·EC's/Japanese environmental regulation drive the Pb-free/Halogen-free application ·Most Japanese electronics companies are preparing the green products. ·All items concerning to Pb-free/halogen-free technology should be coparallely designed and developed. ·More works need to clear the unknowns on Pb-free materials ·Need of consensus on materials and standards ·EBM (Environmental Benign Manufacturing)

Cu is considered as a promising alternative interconnection material to Al-based interconnection materials in Si-based integrated circuits due to its low resistivity and superior resistance to the electromigration. New humping and UBM material systems for solder flip chip interconnection of Cu pads were investigated using electroless-plated copper (E-Cu) and electroless-plated nickel (E-Ni) plating methods as low cost alternatives. Optimally designed E-Ni/E-Cu UBM bilayer material system can be used not only as UBMs for solder bumps but also as bump itself. Electroless-plated E-Ni/E-Cu bumps assembled using anisotropic conductive adhesives on an organic substrate is successfully demonstrated and characterized in this study

본 연구에서는 무전해도금으로 증착된 구리박막의 열적 및 접착특성에 관하여 고찰하였다. Si 기판에 MOCVD 방법으로 TaN 확산방지막을 증착한 후, 무전해 도금으로 구리박막을 증착하여 Cu/TaN/Si 다층구조를 제조공정하였다. 그리고, Ar 분위기에서 열처리시켰으며, 열처리온도에 따른 비저항 변화를 고찰함으로서 Cu/TaN/Si 계의 열적 특성을 분석하였다. 무전해도금 구리박막의 접착특성은 스크래치 테스트에 의해 평가하였으며, 열적 증착방법과 스퍼터 방법으로 증착된 구리 박막과 비교하였다. 스크래치 테스트 결과, 무전해도금 구리 박막의 접착력이 열적 증착과 스퍼터 방법으로 증착된 구리 박막보다 더 우수하였다.

A 355 nm (3.5 eV) neodymium:yttrium aluminum gamet laser, produced by a harmonic generator, was used to create silver metallic particles as seeds for nucleation in photosensitive glass containing Ag+ and Ce3+ ions. The pulse width and frequency of the laser were 8 ns and 10 Hz, respectively. Heat treatment was conducted at 570 C for 1 h, following laser irradiation, to produce crystalline growth, after which a LiAlSi3O8 crystal phase appeared in the laser-irradiated Li2O A1203 SiO2 glass. For the Present study, we compared the effect of laser-induced crystallization on glass crystallization with that of spontaneous crystallization by heat treatment.

ECR(electron cyclotron resonance) 플라즈마 식각 장비를 이용하여 SF$_{6}$/Ar과 Cl$_2$/Ar 플라즈마 가스에 대한 Platinum (이하 Pt) 박막의 식각 특성을 연구하였다. Pt 박막의 경우 Cl$_2$ 가스 혼합물에 대한 식각 특성은 많이 보고가 되어 왔으나 상대적으로 Fluorine 계열의 가스 혼합물에 의한 시각 연구는 미비하였다. 본 연구에서는 SF$_{6}$/Ar과 Cl$_2$/Ar 플라즈마 가스를 이용한 Pt 박막의 식각 특성을 비교 분석하고 각각의 가스와 Pt 박막과의 반응을 분석, 식각 특성을 개선하고자 하였다.

졸-겔법으로 Pt/Ti/$SiO_2$/Si 기판위에 $Bi_{3.7}$/$La_{0.75}$$Ti_3O_{12}$(BLT) 강유전체 박막을 형성하였다. As-coated BLT 박막은 $600^{\circ}C$의 후속 열처리온도에서 결정화 되었으며 전형적인 Bi 층상 페롭스카이트 결정구조를 나타내었다. 또한 후속 열처리온도를 증가함에 따라 결정성이 향상되었다. $700^{\circ}C$의 온도에서 후속 열처리된 BLT 박막의 비 유전상수($\varepsilon_{r}$)와 유전손실($\textrm{tan}\delta$)은 5KHz 주파수에서 약 402와 0.04를 각각 나타내었다 $800^{\circ}C$에서 후속 열처리된 BLT박막의 경우 5V의 인가 전압에서 잔류분극 2Pr($Pr^{+}$-$Pr^{-}$)값은 약 32.5$\mu$C/$Cm^2$을 나타내었다.

Chip-on-glass(COG) mounting of area array electronic packages was attempted by heating the rear surface of a contact pad film deposited on a glass substrate. The pads consisted of an adhesion(i.e. Cr or Ti) and a top coating layer(i.e. Ni or Cu) was heated by an UV laser beam transmitted through the glass substrate. The laser energy absorbed on the pad raised the temperature of a solder ball which is in physical contact with the pad, forming a reflowed solder bump. The effects of the adhesion and top coating layer on the laser reflow soldering were studied by measuring temperature profile of the ball during the laser heating process. The results were discussed based on the measurement of reflectivity of the adhesion layer. In addition, the microstructures of solder bumps and their mechanical properties were examined.

솔더볼의 피로강도에 대한 솔더 조성의 영향을 조사하기 위하여 패키지 신뢰성 시험을 실시하였다. 공정조성 솔더, S $n_{62}$P $b_{36}$A $g_2$, S $n_{63}$P $b_{34.5}$A $g_2$S $b_{0.5}$ 솔더를 사용해 제조된 시편을 MRT Lv 2a 조건에서 전처리 후 TC 시험을 수행하였다. 제조 직후, 전처리 후, TC 후 각각에 대하여 전단강도를 측정하였으며, 미세 조직 사진을 얻었다. 또한, SEM과 EDX를 이용하여 파괴 기구에 대한 분석을 실시하였으며, 신뢰성 시험 후 전단강도의 저하에 대하여 논의하였다.다.

Using the photoimageable thick film conductors, $25\mu\textrm{m}$ line widths and $25\mu\textrm{m}$ spaces can be obtained. Test patterns are made by green tape lamination, paste printing, exposing to UV light, developing in an aqueous process and cofiring. Postfiring method using alumina substrate can be also applied to fine line formation. Series gap resonator formed by photopatterning process showed the improved signal transmission characteristics compared to that obtained by conventional screen printing.

APF optical link용 receiver를 하나의 바이폴라 칩으로 실현하기 위하여 수신파장 영역에서 고속.고감도 특성을 갖는 바이폴라 집적용 Si photodiode를 에피 두게 6$\mu\textrm{m}$(epi06)와 12$\mu\textrm{m}$(epi12)로 제작하고 이의 전기.광학적 특성을 조사하였다. 제작된 소자의 전기.광학적 특성을 -5 V의 동작전압에서 측정한 결과, 6 $\mu\textrm{m}$ 에피두께의 경우 접합커패시턴스와 암전류가 각각 4.8 pF와 2.6 pA로 나타났으며, 광신호 전류와 감도특성은 670 nm의 중심파장을 갖는 3.15 ㎼의 입사광 전력 아래에서 각각 0.568 $\mu\textrm{A}$와 0.18 A/W로 나타났다. 에피층의 두께가 12 $\mu\textrm{m}$의 경우 접합커패시턴스와 암전류는 각각 9.8 pF와 171.3 pA로 나타났으며, 광신호 전류와 감도특성은 3.679$\mu\textrm{A}$와 1.17 A/W로 나타났다. 제작된 두 소자는 적색 파장(λ$_{p}$=670nm)부근에서 최대 spectral response(λ$_{p}$=600nm at epi06, λ$_{p}$=700nm at epi12)를 보이고 있다.이고 있다.