• Journal of the Korean Ceramic Society
• /
• v.34 no.8
• /
• pp.908-913
• /
• 1997

Multilayer NbCxC1-x/Y2O3/Ti were sputter-coated on the alumina substrate, starting with a 0.7 ㎛ thick NbCxC1-x layer grown on substrate, followed by 0.7 ㎛ thick Y2O3 layer and 1 ㎛ thick Ti layer. To find out the optimum conditions for thickness uniformity and adhesion, sputtering works have been done with the variation of sputtering power and Ar pressure. After vacuum annealing at 950℃ and 1000℃, the thermal stability of the NbCxC1-x/Y2O3/Ti coated alumina substrates has been investigated by peel off test. The coating scheme didn't cause any debonded layer after an annealing at 950℃ for 3hrs. However, it was peeled off after annealing at 1000℃ for 3hr. It was found that the thermal stability of Al2O3/NbCxC1-x/Y2O3/Ti coating scheme changed with the NbCxC1-x composition.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.3
• /
• pp.503-507
• /
• 1998

Sintering behavior and dielectric peroperties of $xCaTiO_3-La(Zn_{1/2}Ti_{1/2})O_3$ system were investigated for better understanding of the microwave dielectric materials. In $xCaTiO_3-(1-x)La(Zn_{1/2}Ti_{1/2})O_3$ systems, solid solution type was focused as a function of composition(x=0.4-0.6) and sintered density. With increasing the sintered density, the relative dielectric constant was decreased and Q value was increased and then saturated. In solid solution type, dielectric constant was increased with increasing $CaTiO_3$ content. In $0.5\;CaTiO_3-0.5\; La(Zn_{1/2}Ti_{1/2})O_3$ case, dielectric constant(=48) and temperature coefficient of resonace frequency$(=-1 ppm/^{\circ}C$) were obtained.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1459-1461
• /
• 1997

The microwave dielectric ceramic properties of $CaTiO_3-(Li_{1/2}Nd_{1/2})TiO_3$ were investigated. The solid solution of $CaTiO_3-(Li_{1/2}Nd_{1/2})TiO_3$ had the perovskite structure in the range of all composition. The dielectric constant and temperature coefficient of resonant frequency of solid solution were decreased with the contend of $(Li_{1/2}Nd_{1/2})TiO_3$, whereas, the $Q{\times}f$ value was increased. In the $(1-X)CaTiO_3-X(Li_{1/2}Nd_{1/2})TiO_3$ system, the microwave properties could be controlled by the variation of X, X is weight fraction. Typical value of K=119, $Q{\times}f=2970$ and $TCF=14ppm/^{\circ}C$ were obtained for $0.2CaTiO_3-0.8(Li_{1/2}Nd_{1/2})TiO_3$.

• Journal of Environmental Science International
• /
• v.15 no.3
• /
• pp.221-227
• /
• 2006

Oxidative TCE decomposition over $TiO_2$-supported single and complex metal oxide catalysts has been conducted using a continuous flow type fixed-bed reactor system. Different types of commercial $TiO_2$ were used for obtaining the supported catalysts via an incipient wetness technique. Among a variety of titanias and metal oxides used, a DT51D $TiO_2\;and\;CrO_x$ would be the respective promising support and active ingredient for the oxidative TCE decomposition. The $TiO_2-based\;CrO_x$ catalyst gave a significant dependence of the catalytic activity in TCE oxidation reaction on the metal loadings. The use of high $CrO_x$ contents for preparing $CrO_x/TiO_2$ catalysts might produce $Cr_2O_3$ crystallites on the surface of $TiO_2$, thereby decreasing catalytic performance in the oxidative decomposition at low reaction temperatures. Supported $CrO_x$-based bimetallic oxide systems offered a very useful approach to lower the $CrO_x$ amounts without any loss in their catalytic activity for the catalytic TCE oxidation and to minimize the formation of Cl-containing organic products in the course of the catalytic reaction.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.1
• /
• pp.42-48
• /
• 1998

Synthesis of PLT($Pb_{1-X}La_{2X/3}TiO_3$, x=0.1~0.3) powders was carried out by hydrothermal method. Optimal conditions for synthesis were $250^{\circ}C$ of reaction temperature, 8M-KOH solution of hydrothermal solvent and 12 hrs reaction time, and the monolithic $Pb_{1-X}La_{2X/3}TiO_3$ particles were obtained with the composition of x$\leq$0.2. The tetragonality(c/a) and the phase transition temperature were decreased by the increment of the $La_2O_3$ contents in PLT solid solutions, and the Curie temperature of the $Pb_{1-X}La_{2X/3}TiO_3$(x=0.2) was $400^{\circ}C$. The shape of the synthesized particles were nearly spherical and the size was in the 20~200 nm range.

• Applied Chemistry for Engineering
• /
• v.19 no.3
• /
• pp.270-276
• /
• 2008

$N_2$ doped $TiO_2$ nano-sized powder was prepared using a DC arc plasma jet and investigated with XRD, BET, SEM, TEM, and photo-catalytic decomposition. Recently the research interest about the nano-sized $TiO_2$ powder has been increased to improve its photo-catalytic activity for the removal of environmental pollutants. Nitrogen gas, reacting gas, and titanium tetrachloride ($TiCl_4$) were used as the raw materials and injected into the plasma reactor to synthesize the $N_2$ doped $TiO_2$ power. The particle size and XRD peaks of the synthesized powder were analyzed as a function of the flow rate of the nitrogen gas. Also, the characteristics of the photo-catalytic decomposition using the prepared powder were studied. For comparing the photo-catalytic decomposition performance of $TiO_2$ powder with that of $TiO_2$ coating, $TiO_2$ thin films were prepared by the spin coating and the pulsed laser deposition. For the results of the acetaldehyde decomposition, the photo-catalytic activity of $TiO_{2-x}N_x$ powder was higher than that of the pure $TiO_2$ powder in the visible light region. For the methylene blue decomposition, the decomposition efficiency of $TiO_2$ powder was also higher than that of $TiO_2$ film.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.558-567
• /
• 2001

본 연구에서는 알콕사이드를 전구물질로 하는 졸겔공정을 이용하여 Bi 과잉 12 mol%의 조성인 B $i_4$ $Ti_3$ $O_{12}$ 박막과 B $i_4$ $Ti_{3-x}$T $a_{x}$ $O_{12}$(x=0.1, 0.2, 0.3) 박막을 제조하였다. XPS 분석에 따르면 Ta 치환 x=0.2에서 Bi 4f의 photoemission 곡선이 낮은 결합에너지로 이동하였고 피크 강도가 감소하는 현상이 관측되었다. 이는 x=0.1과 0.2 사이에서 Bi-O 결합이 길어져 인장상태 하에 있었음을 나타내었다. B $i_4$ $Ti_3$ $O_{12}$(BIT) 박막의 유전상수와 유전손실은 100 kHz에서 340, 0.05이었고, B $i_4$ $Ti_{3-x}$T $a_{x}$ $O_{12}$ 박막에서 이들 값은 x=0.1에서 가장 높았으며, 각각 480, 0.13이었다. B $i_4$ $Ti_3$ $O_{12}$ 박막의 잔류분극과 항전계는 1.24$\mu$C/$ extrm{cm}^2$, 31.4 kV/cm 이었으나, Ta 치환 x=0.2에서 이들 값은 각각 19.7$\mu$C/$\textrm{cm}^2$, 49.5 kV/cm 에 이르렀다. 또한, B $i_4$ $Ti_3$ $O_{12}$ 박막의 누설전류 밀도는 ~$10^{-6}$ A/$\textrm{cm}^2$ 정도이었으며, Ta 치환은 누설전류를 감소시켜 Ta 치환 x=0.2 이상에서 BIT 박막에 비해 한 차수 정도 낮아졌다. Ta 치환에 따른 B $i_4$ $Ti_3$ $O_{12}$ 전기 물성에서 변화는 Bi-O 결합에서 관측된 인장상태로의 전이와 연관성이 있었으며, 덧붙여 치환에서 생성된 전자에 의한 정공보상이 이에 영향을 끼쳤다. 정공보상이 이에 영향을 끼쳤다.끼쳤다.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.51 no.12
• /
• pp.567-572
• /
• 2002

In these days, diesel vehicle or power plant emits $NO_X\; and SO_2$ which cause air pollution like acid-rain, ozone layer destroy and optical smoke, therefore there are many kinds of methods considered for removing them such as SCR, catalyst, plasma process, and plasma-catalyst hybrid process. T$TiO_2$ is commonly used as catalyst to remove $NO_X$ gas because it have very excellent chemical characteristic as photo catalyst. In this paper, $NO_X$ sensing characteristic of $TiO_2$ thin film deposited by R.F Magnetron sputtering is investigated. A finger shaped electrode on $Al_2$O$_3$ substrate is designed and $TiO_2$ is deposited on the electrode by the magnetron sputtering deposition system. Chemical composition of the deposited $TiO_2$ thin film is $TiO_{1.9}$ by RBS analysis. When the UV is irradiated on it with flowing air, capacitance of $TiO_2$ thin film increases, however, when NO gas is put into the system with air, it immediately decreases because of photo chemical reaction. and it monotonously decreases with increasing NO concentration.

• Journal of Environmental Science International
• /
• v.17 no.8
• /
• pp.933-941
• /
• 2008

The formation of $Co_nTiO_{n+2}$ compounds, i.e., $CoTiO_3$ and $CO_2TiO_4$, in a 5wt% $CoO_x/TiO_2$ catalyst after calcination at different temperatures has been characterized via scanning electron microscopy (SEM), Raman and X-ray photoelectron spectroscopy (XPS) measurements to verify our earlier model associated with $CO_3O_4$ nanoparticles present in the catalyst, and laboratory-synthesized $Co_nTiO_{n+2}$ chemicals have been employed to directly measure their activity profiles for CO oxidation at $100^{\circ}C$. SEM measurements with the synthetic $CoTiO_3$ and $CO_2TiO_4$ gave the respective tetragonal and rhombohedral morphology structures, in good agreement with the earlier XRD results. Weak Raman peaks at 239, 267 and 336 $cm^{-1}$ appeared on 5wt% $CoO_x/TiO_2$ after calcination at $570^{\circ}C$ but not on the catalyst calcined at $450^{\circ}C$, and these peaks were observed for the $Co_nTiO_{n+2}$ compounds, particularly $CoTiO_3$. All samples of the two cobalt titanate possessed O ls XPS spectra comprised of strong peaks at $530.0{\pm}0.1$ eV with a shoulder at a 532.2-eV binding energy. The O ls structure at binding energies near 530.0 eV was shown for a sample of 5 wt% $CoO_x/TiO_2$, irrespective to calcination temperature. The noticeable difference between the catalyst calcined at 450 and $570^{\circ}C$ is the 532.2 eV shoulder which was indicative of the formation of the $Co_nTiO_{n+2}$ compounds in the catalyst. No long-life activity maintenance of the synthetic $Co_nTiO_{n+2}$ compounds for CO oxidation at $100^{\circ}C$ was a good vehicle to strongly sup port the reason why the supported $CoO_x$ catalyst after calcination at $570^{\circ}C$ had been practically inactive for the oxidation reaction in our previous study; consequently, the earlier proposed model for the $CO_3O_4$ nanoparticles existing with the catalyst following calcination at different temperatures is very consistent with the characterization results and activity measurements with the cobalt titanates.

• Journal of the Korean Magnetics Society
• /
• v.10 no.5
• /
• pp.220-224
• /
• 2000

Ultra-fine $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$ferrite powders have been prepared by the sol-gel method. The crystallographic and magnetic properties of the sample have been investigated by means of x-ray diffraction, Mossbauer spetroscopy and vibrating sample magnetometry. The formation of nano crystallized particles is confirmed. The x-ray diffractions of all samples with various compositions clearly indicate the presence of spinel structure. The Mossbauer spectra could be fitted as the superposition of two sextets due to F $e^{3+}$ A-site and B-site. The IS and QS values nearly constant with substituted Co-Ti contents, whereas $H_{hf}$ of B-site decreases with increasing Co-Ti substitution in $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$. The magnetic behaviour of powders shows that the saturation magnetization and the coercivity decrease with increasing x in $Co_{1+x}$F $e_{2-}$2x/ $Ti_{x}$ $O_4$.$.X>.