• Journal of the Korea Concrete Institute
• /
• v.28 no.5
• /
• pp.593-600
• /
• 2016

The paper presented investigates the effects of kaolinite on strength properties of alkali-activated multi-component cement. The binders of this study was blended of ground granulated blast furnace slag (GGBFS), fly ash (FA), silica fume (SF) and kaolinite (KA). In this study, the specimens of combination of 20%~70% GGBFS, 10%~60% FA, 10% SF (constant ratio) and 10%~50% KA binder were used for strength properties tests. The water/binder ratio was 0.5. The binders (GGBFS + FA + SF + KA) was activated by sodium hydroxide (NaOH) and sodium silicate ($Na_2SiO_3$) was 10% by total binder weight (10% NaOH + 10% $Na_2SiO_3$). The research carried out is on the compressive strength, water absorption, ultrasonic pulse velocity (UPV) and X-ray diffraction (XRD). The compressive strength decreased as the contents of KA increase. One of the major reason for this is the low reactivity of KA compared with other raw materials used as precursors such as GGBFS or FA. The presence of remaining KA indicates that the initially used quantity has not fully reacted during hydration. Moreover, the results have indicated that increased of KA contents decreased UPV under all experimental conditions. The drying shrinkage and water absorption increased as the content of KA increase. Test result clearly showed that the strength development of multi-component blended cement were significantly dependent on the content of KA and GGBFS.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.533-536
• /
• 2008

Recently, in Korea, there has been an increasing number of research papers published which are to improve durability of concrete, particularly by analyzing correlation between diffusivity of chloride and porosity/pore size distribution. In these studies, such test methods as mercury intrusion porosimetry(MIP), gas adsorption or image analysis method are used to analyze the microstructure of materials while MIP is most widely used for concrete. This study analyzes the results of porosity and pore size distribution of paste and concrete adding fly ash or blast furnace slag by using MIP equipment which is widely used for determining micro-porosity structure of cementitious materials. A variation in porosity and pore size distribution at the curing day 3, 7 and 28 has been observed by using MIP equipment for cement paste 35%, 40%, 45%, 50%, 55%, 60% of W/C when using $300kg/m^3$ of cement, 35%, 45%, 55% of W/C when replaced 60% with blast-furnace slag, and 35%, 45%, 55% of W/C when replaced 30% with fly ash. For long-term water cured normal OPC concrete and mixed concrete replaced 60% with blast-furnace slag powder, micro-structure of the sample has been analyzed by using MIP equipment when W/C indicated 40%, 45%, 50% respectively and the binder varied $300kg/m^3$, $350kg/m^3$, $400kg/m^3$, and $450kg/m^3$.

• Journal of the Korea Concrete Institute
• /
• v.29 no.1
• /
• pp.101-107
• /
• 2017

This study aimed to conduct the basic analysis on the fractal characteristics of cementitious materials. The pore structure of cement paste incorporating ground granulated blast furnace slag (GGBFS) was measured using mercury intrusion porosimetry (MIP) and the fractal characteristics were investigated using different models. Because the pore structure of GGBFS-blended cement paste is an irregular system in the various range from nanometer to millimeter, the characteristics of pore region in the different scale may not be adequately described when the fractal dimension was calculated over the whole scale range. While Zhang and Li model enabled analyzing the fraction dimension of pore structure over the three divided scale ranges of micro, small capillary and macro regions, Ji el al. model refined analysis on the fractal characteristics of micro pore region consisting of micro I region corresponding to gel pores and micro II region corresponding to small capillary pores. As the pore size decreased, both models suggested that the pore surface of micro region became more irregular than macro region and the complexity of pores increased.

• Journal of the Korea Institute of Building Construction
• /
• v.21 no.1
• /
• pp.1-10
• /
• 2021

The purpose of this study is to evaluate the improvement of flow, compressive and flexural strengths of polymer cement mortar(PCM) using SBR latex mixed with blast-furnace slag and fly ash. The test specimens were prepared with SBR polymer dispersion, two types of admixture (blast-furnace slag and fly ash), five polymer-cement ratios (P/C; 0, 5, 10, 15 and 20%), and six admixture contents (0, 3, 5, 10, 15 and 20%), plain cement mortar was also made for comparison. From the test results, the flow of PCM was significantly improved compared to ordinary cement mortar, but the flow was slightly reduced when mixed with blast-furnace slag, and the flow was similar to PCM when mixed with fly ash. In addition, the compressive strength of PCM mixed with admixtures was significantly improved, but the flexural strength did not improve except for some mortars. It can be stated that the optimum mix proportions of PCM using SBR with admixture contents 10 to 15% and P/C 10% for the compressive strength improvement, and P/C 20% for flexural strength improvement are recommended respectively in this study.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.804-810
• /
• 2003

The fine powder produced by heating and grinding of the waste concrete in the waste construction was investigated whether utilize as substitution raw material of SiO$_2$, CaO, and Al$_2$O$_3$ source for OPC clinker manufacture is possible or not. In order to synthesize OPC clinker, limestone, shale, converter slag and fly ash were used as main raw materials, and modulus was fixed LSF 91.0, SM 2.60, IM 1.60. The synthesized clinkers were characterized. The Main products of synthesized clinker were C$_3$S, ${\beta}$-C$_2$S, C$_3$A, C$_4$AF as OPC clinker at 1,43$^{\circ}C$. As a result of TG-DTA and burnability index(B.U) analysis of each raw mixtures, the formation temperature of clinker phases was similar and B.I was showed easy burning as 48.6∼51.4.

• Korean Journal of Environmental Agriculture
• /
• v.26 no.3
• /
• pp.259-266
• /
• 2007

Enormous amount of zeolite by-products as a fine powder have been produced while manufacturing commercial zeolite products. Granulation of the zeolite by-products is necessary in order for them to be recycled as soil conditioners or absorbent for various environmental contaminants due to the limitations inherent from their physical properties. We granulated the zeolite powders using Portland cement as a cementing agent and characterized the physical and chemical properties of the granulated zeolite product. The experimental natural zeolite had a Si/Al ratio of 4.8 and CEC of 68.1 $cmol_c\;kg^{-1}$. The X-ray diffractometry (XRD) revealed that clinoptilolite and mordenite were the major minerals of natural zeolite. Smectite, feldspar and quartz also existed as secondary minerals. Optimum conditions of granulated zeolite production occurred when natural zeolite was mixed with Portland cement at a 4:1 ratio and granulated using the extruder, left to harden for one month at $25^{\circ}C$ and treated at $400^{\circ}C$ for 3 hours. The wide spectra of XRD revealed that the granulated zeolite had amorphous oxide minerals. The alkali- or thermal-treated natural zeolite exhibited pH-dependent charge properties. The major minerals of the granulated zeolite were clinoptilolite, mordenite and tobermorite. The buffering capacity and charge density of the granulated zeolite were greater than those of natural zeolite.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.2
• /
• pp.109-115
• /
• 2018

Since the current method of SCW cement milk pouring method uses one to one ratio of cement milk with OPC, there are some problems such as drying shrinkage, increased cost, difficulty of controlling mix proportions for various conditions of applied soil, and precipitation of $Cr^{6+}$ due to the excessively used cement. Specifically, in aspect of sustainability issues of cement manufacturing, the consumption of cement should be reduced. Hence, in this research, as a replacement of cement for SCW method, blast furnace slag with sulfate or alkali as a stimulant, and expansive admixture were used. By using blast furnace slag as a hardening composite of SCW, there are many advantages such as free controllable mix proportions, rapid setting time with less mud occurrence, less cost with less energy for mixing, constant strength development, and less precipitation of $Cr^{6+}$. Regarding the alternative composites for SCW, in this research, durability and chloride resistance were evaluated.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.3
• /
• pp.149-156
• /
• 1997

In order to improve compressive strength of cement mortar, powder admixture(FAS) was mmufactured by mixing fly ash. Il-anhydite and silica hume, and superplasticizer was used for the control of fluidity reduction with the use of this admixture. Cement was substituted by 10, 20wt% of FAS respectively. At W/S = 0.40, the fluidity of' cement paste substituted by PAS was decreased. NSF and NT-2 were very effective fbr the control of fluidity reduction. As the particle size of U -anhydrite was fine, the fluidity of cement mortar was increased. The fluidity reduction of cement mortar substituted by 10wt% of FAS was controlled. The compressive strength of cement mortar substituted by 10wt% of FAS showed higher. value than that of 20wt%, expecially specimen(C1) substituted by 10wt% of $\gamma$ had the highest compressive strength value.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.365-368
• /
• 2008

This research is related to 240MPa ultra-high strength concrete(UHSC) with extremely loss W/B ratio. For this development, High flow cement is mainly used which has a short reaction rate due to the high blaine and high early strength, which can make greater fluidity in case of very low W/C ratio. It made the best mixture using the mineral admixtures silica fume, slag powder and special admixture. For dispersibility and homogeneity of cement binder, cement of premix type is produced using omni-mixer. Moreover, it ensures the fluidity of ultra-high strength concrete(UHSC). For having a good fire performance, we made an experiment special coarse aggregate. As a result, we got 180MPa in case of water curing, 200MPa in case of steam curing and uniform UHSC of 240MPa in case of a special curing method.

• Journal of the Korea Institute of Building Construction
• /
• v.20 no.1
• /
• pp.19-26
• /
• 2020

This study aimed to develop non-sintered cement that could replace portland cement which emits large amount of carbon dioxide during firing process. For this purpose, ground granulated blast furnace slag, type c fly ash and slaked lime were used. In addition, through the experimental results, the characteristics of the non-sintered cement binders according to the mixing ratios will be identified, and the utilization plans for the precast concrete products will be presented. In this experiment, non-sintered cement binders using industrial by-products were prepared to compare the flexural strength and compressive strength of each of the 3, 7 and 28 days. As a result, the results satisfy the KS of the target product proposed in this study. Therefore, this study presents the possibility of using precast concrete products by developing non-sintered cement binders using industrial by-products.