• 한국전기전자재료학회논문지
• /
• 제26권11호
• /
• pp.826-830
• /
• 2013

In this paper, we carried out the investigations of both etch characteristics and mechanisms for the $SnO_2$ thin films in $O_2/BCl_3/Ar$ plasma. The dry etching characteristics of the $SnO_2$ thin films was studied by varying the $O_2/BCl_3/Ar$ gas mixing ratio. We determined the optimized process conditions that were as follows: a RF power of 700 W, a DC-bias voltage of - 150 V, and a process pressure of 2 Pa. The maximum etch rate was 509.9 nm/min in $O_2/BCl_3/Ar$=(3:4:16 sccm) plasma. From XPS analysis, the etch mechanism of the $SnO_2$ thin films in the $O_2/BCl_3/Ar$ plasma can be identified as the ion-assisted chemical reaction while the role of ion bombardment includes the destruction of the metal-oxide bonds as well as the cleaning of the etched surface form the reaction products.

• 한국전기전자재료학회논문지
• /
• 제14권9호
• /
• pp.695-699
• /
• 2001

Cerium dioxide (CeO$_2$) was used as the intermediate layer between the ferroelectric thin film and Si substrate in a metal-ferroelectric-semiconductor field effect transistor (MFSFET), to improve the interface property by preventing the interdiffusion of the ferroelectric material and the Si substrate. In this study, CeO$_2$ thin films were etched with a CF$_4$/Ar gas combination in inductively coupled plasma (ICP). The maximum etch rate of CeO$_2$ thin films was 270$\AA$/min under CF$_4$/(CF$_4$+Ar) of 0.2, 600 W/-200V, 15 mTorr, and $25^{\circ}C$. The selectivities of CeO$_2$ to PR and SBT were 0.21, 0.25, respectively. The surface reaction in the etching of CeO$_2$ thin films was investigated with x-ray photoelectron spectroscopy (XPS). There is a chemical reaction between Ce and F. Compounds such as Ce-F$_{x}$ remains on the surface of CeO$_2$ thin films. Those products can be removed by Ar ion bombardment. The results of secondary ion mass spectrometry (SIMS) were consistent with those of XPS. Scanning electron microscopy (SEM) was used to examine etched profiles of CeO$_2$ thin films. The etch profile of over-etched CeO$_2$ films with the 0.5${\mu}{\textrm}{m}$ line was approximately 65$^{\circ}$.>.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제36회 동계학술대회 초록집
• /
• pp.239-239
• /
• 2009

• 한국진공학회지
• /
• 제4권S2호
• /
• pp.115-130
• /
• 1995

In order to produce Cu nanocrystallite in silicon wafer, the implantation technique was used. The samples of silicon (100) wafers were implanted by $Cu^+$ ions at 100 keV and with varying the doses at room temperature. Post-annealing was performed at $800^{\circ}C$ with Ar environment. To investigate the formation of Cu nanocrystallite with ion doses and growth process by thermal annealing, SIMS and HRTEM(high resolution transmission electron microscopy)spectra were studied.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2005년도 제36회 하계학술대회 논문집 C
• /
• pp.2163-2165
• /
• 2005

A pulsed laser ablation deposition (PLAD) technique has been used for producing fine particle as well as thin film at relatively low substrate temperatures. However, in order to manufacture and evaluate such materials in detail, motions of plume particles generated by laser ablation have to be understood and interactions between the particles by ablation and gas plasma have to be clarified. Therefore, this paper was focused on the understanding of plume motion in laser ablation assisted by Ar plasma at 50(mTorr). Two-dimensional hybrid model consisting of fluid and particle models was developed and three kinds of plume particles which are carbon atom (C), ion $(C^+)$ and electron were considered in the calculation of particle method It was obtained that ablated $C^+$ was electrically captured in Ar plasmas by strong electric field (E). The difference between motions of the ablated electrons and $C^+$ made E strong and the collisional processes active.

• 한국전기전자재료학회논문지
• /
• 제20권11호
• /
• pp.991-994
• /
• 2007

In this paper, we have designed the anti-reflection(AR) coating for $1400{\sim}1600$ nm wavelength range on the ferrule facet of optical connector. The low-temperature ion-assisted deposition was applied to AR coating on the ferrule facet in order to avoid damage of optical connector. We have measured the refractive index of coating film($Ta_2O_5\;and\;SiO_2$) using the ellipsometer and optimized the film thickness using the SEM and thickness measurement equipment. UV-VIS-NIR spectrophotometer is used to measure transmissivity of the AR coated ferrule facet. The refractive index of $Ta_2O_5\;and\;SiO_2$ is $2.123{\sim}2.125$ and $1.44{\sim}1.442$, respectively, for $1400{\sim}1600$ nm wavelength range. The transmissivity of the AR coated ferule facet is more than 99.8 % for $1425{\sim}1575$ nm wavelength range and more than 99.5 % for $1400{\sim}1600$ nm wavelength range. The return loss of the AR coated ferrule facet is 30.1 dB.

• 한국전기전자재료학회논문지
• /
• 제24권6호
• /
• pp.445-448
• /
• 2011

In this study, the etching characteristics of $Al_2O_3$ thin films were investigated using an ICP (inductively coupled plasma) of $BCl_3$/Ar gas mixture. The etch rate of $Al_2O_3$ thin films as well as the $SiO_2/Al_2O_3$ etch selectivity were measured as functions of $BCl_3$/Ar mixing ratio (0~100% Ar) at a constant gas pressure (10 mTorr), total gas flow rate (40 sccm), input power (800 W) and bias power (100 W). The behavior of the $Al_2O_3$ etch rate was shown to be quite typical for ion-assisted etch processes with a dominant chemical etch pathway. To analyze the etching mechanism using DLP (double langmuir probe), OES (optical emission spectroscopy) and surface analysis using XPS (x-ray photoelectron spectroscopy) were carried out.

• 한국전기전자재료학회논문지
• /
• 제24권6호
• /
• pp.504-509
• /
• 2011

The conducting current of non-uniform plasma immersed electrode consists of ion current and secondary electron emission current caused by the impinging ion current. The ion current is determined by the ion dose passing through the sheath in front of electrode and the ion distribution in front of the electrode plays an important role in the secondary electron emission. The investigation of the distributed plasma and secondary electron effect on electrode ion current was carried out as the stainless steel electrode plugged with quartz tube was immersed in the inductively coupled Ar plasma using the antenna powered by 1 kw and the density profile was measured. After that, the negative voltage was applied by 1 kV~6 kV to measure the conduction current for the analysis of ion current.

• 한국세라믹학회지
• /
• 제37권5호
• /
• pp.418-424
• /
• 2000

Effects of Ar ion damage prior to the phase transformation from pyrochlore to perovskite structure of PZT thin films have been investigated. As the degree of damage increased by increasing the acceleration voltage in the ion mass doping system, the phase transformation temperature decreased such that the temperature could be lowered down to 550$^{\circ}C$ when the film was damaged at 15 kV for 5 minutes. When the film was damaged prior to the heat treatment grain size of the perovskite thin films became less than 300${\AA}$. It turned out that relatively high value of the remanent polarization (about 30${\mu}$C/$\textrm{cm}^2$) as well as improvement of the fatigue characteristics to a large extent is closely related to the fine grain size of thus obtained PZT films.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 춘계학술발표대회
• /
• pp.237.1-237.1
• /
• 2011

Resistivity of GaN has been investigated under the influence of ion implantation. n-type, p-type and also undoped GaN has been used here. A ring shape pattern of Au was fabricated on GaN film by the photolithography technique. H, He and Ar were used for implantation. The ion implantation energy, fluence and post-implant annealing temperature varied in this research. Because of the making barrier in some selected area using ions, the resistivity changed in all the samples with the change of both fluence and energy. At room temperature, the resistivity of n-type GaN has been increased from $1.9{\times}10-2$ to $17.7{\times}10-2\;{\Omega}-cm$. This is high for He ion. But undoped and p-type GaN showed some anomalous character.