nanoporous architecture. Both films showed no remarkably discrepancy in crystalline or morphological properties. To investigate the effect of surface passivation exploring the Al₂O₃ layer, the ultra-thin Al₂O₃ layer with a thickness of approximately 2 nm was deposited on BiVO₄ film using the atomic layer deposition (ALD) method. No distinct morphological modification was observed for all prepared BiVO₄ and Mo:BiVO₄ films. Only slightly reduced nanopores were observed. Although both samples showed some reduction of light absorption in the visible wavelength after coating of Al₂O₃ layer, the Al₂O₃ coated BiVO₄ (Al₂O₃/BiVO₄) film exhibited enhanced photoelectrochemical performance in 0.5 M Na₂SO₄ solution (pH 6.5), having higher photocurrent density (0.91 mA/㎠ at 1.23 V vs. reversible hydrogen electrode (RHE), briefly abbreviated as V_RHE) than BiVO₄ film (0.12 mA/㎠ at 1.23 V_RHE). Moreover, Al₂O₃ coating on the Mo:BiVO₄ film exhibited more enhanced photocurrent density (1.5 mA/㎠ at 1.23 V_RHE) than the Mo:BiVO₄ film (0.86 mA/㎠ at 1.23 V_RHE). To examine the reasons, capacitance measurement and Mott-Schottky analysis were conducted, revealing that the significant degradation of capacitance value was observed in both BiVO₄ film and Al₂O₃/Mo:BiVO₄ film, probably due to degraded capacitance by surface passivation. Furthermore, the flat-band potential (V_FB) was negatively shifted to about 200 mV while the electronic conductivities were enhanced by Al₂O₃ coating in both samples, contributing to the advancement of PEC performance by ultra-thin Al₂O₃ layer.

• Journal of the Semiconductor & Display Technology
• /
• v.12 no.3
• /
• pp.47-51
• /
• 2013

Current research trends of solar cells has focused on the high conversion efficiency and low-cost production technology. Passivation technology that can be easily adapted to mass production. Therefore, this study conducted experiments with aim of the following two methods for the fabrication of high-efficiency crystalline silicon solar cells. In the first task, an attempt is formation of local Al-BSF to a number of locally doped dots to increase the conversion efficiency of solar cells to reduce the loss of $V_{oc}$ overcome. The second major task, rear surface apply in $Al_2O_3/SiN_x$ stack layer, $Al_2O_3$ prominent negative fixed charge characteristics. As the result of task, Local Al-BSF and $Al_2O_3/SiN_x$ stack layer applied to the p-type single crystalline silicon solar cells, the average $V_{oc}$ of 644mV, $I_{sc}$ of 918mV and conversion efficiency of 18.70% were obtained.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.319-320
• /
• 2009

In this study, high-quality Al-N doped p-type ZnO thin films were deposited on n-type Si (100) wafer or Si coated with buffer layer by DC magnetron sputtering in the mixture of $N_2$ and $O_2$ gas. The target was ceramic ZnO mixed with $Al_2O_3$ (2 wt%). The p-type ZnO thin film showed higher carrier concentration $2.93\times10^{17}cm^{-3}$, lower resistivity of $5.349\;{\Omega}cm$ and mobility of $3.99\;cm^2V^{-1}S^{-1}$, respectively. According to PL spectrum, the Al donor energy level depth ($E_d$) of Al-N codoped p-type ZnO film was reduced to about 51 meV, and the N acceptor energy level depth ($E_a$) was reduced to 63 meV, respectively.

• Current Photovoltaic Research
• /
• v.4 no.1
• /
• pp.12-15
• /
• 2016

Screen printing technique followed by firing has commonly been used as metallization for both laboratory and industrial based solar cells. In the solar cell industry, the firing process is usually conducted in a belt furnace and needs to be optimized for fabricating high efficiency solar cells. The printed-Al layer on the silicon is rapidly heated at over $800^{\circ}C$ which forms a layer of back surface field (BSF) between Si-Al interfaces. The BSF layer forms $p-p^+$ structure on the rear side of cells and lower rear surface recombination velocity (SRV). To have low SRV, deep $p^+$ layer and uniform junction formation are required. In this experiment, firing process was carried out by using conventional tube furnace with $N_2$ gas atmosphere to optimize $V_{oc}$ of laboratory cells. To measure the thickness of BSF layer, selective etching was conducted by using a solution composed of hydrogen fluoride, nitric acid and acetic acid. The $V_{oc}$ and pseudo efficiency were measured by Suns-$V_{oc}$ to compare cell properties with varied firing condition.