• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.239-240
• /
• 2008

The $V_{1.9}W_{0.1}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.9}W_{0.1}O_5$ thin films annealed at $400^{\circ}C$ were 39.6, with a dielectric loss of 0.255, respectively. Also, the TCR values of the $V_{1.9}W_{0.1}O_5$ thin films annealed at $400^{\circ}C$ were about -3.15%/K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.248-249
• /
• 2007

The $V_{1.9}W_{0.1}O_5$ thin films deposited on Pt/Ti/$SiO_2$/Si substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.9}W_{0.1}O_5$ thin films annealed at $300^{\circ}C$ were 37.7, with a dielectric loss of 2.535, respectively. Also, the TCR values of the $V_{1.9}W_{0.1}O_5$ thin films annealed at $300^{\circ}C$ were about -3.7%/K.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1248-1249
• /
• 2008

The $V_{1.8}W_{0.2}O_5$ thin films deposited on $Pt/Ti/SiO_2/Si$ substrates by RF sputtering method exhibited fairly good TCR and dielectric properties. It was found that film crystallinity, dielectric properties, and TCR properties were strongly dependent upon the annealing temperature. The dielectric constants of the $V_{1.8}W_{0.2}O_5$ thin films annealed at 400$^{\circ}C$ were 38.11, with a dielectric loss of 0.134, respectively. Also, the TCR values of the $V_{1.8}W_{0.2}O_5$ thin films annealed at 400$^{\circ}C$ were about -3.15%/K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.104-107
• /
• 2001

The fabricated La-modified lead titanate (PLT) thin flirt without poling treatment was investigated for modulation frequency dependence of pyroelectric properties by the dynamic method. $Pb_{1-x}La_{x}Ti_{1-x/4}O_3$PLT (x=0.1) thin film having 10 mol% La content was deposited on a Pt/$TiO_{x}$/$SiO_2$/Si substrate by sol-gel method. The PLT(10) thin film exhibits a relatively excellent dielectric property. The pyroelectric coefficient (p) of the PLT(10) thin film is 6.6 x $10^{-9}$C/$\textrm{cm}^2$.K without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are 1.03${\times}$$10^{-11}$/C.cm/J and 1.46 x $10^{-9}$C.cm/J, respectively. The PLT(10) thin film has voltage responsivity ($R_{V}$) of 5.15 V/W at 8 Hz. Noise equivalent power (NEP) and specific detectivity (D＊) of the PLT(10) thin film are 9.93 x $10^{-8}$W/Hz$^{1/2}$ and 1.81 x $10^{6}$ cmHz$^{1/2}$/W at the same frequency of 100 Hz, respectively. The results means that PLT thin film having 10 mol % La content is suitable for the sensing materials of pyroelectric IR sensors.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.39 no.12
• /
• pp.1008-1015
• /
• 2002

The fabricated La-modified lead titanate (PLT) thin film without poling treatment was investigated for modulation frequency dependence of pyroelectric properties by the dynamic method. $Pb_{l-x}La_{x}Ti_{l-x/4}O_3$(x=0.1) (PLT(10)) thin film haying 10 mol% La content was deposited on a Pt/$TiO_{x}$/$SiO_2$/Si substrate by sol-gel method. The PLT(10) thin film exhibits a relatively excellent dielectric property. The pyroelectric coefficient (p) of the PLT(10) thin film is 6.6 x $10^{-9}C$$textrm{cm}^2$$.$K without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are 1.03 x $10^{-11}C$.cm/J and 1.46 x $10^{-10}C$.cm/J, respectively The PLT(10) thin film has voltage responsivity (RV) of 5.IS V/W at 8 Hz. Noise equivalent power (NEP) and specific detectivity ($D^{*}$) of the PLT(10) thin film are 9.93 x $10^{-8}$W/$Hz^{1/2}$ and 1.81 x $10^{6}$cm.$Hz^{1/2}$/W at the same frequency of 100 Hz,, respectively The results means that PLT thin film having 10 mol% La content is suitable for the sensing materials of pyroelectric IR sensors.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.104-107
• /
• 2001

The fabricated La-modified lead titanate (PLT) thin flim without paling treatment was investigated for modulation frequency dependence of pyroelectric properties by the dynamic method. $Pb_{1-x}La_{x}Ti_{1-x/4}O_{3}$ PLT (x=0.1) thin film having 10 mol% La content was deposited on a $Pt/TiO_{x}/SiO_{2}/Si$ substrate by sol-gel method. The PLT(10) thin film exhibits a relatively excellent dielectric property. The pyroelectric coefficient (p) of the PLT(10) thin film is $6.6{\times}10^{-9}C/cm_{2}\cdot K$ without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are $1.03{\times}10^{-11}C\cdot cm/J$ and $1.46\times 10^{-9}C\cdot cm/J$, respectively. The PLT(10) thin film has voltage responsivity (Rv) of 5.15 V/W at 8 Hz. Noise equivalent power (NEP) and specific detectivity (D*) of the PLT(10) thin film are$9.93{\times}10^{-8}W/Hz^{1/2}$ and $1.81\times 10^{6}cmHz^{1/2}/W$ at the same frequency of 100 Hz, respectively. The results means that PLT thin film having 10 mol % La content is suitable for the sensing materials of pyroelectric IR sensors.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.31A no.9
• /
• pp.89-95
• /
• 1994

BaTiO$_{x}$ thin film as insulator and ZnS:Mn film as phosphour layer for thin film electrouminescent device have been deposited by thermal evalporation and dependence of electrical and opeical characeristics have been studied. The optimum deposition conditions for the BaTiO$_{x}$ thin film are such that BaTiO$_{3}$/TiO$_{2}$ mixing ratio was 0.7, sub strate temperature was 100 $^{\circ}C$ and annealing time was 1 hour at 300 $^{\circ}C$. In this case, the dielectric constant of BaTiO$_{x}$ thin film fabricated under those optimum conditions was 26, and for AnS:Mn thin films, the crystallization was done well and the deposition rate was 1300 $\AA$/min when substrate temperature was 200$^{\circ}C$. Thin film Electroluminescent devices were fabricated using BaTiO$_{x}$ and AnS:Mn thin films. The luminescence threshold voltage of device was 41.5 V and brightness was 1.2${\mu}W/cm^{2}$ at appied voltage of 50 V.

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.472-478
• /
• 1998

Ferroelectric SrBi2Ta2O9(SBT) films were deposited on Pt/Ti/SiO2/Si substrates at 50$0^{\circ}C$ using a sintered SBT target Bi and Ta targets by modified rf magnetron sputtering and then were annealed at 80$0^{\circ}C$ for 10min in oxygen ambinet(760 torr) The composition of the SBT films could be easily controlled using the mul-ti-targets. The film composition of {{{{ {Sr }_{0.8 } {Bi }_{2.9 } {Ta}_{2.0 } {O }_{9 } }} was obtained with SBTd sputtering power of 100 W Bi of 25W and Ta of 10 W. A 250nm thick SBT films exhibited a dense and uniform microstructure and showed the remanent polarization(Pr) of 14.4 $\mu$C/cm2 and the coercive field({{{{ {E }_{c } }})of 60 kV/cm at applied voltage of 5 V. The SBT films show practically no polarization fatigue up to {{{{ {10 }_{10 } }} cycles under 5V bipolar pulse. The retention characteristics of the SBT films looked very promising and the leakage current density of the SBT films was about 1.23$\times${{{{ {10 }^{-7 } }}A/c{{{{ {m }^{2 } }} at 120kV/cm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.68-69
• /
• 2005

Low temperature ($\leq900^{\circ}C$) sintering piezoelectric ceramics $0.01Pb(Mg_{1/2}W_{1/2})O_3$-0.41Pb$(Ni_{1/3}Nb_{2/3})O_3-0.35PbTiO_3-0.23PbZrO_3+0.1wt%Y_2O_3+xwt%ZnO$ $(0{\leq}x{\leq}2.5)$ have been developed and investigated. The electromechanical coupling coefficient ($k_p$), piezoelectric constant ($d_{33}$), and mechanical quality factor ($Q_m$) have been measured to characterize the piezoelectric materials system. When 2.0 wt% ZnO is added, the properties of the system, $d_{33}$ = 559 pC/N, $k_p$ = 55.0 % and $Q_m$ = 73.4 are obtained which are very suitable for piezoelectric actuators. A bending mode multilayer actuator has been also developed using the materials which size is $27(L)\times9(W)\times1.07(t)mm^3$. The actuators are fabricated by multilayer ceramic (MLC) process and consist of24 layers and each layer thickness is $35{\mu}m$. At this time, the displacement of actuator was $100{\mu}m$ at 28V.

• Journal of the Korean institute of surface engineering
• /
• v.37 no.6
• /
• pp.307-312
• /
• 2004

Extensive efforts have been made in an attempt to utilize photocatalytic properties of $TiO_2$ in visible range. $TiO_2$ and TiO-N thin films were made by the DC reactive magnetron sputtering method at $300^{\circ}C$. Various gases (Ar, $O_2$ and $N_2$) were used and Ti target was impressed by 0.6 kW-5.8 kW power range. The hysteresis phenomenon of the $TiO_2$ thin film as a function of the discharge voltage characteristic was observed to be higher as applied power increases. That of TiO-N thin film was occurred at the 5.8 kW power. The cross section and surface roughness of thin films were observed by FE-SEM and AFM. Average surface roughness of TiO-N thin film was observed as $15.9\AA$ and that of $TiO_2$ as $13.2\AA$. The crystal phases of both $TiO_2$ and TiO-N thin films were found to be anatase structure. The atomic $\beta$-N (396 eV peak in N 1s XPS) was shown in the rutile crystal of TiO-N and was considered acting as the origin of wavelength shift to the visible light.