6063-T5 alloys are tested in laboratory air, water and 3% NaCl solution to investigate the effects of corrosive environment on the retardation behavior through single overload fatigue test. Also, the fatigue crack propagation and the crack closure behavior are studied. The results obtained in this experimental study are summarized as follows: 1) Behaviors of fatigue crack growth retardation are observed in water and 3% NaCl solution as they do in air. The number of delay cycles and the size of affected region by single overload decrease greatly in water and 3% NaCl compared with those in air. 2) In fractographic results, the overload marking by single overload appear remarkably in air, but indistinctly in water and 3% NaCl solution. 3) The effect of crack closure on crack propagation is most remarkable in the beginning of crack propagation. With crack propagation, the crack closure level and its effect decrease greatly.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.202-207
• /
• 2004

An elastic-plastic finite element analysis of fatigue crack closure is performed for plane strain conditions. The stabilization behavior of crack opening level and the effect of mesh size on the crack opening stress are investigated. In order to obtain a stabilized crack opening level for plane strain conditions, the crack must be advanced through approximately four times the initial monotonic plastic zone. The crack opening load tends to increase with the decrease of mesh size. The mesh size nearly equal to the theoretical plane strain cyclic plastic zone size may provide reasonable numerical results comparable with experimental crack opening data. The crack opening behavior is influenced by the crack growth increment and discontinuous opening behavior is observed. A procedure to predict the most appropriate mesh size for different stress ratio is suggested. Crack opening loads predicted by the FE analysis based on the procedure suggested resulted in good agreement with experimental ones within the error of 5 %. Effect of the distance behind the crack tip on the crack opening load determined by the ASTM compliance offset method based on the load-displacement relation and by the rotational offset method based on the load-differential displacement relation is investigated. Optimal gage location and method to determine the crack opening load is suggested.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.7
• /
• pp.2234-2245
• /
• 1996

In this study residual stress in weldment was considered about the effect on the fatigue propagation and about the effect of redistribution of residual stress. Then, fatigue tests were conducted by the center notched specimens machined with welded plate. The residual stress and its redistribution after the crack growth were measured by the magnetizing stress indicator and hole-drilling method. Fatigue crack propagation was estimated by the specimens having residual stress redistributed after the cracks growth and having the effects of crack closure. Crack growth rates were predicted and compared with experimental results. It had been found that the predicted crack propagation rates have a good agreement with experimental results when the redistribution of residual stress was considerd.

• Journal of Power System Engineering
• /
• v.5 no.2
• /
• pp.50-56
• /
• 2001

In this study, the effect of specimen thickness and stress ratio on fatigue crack growth in S45C steel was investigated. Acoustic emission was monitored during the fatigue crack growth test. Both crack closure and AE technique were used in assessing fatigue crack growth behavior. Constant amplitude loading tests were performed on CT type specimen with three different thicknesses and stress ratios. Crack closure was investigated to explain the influence of specimen thickness and stress ratio on the fatigue crack growth in the second growth region. The crack closure effect was decreased with specimen thickness and stress ratio.

• Journal of the Korean Society for Precision Engineering
• /
• v.22 no.6 s.171
• /
• pp.152-158
• /
• 2005

The stress conditions acting on the practical structure are complex, and thus most cracks existing in the practical structures are under mixed-mode loading conditions. The effect of shear load component of mixed-mode loading acts more greatly in the stage of crack initiation and initial propagation than crack propagation stage. Hence, research on the behavior in the stage of crack initiation and initial propagation need to be examined in order to evaluate behavior of mixed-mode fatigue cracks. In this study, the crack tip displacement(CTD) was measured by using the direct measuring method(DMM). We examined the behavior at crack tip by determining crack opening load$(P_{op})$. From the test results, the propagation behavior of mixed-mode fatigue cracks was evaluated by considering mixed-mode crack closure. Also, we examined the characteristic of crack propagation under mixed-mode loading with crack propagation direction.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.2
• /
• pp.26-33
• /
• 1997

In this study effect of residual stress and its redistribution in weldment on the fatigue crack propagation was investigated. Fatigue tests were conducted by the center notched specimens machined with welded plate. The residual stress and its redistribution after the crack growth were measured by the magnetizing stress indicator and hole-drilling method. Fatigue crack propagation was estimated by the specimens having residual stress redistributed after the cracks growth and having the effects of crack closure. Crack growth rates were predicted and compared with experimental results. It had been found that the predicted crack propagation rates have a good agreement with experimental results when the redistribution of residual stress was considered.

• Journal of the Korean Society for Precision Engineering
• /
• v.7 no.4
• /
• pp.55-64
• /
• 1990

The fatigue crack growth behavior of physically-short cracks(0.2${\Delta}K$ with $da/dN<1{\times}10^{-7}m/cycle$. The transition crack lengths where similtude with ${\Delta}K$ existed was between 1 and 2mm. The effective stress intensity factor range based on COD measurements gave better correlation between the physically-short and long cracks. Thus it can be considered that the crack closure effect is one of the main factors which causes the differences between these two cracks.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1996.11a
• /
• pp.908-912
• /
• 1996

FRMLs consist of thin sheets of high strength metal, which are laminated using a structural adhesive and high strength fibers. ARALL(Aramid-fiber Reinforced Aluminum alloy Laminates) of FRMLs is a new class of hybrid material. HERALL(Heracron Reinforced Aluminum Laminate) i.e. domestic ARALL is made of homemade aramid fibers, adhesives and adhesive technique. Domestic aramid fiber is Heracron manufactured by KOLON and domestic adhesive is epoxy resin manufactured by Han Kuk Fiber. In this study, Fatigue crack propagation behavior was examined in a 2024-T3 aluminum alloy/aramid-fiber epoxy 3/2 laminated composites, HERALL and ARAL $L^{ⓡ}$-2 LAMINATE comparing with 2024-T3 aluminum alloy. The extrinsic toughening mechanisms in HERALL and ARALL were examined, the crack bridging behavior of fibers was analyzed by new algorithm, which measures crack bridging stress, and the crack bridging zone length was measured.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.205-210
• /
• 2001

Fatigue crack growth tests were carried out using high manganese cast steel under constant amplitude loading. Average crystal grain sizes of the material are $200{\mu}m$ and $1000{\mu}m$. For this material, ${\Delta}K_{th}$ is about $8MPa{\sqrt{m}}$ which is quiet large as compared to the general structural steels and the crack growth rate is lower than the general structural steels especilly in the low ${\Delta}K$ regsion. The reason of this behavior is crack closure due to fracture surface roughness and fretting oxide. The relationship between da/dN and the ${\Delta}K_{eq}$ was represented by narrow band regardless of the stress ratio.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.6
• /
• pp.1343-1349
• /
• 1988

In this study, it is investigated for the effects of stress ratio and grain size on fatigue crack growth behavior and crack closure, in ferrite-martensite dual phase steels. The results obtained are as follows ; .DELTA. $K_{th}$ is independent of the ferrite grain size, but decreases with increasing stress ratio. The relation between .DELTA. $K_{th}$ and stress ratio R is as follows : .DELTA. $K_{th}$ =15.1(1-0.95R). But (.DELTA. $K_{eff}$)$_{th}$ in terms of crack closure is approximately 2.5 MPa.root.m. Also, variation of the degree of crack deflection to crack tip opening displacement at the minimum load is considered as a parameter of crack closure.e.e.