• Journal of the Korean Wood Science and Technology
• /
• v.32 no.5
• /
• pp.86-92
• /
• 2004

This research was carried out to examine the ethylene gas adsorption and preservation life of white charcoal boards for packaging. Two types of white charcoal board were made of #40-60 charcoal particles and mixed charcoal particles with PVA and MDI resin by wet process. For not only beauty effect but also avoiding stain from touching, white charcoal boards were overlaid with two kinds of overlay material, thin printed paper and non woven fabric. A charcoal board adsorbed ethylene gas much more than the paper and even white charcoal itself. There was no difference between two board types, between overlay treatments, and between overlay materials. Gray mold growth of strawberry arised after 2 days in a paper box and after 4 days in a white charcoal board. Preservation life of white charcoal board box was approximately twice more than that. of a paper box. There was no difference in the ability of keeping freshness between two board types, between overlay treatments, and between overlay materials.

• Proceedings of KOSOMES biannual meeting
• /
• 2008.05a
• /
• pp.181-183
• /
• 2008

본 연구는 회분식과 연속식으로 나누어 숯의 농약 흡착 능력을 평가하였다. 실험에 사용된 농약은 Simazine, Diazinon, Fenitrothion, Butachlor, Malathion이다. 회분식 실험 결과에 따르면, 흑탄과 백탄 양을 0.1g, 1g, 10g, 50g씩 증가시킬수록 농약 성분의 제거율이 높아지는 것으로 나타났으며, 흑탄이 백탄 보다 농약 성분을 잘 제거하는 것으로 나타났다. 특히, 1g 주입시 흑탄은 백탄보다 Malathion을 약 15%, Rutachlor을 약 19%, Fenitrothion을 약 25%씩 제거율이 더 높게 나타난 것으로 보아 흡착이 잘된다고 판단된다. 반면에 회분식에서 Diazinon의 제거율은 상대적으로 낮게 나타났나. 연속식 실험에서도 흑탄이 백탄보다 더 높은 제거율을 나타내었으며, 특히 흑탄 칼럼에서는 흡착 시간$(21\sim31hr)$에서 농약 성분의 평균 제거율을 비교해 본 결과, Simazine은 90%, Fenitrothion은 82%, Butachlor은 81%로 나타났으며, 특히 Diazinon의 제거율은 55%로 나타나 상대적으로 흡착이 잘 되지 않는 것으로 나타났다.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.5
• /
• pp.527-540
• /
• 2018

In this study, the characteristics of the white charcoal from charcoal kilns made for both charcoal production and thermotherapy and from the traditional charcoal kiln were compared and examined. A charcoal kiln for thermotherapy as a secondary purpose was made to minimize environmental problems such as fine dust and harmful gas generated from sealed charcoal kiln in consideration of comfort and safety. White Charcoal produced from the charcoal kiln for both charcoal production and thermotherapy had higher ash and volatile matter and lower fixed carbon than that from the traditional charcoal kiln. The density of the white charcoal produced from the charcoal kiln for both charcoal production and thermotherapy was slightly higher than that of the traditional one, but the equilibrium moisture content and pH were not significantly different. The calorific value, refinement degree, hardness and anatomical structure were not different between the two. It was concluded that the white charcoal produced from the advanced charcoal kiln for thermotherapy as a secondary purpose meets the quality certification standards of Korea Forest Research Institute.

• Journal of Forest and Environmental Science
• /
• v.23 no.1
• /
• pp.57-63
• /
• 2007

Anatomical characteristics of black and white charcoal of Quercus variabilis and Quercus mongolica manufactured by a Korean traditional kiln were investigated by scanning electron microscopy. In both charcoal, the earlywood vessels shrank in tangential direction, whereas the other cells didn't change. However, in the case of latewood vessels, black charcoal did not show tangential direction shrinkage, but white charcoal did. The wood fiber were changed severly in shape due to the excessive shrinkage. Tyloses in early wood vessel were still shown unchanged shape in both charcoals. Cell wall of ray parenchyma was observed and their shapes were severly distorted. Voids between ray parenchyma were observed in white charcoal, which maybe due to high temperature in white charcoal. Moreover, lumen diameters in the uniseriate ray and multiseriate ray were decreased at the high charring temperature. These results showed that the low charcoal yield of the white charcoal compared to the black charcoal was caused by decrease of cell dimensions as well as loss of wood components associated with the carbonization temperature.

• Journal of the Korean Wood Science and Technology
• /
• v.33 no.3 s.131
• /
• pp.22-29
• /
• 2005

This research was carried out not only to examine the proper manufacturing condition for white charcoal board in relation to charcoal particle size and final mat moisture content (FMC), but also to maintain the advantageous properties of white charcoal as a well being building material against the sick house problem. Excellent functional white charcoal board was produced with two groups of FMC 20~25% and FMC 36~60%. The latter showed best results among tested samples in two types which are #40-60type-P15%, M5%, FMC 60% and mixed type-P15%, M5%, FMC36% with non formaldehyde adhesives [MDI (M), poly vinyl acetate emulsion (P)] and three stage pressing cycle of 30-10-$30kgf/cm^2$ (1 min.-1.5 min.-6 min.). The former gave highly acceptable results in two types which are #6 over-M15%FMC25% and mixed type-M25%FMC20%. White charcoal board gave excellent in dimensional stability, gas adsorption and far-infrared emission.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.1
• /
• pp.27-35
• /
• 2010

To evaluate the basic characteristics and adsorption properties of commercial wood charcoal, we investigated the proximate analysis, porosimetry analysis, methylene blue adsorption, removal ratios of formaldehyde, and removal ratio of ethylene gas. Fixed carbon contents of traditional black and white charcoal, and mechanical charcoal were 51.8~76.6%, 72.9~84.6%, and 48.5~80.3%, respectively. Refining degrees of the most traditional black charcoal were 9, and those of white charcoal and mechanical charcoals were zero. Specific surface area of traditional black charcoal was 0.1~13.7 $m^2/g$, which was quite lower than that of white charcoal (53.2~372.6 $m^2/g$) and mechanical charcoals (224.3~464.6 $m^2/g$). Also, amounts of methylene blue adsorption were quite lower in black charcoal (0.53~1.97 mg/g) compared with white charcoal (2.68~7.68 mg/g) and mechanical charcoal (11.63~26.10 mg/g). Removal ratios of formaldehyde of the black charcoal were 11.4~26.7%, which is quite similar to white charcoal (17.9~34.9%) and mechanical charcoal (5.5~25.8%). Removal ratios of ethylene gas for traditional black charcoal, traditional white charcoal, and mechanical charcoal were 2.2~43.5%, 21.7~39.1%, 21.7~39.1%, respectively. There was no significant difference in the removal ratios of formaldehyde and ethylene gas among traditional black charcoal, traditional white charcoal, and mechanical charcoal.

• Proceedings of the Korean Environmental Sciences Society Conference
• /
• 2008.11a
• /
• pp.314-317
• /
• 2008

본 연구에서는 백탄과 흑탄에서 농약의 제거 능력을 비교하였고, 연속 실험을 통하여 시간의 경과에 따른 농약의 제거율 변화를 평가하는 것을 목적으로 하였다. 실험에 사용된 농약은 Simazine, Diazinon, Fenitrothion, Butachlor, Malathion이다. 회분식 실험 결과에 따르면, 흑탄과 백탄 양을 0.1g, 1g, 10g, 50g씩 증가시킬수록 각 농약 성분의 제거율이 높아지는 것으로 나타났으며, 농약성분에 따른 제거율을 보면, Malathion과 Butachlor는 혹탄에서 상대적으로 잘 제거가 되는 것으로 나타났다. 하지만 Diazinon은 흑탄의 회분식 실험, 연속식 실험 모두 상대적으로 낮은 제거율을 보였다.

• Journal of Korea Foresty Energy
• /
• v.25 no.2
• /
• pp.55-63
• /
• 2006

Physicochemical properties and copper (II) adsorption ability of two oakwood and two pinewood charcoals, which were manufactured in traditional mode and commercialized in Korea, were examined pHs of these four wood charcoals were between 9.5 and 9.8. In the elemental contents of the wood charcoal, the contents of carbon atom (C) in the four samples were between 85-90%, while the content of hydrogen atom (H) in pinewood charcoal of the company 'S' was 1.62% and this value was three time higher than those of other samples. For iodine adsorption and specific surface area, the pinewood charcoal sample showed higher values than those of the oakwood charcoals. In the copper (II) ion adsorption in aqueous solution, the adsorption rate was increased by the increase of treated amounts of charcoal, treatment time, and pH.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.1
• /
• pp.64-76
• /
• 2013

In this study, eco-friendly hybrid composite boards were manufactured from green tea, three kinds of charcoals and wood fiber for developing interior materials to reinforce the strength performances and the functionalities in addition to performances of the green tea-wood fiber hybrid boards. The effects for the kind and the component ratio of raw materials on mechanical properties were investigated. Bending strength performances of hybrid composite boards were highest in the hybrid composite boards composed of green tea, fine charcoal and wood fiber on average. However, the difference caused by the kind of charcoals was not large. These values were was markedly improved than those of green tea - wood fiber hybrid composite boards reported in previous researches. And it was found that the bending strength performance decreased with increasing component ratios of green tea and charcoals. The difference between urea resins used as the binder showed the higher value in hybrid composite boards using $E_1$ grade urea resin than in those using $E_0$ grade urea resin, but the difference between hybrid composite boards manufactured by both resins decreased markedly than the green tea - wood fiber hybrid composite boards reported in previous research. The internal bond strength of hybrid composite boards was in the order of hybrid composite boards with fine charcoal, activated charcoal and black charcoal, and it was found that the hybrid composite boards with fine charcoal had a similar values to control boards composed of only wood fiber.

• Korean Chemical Engineering Research
• /
• v.60 no.2
• /
• pp.208-216
• /
• 2022

Surface morphology and adsorption characteristics of black and white charcoals prepared from Korean traditional kiln were quantitatively analyzed. TGA and elemental analysis of charcoals were different from produced kiln, and thermal degradation temperature and carbon content of white charcoals were apparently higher than those of black charcoals. Surface morphology shows the activation progressed through the longitudinal direction of woods and new micropores were developed to radial direction on the surface of macropores as the furthermore activation resulting in the pore connection. BET adsorption isotherms show that there are low-pressure hysteresis due to the no desorption of adsorbates, which resulted in unique Type of charcoals overlapping Type I and Type IV. Such a low-pressure hysteresis is occurred from expansion of adsorbates, which were embedded in the micropore entrances and did not get out during the desorption run. The characteristics of charcoals such as specific surface area and pore size distribution did not show correct values depending on not only produced company but also sampling sites of one piece of charcoal. Therefore, it is not easy to suggest the quantitative characteristics of charcoals prepared from Korean traditional kiln. On the other hand, preparation the quality standard of charcoal is necessary for their special uses such as adsorbent.