• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.569-572
• /
• 2008

This study carried out to evaluate the quality deviation according to Premixed and Non-Premixed cement for normal and high strength concrete using blast furnace slag and fly ash. The results of experiment are founded that concrete using premixed cement have more performance than non-premixed cement at a point of view for the quality deviations both strength and Chloride ion diffusion. Therefore, it is desirable that premixed cement should be used to decrease strength deviation in high strength concrete and durability deviation in normal strength concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.765-768
• /
• 2008

The prevent methods of Alkali-Silica Reaction (ASR) are studying after the failure cases by ASR were reported in Korea. When ASR failure is causing to the step of maintenance, the available repair methods were rarely studied in the World. In this study, premixed fly ash cement was applied to prevent ASR in the concrete pavement. The ratio of fly ash and cement is 20 percent and 80 percent by weight of total cementious material. The construction performance of premixed fly ash cementious concrete pavement was studied that the application is verify to performance collected data during the constructing in the field. The freeze-thaw test was studied to verify durability of the premixed fly ash cementious material made specimen in the laboratory. The results show that construction performance and durability are well condition in this test section and freeze-thaw test.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.137-138
• /
• 2023

This study proposed the optimal mixing time for pre-mixed cement and post mixed cement using the statistical analysis method of box plots. Pre-mixed cement can prevent material seegregation, strength loss, and quality variation if mixed for at least 60 seconds, and the data median is shown to be within the box range. Post-mixed cement should be mixed for at least 180 seconds to prevent material segregation, strength loss, and quality variation, and compressive strength tends to increase with longer vibrating times. Therefore, it is suggested that using pre-mixed cement can shorten the vibrating time and increase the productivity of the concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.9 no.5
• /
• pp.127-133
• /
• 2009

It is important to increase the strength of binders in order to enhance the strength of concrete. However, when the mineral admixture used for high strength concrete is incorporated individually, its dispersibility decreases due to the phenomenon of compaction, which reduces its fluidity and results in insufficient strength being created. To solve this problem, we can pre-mix each binder in advance to disperse a mineral admixture among binders, which will strengthen the fluidity and strength of concrete. Therefore, this study analyzed the properties of high strength concrete depending on the mix method used, to determine the effect of pre-mix cements ranging from W/B 15 to 35%. It was found that the fluidity of pre-mix increased to a level higher than that of individual mix due to its dispersion and ball bearing effect. The air content was slightly decreased from the result of individual mix due to the micro filler effect, which causes fine particles of silica-fume to fill the voids among cement particles, while the setting time of pre-mix was shorter than that of individual mix, because enhanced dispersion of pre-mix affects hydration heat time. The compressive strength of pre-mix increased due to the phenomenon of compaction of gap structure, and the variation of coefficient decreased by 1.69% on average in strength variation.

• Cement
• /
• s.183
• /
• pp.42-48
• /
• 2009

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.2
• /
• pp.90-96
• /
• 2009

The high rising building construction makes increasing the requirement of high strength concrete. Especially, the workability analysis is related with dispersion of admixture such as SF for improving strength and FA, BS for reducing construction cost and improving durability of Ultra High Strength Concrete which has over 100 MPa of compressive strength is very important. Precisely, decreases dispersion because of lumping situation of each admixture and it causes the workability of admixture is decreased. Therefore, the workability of cement paste is tested for analyze effects of pre-mixed cement for solving those problems with it to this research. The summary of the results are like below. First of all, OBS is increasing workability more than OFS. This result causes that the glassy surface of BS in the OBS is increasing workability and the absorption of admixture of FA in the OFS is decreasing workability. In the case of mixing methods, pre-mixing method is increasing workability more than normal one. This result shows that the normal mixing method is bad dispersion of binders. The other side, the pre-mixing method is good. Furthermore, depending on the mixing time, according to the increasing mixing time such as 30, 60, and 120 seconds, the dispersion of binders and workability turns better.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.381-384
• /
• 2008

This study investigated spalling prevention and fire resistance properties of the high strength concrete using pre-mixed cement containing fiber to prepare the method for the effective throwing of hybrid fiber. For result of a fire test, almost specimens were protected from fire except 15% of W/C. Totally, the pre-mixed cement containing fiber was favorable compared with passive mixing method for the spalling prevention. It is more effective to prevent spalling caused by fine diversion of fiber even in high strength concrete because it contained many corporate materials. Moreover, the temperature history of the side steel bar on the column test with pre-mixed cement containing fiber did not over 538$^{\circ}C$ which is the average for the standard of fire resistance performance.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.154-155
• /
• 2022

In this study, propose a plan to efficiently utilize CGS, a by-product generated from IGCC, as a mixed fine aggregate for concrete. The effect of the premixed cement types and CGS replacement rate on the overall characteristics and length change rate of concrete was analyzed. As a result of the analysis, the effect of CGS was found to be insignificant, and the effect of cement was found to be dominant.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.3
• /
• pp.247-252
• /
• 2017

The aim of this research is the feasibility analysis of the reject ash premixed cement mortar with combined aggregate. Namely, for the combined aggregate with two different qualities of aggregates, a fundamental properties of cement mortar was evaluated depending on various replacing ratios of reject ash(Ri). According to the experimental results, the combined aggregate consisted with low-quality aggregate and sea sand did not change the flow value depending on the reject ash while the combined aggregates consisted with low quality aggregate and sea sand; and consisted exploded debris sand and sea sand the increasing reject ash increased the air content with increased replacing ratio of reject ash. In the case of compressive strength, as the replacing ratio of reject ash was increased, the compressive strength was increased. It is considered that when 5% of reject ash replacing ratio made similar quality of cement mortar with favorable quality aggregate, hence, it can be suggested that 5% replacement of reject ash for desirable fluidity and compressive strength of concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.63-64
• /
• 2021

In this study, Coal gasification slag(CGS) was replaced with fine aggregate to verify the physical properties of the concrete according to the change in cement types. As a result of the study, the use of CGS resulted in a decrease of superplasticizer and an decrease of AE agent. In addition, when 50% of mixed cement and CGS were replaced, the initial strength expression was delayed, and the strength enhancing effect was judged to be weak.