The combination of mechano-chemical activation (MCA)and Self-propagating High-temperature Synthesis (SHS) has widened the technical possibilities for both methods. For YBCO systems the investigation showed that a short-term MCA of initial powders before SHS leads to single-phase and ultra-fine products. A new technique for preparation ultra-fine high-temperature superconductors (HTS) of YBCO composition with a grain size d <1m is developed using combination of MCA and SHS. The specific feature of the technique is formation of the $YBa_2Cu_3O_7-$ crystalline lattice directly from an X-ray amorphous state arising as a result of mechanical activation of the original oxide mixture. The technique allows the stage of formation of any intermediate reaction products to be ruled out. X-ray and magnetic studies of ultra-fine high temperature superconductors are carried out. Dimension effects associated with the microstructure peculiarities are revealed. A considerable enhancement of inter-grain critical currents is found to take place in the ultra-fine samples.

The materials showing high structure dispersion with functional properties were developed on the quartz base and those were obtained by mechano-chemical reaction technology. Depending on the processing conditions and subsequent applications the materials produced by mechano-chemical reaction show concurrently magnetic, dielectric and electrical properties. The obtained magnetic-electrical powders classified by aggregate complex of their features as segnetomagnetics, containing a dielectric material as a carrying nucleus, particularly the quartz on that surface one or more layers of different compounds were synthesized having thickness up to 1050nm showing magnetic, electrical properties and others. The similarity of the structure of surface layers of quartz particles subjected to mechano-chemical processing and nano-structure cluspol (clusters in a polymer matrics) material was alsoconfirmed by the fact that the characteristics of ferromagnetic quartz of insulating nano-composite powder were changed with time, after its preparing process was completed.

The melting temperature and critical temperature (Tc) of $YBa_2Cu_3O_x$ with deferent content impurities of PbO and $BaPbO_3$ were studied. When the PbO was used as addition in $YBa_2Cu_3O_x$, although the melting point could be reduced, the superconductivity (the transition wide, ${\Delta}T_c$) became poor. From the XRD pattern of the sintered mixture of $YBa_2Cu_3O_x$ and PbO it was known that there is a reaction between $YBa_2Cu_3O_x$ and PbO, and the product is $BaPbO_3$. In the process of the reaction the superconducting phase of $YBa_2Cu_3O_x$ was decreased and in the sample $BaPbO_3$ became the main phase. Therefore the superconductivity was reduced. $BaPbO_3$ was chosen as the impurity for the comparative study. The single phase $BaPbO_3$ was synthesized by the simple way from both mixtures of $BaCO_3$ and PbO, $BaCO_3$ and $PbO_2$. Deferent contents of $BaPbO_3$ (10%, 20%, 30%) were added in the $YBa_2Cu_3O_x$. By the phase analysis in the XRD patterns it was proved that there were not reactions between $YBa_2Cu_3O_x$ and $BaPbO_3$. When $BaPbO_3$ was used as impurity in $YBa_2Cu_3O_x$ the superconductivity was much better than PbO as impurity in $YBa_2Cu_3O_x$. But the melting point of $YBa_2Cu_3O_x$ with $BaPbO_3$ could not be found when the temperature was lower than $1000^{\circ}C$ in the DTA measurement.

In this paper, we have investigated the characteristics of the magnetic abrasive using sludge on polishing of internal finishing of seamless stainless steel tube applying magnetic abrasive polishing. Either white alumina grain was used to resin sludge at a low temperature, and the sludge of magnetic abrasive powder was synthesized and crushed into 200 meshes. Surface roughness was measured before and after polishing, and more than 40% of improvement of surface roughness was achieved when grain was used under a specific condition. Even though some degree of surface roughness due to deeper scratches still exist, but the result showed a prospective magnetic abrasive polishing using sludge with white alumina grains.

This paper is devoted to a study of the characterization of the plasma state. For the purpose of monitoring plasma condition, we experiment on reactive ion etching (RIE) process. Without actual etch process, generated oxygen plasma, measurement of plasma emission intensity. Changing plasma process parameters, oxygen flow, RF power and chamber pressure have controlled. Using the optical emission spectroscopy (OES), we conform to the unique oxygen wavelength (777nm), the most powerful intensity region of the designated range. Increase of RF power and chamber pressure, emission intensity is increased. oxygen flow is not affect to emission intensity.

Alpine caves, subterranean passages, are extensively controlled by folds and faults. Caves of the regions demonstrate a significant dip of the passages due to the structural deformations. There are many vertical voids and shaft. Speleo-scapes in the internal caves are various. Calcite formations show the water table alternations which indicate the uplifting and erosional base level droppings during at least the Quaternary. Around cave entrenches there are remnants of the Fluvial terraces on the middle of the hills. These relationship between cave locations and terraces will generate a key to the Plestocene history of the south Korean peninsula. Hence, the Korean karst is turned as "the overburden alpine karst".