• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06a
• /
• pp.519-521
• /
• 1996

Emerald (3BeO.Al2O3.6SiO2 : Cr3+) single crystals were crystals were grown by reflux method of temperature gradient in the flux solution of Li2O-MoO3-V2O5 system. The composition of flux materials were 3 mole ratio of MoO3-V2O5/Li2O, subtituted 0.2 mole% of K2O, Na2O, Nb2O5 etc to Li2O content, solved 10-15% of beryl to flux quantity and doped 1% of Cr2O3 to emerald amount. Those of mixing were melted at 110$0^{\circ}C$ in Pt containers of the 3 zone furnace of melt-growth-return to circulate continniously, specially it has been grown large emerald single crystal when thermal fluctuation was treated for 2hrs of once time a day at 1050-95$0^{\circ}C$ in growth zone, substitutional solid solution effect of Cr+3 ion for Al+3 to the growth of emerald single crystal was good. Emerald single crystals were c(0001) hexagonal crystal face of preferencial growth direction and m(1010) post side. When it had been durated for 5 months emerald single crystals of the firet size of 0.6mm thickness of seed crystal were grown 32$\times$65mm(c x m) of maximum size and 6.2mm thickness.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.1
• /
• pp.44-55
• /
• 1996

Emerald (3BeO{\cdot}Al$_{2}$O_{3}{\cdot}6SiO_2 : Cr^{3+}$) single crystals were grown by flux method of $Li_2O-MoO_3 - V_2O_5$ system. The composition of starting materials were 1, 3, 5 mole ratio of $MoO_3 - V_2O_5/$Li_2O$, 20 - 15% of emerald content to flux composition and 1% of $Cr_2O_3$ colordopant to emerald composition. After mixing those were melted at $1100^{\circ}C$ in Pt crucible of electric furnace. Single crystal growth was cooled down slowly rate of $3^{\circ}C$/hr from $1100^{\circ}C$ to $650^{\circ}C$, for the cooling period it was controlled and prevented the nucleation of microcrystallite from variation of each thermal fluctuation range. Specially it has been obtained plenty of large emerald single crystal when thermal fluctuation was treated for cooling period at $1050 ~ 950^{\circ}C$, in 3 mole ratio of $V_2O_5 - MoO_3/Li_2O$ flux. Emerald single crystal growing effect and $Cr_{+3}$ ion of substitutional solid solution effect for $Al_{+3}$ ion was good than mole ratio of 5. Emerald single crystals were c (0001) hexagonal rystal face of preferencial direction and m (1010) post side. Emerald was hexagonal columnar greenish transparent and 2.65 ~ 2.66 of specific gravity.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2003.11a
• /
• pp.221-225
• /
• 2003

The MFIS-FET(Field Effect Transistor) devices using $BLT/Y_2O_3$ buffer layer on p-Si(100) substrates were fabricated by the Sol-Gel method and conventional memory processes. The crystal structure, morphologies and electrical properties of prepared devices were investigated by using various measuring techniques. From the C-V(capacitance-voltage) data at 5V, the memory window voltage of the $Pt/BLT/Y_2O_3/si$ structure decreased from 1.4V to 0.6V with increasing the annealing temperature from $700^{\circ}C\;to\;750^{\circ}C$. The drain current (Ic) as a function of gate voltages $(V_G)$ for the $MFIS(Pt/BLT/Y_2O_3/Si(100))-FET$ devices at gate voltages $(V_G)$ of 3V, 4V and 5V, the memory window voltages increased from 0.3V to 0.8V as $V_G$ increased from 3V to 5V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.295-299
• /
• 1999

The (S $r_{1-x}$C $a_{x}$)Ti $O_3$(SCT) thin films are deposited on Pt-coated electrode(Pt/TiN/ $SiO_2$/ Si) using RF sputtering method with substitutional contents of Ca. The maximum grain of thin films is obtained by substitution of Ca at 15[mol%]. The dielectric constant was increased with increasing the substitutional contents of Ca, while it was decreased if the substitutional contents of Ca exceeded over 15[mo1%]. The dielectric constant changes almost linearly in temperature ranges of -80~ +90[$^{\circ}C$]. The temperature properties of the dielectric loss have a stable value within 0.02 independent of the substitutional contents of Ca. All SCT thin films used in this study show the phenomena of dielectric relaxation with the increase of frequency, and the relaxation frequency is observed above 200(kHz).)..

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.05a
• /
• pp.150-150
• /
• 2012

본 연구는 1차원 나노 구조의 합성과 기초적 분석에 관한 연구로써 특히 무기 산화물 나노재료를 그 대상으로 하였다. 내용으로는 첫째, 1차원 코어 나노와이어의 합성을 하였고 Thermal evaporation, substrate의 가열, 그리고 MOCVD 를 사용한 결과들을 나열한다. 둘째, 코어-쉘 나노와이어를 제작하기 위하여 특히 쉘층의 제작방법을 연구하였는데 PECVD, ALD, 그리고 sputtering에 의한 결과들을 나열하고 간단히 설명한다. Thermal evaporation에 의한 1차원 나노와이어 합성의 경우는 MgO의 예를 들었는데 MgO 나노와이어는 Au가 증착된 기판을 열처리하여 Au dot를 형성하고 이의 morphology를 조절하여 최적의 나노와이어 합성조건을 선정하였다. 이로써 기판 morphology가 나노선의 성장및 형상에 영향을 준다는 사실을 알게 되었다. 이 사실은 In2O3기판을 사용하고 이의 표면거칠기를 열처리로 조절하므로써 역시 나노와이어의 성장을 촉진하는 방법을 찾아내었다. 또한 thermal evaporation공법은 source분말의 선택에 따라 다양한 소재를 제작가능하다는 결과를 제시하였다. 예를 들면 SiOx 층이 precoating된 chamber내에서 MgO 나노선을 합성하는 것과 동일한 조건으로 실험을 진행하면 Mg2SiO4 나노와이어가 형성된 것을 확인하였다. 또한 Sn과 MgB2 분말을 함께 적용할 경우 Sn tip을 가진 MgO 나노와이어를 얻을 수 있었다. 이는 Sn이 동시에 촉매의 역할을 하였기 때문일 것으로 추정된다. 한편 Sn과 Bi 혼합분말을 적용한 경우 Bi2Sn2O7 신소재 tip을 포함한 SnO2 나노와이어를 얻을 수 있었다. 이 경우 Bi원자가 적절한 촉매의 역할을 수행한 것으로 사료된다. Substrate의 가열공법에서는 Si wafer상에 각종 금속 즉 Au, Ag, Cu, Co, Mo, W, Pt, Pd등 초박막을 DC sputter 로 형성한후 annealing하는 기술을 사용하였다. 특기할 만한 것은 Co를 사용한 경우 나노와이어의 spring구조를 얻을 수 있었다는 점이다. MOCVD에 의하여는 Ga2O3및 Bi2O3 나노와이어를 비교적 저온에서 합성하였고 In2O3의 경우는 독특한 나노구조를 형성하였고 이의 결정학적 특성에 대하여 조사하였다.

• Journal of the Korean Vacuum Society
• /
• v.4 no.S1
• /
• pp.145-150
• /
• 1995

PZT thin films were fabricated on Pt/Ti/SiO2/Si substrates at $500^{\circ}C$ by ECR-PECVD for the application to the charge storage capacitor of ULSI DRAMs. Perovskite single phase PZT films were obtained by controling the film compositional ratio Pb/(Zr+Ti) close to 1. The anion concentrations in the PZT films were successfully controlled by adjusting the flow rates of each MO sources. Capacitance of a typical 94 nm thick PZT film prepared at $500^{\circ}C$ in this work was about 5.3 uF/$\textrm{cm}^2$, which corresponds to the equivalent SiO2 thickness of 0.65nm.

• Economic and Environmental Geology
• /
• v.44 no.5
• /
• pp.373-386
• /
• 2011

Geochemical study was performed on black slates and interbedded U-bearing coaly slates in Deokpyeongri area, the representative uranium mineralized district of the Ogcheon Metamorphic Belt, to discuss the genetic environments of the uranium deposit. REE concentration (254 ppm) of the black slates is higher than that (169 ppm) of the coaly slates and NASC-normalized REE patterns of the coaly slates show remarkable positive Eu anomaly. l11e redox-sensitive trace elements such as V, Cr, Co, Ni, Mo and U in the coaly slates are highly enriched compared to the black slates, especially for V of 24 times, Mo of 62 times, and U of 60 times. In additions, Pd and Pt are also enriched in the coaly slates. Positive Eu anomaly and the noticeable enrichment of the elements listed above compared to those of NASC indicate that those elements were not derived from common seawater but deposited under high temperature and reducing environment of submarine hydrothermal activities. Wide compositional ranges of major elements ($SiO_2/Al_2O_3$: 3.98~11.88, $Al_2O_3/Na_2O$: 25.6~139.06, $K_2O/Na_2O$: 6.80~46.85) also suggest that the source rocks of the sediments are mixtures of sedimentary rocks and igneous rocks. Higher sulfur contents in the coaly slates, 2.6 wt.%, than those in the black slates, 0.6 wt.% also indicates that the former was influenced by hydrothermal activities containing much sulfur. These geochemical characteristics are similar to the genetic environments of South China type PGE deposits (Mo-Ni-Zn-PGE) which is geotectonically correlated with the Ogcheon Metamorphic Belt and is known as sedimentary-exhalative deposits. In conclusions, the uranium and other metallic elements mineralization seems to have occurred in the sedimentary basin that was affected by submarine hydrothermal activities and rich in organic materials under oxygen-poor environments as well.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.39 no.12
• /
• pp.1008-1015
• /
• 2002

The fabricated La-modified lead titanate (PLT) thin film without poling treatment was investigated for modulation frequency dependence of pyroelectric properties by the dynamic method. $Pb_{l-x}La_{x}Ti_{l-x/4}O_3$(x=0.1) (PLT(10)) thin film haying 10 mol% La content was deposited on a Pt/$TiO_{x}$/$SiO_2$/Si substrate by sol-gel method. The PLT(10) thin film exhibits a relatively excellent dielectric property. The pyroelectric coefficient (p) of the PLT(10) thin film is 6.6 x $10^{-9}C$$textrm{cm}^2$$.$K without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are 1.03 x $10^{-11}C$.cm/J and 1.46 x $10^{-10}C$.cm/J, respectively The PLT(10) thin film has voltage responsivity (RV) of 5.IS V/W at 8 Hz. Noise equivalent power (NEP) and specific detectivity ($D^{*}$) of the PLT(10) thin film are 9.93 x $10^{-8}$W/$Hz^{1/2}$ and 1.81 x $10^{6}$cm.$Hz^{1/2}$/W at the same frequency of 100 Hz,, respectively The results means that PLT thin film having 10 mol% La content is suitable for the sensing materials of pyroelectric IR sensors.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.413-413
• /
• 2011

최근 전기, 전자, 반도체 산업의 발전으로 전 고상 박막리튬전지는 초소형, 초경량의 마이크로 소자의 구현을 위한 고밀도 에너지원으로 각광받고 있다. 현재 양극박막은 대부분LCO(LiCoO2)계열이 이용되고 있으나, 코발트는 높은 가격과 인체 유해성 뿐만 아니라 상대적으로 낮은 용량(~140 mAh/g)등의 단점을 갖고 있어 향후 보다 고용량의 양극박막이 요구된다. 3원계 양극활물질 LiMO2(M=Co,Ni,Mn,etc.)은 우수한 충방전 효율 과 열적 안정성 뿐 아니라 277mAh/g의 높은 이론용량을 갖고 있어 고용량 양극박막으로의 적용시 고용량 박막이차전지 제작이 가능하다. 본 연구에서는 전 고상 박막 전지의 구현을 위하여 RF 스퍼터링법을 사용하여 Li[Li0.2Mn0.54Co0.13Ni0.13]O2 박막을 증착하였다. Li/MnCoNi의 몰 비율을 변화시켜 높은 전기화학적 특성을 갖는 분말을 합성하여 제조한 타겟으로 Pt/TiO2/SiO2/Si 기판위에 RF 스퍼터법을 이용하여 박막을 성장시켰다. 박막 증착 시 가스의 비율은 Ar:O2=3:1로 하고 증착 압력의 조절(0.005~0.02 torr)을 통하여 박막의 두께와 표면 특성을 조절하며 성장시켰다. 또한 박막을 다양한 온도에서($400{\sim}550^{\circ}C$) 열처리하여 결정화도와 전기화학적 특성을 측정하였다. 증착 된 박막의 구조적 특성은 X-ray diffraction(XRD) 과 scanning electron microscopy(SEM)로 관찰되었다. 박막의 전기화학적 특성 평가를 위하여 Cyclic voltammatry를 측정하여 가역성의 정도를 확인하고 WBC3000 battery cycler를 이용한 half-cell 테스트를 통하여 박막의 용량을 평가하였다.

• JSTS:Journal of Semiconductor Technology and Science
• /
• v.8 no.1
• /
• pp.66-79
• /
• 2008

Several oxides have recently been reported to have resistance-switching characteristics for nonvolatile memory (NVM) applications. Both binary and ternary oxides demonstrated great potential as resistive-switching memory elements. However, the switching mechanisms have not yet been clearly understood, and the uniformity and reproducibility of devices have not been sufficient for gigabit-NVM applications. The primary requirements for oxides in memory applications are scalability, fast switching speed, good memory retention, a reasonable resistive window, and constant working voltage. In this paper, we discuss several materials that are resistive-switching elements and also focus on their switching mechanisms. We evaluated non-stoichiometric polycrystalline oxides ($Nb_2O_5$, and $ZrO_x$) and subsequently the resistive switching of $Cu_xO$ and heavily Cu-doped $MoO_x$ film for their compatibility with modem transistor-process cycles. Single-crystalline Nb-doped $SrTiO_3$ (NbSTO) was also investigated, and we found a Pt/single-crystal NbSTO Schottky junction had excellent memory characteristics. Epitaxial NbSTO film was grown on an Si substrate using conducting TiN as a buffer layer to introduce single-crystal NbSTO into the CMOS process and preserve its excellent electrical characteristics.