• Magazine of the Korean Society of Agricultural Engineers
• /
• v.18 no.4
• /
• pp.4226-4231
• /
• 1976

The objective of this study is to investigate the characteristics of the concrete mixture and the plastic shrinkage of concrete exposed to a rapid evaporation immediately after placement, and to measure the shringkage rate according to the cement-mixture. Drying of concrete was conducted under a controlled chamber in which the temperature was 36${\pm}$2$^{\circ}C$, the relative humidity 45${\pm}$2%, and the wind velocity 4${\pm}$1m/sec. All of the concrete mo1ds were made to have good workability as 6${\pm}$0.5cm in slump. The results obtained are as follows; 1) The evaporation rate was 3.36kg/$\textrm{km}^2$, 2.98kg/$\textrm{km}^2$ and 2.91kg/$\textrm{km}^2$ respectively for each concretemixtures 365kg, 335kg and 317kg after 5 hour exposure, and the evaporation was measured at all 55∼57% after 2 hours and additional in 10% on after 5 hours exposure. 2) The weight of the concrete were was reduced to 3.0%, 2.6% and 2.4% respectively for each of them. 3) The shrinkage of concrete was 0.87 mm/m, 0.56mm/m and 0.31 mm/m after 5 hour exposure, and the shringkage of concrete was measured at 84%, 59% and 45% after 2 hours and it in 1∼5% after 5 hour exposure and then stopped. 4) A recommendation for good concrete is that the evaporation should be minimized during 2 hours after placement of concrete, if possible.

• Journal of the Korean Ceramic Society
• /
• v.44 no.9
• /
• pp.524-528
• /
• 2007

The results of evaluating steel corrosion in concrete containing chloride content of various levels indicated that the more chloride content in concrete leads to the lower potential and higher corrosion current density. However, the open circuit potential of steel varied with time and exposure condition, and the corelation between the open circuit potential and corrosion current density was not obvious. In order to determine the critical threshold content of chloride of steel corrosion in concrete, the concept of average corrosion current density was employed. The range of critical chloride content in portland cement concretes was about $1.56{\sim}1.77%$($Cl^-$, %, wt of cement content) along with water-cement ratio, and higher water-cement ratio resulted in reduction in critical threshold chloride content.

• Resources Recycling
• /
• v.12 no.2
• /
• pp.45-53
• /
• 2003

In 2001, Korea produced a total of 4.91 million metric tons of fly ash, approximately 63.3% of which was recycled. Almost all of the recycled fly ash are used in concrete mixtures and cement industry. Therefore, in order to develop a new usage to increase the utilization of the fly ash, conductive induction was used in this research rather than triboelectrostatic. By applying conductive induction, we could verify the possibility of obtaining high purity fly ash below 1%LOI and high carbon fly ash over 70%LOI from raw fly ash. In this test, the potential difference between the two electrodes was conducted by changing the range of 8 to 16 kV.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.11a
• /
• pp.37-40
• /
• 2007

This study investigates the effect of the pre-mix cement to the physical properties of the concrete according to the various combinations of the binders and the silica fume types. The results are summarized as following. For the properties of the fresh, the fluidity in the case that OPC+cilica fume-blast-furnace slag is appropriate compared to OPC+cilica fume+fly ash. Expecially, it is favorable when pre-mix is used. The fluidity time of the A, B depending on silica fume types is favorable, but it is decreased on C. The air content depending on silica fume types is low when the fly ash is used. Specially, the air content in the case that pre-mix is used is low caused by the dispersion of the silica fume. For the properties of the hardened concrete, the compressive and flexible strength when the blast-furnace slag is pre-mixed are high, and they exceed OPC. The strength depending on the silica fume types is high on B, and the strength of the others is similar.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.42-43
• /
• 2018

The research is to suggest the compensating strength values depending on various managing periods of concrete based on the strength development model calculated with equivalent age method for 20% of blast furnace slag replaced concrete. As a result, for 28 days of managing period, 9, 6, and 3MPa of compensating strength values were suggested when the temperatures were from 4 to 6℃, from 6 to 12℃, from 12 to 17℃, respectively. Additionally, for 42 days of managing period, 6 and 3MPa of compensating strength value was suggested when the temperature was from 4 to 7℃, from 7 to 12℃, and for 56 days of managing period, 3MPa of compensating strength value was suggested when the temperature was from 4 to 9℃. Furthermore, for 28, 42, 56, and 91 days of managing periods, any compensating strength values were needed when the temperature were higher than 17, 12, 9, and 4℃, respectively.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.11a
• /
• pp.133-136
• /
• 2009

This study analyzes the mixing and basic characteristics of concrete according to the unit quantity and mixing method of ternary blended cement and the results of this study can be summarized as follows. In the case of the premixed cement (hereafter referred as POBF) of POBF135, it satisfies the target level of fluidity and air content in which it shows relatively small bleedings even though it represents the latest initial and final setting. Also, although the POBF135 represents small initial strength, it shows an increase in the strength according to the increase in aging. In addition, it shows the lowest temperature in the POBF135. As a result, it can be seen that the POBF135 indicates the most optimal mixing subject to considering the aspect of fluidity, compressive strength, and heat of hydration in general figures.

• Korean Journal of Materials Research
• /
• v.20 no.1
• /
• pp.1-6
• /
• 2010

Geopolymer materials are attractive as inorganic binders due to their superior mechanical and eco-friendly properties. In the current study, geopolymer-based cement was prepared using aluminosilicate minerals from fly-ash with KOH as an alkaline-activator and $Na_2SiO_3$ as liquid glass. Then, calcium carbonate powder from a clam shell was mixed with the geopolymer and the mixture was coated on a concrete surface to provide points of attachment for environmental organisms to grow on the geopolymers. We investigated the effect of the shell powder grain size on the microstructure and bonding property of the geopolymers. A homogeneous geopolymer layer coated well on the concrete surface via aluminosilicate bonding, but the adhesiveness of the shell powder on the geopolymer cement was dependent on the grain size of the shell powder. Superior adhesive characteristics were shown in the shell powder of large grain size due to the deep penetration into the geopolymer by their large weight. This kind of coating can be applied to the adhesiveness of eco-materials on the surface of seaside or riverside blocks.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2009.05b
• /
• pp.53-56
• /
• 2009

This study reviewed the characteristics of concrete made of performance improving mixture materials based on KOH as a means to resolve the problems of initial quality reduction that result in concretes with blast furnace slag powder. Summarizing the results, first as the characteristics of fresh concrete, liquidity was found to reduce in general with increased BS substitution ratio. Objective range of liquidity was not satisfied in all mixes according to the use of performance improving mixture materials. Air capacity was satisfied to the objective range in all mixes. As the characteristics of hardened concrete, while compressive strength showed a decreasing trend with increasing BS substitution ratio at early age, increasing trend was shown by the plain with increasing BS substitution ratio at later age. On the other hand, K1 and K2 were only effective among mixture materials at early age, but K1F30 showed excellent strength at both early and later ages.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2017.05a
• /
• pp.345-345
• /
• 2017

급격한 도시화 현상으로 많은 인구가 밀집되고 토지를 집약적으로 이용을 하며 시멘트 콘크리트, 블록 등 도로포장으로 인해 불투수층이 증가하여, 폭우와 홍수로 인한 인명과 재산 및 교통체증 등과 같은 다양한 피해를 야기할 수 있다. 침수피해를 발생시키는 인자들은 지표면의 침수심, 침수면적 및 지속시간 등이 있으며, 이러한 인자들을 이용하여 침수에 관한 다양한 연구들이 이루어지고 있다. 본 연구에서 연구할 지역은 도림천 지역 대림 1동, 대림 2동, 대림 3동, 신대방동의 일부분 지역을 대상으로, 침수가 발생한 2010년 강우를 활용하여 도림천 지역의 도시침수를 분석을 하였다. 침수가 일어난 원인으로는 관의 허용용량 초과로 인해 침수가 되었던 것으로 보이고 각 지선관거가 간선관거로 합류하는 과정에서 과부하로 인해 주요 간선관거에서 월류가 발생한것으로 판단된다. 이와 같이 내수배제시설 용량의 초과로 인한 침수가 발생하였을 경우 막대한 피해가 발생하게 되고 이를 저감하기 위해서는 침수심 및 침수면적 등 피해정도를 미리 예측하여 관리 할 수 있는 방안에 대한 연구가 필요하다. 본 연구는 도림천의 우수관망을 이용하여 침수해석모형인 SWMM을 활용하여 문제점들을 파악하였으며, 침수방어능력을 향상 시킬 수 있는 방안을 연구하고자 한다.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.176-177
• /
• 2021

In order to compensate for the defects of concrete made using only Portland cement, three-component powder mixed with blast slag and fly ash, and four-component powder concrete mixed with silica fume are being produced. When each of the admixtures is used alone, the above-described excellent performance is expressed and up to 70% of the powder is used. These technologies are also contributing to the reduction of greenhouse gases under Act on Low Carbon. Green Growth. However, calcium hydroxide is consumed as a stimulator or reaction in the case of silica fume, which causes latent hydroponicity of slag, pozzolane reaction, and silica mixtures represented by fly ash. It is known that the consumption of calcium hydroxide affects the alkalinity of concrete. As a result, the carbonation resistance is significantly lower among the durability of concrete. Research on quantification of such effects is insufficient. In this study, an experiment was conducted to quantify calcium hydroxide of the three-component and four-component powder paste using thermal analysis equipment (DTG), and the effect of the mixing amount was discussed.